CN102978351A - 一种提高钢材韧性的热处理方法 - Google Patents
一种提高钢材韧性的热处理方法 Download PDFInfo
- Publication number
- CN102978351A CN102978351A CN 201210491086 CN201210491086A CN102978351A CN 102978351 A CN102978351 A CN 102978351A CN 201210491086 CN201210491086 CN 201210491086 CN 201210491086 A CN201210491086 A CN 201210491086A CN 102978351 A CN102978351 A CN 102978351A
- Authority
- CN
- China
- Prior art keywords
- steel
- temperature
- quenching
- heat treatment
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种提高钢材韧性的热处理方法，其特征在于包括以下热处理步骤：（1）所述钢材经过粗加工后，置于加热炉内预热，在650℃～800℃升温预热，持续8小时；（2）所述钢材预热处理后进行高温淬火，淬火温度在900℃～950℃，保温3小时；（3）将所述钢材保温炉中，将炉内温度升至300℃～450℃，进行保温处理，持续6小时；（4）所述钢材保温处理后，在保温炉温降至80℃～120℃后，将所述钢材从炉内取出，空冷至室温。本发明所述的热处理方法采用高温淬火油淬火，使热处理后的钢材韧性提高，是一种工业中使用的热处理方法。
Description
技术领域
本发明涉及一种工业中使用的热处理方法。
背景技术
现有的钢材在工业生产中和日常生活中都有广泛的应用，因此钢材的性能是非常重要的，但现有的钢材在使用的过程中，往往因为韧性的不够在压力或拉力过大的情况下会导致钢材的断裂，所以怎样提高钢材的韧性成为了人们急待解决的问题。
发明内容
本发明对以上问题的提出，而研究设计一种热处理方法，用以解决现有的热处理方法生产的钢材韧性不够，往往在使用的过程中容易断裂的缺点。本发明采用的技术手段如下：
一种提高钢材韧性的热处理方法，其特征在于包括以下热处理步骤：
（1）所述钢材经过粗加工后，置于加热炉内预热，在650℃～800℃升温预热，持续8小时；
（2）所述钢材预热处理后进行高温淬火，淬火温度在900℃～950℃，保温3小时，将钢材置于450℃～600℃的高温淬火油中淬火，使淬火油和钢材同时放在空气中冷却，当钢材冷却到80℃～120℃时，从淬火油中取出钢材，空冷至室温；
（3）将所述钢材保温炉中，将炉内温度升至300℃～450℃，进行保温处理，持续6小时；
（4）所述钢材保温处理后，在保温炉温降至80℃～120℃后，将所述钢材从炉内取出，空冷至室温。
作为优选所述步骤（2）中所述的空冷至室温，还可以是水冷。
与现有技术比较，本发明所述的热处理方法采用高温淬火油进行淬火，并且将淬火油和钢材同时放在空气中冷却，加强了钢材的韧性。
本发明具有简单易行，可用于工业批量生产，适于规模化工业生产的需要，具有较高的工程应用价值，其投入市场必将产生显著地社会效益和经济效益。
具体实施方式
实施例1，一种提高钢材韧性的热处理方法，其特征在于包括以下热处理步骤：
（1）所述钢材经过粗加工后，置于加热炉内预热，在650℃～800℃升温预热，持续8小时；
（2）所述钢材预热处理后进行高温淬火，淬火温度在900℃～950℃，保温3小时，将钢材置于450℃～600℃的高温淬火油中淬火，使淬火油和钢材同时放在空气中冷却，当钢材冷却到80℃～120℃时，从淬火油中取出钢材，空冷至室温；
（3）将所述钢材保温炉中，将炉内温度升至300℃～450℃，进行保温处理，持续6小时；
（4）所述钢材保温处理后，在保温炉温降至80℃～120℃后，将所述钢材从炉内取出，空冷至室温。
所述步骤（2）中所述的空冷至室温，还可以是水冷。
与现有技术比较，本发明所述的热处理方法采用高温淬火油进行淬火，并且将淬火油和钢材同时放在空气中冷却，加强了钢材的韧性。可用于工业批量生产，适于规模化工业生产的需要，具有较高的工程应用价值，其投入市场必将产生显著地社会效益和经济效益。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (2)
1.一种提高钢材韧性的热处理方法，其特征在于包括以下热处理步骤：
（1）所述钢材经过粗加工后，置于加热炉内预热，在650℃～800℃升温预热，持续8小时；
（2）所述钢材预热处理后进行高温淬火，淬火温度在900℃～950℃，保温3小时，将钢材置于450℃～600℃的高温淬火油中淬火，使淬火油和钢材同时放在空气中冷却，当钢材冷却到80℃～120℃时，从淬火油中取出钢材，空冷至室温；
（3）将所述钢材保温炉中，将炉内温度升至300℃～450℃，进行保温处理，持续6小时；
（4）所述钢材保温处理后，在保温炉温降至80℃～120℃后，将所述钢材从炉内取出，空冷至室温。
2.根据权利要求1所述的一种钢材的防氧化热处理方法，其特征在于：所述步骤（2）中所述的空冷至室温，还可以是水冷。