CN102931399A - 铅酸蓄电池正极铅膏的配方 - Google Patents
铅酸蓄电池正极铅膏的配方 Download PDFInfo
- Publication number
- CN102931399A CN102931399A CN2012104563980A CN201210456398A CN102931399A CN 102931399 A CN102931399 A CN 102931399A CN 2012104563980 A CN2012104563980 A CN 2012104563980A CN 201210456398 A CN201210456398 A CN 201210456398A CN 102931399 A CN102931399 A CN 102931399A
- Authority
- CN
- China
- Prior art keywords
- lead
- oxide
- acid battery
- prescription
- improved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铅酸蓄电池正极铅膏的配方，其特征在于：包括以下组份，各组分重量百分比为：铅粉：70%～75%；铝的氧化物：2%～6%；导电纤维：0.05%～0.1%；硫酸：5%～8%；三氧化二锑：0.1%～0.6%；二氧化硅：0.005%～0.01%；硫酸镁：0.005%～0.01%；硫酸钾：0.005%～0.01%；其余：去离子水。本发明的优点是：除正常的组份外，还加入了新型材料三氧化二锑、SiO2、MgSO4、K2SO4，以增强极板结构强度，增加极板中活性物质孔隙，提高正极活性物质的容量，减少容量衰减，提高正板性能，延长蓄电池一次放电时间和使用寿命，提高蓄电池的动力。
Description
技术领域
本发明涉及一种铅酸蓄电池正极铅膏的配方。
背景技术
目前的电动车配套的电池多铅酸蓄电池，该种电池的一次性充电续行里程约在50—60公里，使用寿命约在8—10个月，使用寿命过短，不能满足用户要求。电池在正常情况下使用，寿命应在15—24个月，该类电池之所以续行里程和使用使用寿命都短于一般电池，主要是因为蓄电池在较大功率下持续使用，电池的使用负荷过大，超出了电池的承受能力，导致电池放电容量下降，而导致电池容量下降的主要原因是正极板功能下降。因此，如何提高电池正极板的功能是当今急需解决的技术问题。
发明内容
本发明的目的在于提高一种正极铅膏的配方，能有效地解决现有蓄电池放电时间短、动力弱等问题。
为解决上述技术问题，本发明是通过以下技术方案来实现的：
铅酸蓄电池正极铅膏的配方，包括以下组份，各组分重量百分比为：
铅粉 70%～75%
铝的氧化物 2%～6%
导电纤维 0.05%～0.1%
硫酸 5%～8%
三氧化二锑 0.1%～0.6%
二氧化硅 0.005%～0.01%
硫酸镁 0.005%～0.01%
硫酸钾 0.005%～0.01%
其余 去离子水。
优选地，各组分重量百分比为：
铅粉 73%
铝的氧化物 4%
导电纤维 0.08%
硫酸 6%
三氧化二锑 0.5%
二氧化硅 0.008%
硫酸镁 0.008%
硫酸钾 0.008%
其余 去离子水。
进一步的，所述铅的氧化物为二氧化铅或红丹。
进一步的，所述硫酸的质量百分比浓度为45%。
进一步的，所述导电纤维为聚乙炔纤维、聚吡咯纤维、聚噻吩纤维中的一种。
本发明的优点是：除正常的组份外，还加入了新型材料三氧化二锑、SiO2、MgSO4、K2SO4，以增强极板结构强度，增加极板中活性物质孔隙，提高正极活性物质的容量，减少容量衰减，提高正板性能，延长蓄电池一次放电时间和使用寿命，提高蓄电池的动力。
具体实施方式
实施例1
铅酸蓄电池正极铅膏的配方，包括以下组份，各组分重量百分比为：
铅粉 70%
二氧化铅 6%
聚乙炔纤维 0.1%
质量浓度为45%的硫酸 5%
三氧化二锑 0.1%
二氧化硅 0.005%
硫酸镁 0.005%
硫酸钾 0.005%
其余 去离子水。
实施例2
铅酸蓄电池正极铅膏的配方，包括以下组份，各组分重量百分比为：
铅粉 73%
红丹 4%
聚吡咯纤维 0.08%
质量浓度为45%的硫酸 6%
三氧化二锑 0.5%
二氧化硅 0.008%
硫酸镁 0.008%
硫酸钾 0.008%
其余 去离子水。
实施例3
铅酸蓄电池正极铅膏的配方，包括以下组份，各组分重量百分比为：
铅粉 75%
二氧化铅 2%
聚噻吩纤维 0.05%
质量浓度为45%的硫酸 8%
三氧化二锑 0.6%
二氧化硅 0.01%
硫酸镁 0.01%
硫酸钾 0.01%
其余 去离子水。
Claims (5)
1.铅酸蓄电池正极铅膏的配方，其特征在于：包括以下组份，各组分重量百分比为：
铅粉 70%～75%
铝的氧化物 2%～6%
导电纤维 0.05%～0.1%
硫酸 5%～8%
三氧化二锑 0.1%～0.6%
二氧化硅 0.005%～0.01%
硫酸镁 0.005%～0.01%
硫酸钾 0.005%～0.01%
其余 去离子水。
2.根据权利要求1所述的铅酸蓄电池正极铅膏的配方，其特征在于：各组分重量百分比为：
铅粉 73%
铝的氧化物 4%
导电纤维 0.08%
硫酸 6%
三氧化二锑 0.5%
二氧化硅 0.008%
硫酸镁 0.008%
硫酸钾 0.008%
其余 去离子水。
3.根据权利要求1或2所述的铅酸蓄电池正极铅膏的配方，其特征在于：所述铅的氧化物为二氧化铅或红丹。
4.根据权利要求1或2所述的铅酸蓄电池正极铅膏的配方，其特征在于：所述硫酸的质量百分比浓度为45%。
5.根据权利要求1或2所述的铅酸蓄电池正极铅膏的配方，其特征在于：所述导电纤维为聚乙炔纤维、聚吡咯纤维、聚噻吩纤维中的一种。