CN102922584A - Processing method of elastic bamboo floor - Google Patents
Processing method of elastic bamboo floor Download PDFInfo
- Publication number
- CN102922584A CN102922584A CN2012104305372A CN201210430537A CN102922584A CN 102922584 A CN102922584 A CN 102922584A CN 2012104305372 A CN2012104305372 A CN 2012104305372A CN 201210430537 A CN201210430537 A CN 201210430537A CN 102922584 A CN102922584 A CN 102922584A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- floor
- bamboo floor
- elastic
- bark
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing method of an elastic bamboo floor. The processing method comprises the following steps of: (1) preparation of an elastic material: uniformly spreading eucommea rubber powder on hard foam plastic or honeycomb paper, warming for 1 to 2 hours at the temperature of 70 to 80 DEG C, and dipping eucommea rubber into the hard foam plastic or the honeycomb paper, and then cooling to be at room temperature, so as to obtain an elastic material, wherein 500 to 800g/m2 of eucommea rubber powder is used; (2) preparation of bamboo floor blank: processing laminated bamboo materials or integrated materials to obtain a floor blank; and (3) formation of elastic floor: coating eucommea rubber liquid on the single surface of the bamboo floor blank, and immediately assembling according to the structure of the elastic bamboo floor, and then forming in a cold pressing way, wherein 80 to 120g/m2 of eucommea rubber liquid is used; the cold pressing is carried out for 5 to 10 seconds at the room temperature under 3.0 to 1.0MPa. The processing method is easy to implement, the operation is convenient, and the production cost is low.
Description
Technical field
The present invention relates to the processing method on a kind of elastic bamboo floor, specifically, relate to a kind of bionical Culm, preparation has the method on certain flexible bamboo floor.
Background technology
The utilization of bamboo wood has former bamboo to utilize and processing and utilization two classes.Former bamboo utilizes, and bamboo wood is that big bamboo is used as construction material, transportation bamboo raft, liquid-transport pipe-line; Middle or small bamboo wood is made stationery, musical instrument, farm implements, bamboo weaving etc.Processing and utilization has multiple use, but such as bamboo laminated board manufacturing machine wear part etc.; Bamboo-wood plyboard was once made First bamboo wood single-blade advaced trainer; Artificial bamboo board can be made the engineering material.Tabasheer also can be made into the kinds of processes artistic products in addition.Bamboo wood also is the important source material of papermaking, fibreboard made and acetate fiber, nitrocellulose.The bamboo charcoal case hardness is higher than charcoal, can be used for metallurgy industry and produces active carbon.
Bamboo stalk merogenesis is internode (seeing bamboo) between two joints.The stalk wall cross section of internode is from being outside to inside: epidermis, hypodermic layer, cortex, basic parenchymal tissue (vascular bundle is wherein arranged) and marrow ring.The vascular bundle of joint is outwards or inwardly slightly existing crooked, also has to enter joint and appear again every tortuous.Joint every the vascular bundle outer rim close, central authorities dredge, diameter and direction are without fixed; Being divided into many withes, circuitous being woven into nettedly, is the main thoroughfare of bamboo liquid lateral flow.Joint every substantially parenchymatous cell thickening hardening.
Studies show that epidermis and cortex hardness are larger, and hypodermic layer, substantially parenchymatous hardness are less, if according to the floor of Culm preparation, comfortable foot feeling can increase substantially the commercial value on bamboo floor.The present patent application people has carried out scientific research and research of technique for many years to bamboo floor process technology, utilize gutta-percha high resiliency characteristic, finally invented this technology, this technique is easy to realization, easy to operate, realize the maximization commercial exploitation of bamboo timber resource, provide technical support for increasing woods people income.
Summary of the invention
Technical problem to be solved by this invention provides and a kind ofly is easy to realize, the processing method on easy to operate, elastic bamboo floor that production cost is low.
In order to solve the problems of the technologies described above, the processing method on a kind of elastic bamboo floor that the present invention adopts, the elastic bamboo floor is that bamboo floor blank, middle level are that elastomeric material and lower floor are that three layers of bamboo floor blanks form by the upper strata, is comprised of following steps:
(1) elastomeric material preparation: on rigid foam or honeycomb paper, evenly sprinkle bark of eucommia rubber powder, 70 ℃～80 ℃ lower temperatureization processing 1 hour～2 hours, gutta-percha is immersed in rigid foam or the honeycomb paper, then be cooled to room temperature, namely get elastomeric material; Rigid foam or honeycomb paper specification are length 60cm～120cm, width 10cm～50cm, thickness 1mm～2.5mm; Bark of eucommia rubber powder use amount 500g/m
2～800g/m
2
(2) bamboo floor blank: bamboo wood level material or integrated timber are processed into the floor blank, and its specification is length 60cm～120cm, width 10cm～50cm, thickness 3mm～7mm;
(3) resiliently-mounted floor moulding: apply bark of eucommia glue at bamboo floor blank material list face, according to elastic bamboo floor panel structure assembly, cold moudling gets final product immediately, bark of eucommia glue use amount 80g/m
2～120g/m
2The condition of colding pressing is pressure 0.3MPa～1.0MPa, room temperature, time 5s～10s.
Adopt the processing method on the elastic bamboo floor of technique scheme, be easy to realize, easy to operate, production cost is low, is fit to large-scale production, improves bamboo floor commercial value, realize simultaneously the utilization of largeizationr of eucommia resource economy, can increase self-employed tree cultivator's income, significant to building a harmonious society.This invention can produce significant economic and social profit, has good promotional value.
In sum, the present invention be a kind ofly be easy to realize, the processing method on easy to operate, elastic bamboo floor that production cost is low.
Description of drawings
Fig. 1 is the structural representation on elastic bamboo floor.
The specific embodiment
Can further be expressly understood the present invention by specific embodiments of the invention given below, but following embodiment is not limitation of the invention.
Embodiment 1:
The processing method on a kind of elastic bamboo floor, referring to Fig. 1, the elastic bamboo floor is that the first bamboo floor blank 1, middle level are that elastomeric material 2 and lower floor are that three layers of the second bamboo floor blank 3 form by the upper strata, is comprised of following steps:
(1) elastomeric material preparation: on rigid foam, evenly sprinkle bark of eucommia rubber powder, 70 ℃ of lower temperatureization processing 2 hours, gutta-percha is immersed in rigid foam or the honeycomb paper, then be cooled to room temperature, namely get elastomeric material; Rigid foam or honeycomb paper specification are length 60cm, width 10cm, thickness 1mm; Bark of eucommia rubber powder use amount 500g/m
2
(2) bamboo floor blank: bamboo wood level material or integrated timber are processed into the floor blank, and its specification is length 60cm, width 10cm, thickness 3mm;
(3) resiliently-mounted floor moulding: apply bark of eucommia glue at bamboo floor blank material list face, according to elastic bamboo floor panel structure assembly shown in Figure 1, cold moudling gets final product immediately, bark of eucommia glue use amount 80g/m
2The condition of colding pressing is pressure 0.3MPa, room temperature, time 5s.
Embodiment 2:
The processing method on a kind of elastic bamboo floor, referring to Fig. 1, the elastic bamboo floor is that the first bamboo floor blank 1, middle level are that elastomeric material 2 and lower floor are that 3 three layers of the second bamboo floor blanks form by the upper strata, is comprised of following steps:
(1) elastomeric material preparation: on rigid foam, evenly sprinkle bark of eucommia rubber powder, 75 ℃ of lower temperatureization processing 1.5 hours, gutta-percha is immersed in rigid foam or the honeycomb paper, then be cooled to room temperature, namely get elastomeric material; Rigid foam or honeycomb paper specification are length 80cm, width 20cm, thickness 2.0mm; Bark of eucommia rubber powder use amount 600g/m
2
(2) bamboo floor blank: bamboo wood level material or integrated timber are processed into the floor blank, and its specification is length 80cm, width 20cm, thickness 4mm;
(3) resiliently-mounted floor moulding: apply bark of eucommia glue at bamboo floor blank material list face, according to elastic bamboo floor panel structure assembly shown in Figure 1, cold moudling gets final product immediately, bark of eucommia glue use amount 90g/m
2The condition of colding pressing is pressure 0.5MPa, room temperature, time 6s.
Embodiment 3:
The processing method on a kind of elastic bamboo floor, referring to Fig. 1, the elastic bamboo floor is that the first bamboo floor blank 1, middle level are that elastomeric material 2 and lower floor are that 3 three layers of the second bamboo floor blanks form by the upper strata, is comprised of following steps:
(1) elastomeric material preparation: on honeycomb paper, evenly sprinkle bark of eucommia rubber powder, 78 ℃ of lower temperatureization processing 1 hour, gutta-percha is immersed in rigid foam or the honeycomb paper, then be cooled to room temperature, namely get elastomeric material; Rigid foam or honeycomb paper specification are length 100cm, width 40cm, thickness 2.0mm; Bark of eucommia rubber powder use amount 700g/m
2
(2) bamboo floor blank: bamboo wood level material or integrated timber are processed into the floor blank, and its specification is length 100cm, width 40cm, thickness 5mm;
(3) resiliently-mounted floor moulding: apply bark of eucommia glue at bamboo floor blank material list face, according to elastic bamboo floor panel structure assembly shown in Figure 1, cold moudling gets final product immediately, bark of eucommia glue use amount 100g/m
2The condition of colding pressing is pressure 0.8MPa, room temperature, time 8s.
Embodiment 4:
The processing method on a kind of elastic bamboo floor, referring to Fig. 1, the elastic bamboo floor is that the first bamboo floor blank 1, middle level are that elastomeric material 2 and lower floor are that 3 three layers of the second bamboo floor blanks form by the upper strata, is comprised of following steps:
(1) elastomeric material preparation: on honeycomb paper, evenly sprinkle bark of eucommia rubber powder, 80 ℃ of lower temperatureization processing 1 hour, gutta-percha is immersed in rigid foam or the honeycomb paper, then be cooled to room temperature, namely get elastomeric material; Rigid foam or honeycomb paper specification are length 120cm, width 50cm, thickness 2.5mm; Bark of eucommia rubber powder use amount 800g/m
2
(2) bamboo floor blank: bamboo wood level material or integrated timber are processed into the floor blank, and its specification is length 120cm, width 50cm, thickness 7mm;
(3) resiliently-mounted floor moulding: apply bark of eucommia glue at bamboo floor blank material list face, according to elastic bamboo floor panel structure assembly shown in Figure 1, cold moudling gets final product immediately, bark of eucommia glue use amount 120g/m
2The condition of colding pressing is pressure 1.0MPa, room temperature, time 10s.
Claims (1)
1. the processing method on an elastic bamboo floor, the elastic bamboo floor is that bamboo floor blank, middle level are that elastomeric material and lower floor are that three layers of bamboo floor blanks form by the upper strata, it is characterized in that: be comprised of following steps:
(1) elastomeric material preparation: on rigid foam or honeycomb paper, evenly sprinkle bark of eucommia rubber powder, 70 ℃～80 ℃ lower temperatureization processing 1 hour～2 hours, gutta-percha is immersed in rigid foam or the honeycomb paper, then be cooled to room temperature, namely get elastomeric material; Rigid foam or honeycomb paper specification are length 60cm～120cm, width 10cm～50cm, thickness 1mm～2.5mm; Bark of eucommia rubber powder use amount 500g/m
2～800g/m
2
(2) bamboo floor blank: bamboo wood level material or integrated timber are processed into the floor blank, and its specification is length 60cm～120cm, width 10cm～50cm, thickness 3mm～7mm;
(3) resiliently-mounted floor moulding: apply bark of eucommia glue at bamboo floor blank material list face, according to elastic bamboo floor panel structure assembly, cold moudling gets final product immediately, bark of eucommia glue use amount 80g/m
2～120g/m
2The condition of colding pressing is pressure 0.3MPa～1.0MPa, room temperature, time 5s～10s.