CN102662315A - Manufacturing method of colored ceramic watch - Google Patents
Manufacturing method of colored ceramic watch Download PDFInfo
- Publication number
- CN102662315A CN102662315A CN2012101233103A CN201210123310A CN102662315A CN 102662315 A CN102662315 A CN 102662315A CN 2012101233103 A CN2012101233103 A CN 2012101233103A CN 201210123310 A CN201210123310 A CN 201210123310A CN 102662315 A CN102662315 A CN 102662315A
- Authority
- CN
- China
- Prior art keywords
- watch
- solution
- ceramic
- metal oxide
- soluble metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a manufacturing method of a colored ceramic watch, which comprises the following steps that: (1) the raw blank of a ceramic watchcase is provided; (2) inorganic salt solution and soluble metal oxide solution are provided to prepare mixed solution; the inorganic salt solution and the soluble metal oxide solution are mixed in the ratio of (1-5):1 or 1:(1-5); (3) the raw blank of the ceramic watchcase is arranged in the prepared mixed solution to be soaked for 5 seconds to 12 hours, and the blank has a colored effect after being soaked; and (4) the blank is taken out and dried. According to the manufacturing method of the colored ceramic watch, colors with corresponding camouflage effects are formed by oxidizing the watchcase with soluble metal oxide, the operation is simple, the manufactured ceramic watch is novel and attractive, and the colors are fashionable and long-lasting.
Description
Technical field
The present invention relates to the stupalith field, relate in particular to a kind of method for making of camouflage color pottery wrist-watch.
Background technology
Along with growth in the living standard, people are also increasingly high to the requirement of quality of the life and external image, and one of article that wrist-watch is generally worn as people have been not limited only to show time function, and the function of its collocation decoration aspect is occupied an leading position gradually.Ceramic ornaments such as pottery wrist-watch, because of good characteristics such as its hardness is high, wear-resistant, good toughness, electroless plating pollutions, very popular.Ceramic product in the market such as ceramic wrist-watch are solid color mostly, and its color is to obtain through adding toner therein, and for the interpolation of toner, wayward, and the color that forms is not lasting.
Summary of the invention
A purpose of the present invention is, a kind of method for making of camouflage color pottery wrist-watch is provided, the wrist-watch that can obtain to have the camouflage color effect, and novel and beautiful, color fashion are lasting.
For realizing above-mentioned purpose, the present invention provides a kind of method for making of camouflage color pottery wrist-watch, and it comprises the steps:
Step 1 provides ceramic wristwatch case green compact;
Step 2 provides inorganic salt solution and soluble metal oxide solution, the preparation mixed solution: with inorganic salt solution and soluble metal oxide solution 1-5 in proportion: 1 or 1: 1-5 mixes;
Step 3 places the mixed solution of above-mentioned preparation with ceramic wristwatch case green compact, soaks 5 seconds-12 hours, has the camouflage color effect on it after soaking.
The concentration of said inorganic salt solution and soluble metal oxide solution is 0.5-30%.
Also comprise step 5, the ceramic wristwatch case green compact that step 4 back is obtained carry out sintering, molding.
Adopt microwave drying oven that the ceramic wristwatch case green compact after soaking are carried out drying in the step 4.
Beneficial effect of the present invention: the method for making of camouflage color pottery wrist-watch of the present invention, utilize soluble metal oxide oxidation watchcase to form the color that correspondence has the camouflage color effect, simple to operate, the ceramic wrist-watch novel and beautiful that makes, color fashion is permanent.
Embodiment
The present invention provides a kind of method for making of camouflage color pottery wrist-watch, comprises the steps:
Step 1 provides ceramic wristwatch case green compact.Said ceramic wristwatch case comprises ceramic components such as watchband, watch core shell.
Step 2 provides inorganic salt solution and soluble metal oxide solution, the preparation mixed solution: inorganic salt solution and soluble metal oxide solution are by 1-5: 1 or 1: 1-5 mixes, and obtains mixed solution.The concentration of inorganic salt solution and soluble metal oxide solution is 0.5-30%.Said inorganic salts can be hydrochloride, nitrate (like PrNO
3, CoNO
3) or other inorganic salts, the soluble metal oxide can be ability water-soluble coloured oxide or nitric acid thing, like Cr
2O
3This mixed solution preferably preparation before use gets final product, and the mixed solution of preparation result of use in 2 hours is best.
Step 3 places the mixed solution of above-mentioned preparation with ceramic wristwatch case green compact, soaks 5 seconds-12 hours, has the camouflage color effect on it after soaking.Wherein, utilize mixed solution that ceramic wristwatch case green compact are carried out oxidation during immersion, do not need painstakingly to stir, the metallic ion in the soluble metal oxide solution can freely be absorbed by green compact, makes green compact be formed with the camouflage color effect that color differs.Said green compact various colors occurs after through different soluble metal oxide oxidations, and color is selected corresponding soluble metal oxide solution as required.As adopt PrNO
3Solution and Cr
2O
3The mixed solution that solution is mixed with soaks ceramic wristwatch case green compact, can obtain yellowish green alternate camouflage color effect.
Step 4, taking-up drying can adopt microwave drying oven that the ceramic wristwatch case green compact after soaking are carried out drying.
Further can comprise step 5, the camouflage color pottery wristwatch case green compact that step 4 back is obtained carry out sintering, molding.Then with after the assembling of wrist-watch watch core can obtain the finished product wrist-watch.
In sum, the method for making of camouflage color pottery wrist-watch of the present invention utilizes soluble metal oxide oxidation watchcase to form the color that correspondence has the camouflage color effect, and is simple to operate, the ceramic wrist-watch novel and beautiful that makes, and color fashion is permanent.This method for making of the present invention also can be applicable to the making of goods such as ceramic jewelry, mobile phone shell, to obtain the camouflage color effect.
The above; For the person of ordinary skill of the art; Can make other various corresponding changes and distortion according to technical scheme of the present invention and technical conceive, and all these changes and distortion all should belong to the protection domain of accompanying Claim of the present invention.
Claims (4)
1. the method for making of a camouflage color pottery wrist-watch is characterized in that, comprises the steps:
Rapid 1, ceramic wristwatch case green compact are provided;
Step 2 provides inorganic salt solution and soluble metal oxide solution, the preparation mixed solution: with inorganic salt solution and soluble metal oxide solution 1-5 in proportion: 1 or 1: 1-5 mixes;
Step 3 places the mixed solution of above-mentioned preparation with ceramic wristwatch case green compact, soaks 5 seconds-12 hours, has the camouflage color effect on it after soaking;
Step 4, taking-up drying.
2. the method for making of camouflage color pottery wrist-watch as claimed in claim 1 is characterized in that the concentration of said inorganic salt solution and soluble metal oxide solution is 0.5-30%.
3. the method for making of camouflage color pottery wrist-watch as claimed in claim 1 is characterized in that, also comprises step 5, and the ceramic wristwatch case green compact that step 4 back is obtained carry out sintering, molding.
4. the method for making of camouflage color pottery wrist-watch as claimed in claim 1 is characterized in that, adopts microwave drying oven that the ceramic wristwatch case green compact after soaking are carried out drying in the step 4.