CN102363702A - 水性单组分消光型清面漆及其制备方法 - Google Patents

水性单组分消光型清面漆及其制备方法 Download PDF

Info

Publication number
CN102363702A
CN102363702A CN201110181662XA CN201110181662A CN102363702A CN 102363702 A CN102363702 A CN 102363702A CN 201110181662X A CN201110181662X A CN 201110181662XA CN 201110181662 A CN201110181662 A CN 201110181662A CN 102363702 A CN102363702 A CN 102363702A
Authority
CN
China
Prior art keywords
parts
water
agent
aqueous
varnish
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201110181662XA
Other languages
English (en)
Other versions
CN102363702B (zh
Inventor
吕跃文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHENGDU BEIDA COATING Co Ltd
Original Assignee
CHENGDU BEIDA COATING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHENGDU BEIDA COATING Co Ltd filed Critical CHENGDU BEIDA COATING Co Ltd
Priority to CN 201110181662 priority Critical patent/CN102363702B/zh
Publication of CN102363702A publication Critical patent/CN102363702A/zh
Application granted granted Critical
Publication of CN102363702B publication Critical patent/CN102363702B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种水性单组分消光型清面漆及其制备方法,属于涂料领域,它的配方为:以重量计,水性聚氨酯分散体40~50份,聚丙烯酸改性聚氨酯20~30份,润湿剂0.1~0.5份,增稠剂1.0~2.0份,消泡剂0.1~0.5份,消光剂2.0~8.0份,流平剂0.1~0.5份,成膜助剂0.1~2.0份,水1.0~5.0份。本发明具有优异的光泽和外观,耐污染性和化学品性优,优异的机械性能,可与乳胶漆等其他油漆同时施工,操作容易且多样化。

Description

水性单组分消光型清面漆及其制备方法
技术领域
本发明属于涂料领域,具体涉及一种水性单组分消光型清面漆及其制备方法。
背景技术
现在市面上的各种涂料种类繁多,主要分为有机涂料和无机涂料,有机涂料根据使用的溶剂不同又分为有机溶剂型涂料和有机水性涂料。有机溶剂型涂料由于VOC高,不能满足人们日益增强的对环保的要求。
有机水性涂料,即水性涂料,现在日益成为研究的热点。常规的水性漆对木材润湿性差,与其他水性体现相容性也常常不好,乳液在高速搅拌下容易破坏。
发明内容
本发明要解决的技术问题是现有技术中水性漆对木材润湿性差,与其他水性体现相容性也常常不好,乳液在高速搅拌下容易破坏。
本发明解决该技术问题的技术方案是:水性单组分消光型清面漆,它的配方为:以重量计,水性聚氨酯分散体40~50份,聚丙烯酸改性聚氨酯20~30份,润湿剂0.1~0.5份,增稠剂1.0~2.0份,消泡剂0.1~0.5份,消光剂2.0~8.0份,流平剂0.1~0.5份,成膜助剂0.1~2.0份,水1.0~5.0份。
优选地,上述所述配方中,水性聚氨酯分散体45份,聚丙烯酸改性聚氨酯25份,润湿剂0.3份,增稠剂1.5份,消泡剂0.3份,消光剂5份,流平剂0.3份,成膜助剂1份,水3份。
本发明还提供了一种水性单组分消光型清面漆的制备方法,以重量计,在搅拌速度为600~800r/min条件下向容器依次加入水性聚氨酯分散体40~50份、聚丙烯酸改性聚氨酯20~30份、润湿剂0.1~0.5份、增稠剂1.0~2.0份、消泡剂 0.1~0.5份,搅拌均匀后缓慢加入消光剂2.0~8.0份,将搅拌转速调至1200~1500r/min,分散至细度≤30um,然后依次加入流平剂 0.1~0.5份、成膜助剂 0.1~2.0份,再将搅拌转速调至600~800r/min,搅拌均匀,用水1.0~5.0份清洗设备和调整粘度到120KU~130KU,过滤得到成品。
使用时,按本产品︰水=1︰0.3~0.5的配比调配均匀,静置10分钟至气泡消除后即可施工。
本发明是以水为溶剂或分散介质的涂料,它具有重要的环保意义,无毒环保,不含苯类等有害溶剂,不含游离TDI。
本发明采用聚丙烯酸改性聚氨酯、水性聚氨酯分散体、丙烯酸乳液经过自身化学交联发应,生成一种高性能的高分子聚合物。解决了常规水性漆对木材润湿性差的问题,以及与其他水性体系相容性不好的现象;解决了乳液在高速搅拌下会破乳的可能。
本发明具有优异的光泽和外观,耐污染性和化学品性优,优异的机械性能,可与乳胶漆等其他油漆同时施工,操作容易且多样化。
具体实施方式
实施例1
以重量计,在搅拌速度为600r/min条件下向容器依次加入水性聚氨酯分散体(欧宝迪AC 2514)40份、聚丙烯酸改性聚氨酯(欧宝迪MAC 34)20份、润湿剂(NOPCO SN 990)0.1份、增稠剂(罗门哈斯 RM 2020)1.0份、消泡剂(毕克 BYK 028) 0.1份,搅拌均匀后缓慢加入消光剂(格雷斯ED40)2.0份,将搅拌转速调至1200r/min,分散至细度≤30um,然后依次加入流平剂()毕克BYK 346)0.1份、成膜助剂(伊士曼 醇酯-12)0.1份,再将搅拌转速调至600r/min,搅拌均匀,用水1.0份清洗设备,调整粘度到120KU,过滤得到成品。
实施例2
以重量计,在搅拌速度为800r/min条件下向容器依次加入水性聚氨酯分散体(欧宝迪AC 2514)50份、聚丙烯酸改性聚氨酯(欧宝迪MAC 34)30份、润湿剂(毕克BYK 194)0.5份、增稠剂(NOPCO SN612)2.0份、消泡剂(Tego 902W)0.5份,搅拌均匀后缓慢加入消光剂(格雷斯ED40)8.0份,将搅拌转速调至1500r/min,分散至细度≤30um,然后依次加入流平剂(Tego 410)0.5份、成膜助剂(伊士曼 醇酯-12)2.0份,再将搅拌转速调至800r/min,搅拌均匀,用水5.0份清洗设备,调整粘度到130KU,过滤得到成品。
实施例3
以重量计,在搅拌速度为700r/min条件下向容器依次加入水性聚氨酯分散体(欧宝迪AC 2514)45份、聚丙烯酸改性聚氨酯(欧宝迪MAC 34)25份、润湿剂(毕克 BYK 194)0.3份、增稠剂(罗门哈斯 RM 2020)1.5份、消泡剂 (NOPCO SN 1370)0.3份,搅拌均匀后缓慢加入消光剂(格雷斯ED40)5份,将搅拌转速调至1400r/min,分散至细度≤30um,然后依次加入流平剂(Tego 410)0.3份、成膜助剂(伊士曼 醇酯-12)1份,再将搅拌转速调至700r/min,搅拌均匀,用水3份清洗设备,调整粘度到125KU,过滤得到成品。
 
表1 各实施例产品性能对比:
测试项目 溶剂型 实施例1 实施例2 实施例3
漆膜外观 平整光滑 平整光滑 平整光滑 平整光滑
环保性 含苯等有害溶剂 不含苯等有害溶剂 不含苯等有害溶剂 不含苯等有害溶剂
游离TDI 含游离TDI 不游离TDI 不游离TDI 不游离TDI
附着力 0级 0级 0级 0级
铅笔硬度 HB HB HB HB
耐化学品性
消泡性 一般
流平性 可接受
表干(min) 10-20 17 16 14
指压干(h) 2-4 3 3 3
VOC(g/l) 小于580 180 180 180
施工性
从表1看出,本发明的产品VOC含量明显低于溶剂型的漆,并且不含苯及游离TDI,更加环保,其他指标也与溶剂型差别不大。

Claims (3)

1.水性单组分消光型清面漆,其特征在于,它的配方为:以重量计,水性聚氨酯分散体40~50份,聚丙烯酸改性聚氨酯20~30份,润湿剂0.1~0.5份,增稠剂1.0~2.0份,消泡剂0.1~0.5份,消光剂2.0~8.0份,流平剂0.1~0.5份,成膜助剂0.1~2.0份,水1.0~5.0份。
2.根据权利要求1所述的水性单组分消光型清面漆,其特征在于:所述配方中,水性聚氨酯分散体45份,聚丙烯酸改性聚氨酯25份,润湿剂0.3份,增稠剂1.5份,消泡剂0.3份,消光剂5份,流平剂0.3份,成膜助剂1份,水3份。
3.水性单组分消光型清面漆的制备方法,其特征在于:以重量计,在搅拌速度为600~800r/min条件下向容器依次加入水性聚氨酯分散体40~50份、聚丙烯酸改性聚氨酯20~30份、润湿剂0.1~0.5份、增稠剂1.0~2.0份、消泡剂 0.1~0.5份,搅拌均匀后缓慢加入消光剂2.0~8.0份,将搅拌转速调至1200~1500r/min,分散至细度≤30um,然后依次加入流平剂 0.1~0.5份、成膜助剂 0.1~2.0份,再将搅拌转速调至600~800r/min,搅拌均匀,用水1.0~5.0份清洗设备和调整粘度到120KU~130KU,过滤得到成品。
CN 201110181662 2011-06-30 2011-06-30 水性单组分消光型清面漆及其制备方法 Expired - Fee Related CN102363702B (zh)