CN102320816A - Blank material for manufacturing medium-temperature red porcelain liner and preparation method thereof - Google Patents
Blank material for manufacturing medium-temperature red porcelain liner and preparation method thereof Download PDFInfo
- Publication number
- CN102320816A CN102320816A CN201110156472A CN201110156472A CN102320816A CN 102320816 A CN102320816 A CN 102320816A CN 201110156472 A CN201110156472 A CN 201110156472A CN 201110156472 A CN201110156472 A CN 201110156472A CN 102320816 A CN102320816 A CN 102320816A
- Authority
- CN
- China
- Prior art keywords
- parts
- manufacturing
- blank material
- liner
- blank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a blank material for manufacturing a medium-temperature red porcelain liner and a preparation method thereof. In order to overcome the defects of long food cooking time, easy cracking, difficult cleaning and the like of the existing red porcelain vessel used as a liner of a cooking electric appliance, the blank material for manufacturing the medium-temperature red porcelain liner contains the following substances in parts by weight: 70 parts of silica, 19.5 parts of alumina, 3.2 parts of iron oxide, 0.2 part of calcium oxide, 0.5 part of magnesium oxide, 0.5 part of potassium oxide and 1.4 parts of sodium oxide, and is prepared from the following raw materials in parts by weight: 60 parts of purple clay, 8 parts of kaolin, 4 parts of metahalloysite, 18 parts of quartz sand, 5 parts of potassium feldspar and 5 parts of sodium feldspar. The preparation method of the blank material comprises the following steps of: uniformly mixing the raw materials of the blank material for manufacturing the medium-temperature red porcelain liner in parts by weight, grinding, and sieving by a 250-mesh sieve to obtain the blank material for manufacturing the medium-temperature red porcelain liner. Used for manufacturing the liner of the cooking electric appliance, the blank material has the advantages of good heat conductivity, good heat impact resistance, high heating speed, short food cooking time, no cracking in a higher-power heating process, low hydroscopicity and easy cleaning.
Description
Technical field
The present invention relates to a kind of main blank that is used as the middle temperature red-clay inner of cooking appliance inner bag, be specially the blank and the compound method thereof of warm red-clay inner in a kind of the manufacturing.
Background technology
Boccaro is meant that quality is fine and smooth, the higher natural clay of iron content is processed, and colour generation is main with russet, the harder and gas-pervious Unglazed ceramic device of quality.
The making of zisha earthenware has history of more than one thousand years, and the part that red stoneware ware is made tea as traditional Chinese culture is loved by the people.Along with society constantly develops, people's living standard improves constantly; People's environmental consciousness is more and more stronger; Cooking appliance product with red-clay inner, because of the food of its environmental protection, culinary art has unique mouthfeel and health care special efficacy, has certain cultural connotation again and be favourably welcome, market potential is huge.
But when existing red stoneware ware is used as cooking appliance inner bag (as the heating container of cooking appliance); There are deficiencies such as cooking foodstuffs time length, easy of crack, difficult cleaning; Boccaro is difficult to performance as the meliority of culinary art inner bag; Had a strong impact on red stoneware ware applying in cooking appliance; Therefore, market presses for the red-clay inner that a kind of novel purple sand material is made, can in cooking appliance, promote the use of to satisfy, rapid heating, in more high-power heat-processed, do not ftracture, product uses the back to be prone to requirements such as cleaning.
Summary of the invention
The object of the invention is exactly to be directed against above-mentioned deficiency; The blank and the compound method thereof of warm red-clay inner in a kind of can the manufacturing are provided, and the middle temperature red-clay inner thermal conductivity of processing with this blank is good, thermal-shock resistance is good, heating is fast, the cooking foodstuffs time lacks, in more high-power heat-processed, do not ftracture, water-absorbent is low, not taint of odour, be prone to clean.
For achieving the above object, technical scheme of the present invention is, the blank of warm red-clay inner during this is made contains the material of following weight parts proportioning:
The blank of warm red-clay inner is made up of the following weight parts proportion raw material in the said manufacturing:
Boccaro soil 58-62 kaolin 7-9 halloysite 3-5
Silica sand 16-20 potassium felspar sand 4-6 albite 4-6
Because raw material sources are different, the proportional quantity of above-mentioned raw materials in weight portion can be revised according to the content of the above-mentioned substance of concrete raw material, makes the content of the material that meets above-mentioned weight part proportioning.
With raw material blending, the grinding of the blank of warm red-clay inner in the above-mentioned manufacturing, cross 250 mesh sieves, the blank of warm red-clay inner in must making.
Boccaro soil of the present invention is fast shape or sheet, and rate of decay is high, in prescription, makes the main body raw material.
Kaolin of the present invention, bulk, viscosity is good, and dry tenacity is big, in prescription, regulates plasticity and improves dry tenacity.
Silica sand pearl of the present invention or light yellow is Powdered, SiO
2Reach more than 99.5% the main SiO that improves in prescription
2Content; Thereby improved the firing temperature of red-clay inner, made firing temperature of the present invention reach 1260 ℃-1280 ℃, reduced the glassy phase content in the red-clay inner; And then reduced the thermal expansivity of warm red-clay inner among the present invention; Improved thermal shock resistance, high-power heating is not ftractureed, heat-up time is short.
Halloysite white according to the invention or light yellow belongs to halloysite, in prescription, regulates plasticity and improves dry tenacity.
Potassium felspar sand: white is Powdered, the main solvent action that rises in prescription;
Albite: white is Powdered; The main solvent action that rises in prescription.
After the weight part proportioning according to above-mentioned raw materials, the present invention contains the material of following weight part proportioning:
The result shows that the red-clay inner that the present invention processes and the performance comparison of common red-clay inner are following:
Use shows that it is good that the middle temperature red-clay inner that the present invention processes has thermal conductivity, and thermal-shock resistance is good; Heating is fast; The cooking foodstuffs time lacks, in more high-power heat-processed, do not ftracture, water-absorbent is low, not taint of odour, is prone to clean, and is well suited for the inner bag as cooking appliance.
Embodiment
Embodiment 1
The blank of warm red-clay inner contains the material of following weight parts proportioning in this manufacturing:
The blank that contains warm red-clay inner in the manufacturing of material of above-mentioned weight part proportioning is made up of the following weight parts proportion raw material:
Boccaro soil 60 kaolin 8 halloysites 4
Silica sand 18 potassium felspar sands 5 albites 5
Its compound method is, with raw materials in weight portion mixing, the grinding of the blank of warm red-clay inner in the above-mentioned manufacturing, crosses 250 mesh sieves, the blank of warm red-clay inner in must making.
Embodiment 2
The blank of warm red-clay inner contains the material of following weight parts proportioning in this manufacturing:
The blank that contains warm red-clay inner in the manufacturing of material of above-mentioned weight part proportioning is made up of the following weight parts proportion raw material:
Boccaro soil 58 kaolin 7 halloysites 3
Silica sand 16 potassium felspar sands 4 albites 4
Because raw material sources are different, the proportional quantity of above-mentioned raw materials in weight portion can be revised according to the content of the above-mentioned substance of concrete raw material, makes the material that meets above-mentioned weight part proportioning.
Its compound method is, with raw materials in weight portion mixing, the grinding of the blank of warm red-clay inner in the above-mentioned manufacturing, crosses 250 mesh sieves, the blank of warm red-clay inner in must making.
Embodiment 3
The blank of warm red-clay inner contains the material of following weight parts proportioning in this manufacturing:
The blank that contains warm red-clay inner in the manufacturing of material of above-mentioned weight part proportioning is made up of the following weight parts proportion raw material:
Boccaro soil 62 kaolin 9 halloysites 5
Silica sand 20 potassium felspar sands 6 albites 6
Because raw material sources are different, the proportional quantity of above-mentioned raw materials in weight portion can be revised according to the content of the above-mentioned substance of concrete raw material, makes the material that meets above-mentioned weight part proportioning.
Its compound method is, with raw materials in weight portion mixing, the grinding of the blank of warm red-clay inner in the above-mentioned manufacturing, crosses 250 mesh sieves, the blank of warm red-clay inner in must making.
Claims (3)
1. the blank of warm red-clay inner in the manufacturing is characterized in that it contains the material of following weight parts proportioning:
2. the blank of warm red-clay inner is characterized in that in the manufacturing according to claim 1, and it is made up of the following weight parts proportion raw material:
Boccaro soil 58-62 kaolin 7-9 halloysite 3-5
Silica sand 16-20 potassium felspar sand 4-6 albite 4-6.
3. the compound method of the blank of warm red-clay inner is characterized in that in the manufacturing according to claim 2, with above-mentioned raw materials mixing, grinding, crosses 250 mesh sieves, the blank of warm red-clay inner in must making.