CN102146981B - Method for producing triangular belt by adopting water emulsion slurry leaching cloth - Google Patents
Method for producing triangular belt by adopting water emulsion slurry leaching cloth Download PDFInfo
- Publication number
- CN102146981B CN102146981B CN2010106054492A CN201010605449A CN102146981B CN 102146981 B CN102146981 B CN 102146981B CN 2010106054492 A CN2010106054492 A CN 2010106054492A CN 201010605449 A CN201010605449 A CN 201010605449A CN 102146981 B CN102146981 B CN 102146981B
- Authority
- CN
- China
- Prior art keywords
- water
- canvas
- rubber cement
- belt
- impregnation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a method for producing a triangular belt by adopting water emulsion slurry leaching cloth, which comprises the following steps: preparing raw auxiliary materials, preprocessing water emulsion slurry, gumming a canvas, wrapping the triangular belt and vulcanizing the triangular belt. The method can solve the technical problem that the water emulsion slurry is replaced by gasoline emulsion slurry in the cloth leaching process, eliminates the potential safety hazards and the volatilization of harmful gas during the production and greatly reduces the production cost, thereby ensuring that the comprehensive quality performance of the triangular belt is stably improved.
Description
Technical field
The present invention relates to a kind of processing method of vee belt, particularly adopt the water and milk rubber cement to soak the method for cloth production vee belt.
Background technique
China produces the enterprise of classical V-belt at present; The canvas rubberizing has 2/3 to adopt gum dipping process approximately, and rubber cement all uses the gasoline rubber cement, and the gasoline rubber cement (is prone to breaking out of fire) in preparation and immersing glue process potential safety hazard is outstanding; The harmful gas volatilization is more serious, befouling environment; And because International Crude Oil constantly soaring in recent years, the price of the main body industrial naptha of gasoline rubber cement is also high synchronously always, causes V band cost of production to improve constantly; Because the canvas that soaks of gasoline rubber cement receives ambient temperature, humidity effect bigger before use, the technology capability quality is unstable, thereby directly has influence on the combination property quality of finished product V band.
Summary of the invention
The objective of the invention is to overcome above deficiency, a kind of method that adopts the water and milk rubber cement to soak cloth production vee belt is provided.Can solve the alternative gasoline rubber cement of water latex slurry and soak cloth process engineering problem; The potential safety hazard in the elimination production process and the volatilization of harmful gas; Reduce production costs significantly; Simultaneously, make the other problem that exists in the background technique also be able to solve, thereby guaranteed the stable raising of V band comprehensive quality performance.
The object of the invention is realized through following measure: a kind of method that adopts the water and milk rubber cement to soak cloth production vee belt may further comprise the steps:
⑴ the outfit of supplementary material:
A. polyester-cotton blend canvas 80-120m;
B. vee belt made-up belt 200Am;
C. water and milk rubber cement 80-120kg;
D. anti-coke agent 0.8-1.2kg;
E. postcure stabilizer 1-1.5kg.
⑵ the pretreatment of water and milk rubber cement:
A. the water and milk rubber cement is 20-24 hour before use, adds the above-mentioned anti-coke agent of getting ready by the 0.5-1% that is got the raw materials ready; To improve the heat resistance of rubber cement, reduce rubber cement and give birth to heat, enhancing adhesive strength.
B. with above-mentioned treated water latex slurry 3-4 hour before use, add the above-mentioned postcure stabilizer of getting ready, the back that stirs is subsequent use.
⑶ canvas impregnation:
A. on dryer, the canvas of getting ready is carried out pretreatment; Be set in 0.7-0.8MPa to the baking oven vapor pressure, the guiding motor speed is adjusted into 350-450r/min, and the canvas contained humidity is fully volatilized; Improve the technology capability of immersing glue process, strengthen Adhesion force with sizing material;
B. water latex slurry impregnation is twice gum dipping process:
Impregnation for the first time: will soaking cloth machine drying alley vapor pressure, to be set in 0.3-0.4MPa guiding motor speed be 400-500r/min, and the master control roll spacing is adjusted by canvas spread 100g/m, and impregnation is accomplished machine under the adhesive plaster is parked for the first time;
Impregnation for the second time: will park the first time of the dipped canvas more than 8 hours; Soak the cloth machine again and carry out the impregnation second time, and will soak cloth machine drying alley vapor pressure and be set in 0.5-0.6MPa, the guiding motor speed is 300-400r/min; Canvas spread 80g/m is pressed in the master control roll spacing, adjusts.Impregnation is accomplished for the second time, parks machine under the adhesive plaster subsequent use.Because what impregnation can not dry by the fire for the first time is too dried, fully oven dry behind the impregnation for the second time fully mixes with the dried glue composition that guarantees twice impregnation, avoids occurring interfacial separation, and causing can not be fine bonding between infantees, influences V band quality.
⑷ vee belt infantees is handled:
A. with water and milk rubber cement secondary dipping and park the canvas more than 8 hours, become the direction of miter angle to carry out the severing clot with warp by the standard edge, subsequent use;
B. on the infantees machine, the impregnated fabric cloth is combined with made-up belt, and reach even, accurate, tight, positive requirement.
⑸ the vulcanizing treatment of vee belt:
A. sulfuration steam pressure: press 0.35-0.4MPa in the circle mould vulcanizer, external pressure 0.75-0.8MPa makes inside and outside differential pressure remain on 0.4MPa; Avoid occurring foam body, fillet and foaming phenomenon.
B. sulfurize temperature: cavity temperature remains on 140-155 ℃ in the vulcanizer;
C. cure time: should be controlled at 11-16 minute;
D. cooling shaping water temperature 30-40 ℃, 50-60 ℃ of mould water-exit temperature;
Vee belt after infantees is handled is product through vulcanizing treatment.
Above-mentioned canvas is the polyester-mixed cotton cloth that 3 * 3 of thread count 36 * 36 contains cotton 35-50%.
Above-mentioned water and milk rubber cement is natural latex and compounding ingredient mixed solution, and its mixed proportion is 1:2-3.5.
Above-mentioned anti-coke agent is HAV-2 or WK-901.
Above-mentioned postcure stabilizer is HS-252 or HS-258.
Above-mentioned vee belt made-up belt is A type, Type B or C type vee belt made-up belt.
Above-mentioned natural latex is LIR-30, and compounding ingredient is PKL-101.
Effect of the present invention:
1, employs new technology after the scheme, eradicated the potential safety hazard that petrolic solvent is prone to take place electrostatic fire, stopped the accidental damage that fire brings.
2, the scheme of employing new technology has been eliminated the environmental pollution that harmful gas brings of volatilizing fast of high-grade gasoline solvent.A medium-sized V band production unit can reduce 4000 tons of noxious gas emissions every year, and its environment contribution is huge.
3, the scheme of employing new technology, the per kilogram dipped canvas can be practiced thrift 0.6 liter of petrolic solvent, amounts to RMB more than 4 yuan.Reduced cost of production significantly, its economic benefit is very considerable.
4, the scheme of employing new technology has solved rubber cement and has stored problem of unstable, has not only reduced economic loss, and has stablized the technology capability quality of rubber cement, and simultaneously, the vee belt combination property quality that the water latex slurry soaks cloth production is able to stable the raising.The physical and mechanical properties of V band finished product can reach the GB/T1171-1998 national Specification fully.
Embodiment
Embodiment 1: a kind of method that adopts the water and milk rubber cement to soak cloth production vee belt may further comprise the steps: (
⑴ the outfit of supplementary material:
A. polyester-cotton blend canvas 80m;
B. vee belt made-up belt 200Am;
C. water and milk rubber cement 80kg;
D. anti-coke agent 1.0kg;
E. postcure stabilizer 1.0kg.
⑵ the pretreatment of water and milk rubber cement:
A. the water and milk rubber cement is 22 hours before use, by the above-mentioned anti-coke agent of getting ready of 0.6% adding of being got the raw materials ready; To improve the heat resistance of rubber cement, reduce rubber cement and give birth to heat, enhancing adhesive strength.
B. with above-mentioned treated water latex slurry 3 hours before use, add the above-mentioned postcure stabilizer of getting ready, the back that stirs is subsequent use.
⑶ canvas impregnation:
A. on dryer, the canvas of getting ready is carried out pretreatment, be set in 0.7MPa to the baking oven vapor pressure, the guiding motor speed is adjusted into 350r/min, and the canvas contained humidity is fully volatilized, and improves the technology capability of immersing glue process, strengthens the Adhesion force with sizing material;
B. water latex slurry impregnation is twice gum dipping process:
Impregnation for the first time: will soaking cloth machine drying alley vapor pressure, to be set in 0.3MPa guiding motor speed be 400r/min, and the master control roll spacing is adjusted by canvas spread 100g/m, and impregnation is accomplished machine under the adhesive plaster is parked for the first time;
Impregnation for the second time: will park 8 hours the first time of dipped canvas; Soak the cloth machine again and carry out the impregnation second time, and will soak cloth machine drying alley vapor pressure and be set in 0.5MPa, the guiding motor speed is 300r/min; Canvas spread 80g/m is pressed in the master control roll spacing, adjusts.Impregnation is accomplished for the second time, parks machine under the adhesive plaster subsequent use.Because what impregnation can not dry by the fire for the first time is too dried, fully oven dry behind the impregnation for the second time fully mixes with the dried glue composition that guarantees twice impregnation, avoids occurring interfacial separation, and causing can not be fine bonding between infantees, influences V band quality.
⑷ vee belt infantees is handled:
A. with water and milk rubber cement secondary dipping and park 8 hours canvas, become the direction of miter angle to carry out the severing clot with warp by the standard edge, subsequent use;
B. on the infantees machine, the impregnated fabric cloth is combined with made-up belt, and reach even, accurate, tight, positive requirement.
⑸ the vulcanizing treatment of vee belt:
A. sulfuration steam pressure: being pressed in 0.35MPa in the circle mould vulcanizer, being pressed in 0.75MPa outward, making inside and outside differential pressure remain on 0.4MPa;
B. sulfurize temperature: cavity temperature remains on 145 ℃ in the vulcanizer;
C. cure time: should be controlled at 12 minutes;
D. the cooling shaping water temperature is 38 ℃, 56 ℃ of mould water-exit temperatures;
Vee belt after infantees is handled is product through vulcanizing treatment.
Above-mentioned canvas is that 3 * 3 of thread count 36 * 36 contains cotton 45% polyester-mixed cotton cloth.
Above-mentioned water and milk rubber cement is natural latex LIR-30 and compounding ingredient PKL-101 mixed solution, and its mixed proportion is 1:2.
Above-mentioned anti-coke agent is HAV-2.
Above-mentioned postcure stabilizer is HS-258.
Above-mentioned vee belt made-up belt is A type and Type B vee belt made-up belt.
Parameter comparison:
The gasoline rubber cement: mixglue and ratio of solvent are 1:3.5.
The water and milk rubber cement: natural latex is 1:2 with the compounding ingredient ratio.
The water latex slurry soaks cloth and soaks cloth with the gasoline rubber cement and compare, and its infantees bonding strength and V band finished product have more superiority fatigue life, and concrete data are following:
One, the bonding strength of two kinds of rubber cements
Rubber cement kind gasoline rubber cement (background technique) water and milk rubber cement (present technique)
Infantees bonding strength/(KN.M-1) 2.63 2.67
Two, the v of two kinds of rubber cements band finished product fatigue life
NBS gasoline rubber cement (background technique) water and milk rubber cement (present technique)
4×10
6 5.6×10
6 5.7×10
6
Embodiment 2:
A kind of method that adopts the water and milk rubber cement to soak cloth production vee belt may further comprise the steps:
⑴ the outfit of supplementary material:
A. polyester-cotton blend canvas 100m;
B. vee belt made-up belt 200Am;
C. water and milk rubber cement 100kg;
D. anti-coke agent 1.2kg;
E. postcure stabilizer 1.5kg.
⑵ the pretreatment of water and milk rubber cement:
A. the water and milk rubber cement is 24 hours before use, by the above-mentioned anti-coke agent of getting ready of 1% adding of being got the raw materials ready; To improve the heat resistance of rubber cement, reduce rubber cement and give birth to heat, enhancing adhesive strength.
B. with above-mentioned treated water latex slurry 4 hours before use, add the above-mentioned postcure stabilizer of getting ready, the back that stirs is subsequent use.
⑶ canvas impregnation:
A. on dryer, the canvas of getting ready is carried out pretreatment, be set in 0.8MPa to the baking oven vapor pressure, the guiding motor speed is adjusted into 450r/min, and the canvas contained humidity is fully volatilized, and improves the technology capability of immersing glue process, strengthens the Adhesion force with sizing material;
B. water latex slurry impregnation is twice gum dipping process:
Impregnation for the first time: will soaking cloth machine drying alley vapor pressure, to be set in 0.4MPa guiding motor speed be 500r/min, and the master control roll spacing is adjusted by canvas spread 100g/m, and impregnation is accomplished machine under the adhesive plaster is parked for the first time;
Impregnation for the second time: will park the first time of the dipped canvas more than 8 hours; Soak the cloth machine again and carry out the impregnation second time, and will soak cloth machine drying alley vapor pressure and be set in 0.6MPa, the guiding motor speed is 400r/min; Canvas spread 80g/m is pressed in the master control roll spacing, adjusts.Impregnation is accomplished for the second time, parks machine under the adhesive plaster subsequent use.Because what impregnation can not dry by the fire for the first time is too dried, fully oven dry behind the impregnation for the second time fully mixes with the dried glue composition that guarantees twice impregnation, avoids occurring interfacial separation, and causing can not be fine bonding between infantees, influences V band quality.
⑷ vee belt infantees is handled:
A. with water and milk rubber cement secondary dipping and park 9 hours canvas, become the direction of miter angle to carry out the severing clot with warp by the standard edge, subsequent use;
B. on the infantees machine, the impregnated fabric cloth is combined with made-up belt, and reach even, accurate, tight, positive requirement.
⑸ the vulcanizing treatment of vee belt:
A. sulfuration steam pressure: being pressed in 0.4MPa in the circle mould vulcanizer, being pressed in 0.8MPa outward, making inside and outside differential pressure remain on 0.4MPa;
B. sulfurize temperature: cavity temperature remains on 152 ℃ in the vulcanizer;
C. cure time: should be controlled at 16 minutes;
D. the cooling shaping water temperature is no more than 32 ℃, 50 ℃ of mould water-exit temperatures;
Vee belt after infantees is handled is product through vulcanizing treatment.
Above-mentioned canvas is that 3 * 3 of thread count 36 * 36 contains cotton 35% polyester-mixed cotton cloth.
Above-mentioned water and milk rubber cement is natural latex (LIR-30) and compounding ingredient (PKL-101) mixed solution, and its mixed proportion is 1:3.5.
Above-mentioned anti-coke agent is WK-901.
Above-mentioned postcure stabilizer is HS-252.
Above-mentioned vee belt made-up belt is a C type vee belt made-up belt.
Adopting thread count is 36 * 36 3 * 3 contain cotton 35% polyester-mixed cotton cloth and substitute common 110 type Wei Lunbu, and water latex slurry impregnation, as the outsourcing cloth of v band; Overcome because common less, the stretching easy deformation of Wei Lunbu density; Shortcomings such as sulfuration fillet and defect limit phenomenon have improved wear-resisting ageing resistance and non-deformability that v is with, have reduced elongation percentage and dynamic heat build up; Strengthened the bonding adhesive attraction of infantees
-adopt thread count be 36 * 36 3 * 3 contain cotton 35% polyester-cotton blend water and milk rubber cement impregnated fabric production the v band compare with the v band that background technique is produced and have superior physical and mechanical properties.Correlation data is following:
Project gasoline rubber cement (background technique) water and milk rubber cement (present technique)
Tensile strength/KN 4.9 7.2
With reference to elongation percentage/% 13 8.2
Subdue after-drawing brute force/KN 4 6.9.
Claims (4)
1. method that adopts the water and milk rubber cement to soak cloth production vee belt is characterized in that may further comprise the steps:
(1) outfit of supplementary material:
A. polyester-cotton blend canvas 80-120m;
B. vee belt made-up belt 200Am;
C. water and milk rubber cement 80-120kg;
D. anti-coke agent 0.8-1.2kg;
E. postcure stabilizer 1-1.5kg;
(2) water and milk rubber cement pretreatment:
A. the water and milk rubber cement is 20-24 hour before use, adds the above-mentioned anti-coke agent of getting ready by the 0.5-1% that is got the raw materials ready;
B. with above-mentioned treated water latex slurry 3-4 hour before use, add the above-mentioned postcure stabilizer of getting ready, the back that stirs is subsequent use;
(3) canvas impregnation:
A. on dryer, the canvas of getting ready is carried out pretreatment, be set in 0.7-0.8MPa to the baking oven vapor pressure, the guiding motor speed is adjusted into 350-450r/min, and the canvas contained humidity is fully volatilized;
B. water latex slurry impregnation is twice gum dipping process:
Impregnation for the first time: will soaking cloth machine drying alley vapor pressure, to be set in 0.3-0.4MPa guiding motor speed be 400-500r/min, and the master control roll spacing is adjusted by canvas spread 100g/m, and impregnation is accomplished machine under the adhesive plaster is parked for the first time;
Impregnation for the second time: will park the first time of the dipped canvas more than 8 hours; Soak the cloth machine again and carry out the impregnation second time, and will soak cloth machine drying alley vapor pressure and be set in 0.5-0.6MPa, the guiding motor speed is 300-400r/min; Canvas spread 80g/m is pressed in the master control roll spacing; Adjust, impregnation is accomplished for the second time, parks machine under the adhesive plaster subsequent use;
(4) the vee belt infantees is handled:
A. with water and milk rubber cement secondary dipping and park the canvas more than 8 hours, become the direction of miter angle to carry out the severing clot with warp by the standard edge, subsequent use;
B. will the impregnated fabric cloth that canvas carries out obtaining after the severing clot combined with made-up belt on the infantees machine, and reaching even, accurate, tight, positive requirement;
(5) vulcanizing treatment of vee belt:
A. sulfuration steam pressure: press 0.35-0.4MPa in the circle mould vulcanizer, external pressure 0.75-0.8MPa makes inside and outside differential pressure remain on 0.4MPa;
B. sulfurize temperature: cavity temperature remains on 140-155 ℃ in the vulcanizer;
C. cure time: be controlled at 11-16 minute;
D. cooling shaping water temperature 30-40 ℃, 50-60 ℃ of mould water-exit temperature;
Vee belt after infantees is handled is product through vulcanizing treatment.
2. employing water and milk rubber cement according to claim 1 soaks the method for cloth production vee belt, it is characterized in that described canvas be thread count be 36 * 36 3 * 3 contain the cotton polyester-mixed cotton cloth of 35-50% that is.
3. employing water and milk rubber cement according to claim 1 soaks the method for cloth production vee belt, it is characterized in that described water and milk rubber cement is natural latex and compounding ingredient mixed solution, and its mixed proportion is 1: 2-3.5.
4. employing water and milk rubber cement according to claim 1 soaks the method for cloth production vee belt, it is characterized in that described vee belt made-up belt is A type, Type B or C type vee belt made-up belt.