CN101285494A - Fastening piece and its manufacturing technique - Google Patents
Fastening piece and its manufacturing technique Download PDFInfo
- Publication number
- CN101285494A CN101285494A CNA2008100304707A CN200810030470A CN101285494A CN 101285494 A CN101285494 A CN 101285494A CN A2008100304707 A CNA2008100304707 A CN A2008100304707A CN 200810030470 A CN200810030470 A CN 200810030470A CN 101285494 A CN101285494 A CN 101285494A
- Authority
- CN
- China
- Prior art keywords
- fastening piece
- fastener
- density
- carbon
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a fastener which is made by processing carbon/carbon composite materials and a process for producing the same. The fastener comprises a screw [1], a bolt [2], a stud [2], a nut [4] and a gasket, the fastener replaces a graphite fastener or a molybdenum fastener in a high temperature furnace or corrosive environment, which is made by carbon fiber after processes of blank-making, densification, plastication modification, machine tooling and purification. Because the interior of the carbon fiber composite materials has a quasi three-dimensional structure, the fastener which is processed by the invention has the advantages of excellent high specific strength, small thermal expansion coefficient and heat shock resistance without deformation and cracking, wherein bending strength of the fastener is about ten times of the graphite, and the service life is available for more than one year; because of lubrication performance of the graphite, the fastener is convenient in assembly and disassembly in use; after the fastener undergoes surface processing, the surface of the fastener is clean without ash falling, which has no pollution to surrounding environment, parts, raw materials and finished products.
Description
Technical field:
The present invention relates to a kind of High Temperature Furnaces or corrosive atmosphere part, specifically a kind of fastening piece and production technology thereof.
Background technique:
At present, the heater of pyrometallurgy stove generally is made up of heater, contiguous block and fastening piece etc., its material is made by graphite, exist during use because of graphite screw poor mechanical property, often fracture and losing efficacy causes heater to fall apart, and causes to stop production or accident, have a strong impact on ordinary production, the working life that has is ten days only; The crucible tray of polycrystalline furnace is made up of graphite cake and graphite screw, and the graphite screw often ruptures because of being subjected to the thermal stress effect, in the only several days working life that has, cost of production is increased.In addition, graphite product falls ash, and hand can glue the evil backstage manipulator when taking; During use, can pollute, influence the purity and the quality of product surrounding environment, part, raw material and finished product etc.The molybdenum matter screw that uses in the pyrometallurgy stove uses after a period of time in hot environment, sintering phenomenon often occurs, and screw rod and screw are bonded to one, and is difficult to dismounting, makes troubles for the stove maintenance work, and the stove maintenance cost is increased.Carbon/carbon composite is a kind of net tire and net tire that the charcoal fiber is made, or charcoal cloth and charcoal cloth, or net tire and charcoal cloth are compound, pass through density again, the carbon/carbon composite that charing and graphitization processing form, has high specific strength, high ratio modulus, high temperature resistant, anti-ablation, thermal expansion coefficient is little, anti-rapid heat cycle and indeformable premium properties such as do not ftracture, be adapted to the high temperature field especially, now become or will progressively become Aero-Space, metallurgical, one of the important foundation material in fields such as new energy, being used to make fastening piece, is the ideal substitute of graphite fastening piece and molybdenum matter fastening piece.
Summary of the invention:
The purpose of this invention is to provide a kind of fastening piece and production technology thereof that adopts carbon/carbon composite to be processed into, its fastening piece comprises screw, bolt, double-screw bolt, nut and pad, be used for High Temperature Furnaces or corrosive atmosphere, substitute graphite fastening piece or molybdenum matter fastening piece.
The present invention adopts following technological scheme to realize its goal of the invention, a kind of fastening piece, and it is processed into by carbon/carbon composite.
A kind of fastening piece, it is made through base-density-plasticization and modification-machining-purification by the charcoal fiber.
It comprises screw, bolt, double-screw bolt, nut, pad fastening piece of the present invention.
The production technology of a kind of fastening piece of the present invention, it may further comprise the steps:
(1) base: the net tire that will be made by the charcoal fiber and net tire or charcoal cloth and charcoal cloth or net tire and charcoal cloth crossover are placed to required thickness, make it compound by acupuncture or puncture, make the carbon/carbon composite base substrate of necessary requirement;
(2) density: the base substrate of step (1) gained through chemical vapor infiltration (deposition) and/or liquid infiltration density, is made the carbon/carbon composite of necessary requirement;
(3) plasticization and modification: step (2) gained carbon/carbon composite be impregnated in the resin adhesive liquid;
(4) machining:, be machined to the fastening piece of required form and size with the carbon/carbon composite of step (3) gained;
(5) purify: the fastening piece of step (4) gained is put into High Temperature Furnaces, under vacuum condition, add wherein impurity of heat abstraction.
As a kind of improvement of the present invention, be to carry out step (6) to clean after step (5): be about to fastening piece and rinse well, make its cleaning surfaces free from dust and any staining, baking is dry then; After step (6), carry out step (7) surface treatment, be about to fastening piece and place the CVD stove, carry out chemical vapor deposition; Fastening piece under 800 ℃～1100 ℃ temperature, in propylene and/or rock gas atmosphere, carries out surface treatment to it in chemical vapor deposition stove.
The present invention is in step (1), and the surface density of described net tire is 30g/m
2～130g/m
2Depth of needling is 15mm～30mm; Needling density is 3 times/cm
2～10 times/cm
2Charcoal cloth density is 120g/m
2～300g/m
2, layer density is 7 layers/cm～30 layer/cm.
The present invention is in step (2), and density is 1.1g/m after the base substrate density
3～1.8g/m
3
The present invention is in step (3), and dip time is 10 minutes～90 minutes.
Because adopt technique scheme, the present invention has realized goal of the invention preferably.Because carbon fiber composite inside has accurate three-dimensional structure, the fastening piece of being processed into, has the excellent little and anti-rapid heat cycle of high specific strength, thermal expansion coefficient and indeformable indehiscent performance, its resistance to flexure is about ten times of graphite, make it to be not easy under the effect of external force or in the working environment of rapid heat cycle, to break, significantly improve its working life, can reach more than 1 year through the life-span on probation; Because it is it has the greasy property of graphite, easy to loading and unloading during use again; Through after the surface treatment, its cleaning surfaces does not fall ash, can not pollute surrounding environment, part, raw material and finished product etc.
Description of drawings:
Fig. 1 is the structural representation of double-screw bolt 3 of the present invention, nut 4;
Fig. 2 is the structural representation of bolt 2 of the present invention, nut 4;
Fig. 3 is the structural representation of screw 1 of the present invention.
Embodiment:
The invention will be further described below in conjunction with accompanying drawing.
Embodiment 1:
Double-screw bolt 3 can be made into isometrically in the accompanying drawing 1, i.e. each section diameter basically identical also can be made into waneyly, and its two is threaded, be used with nut 4, during use by the nut 4 at two or add clamping plate connected piece is clamped.Nut 4 can be made into circle, square, hexagon and bent limit shape (present embodiment is a hexagon).Its production technology may further comprise the steps:
(1) base:
Shredding becomes net: choose the long short carbon fiber of 6～70mm, become fluffy single shape fiber through the shredding of shredding equipment, then the good charcoal fiber of shredding through air lay and/or carding, utilize the lapping machine to be paved into fleece again, sting into the net tire in advance.The surface density of described net tire is 30g/m
2～130g/m
2(present embodiment is 100g/m
2); Charcoal cloth is formed by the braiding of charcoal fiber tuft, and charcoal cloth density is 120g/m
2～300g/m
2(present embodiment is 230g/m
2).
Lamination is compound: the net tire of gained is tiled on the worktable, spreads layer charcoal cloth then in the above, a shop layer net tire on charcoal cloth makes it compound by acupuncture again, and depth of needling is 15mm～30mm (present embodiment is 23mm); 3 times/cm of needling density
2～10 times/cm
2(present embodiment is 9 times); Layer density be 7 layers/cm～30 layer/cm (present embodiment be 12 layers/cm), so repeat to make the carbon/carbon composite base substrate of necessary requirement.Maybe net tire and charcoal cloth crossover are placed to required thickness, make the carbon/carbon composite base substrate of necessary requirement by puncture.
Also can adopt net tire and net tire or charcoal cloth and charcoal cloth to make the carbon/carbon composite base substrate of necessary requirement by acupuncture or puncture.
(2) density: the base substrate density of step (1) gained is become carbon/carbon composite.Thickening technology includes but not limited to chemical vapor infiltration (deposition) and/or liquid infiltration, its density is progressively increased and through charing (as needs) and graphitization processing, it is 1.1g/m that prefabricated component is processed into density
3～1.8g/m
3(present embodiment is 1.5g/m
3) carbon/carbon composite;
(3) plasticization and modification: step (2) gained carbon/carbon composite be impregnated in (present embodiment is an epoxy resin adhesive liquid) in the resin adhesive liquid, and dip time is 10 minutes～90 minutes (present embodiment is 35 minutes); Strengthen its plasticity, improve its processibility, eliminate the phenomenon that collapses in the machining process.The present invention can also adopt alkyd resin, acrylic resin etc.
(4) machining:, be machined to needed double-screw bolt 3 and nut 4 with the carbon/carbon composite of step (3) gained plasticization and modification.
(5) purify: the fastening piece of step (4) gained is put into High Temperature Furnaces, be heated to 800 ℃-1600 ℃ (present embodiment is 1200 ℃) under vacuum condition ,-360 minutes (present embodiment is 200 minutes) removes wherein impurity to be incubated 60 minutes.
For making its cleaning surfaces free from dust and any staining, increase step (6) and clean: be about to double-screw bolt 3 and nut 4 and rinse well, baking is dry then.
For making double-screw bolt 3 and nut 4 cleaning surfaces not fall ash, during use, can not stain surrounding enviroment; Hand can not glue the evil backstage manipulator when taking yet.Increase step (7) surface treatment: be about to double-screw bolt 3 and nut 4 and place the CVD stove, carry out chemical vapor deposition.Promptly under 800 ℃～1100 ℃ (present embodiment is 900 ℃) temperature, (present embodiment is a propylene) carries out surface treatment to it in propylene and/or rock gas atmosphere.
According to usage requirement, also can will directly come into operation through double-screw bolt 3 and nut 4 after the step (5), and without step (6) and step (7).
Embodiment 2:
Present embodiment adopts the dipping thickening technology to make its density density to 1.7g/cm in step (2)
3In step (3), adopt 191 unsaturated polyester resins.
Surplus with embodiment 1.
Embodiment 3:
Present embodiment adopts the chemical vapor deposition method density in step (2), density is 1.3g/cm
3In step (3), adopt urea formaldehyde resin.
Surplus with embodiment 1.
Claims (10)
1, a kind of fastening piece is characterized in that it is processed into by carbon/carbon composite.
2, a kind of fastening piece is characterized in that it is made through base-density-plasticization and modification-machining-purification by the charcoal fiber.
3, a kind of fastening piece according to claim 1 and 2, it comprises screw [1], bolt [2], double-screw bolt [3], nut [4], pad to it is characterized in that described fastening piece.
4, a kind of production technology as a kind of fastening piece as described in the claim 2 is characterized in that may further comprise the steps:
(1) base: the net tire that will be made by the charcoal fiber and net tire or charcoal cloth and charcoal cloth or net tire and charcoal cloth crossover are placed to required thickness, make it compound by acupuncture or puncture, make the carbon/carbon composite base substrate of necessary requirement;
(2) density: the base substrate of step (1) gained through chemical vapor infiltration (deposition) and/or liquid infiltration density, is made the carbon/carbon composite of necessary requirement;
(3) plasticization and modification: step (2) gained carbon/carbon composite be impregnated in the resin adhesive liquid;
(4) machining:, be machined to the fastening piece of required form and size with the carbon/carbon composite of step (3) gained;
(5) purify: the fastening piece of step (4) gained is put into High Temperature Furnaces, under vacuum condition, add wherein impurity of heat abstraction.
5, according to the production technology of the described a kind of fastening piece of claim 4, it is characterized in that carrying out step (6) and clean after step (5): be about to fastening piece and rinse well, make its cleaning surfaces free from dust and any staining, baking is dry then.
6, according to the production technology of the described a kind of fastening piece of claim 5, it is characterized in that after step (6), carrying out step (7) surface treatment, be about to fastening piece and place the CVD stove, carry out chemical vapor deposition.
7, according to the production technology of the described a kind of fastening piece of claim 6, it is characterized in that fastening piece in chemical vapor deposition stove, under 800 ℃～1100 ℃ temperature, in propylene and/or rock gas atmosphere, carry out surface treatment.
8,, it is characterized in that in the step (1), the surface density of described net tire is 30g/m according to the production technology of the described a kind of fastening piece of claim 4
2～130g/m
2Depth of needling is 15mm～30mm; Needling density is 3 times/cm
2～10 times/cm
2Charcoal cloth density is 120g/m
2～300g/m
2, layer density is 7 layers/cm～30 layer/cm.
9,, it is characterized in that in step (2), density is 1.1g/m after the base substrate density according to the production technology of the described a kind of fastening piece of claim 4
3～1.8g/m
3
10,, it is characterized in that in step (3) dip time is 10 minutes～90 minutes according to the production technology of the described a kind of fastening piece of claim 4.