CN101250039A - Preparation technology of coal ash fiberboard material - Google Patents
Preparation technology of coal ash fiberboard material Download PDFInfo
- Publication number
- CN101250039A CN101250039A CNA2008100350349A CN200810035034A CN101250039A CN 101250039 A CN101250039 A CN 101250039A CN A2008100350349 A CNA2008100350349 A CN A2008100350349A CN 200810035034 A CN200810035034 A CN 200810035034A CN 101250039 A CN101250039 A CN 101250039A
- Authority
- CN
- China
- Prior art keywords
- coal ash
- water
- fly ash
- ash fiber
- agent solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Disclosed is a preparing technique for fly ash fiber plate, which is characterized by preparing water-resistant agent solution in advance, the steps comprise heating water to a certain temperature, adding ethylene glycol monobutyl ether in the heating water, adding organic acid in the heating water, stirring until the organic acid is dissolved completely, thereby obtaining the water-resistant agent, further heating fly ash fiber to 100-150 DGE C, uniformly spraying acrylic resin emulsion on the fly ash fiber, keeping in the temperature and hot pressing in certain pressure intensity, thereby forming the fly ash fiber plate, further putting the fly ash fiber plate in a baking oven to a temperature from 100 DGE C to 150 DGE C, keeping the temperature, uniformly spraying the water-resistant agent solution on the fly ash fiber plate and then drying, thereby the final fly ash fiber plate is obtained. The fly ash fiber plate prepared according to the preparing technique is lightweight, water-resistant and is good in flame-proof property, which is capable of using as building materials and adapting for heat preservation of suspended ceiling and external and internal wall.
Description
Technical field
The present invention relates to a kind of technology of preparing of coal ash fiberboard material, specifically, is to prepare coal ash fiberboard material with emulsion as caking agent, the coal ash fiberboard material surface is carried out the processing method of anti-water treatment again.
Background technology
Coal ash fiber is a specific admixture inorganic oxide fibres of development in recent years.Flyash is the industrial residue and the discharge of China's maximum, is mainly derived from the residue of combustion of burning blast furnace and thermal power generation, goes beyond 600,000,000 tons every year.The main body Chemical Composition of flyash is SiO
2, Al
2O
3, CaO, Fe
2O
3And a spot of TiO
2, MgO.Its most elements is identical with the contained element of original mineral products material.Along with the long-term exploitation and the use of industry, the mineral products natural resource are day by day exhausted, and coal burning waste flyash day by day increases, and is piled into sorrow.Therefore, utilize the Chemical Composition and the structural performance of flyash, its deep processing is changed into the industrial application raw material, the instead of part natural mineral resource is one of problem of investigator's interest in recent years.Fly-ash Preparation is become to have the ultra-fine inorganic fibre of high value, and then utilize fiber to realize multiple use: make paper pulp and be used to produce the cardboard paper product; Make heat preservation and soundproof lagging material and energy-saving wall material; Make light flame-retardant building room furred ceiling; Make fiber-resin composite; Be used for industrial filter material; Be used to pessimum of improving road asphalt cold cracking, hot mastication etc.
Flyash can with its fusion, adopt centrifuging, multiple roll centrifuging or blowing process to produce cellucotton by high temperature under the collocation of inorganic fusing assistant (magnesite, rhombspar, Wingdale etc.) and cullet, and its diameter is between 4 μ m-9 μ m.
The present domestic flyash fibrillating technique that realized, in the production solid residue behind flyash or the blast-furnace roasting is added necessary auxiliary agent and water, fusing at high temperature after stirring and granulation, again through pressurization, by the centrifugal silk that throws away into of multistage running roller, by cooling and surface treatment, make inorganic coal ash fiber.This fiber has been applied to the industrial heat preservation material and has made inorganic fiber paper pulp partly substituting the xylon pulp applications in paper industry.Further rationally utilize this inorganic fibre from the waste preparation, turning waste into wealth has important strategic meaning and economic worth.
Chinese patent CN1457965 discloses a kind of method of bionic reinforced plate, and it is to be the technology of main material production processing non-wood plate with the agricultural crop straw.Its technical essential is to adopt semidrying, chooses the blank of different classes of, different size and structure according to the purposes of finished product, adopts after the atomization applying glue and mats formation compression moulding then with station or flowing water dystopy.In pavement process, adopt the atomizing spray glue limit, blank limit of different size to mat formation, and precompressed successively.Being distributed as of each layer: middle is the reinforcement layer, and the both sides of reinforcement layer are followed successively by the coarse fodder layer, and fines layer, described glue are dialdehyde starch, protein complex, the polymer-binder of perhaps selecting the water-soluble polymer resin treatment to become.
Chinese patent CN1450017 discloses a kind of environment protection type inorganic inner/outer dry wallboard making process and prescription, and this invention is a kind of by magnesium chloride, magnesium oxide, long fibered pulp, anti reversed halogen agent, and release agent, enhancing toughner prescription are formed.Ooze technologies such as waterproof layer, packing, warehouse-in through mixing of materials, depositing, repeatedly roll-in, curing, the demoulding, maintenance, deburring, washing, drying, surface and make a kind of decorating inner and external walls sheet material of complete environmental protection, his characteristics are in light weight, can follow closely, can dig, Pasting, do not contain oxious components such as glass fibre, asbestos, mineral wool, but can guarantee that sheet material has enough intensity, convenient transportation, feel and sense organ are very good, can also carry out mechanize production and the production of surface pressure decorative pattern streamline.Overcome common magnesium chloride, magnesium oxide is the inside and outside wall board of base-material.Glass emergence on the surface, texture be as tile, and surperficial steam bubble is many can not mass mechanized production and the plate embossed surface streamline shortcoming of producing.
Chinese patent CN1141992 discloses a kind of light sound-insulation building plate of cinder and concrete, it is the light sound-insulation building board of main raw material with the slag that this invention belongs to a kind of, it mainly is made of cinder concrete base material and enhancing material, the umber that it is characterized in that the main ingredient of described cinder concrete base material is respectively slag 100 by its parts by weight, gelling material 10-35, water-resisting agent 0.1-1, conditioning agent 0.1-1, water 15-35, described enhancing material is glass fibre, reinforcing bar or non-woven fabrics.
Chinese patent CN1162520 discloses a kind of ceramsite concrete light-weight wall boards and manufacturing process thereof, and this invention relates to a kind of material of construction, particularly materials for wall.It is to be jelling agent with cement, is aggregate with the haydite, is stopping composition with the pearlstone, adds special building glue, and strengthens with the alkali resistant glass fiber net at surface layer, makes through special procedure.
Chinese patent CN1408671 discloses a kind of method for making of high temperature resistant, high strength and high density degree calcium silicate board, with silicon metal micro mist, non-crystalline silicon micro mist, calcareous raw material, mineral add material, filamentary material is a raw material, with CaO: SiO
2Mol ratio is 0.95～1.05 batching, add 1～8% filamentary material then, 0～12% mineral add material, mix the back and make sheet material or bulk with die mould method or casting, sheet material or bulk are delivered to steam-cured still under 190 ℃～200 ℃ saturated vapor condition steam-cured 6～20 hours, oven dry is finished product to moisture below 5% in 100 ℃～180 ℃ hot blasts.
Chinese patent CN85107095 discloses a kind of bamboo fiber reinforced composite material, this invention proposes to substitute timber and steel with bamboo-plastic composite material, manufacture various types of sheet materials and section bar, and propose to replace glass fibre, make enhanced artificial marble, plastering, concrete, asphalt waterproofing material and wood-based plate with bamboo-plastic composite material.
Chinese patent CN1048003 discloses a kind of manufacture method of diversity composite sheet, refers to a kind of manufacture method of the compound plate material with characteristics such as high strength, vibration strength, thermal insulation and sound insulations especially; Its main process is that regenerated fiber is prefabricated into cloth, this cloth is mixed uniformly with modulation in advance soak the material dipping again, again through neutralization, the baking universe, roll extrusion, applying and roll extrusion once more, and makes a kind of composite sheet.
Chinese patent CN1393609 discloses a kind of fire-proof board and manufacture method thereof, it is that a kind of to make a kind of by material step, feeding step, cutting step, fixating shape step and baking step be base material with the polyester capillaries to comprise at least, and in the base material outside and internal fiber gap completely filled mineral matter filler material, and the high structural strength that constitutes, and fire-proof board with sound insulation, effect such as heat insulation.
Chinese patent CN1459431 discloses electro-conductive fiber and has strengthened calcium silicate board, and the shape of product of this invention is a sheet material, and it comprises the raw material of following weight parts: silica powder 30-50 part, conductive carbon black 1-10 part, slaked lime 25-45 part, fortifying fibre 8-13 part.It has excellent conducting performance, anti-electrostatic, can absorb electromagnetism involves the intensity advantages of higher.
Innovative point of the present invention is: the fiber that utilizes trade waste flyash to make helps environment protection; Flyash is used to make sheet material after making fiber, helps moulding, simultaneously the timber intensity of making is improved greatly; Flyash makes that structure is fluffy behind the fiber, bulk density is little, so the sheet material proportion of making is little, is used for the load that building materials can reduce buildings; Coal ash fiber belongs to inorganic materials, and the good flame resistance than organic materials helps safety; The present invention carries out surperficial anti-water treatment to coal ash fiberboard material, can intensity not reduce after making sheet material meet water, also make sheet material meet water simultaneously after, deadweight is increased, help the safety of buildings.
Summary of the invention
A kind of technology of preparing of coal ash fiberboard material is characterized in that, earlier preparation water repellent agent solution, its method is: water is heated to certain temperature, butyl glycol ether is joined in the hot water, organic acid is joined in the hot water again, stirring is dissolved organic acid fully, obtains water repellent agent solution.Coal ash fiber is heated to 100-150 ℃ then, spray after the acrylic resin emulsion equably thereon, continuation is carried out hot-forming under this temperature and certain pressure, obtain coal ash fiberboard material, again sheet material is put into 100-150 ℃ baking oven, under this temperature, water repellent agent solution is sprayed onto on the coal ash fiberboard material equably, promptly obtains final coal ash fiberboard material after the drying.
Described hot water temperature is 60--80 ℃.
Described organic acid can be: one or more in oleic acid, stearic acid, Witco 1298 Soft Acid, the lauric acid.
Described water repellent agent solution is made up of butyl glycol ether, organic acid, water; Wherein the mass content of butyl glycol ether is 1-20%, and the organic acid mass content is 1-20%, and the mass content of water is 60-98%.
Described acrylic resin emulsion can be in benzene emulsion, pure-acrylic emulsion, acrylate and vinyl acetate emulsion, the organosilicon crylic acid latex one or more.
Described sprinkling acrylic resin emulsion uses the emulsion of commercially available 45-50%wt solid content, and its consumption is 0.5%～3% of a dry state coal ash fiber quality.
Described coal ash fiber hot press molding pressure is 0.5-10MPa.
The sprinkling consumption of described water repellent agent solution on coal ash fiberboard material is 30---150g/m
2Coal ash fiberboard material.
The density of coal ash fiberboard material adopts ISO 1183-2-2004 method to measure.
Sample preparation of sample compressive strength and testing method are carried out with reference to GB/T 1964-1996, and sample preparation of sample shock strength and testing method are carried out with reference to GB/T 1843-1996, and sample preparation of sample tensile strength and testing method are carried out with reference to GB/T 1446-2005.
The coal ash fiberboard material of the present invention's preparation, density 350～500kg/m3; Compressive strength 1.48～1.56MPa; Shock strength 0.49～0.60 (kJ/m2); Tensile strength 0.10～0.13MPa.
With the coal ash fiberboard material of present technique preparation, light weight, anti-water have better flame retardant properties again, can make material of construction, are used for the insulation of furred ceiling, interior exterior wall.
Embodiment
Embodiment 1
In the glass flask that the 2000ml band stirs, add 680g water, open and stir, begin heating, when temperature rises to 60 ℃, the 95g butyl glycol ether is joined in the hot water, the stearic acid with 95g joins in the glass flask again, stirring is dissolved stearic acid fully, promptly obtains water repellent agent solution 850g.The 150kg coal ash fiber is heated to 150 ℃, 1kg benzene emulsion (solid content is 48%wt) is diluted with 5kg water, be sprayed onto on the coal ash fiber equably then, it is framed to put into 0.5m * 0.5m again, hot-forming under 150 ℃, the pressure of 10MPa, obtain being of a size of 0.5m * 0.5m, thickness after the demoulding and be 21 of the coal ash fiberboard materials of 0.05m, gross weight 131kg, again sheet material is put into 150 ℃ baking oven, 850g water repellent agent solution is sprayed onto the coal ash fiberboard material surface equably.150 ℃ of oven dry down, promptly obtain coal ash fiberboard material.Coal ash fiberboard material is measured density according to the ISO1183-2-2004 method; Make batten according to GB/T 1964-1996, GB/T 1843-1996, GB/T1446-2005 etc., difference test compression intensity, shock strength and tensile strength, data are listed in table 1.
Table 1 coal ash fiberboard material mechanical property
| Coal ash fiberboard material | Density (kg/m 3) | Compressive strength (MPa) | Shock strength (kJ/m 2) | Tensile strength (MPa) |
| No.1 | 500 | 1.56 | 0.60 | 0.13 |
Embodiment 2
In the glass flask that the 500ml band stirs, add 300g water, open and stir, begin heating, when temperature rises to 80 ℃, the 60g butyl glycol ether is joined in the hot water, the lauric acid with 60g joins in the glass flask again, stirring is dissolved lauric acid fully, promptly obtains water repellent agent solution 405g.The 150kg coal ash fiber is heated to 100 ℃, 4.5kg pure-acrylic emulsion (solid content is 46%) is diluted with 10kg water, be sprayed onto on the coal ash fiber equably then, it is framed to put into 0.5m * 0.5m again, hot-forming under 100 ℃, the pressure of 2MPa, obtain being of a size of 0.5m * 0.5m, thickness after the demoulding and be 30 of the coal ash fiberboard materials of 0.05m, gross weight 133kg, again sheet material is put into 100 ℃ baking oven, 405g water repellent agent solution is sprayed onto the coal ash fiberboard material surface equably.100 ℃ of oven dry down, promptly obtain coal ash fiberboard material.Coal ash fiberboard material is measured density according to the ISO1183-2-2004 method; Make batten according to GB/T 1964-1996, GB/T 1843-1996, GB/T1446-2005 etc., difference test compression intensity, shock strength and tensile strength, data are listed in table 2.
Table 2 coal ash fiberboard material mechanical property
| Coal ash fiberboard material | Density (kg/m 3) | Compressive strength (MPa) | Shock strength (kJ/m 2) | Tensile strength (MPa) |
| No.2 | 357 | 1.48 | 0.49 | 0.10 |
Embodiment 3
In the glass flask that the 500ml band stirs, add 255g water, open and stir, begin heating, when temperature rises to 65 ℃, the 10g butyl glycol ether is joined in the hot water, the oleic acid with 10g joins in the glass flask again, stirring is dissolved oleic acid fully, promptly obtains water repellent agent solution 259g.The 150kg coal ash fiber is heated to 110 ℃, 2kg acrylate and vinyl acetate emulsion (solid content is 45%) is diluted with 6kg water, be sprayed onto on the coal ash fiber equably then, it is framed to put into 0.5m * 0.5m again, hot-forming under 110 ℃, the pressure of 4MPa, obtain being of a size of 0.5m * 0.5m, thickness after the demoulding and be 24 of the coal ash fiberboard materials of 0.05m, gross weight 128kg, again sheet material is put into 110 ℃ baking oven, 259g water repellent agent solution is sprayed onto the coal ash fiberboard material surface equably.110 ℃ of oven dry down, promptly obtain coal ash fiberboard material.Coal ash fiberboard material is measured density according to the ISO1183-2-2004 method; Make batten according to GB/T 1964-1996, GB/T 1843-1996, GB/T1446-2005 etc., difference test compression intensity, shock strength and tensile strength, data are listed in table 3.
Table 3 coal ash fiberboard material mechanical property
| Coal ash fiberboard material | Density (kg/m 3) | Compressive strength (MPa) | Shock strength (kJ/m 2) | Tensile strength (MPa) |
| No.3 | 428 | 1.49 | 0.50 | 0.11 |
Embodiment 4
In the glass flask that the 1000ml band stirs, add 600g water, open and stir, begin heating, when temperature rises to 70 ℃, the 40g butyl glycol ether is joined in the hot water, Witco 1298 Soft Acid with 60g joins in the glass flask again, stirs Witco 1298 Soft Acid is dissolved fully, promptly obtains water repellent agent solution 682g.The 150kg coal ash fiber is heated to 120 ℃, 3kg organosilicon crylic acid latex (solid content is 49%) is diluted with 8kg water, be sprayed onto on the coal ash fiber equably then, it is framed to put into 0.5m * 0.5m again, hot-forming under 120 ℃, the pressure of 7MPa, obtain being of a size of 0.5m * 0.5m, thickness after the demoulding and be 23 of the coal ash fiberboard materials of 0.05m, gross weight 130kg, again sheet material is put into 120 ℃ baking oven, 682g water repellent agent solution is sprayed onto the coal ash fiberboard material surface equably.120 ℃ of oven dry down, promptly obtain coal ash fiberboard material.Coal ash fiberboard material is measured density according to ISO 1183-2-2004 method; Make batten according to GB/T 1964-1996, GB/T1843-1996, GB/T 1446-2005 etc., difference test compression intensity, shock strength and tensile strength, data are listed in table 4.
Table 4 coal ash fiberboard material mechanical property
| Coal ash fiberboard material | Density (kg/m 3) | Compressive strength (MPa) | Shock strength (kJ/m 2) | Tensile strength (MPa) |
| No.4 | 454 | 1.51 | 0.52 | 0.12 |
Embodiment 5
In the glass flask that the 1000ml band stirs, add 450g water, open and stir, begin heating, when temperature rises to 68 ℃, the 42g butyl glycol ether is joined in the hot water, the stearic acid with 68g joins in the glass flask again, stirring is dissolved stearic acid fully, promptly obtains water repellent agent solution 549g.The 150kg coal ash fiber is heated to 140 ℃, 2.6kg benzene emulsion (solid content is 48%) is diluted with 7kg water, be sprayed onto on the coal ash fiber equably then, it is framed to put into 0.5m * 0.5m again, hot-forming under 120 ℃, the pressure of 7MPa, obtain being of a size of 0.5m * 0.5m, thickness after the demoulding and be 22 of the coal ash fiberboard materials of 0.05m, gross weight 129kg, again sheet material is put into 140 ℃ baking oven, 549g water repellent agent solution is sprayed onto the coal ash fiberboard material surface equably.140 ℃ of oven dry down, promptly obtain coal ash fiberboard material.Coal ash fiberboard material is measured density according to the ISO1183-2-2004 method: make batten according to GB/T 1964-1996, GB/T 1843-1996, GB/T1446-2005 etc., difference test compression intensity, shock strength and tensile strength, data are listed in table 5.
Table 5 coal ash fiberboard material mechanical property
| Coal ash fiberboard material | Density (kg/m 3) | Compressive strength (MPa) | Shock strength (kJ/m 2) | Tensile strength (MPa) |
| No.5 | 469 | 1.52 | 0.54 | 0.12 |
Embodiment 6
In the glass flask that the 500ml band stirs, add 300g water, open and stir, begin heating, when temperature rises to 75 ℃, the 33g butyl glycol ether is joined in the hot water, Witco 1298 Soft Acid with 42g joins in the glass flask again, stirs Witco 1298 Soft Acid is dissolved fully, promptly obtains water repellent agent solution 363g.The 150kg coal ash fiber is heated to 145 ℃, 4kg acrylate and vinyl acetate emulsion (solid content is 47%) is diluted with 9kg water, be sprayed onto on the coal ash fiber equably then, it is framed to put into 0.5m * 0.5m again, hot-forming under 120 ℃, the pressure of 7MPa, obtain being of a size of 0.5m * 0.5m, thickness after the demoulding and be 21 of the coal ash fiberboard materials of 0.05m, gross weight 127kg, again sheet material is put into 145 ℃ baking oven, 363g water repellent agent solution is sprayed onto the coal ash fiberboard material surface equably.145 ℃ of oven dry down, promptly obtain coal ash fiberboard material.Coal ash fiberboard material is measured density according to ISO 1183-2-2004 method; Make batten according to GB/T 1964-1996, GB/T1843-1996, GB/T 1446-2005 etc., difference test compression intensity, shock strength and tensile strength, data are listed in table 6.
Table 6 coal ash fiberboard material mechanical property
| Coal ash fiberboard material | Density (kg/m 3) | Compressive strength (MPa) | Shock strength (kJ/m 2) | Tensile strength (MPa) |
| No.6 | 484 | 1.55 | 0.57 | 0.13 |
Claims (8)
1. the technology of preparing of a coal ash fiberboard material is characterized in that, earlier preparation water repellent agent solution, its method is: water is heated to certain temperature, butyl glycol ether is joined in the hot water, organic acid is joined in the hot water again, stirring is dissolved organic acid fully, obtains water repellent agent solution.Coal ash fiber is heated to 100-150 ℃ then, spray after the acrylic resin emulsion equably thereon, continuation is carried out hot-forming under this temperature and certain pressure, obtain coal ash fiberboard material, again sheet material is put into 100-150 ℃ baking oven, under this temperature, water repellent agent solution is sprayed onto on the coal ash fiberboard material equably, promptly obtains final coal ash fiberboard material after the drying.
2. the hot water temperature described in the claim 1 is 60--80 ℃.
3. the organic acid described in the claim 1 can be: one or more in oleic acid, stearic acid, Witco 1298 Soft Acid, the lauric acid.
4. the water repellent agent solution described in the claim 1 is made up of butyl glycol ether, organic acid, water; Wherein the mass content of butyl glycol ether is 1-20%, and the organic acid mass content is 1-20%, and the mass content of water is 60-98%.
5. the acrylic resin emulsion described in the claim 1 can be in benzene emulsion, pure-acrylic emulsion, acrylate and vinyl acetate emulsion, the organosilicon crylic acid latex one or more.
6. the sprinkling acrylic resin emulsion described in the claim 1 uses the emulsion of commercially available 45-50%wt solid content, and its consumption is 0.5%～3% of a dry state coal ash fiber quality.
7. the coal ash fiber hot press molding pressure described in the claim 1 is 0.5-10MPa.
8. the sprinkling consumption of the water repellent agent solution described in the claim 1 on coal ash fiberboard material is 30---150g/m
2Coal ash fiberboard material.