CN101210149A - Antiskid ventilating epoxide terrace paint - Google Patents
Antiskid ventilating epoxide terrace paint Download PDFInfo
- Publication number
- CN101210149A CN101210149A CNA2007103080366A CN200710308036A CN101210149A CN 101210149 A CN101210149 A CN 101210149A CN A2007103080366 A CNA2007103080366 A CN A2007103080366A CN 200710308036 A CN200710308036 A CN 200710308036A CN 101210149 A CN101210149 A CN 101210149A
- Authority
- CN
- China
- Prior art keywords
- epoxy
- antiskid
- ventilating
- powder
- epoxide terrace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an antiskid and ventilating epoxy floor coating, which comprises base material and powder material with weight mixture ratio of 1 portion of base material and 1-2 portions of powder material. The base material mainly comprises epoxy resin, epoxy hardener and addition agent with weight mixture ratio of 60 portions of epoxy resin, 25 portions of epoxy hardener and 15 portions of addition agent. The invention has the advantages of: 1. no formaldehyde and no VOC after curing; 2. excellent binding capacity with the base material without peeling and hollowing; 3. certain air permeability, thus being capable of avoiding phenomena such as bubbling, cracking, etc., resulted from vapor pressure; 4. high strength and excellent antiskid, wear resistant and impact resistant performances; 5. excellent corrosion resistance and water resistance; 6. certain flexibility and cracking prevention, thereby being capable of avoiding cracking to certain degree.
Description
Technical field
The present invention relates to building material field, mainly is a kind of antiskid ventilating epoxide terrace paint.
Background technology
Raising day by day along with China's economic level, to the also corresponding raising of environment requirement, at present the most large-scale underground garage of China, industrial building, market, hospital and real dangerous chamber etc. all begin to adopt all types of industries terrace lacquer system to satisfy the requirement of dustproof, corrosion-resistant, resistance to compression, washability.Because the epoxy paint film has better physical mechanical property and excellent chemical resistance, and smooth bright and clean, ornamental strong advantage, can satisfy the requirement of modern various industry and civilian terrace, uses very extensive.
But, do not lay flooring base the problem that waterproof layer or waterproof layer have the underground aqueous vapor effusion ground that breakage etc. causes because all existing, caused epoxide terrace in construction and solidification process because aqueous vapor influence, caused the downgrade of the geographic epoxide terrace of this infiltration, in addition destroyed fully.
In practical project,, also there are not a kind of cost-effective construction and remedial measures at present to not laying the flooring base of waterproof layer; And repair damaged waterproof layer and need chisel thick concrete layer, also be difficult to reach and prevent that fully aqueous vapor from oozing the ease and the effect of ground water seepage.
Summary of the invention
The present invention is for overcoming above-mentioned deficiency, invent a kind of antiskid ventilating epoxide terrace paint, under the prerequisite that satisfies functions such as general terrace lacquer is dustproof, corrosion-resistant, resistance to compression, washability, and advantage such as carried out anti-skidding, environmental protection again, breathe freely.
The present invention solves the technical scheme of its technical problem.This antiskid ventilating epoxide terrace paint comprises base-material and powder, and the weight proportion of base-material and powder is: 1 part of base-material, 1 ~ 2 part of powder; Base-material mainly comprises Resins, epoxy, epoxy hardener, auxiliary agent, and its weight proportion is: 60 parts of Resins, epoxy, 15 parts of 25 parts of epoxy hardeners and auxiliary agents.
Described auxiliary agent is ventilative particle, and described powder is 20 ~ 80 order quartz sands, and epoxy hardener adopts polyamide-based epoxy curing agent, reacts the eleostearic acid dimer polyamine of making by eleostearic acid and polyamine.
The effect that the present invention is useful is:
1, do not contain formaldehyde, solidify the back VOC free.
2, with base material good viscosifying power is arranged, do not flake, not hollowing.
3, have certain permeability, can prevent because of phenomenons such as bubbling that vapour pressure produces, crackings.
4, intensity height, superior anti-skid wearable and impact resistance.
5, superior erosion resistance and water resistance.
6, have certain flexible and anti-cracking effect, can play bridging effect to be full of cracks within the specific limits.
7, easy construction reduces construction intensity, improves operating efficiency.
8, artistic texture is strong, and color can be selected arbitrarily, good decorating effect.
Embodiment
The present invention is further detailed explanation below in conjunction with embodiment.
One, composition of the present invention:
Performances such as dustproof, corrosion-resistant, resistance to compression, washability are the basic demands of terrace lacquer, and bi-component epoxide-resin is because its superior physical and chemical performance forms and is first-selection, and wherein Resins, epoxy is host.
Choosing proper curing agents also is important link.Actual from engineering construction, it is better that we have chosen a kind of workability, proportion scale compares broad, nontoxicity, no volatile matter, can be in the metal and the concrete surface construction of humidity, the epoxy curing agent of ambient cure, it also can make cured product have high elasticity and bonding force and water tolerance.
The adding of auxiliary agent can further improve the various performances of epoxide terrace.Wherein ventilative particle can produce micron-sized breather hole on epoxy film behind the epoxy resin cure.In Resins, epoxy, add various pigment and can reach different color effects, thereby make epoxide terrace have abundant decorative effect.
In the practice of construction process,, must add 20～80 purpose quartz sands, mix for reaching the effect of anti-skid wearable.
Two, Analysis on Mechanism of the present invention
1, Resins, epoxy
Resins, epoxy is the organic high molecular compound that contains two or more epoxide groups in the general reference molecule.The molecular structure of Resins, epoxy is containing active epoxide group in the molecular chain for its feature, and epoxide group can be positioned at the end, centre of molecular chain or structure circlewise.Owing to contain active epoxide group in the molecular structure, make them form insoluble, the infusible cancellated superpolymer of three-dimensional that has with polytype solidifying agent generation crosslinking reaction.The performance of its Resins, epoxy and characteristic
(1) various informative.Various resins, solidifying agent, modifier system almost can adapt to various application to the form requirement, and its scope can be from extremely low viscosity to high melting solid.
(2) solidify conveniently.Select various solidifying agent for use, epoxy-resin systems almost can solidify in 0～180 ℃ of temperature range.
(3) adhesive power is strong.The existence of inherent polarity hydroxyl and ehter bond in the Resins, epoxy molecular chain makes it have very high adhesive power to various materials.Shrinkability during epoxy resin cure is low, and the internal stress of generation is little, also helps to improve adhesion strength.
(4) shrinkability is low.The reaction of Resins, epoxy and used solidifying agent is that the ring-opening polymerization by epoxy group(ing) in direct addition reaction or the molecular resin carries out, and does not have water or other volatile byproducts to emit.They are compared with unsaturated polyester resin, resol, demonstrate very low shrinkability in solidification process.
(5) mechanical property.Epoxy-resin systems after the curing has excellent mechanical property.
(6) electrical insulation capability.Epoxy-resin systems after the curing is a kind of superior isolation material with high dielectric property, anti-surface leakage, anti-electric arc.
(7) chemical stability.Epoxy-resin systems after the curing has good alkali resistance, acid resistance and solvent resistance.Chemical stability depends on selected resin and solidifying agent.Suitably select Resins, epoxy and solidifying agent for use, can make it have special chemical stability.
(8) dimensional stability.Above-mentioned many performances comprehensive makes epoxy-resin systems have outstanding dimensional stability and weather resistance.
(10) anti-mould.The anti-most of moulds of solidified epoxy-resin systems can be used under the tropicalization of harshness.
2, solidifying agent
In the selection of solidifying agent, we are through a series of real danger and contrast, finally adopted a kind of polyamide-based epoxy curing agent, reacted the eleostearic acid dimer polyamine of making, owing to contain long fatty acid carbon chain and amino in the structure by eleostearic acid and polyamine, can make cured product have high elasticity and bonding force and water tolerance, its workability is better, and proportion scale is wide, nontoxicity, no volatile matter can be in the metal and the concrete surface construction of humidity.
3, auxiliary agent
The adding of auxiliary agent is in order further to improve the performance of epoxide terrace paint.Wherein most important auxiliary agent is ventilative particle in the new-type antiskid ventilating epoxide terrace.Because it had breather hole originally, after Resins, epoxy fully solidifies, can produce micron-sized breather hole on epoxy film.In order to enrich the color of epoxide terrace, generally also to add suitable pigment in addition.
4, quartz sand
In order to reach the effect of anti-skid wearable and ventilation property, in construction process, must add 20～80 purpose quartz sands, make terrace surface produce anti-skidding fluctuating, increase frictional force.Under the acting in conjunction of resin, solidifying agent and auxiliary agent, quartz sand produces micropore during with the above-mentioned materials bonding forming and film-forming type becomes ventilation property terrace face preferably.By various constructional methods, make quartz sand form various arrangements and pattern on the surface, thereby reach various artistic effect.
Embodiment 1: this antiskid ventilating epoxide terrace paint, comprise base-material and powder, and the weight proportion of base-material and powder is: base-material 1, powder 1.2; Base-material mainly comprises Resins, epoxy, epoxy hardener, auxiliary agent, and its weight proportion is: Resins, epoxy 60, epoxy hardener 25, auxiliary agent 15; Powder is 20 ~ 80 order quartz sands.
Embodiment 2: this antiskid ventilating epoxide terrace paint, comprise base-material and powder, and the weight proportion of base-material and powder is: base-material 1, powder 1.8; Base-material mainly comprises Resins, epoxy, epoxy hardener, auxiliary agent, and its weight proportion is: Resins, epoxy 60, epoxy hardener 25, auxiliary agent 15; Powder is 20 ~ 80 order quartz sands.
Three, construction technology of the present invention
1, basic unit checks and handles
Basic unit checks and comprises the mensuration of concrete water ratio, the mensuration of planeness, the mensuration of pH value, the mensuration of intensity.For ground grading, generally adopt mechanical means: remove surperficial projection with sandblast or electrical grinding machine, loosening particle destroys pore, and traction-increasing surface is long-pending, absorbs sand grains, impurity, dust with suction cleaner.For more depression, ground, hole, hole are arranged, application of epoxy mortar or epoxy putty carry out next-step operation after filling and leading up repairing again.
2, construction process
Construction technology: be coated with in floor treatment → primary coat → epoxy → dust suction → face is coated with
(1) priming paint construction: with the on-the-spot machinery modulation of composition material, the engineering time of every cover material is no more than 1 hour, and the thickness of construction is 0.10-0.15mm.Tool using is a cylinder, does not stay to connect stranding, requires not leak to scrape priming paint, can not be blocked up, and consumption is roughly 0.10kg/m
2
(2) intermediate layer paint construction: after treating that basal plane is repaired drying, go up the epoxy intermediate layer paint again a time, increase thickness and intensity.
(3) finish paint construction: after treating that the intermediate layer paint thorough drying is solidified, stir antiskid ventilating epoxide terrace paint by the fixed proportion proportioning, the add-on of quartz sand is looked anti-skidding, artistic design etc. require corresponding adding.Decide on basal plane and temperature set time, is generally more than 4-6 hour.
(4) new-type antiskid ventilating epoxide terrace maintenance: complete drying time: 3 days.Curing time at least 10 days.
In addition to the implementation, the present invention can also have other embodiments.All employings are equal to the technical scheme of replacement or equivalent transformation formation, all drop on the protection domain of requirement of the present invention.
Claims (4)
1. antiskid ventilating epoxide terrace paint, it is characterized in that: comprise base-material and powder, the weight proportion of base-material and powder is: 1 part of base-material, 1 ~ 2 part of powder; Base-material comprises Resins, epoxy, epoxy hardener and auxiliary agent, and its weight proportion is: 60 parts of Resins, epoxy, 25 parts of epoxy hardeners, 15 parts of auxiliary agents.
2. according to the described antiskid ventilating epoxide terrace paint of claim 1, it is characterized in that: described auxiliary agent is ventilative particle.
3. according to the described antiskid ventilating epoxide terrace paint of claim 1, it is characterized in that: described powder is 20 ~ 80 order quartz sands.
4. according to the described antiskid ventilating epoxide terrace paint of claim 1, it is characterized in that: epoxy hardener adopts polyamide-based epoxy curing agent, reacts the eleostearic acid dimer polyamine of making by eleostearic acid and polyamine.