CN100593030C - Radium emanation spraying paint - Google Patents
Radium emanation spraying paint Download PDFInfo
- Publication number
- CN100593030C CN100593030C CN 200710048480 CN200710048480A CN100593030C CN 100593030 C CN100593030 C CN 100593030C CN 200710048480 CN200710048480 CN 200710048480 CN 200710048480 A CN200710048480 A CN 200710048480A CN 100593030 C CN100593030 C CN 100593030C
- Authority
- CN
- China
- Prior art keywords
- radium
- spraying paint
- grams
- emanation spraying
- paint according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a radium spraying paint, which comprises the following parts: 0.1-10% Gx radium ink, 1-38% colorful dye and 52-98.5% ester or alcohol solvent. The invention possesses good connection with base, which makes reflective mirror bright enough.
Description
Technical field
The present invention relates to a kind of coating, especially a kind of radium emanation spraying paint.
Background technology
Raising and social progress along with the human living standard, product, advertisement housing decoration effect requirements that people cover with paint, lacquer, colour wash, etc. need are more and more higher, consequent coating of multi-colour pattern, laser luminous coating etc. arise at the historic moment, but up to the present, do not have a kind of can be applicable to industry spraying, color with illumination differently change, specular light is according to the radium emanation spraying paint of foot and anti-high or low temperature.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, provide a kind of be suitable for industry spraying, color with the illumination difference radium emanation spraying paint of conversion, mirror surface illumination foot.
The present invention is mixed by following component and weight ratio:
Radium-shine printing ink GX-5202 0.1-10
Coloured pigment 1-38
Ester or alcoholic solvent 52-98.5
Consider fast in colour durablely, can increase the m-70 laking agent of 0-5 weight part.
Consider thickness degree in the construction of radium emanation spraying paint, can increase 0-5 weight part thickening material.
Production method of the present invention is accurately to take by weighing each component respectively to be placed in the molten device, stirs to get final product in 5-10 minute.
Said radium-shine printing ink GX-5202 is that Eckart GmbH ﹠ Co. KG of German ALTANA AG (ECKART/PRISMATAR) produces.Its fineness is 1 μ m-50 μ m, sheet footpath 1-2 μ m.
Said coloured pigment is nitrocellulose color chips or CAB cellulose acetate color chips, also can be water soluble acrylic acid color chips, vinyl chloride vinegar color chips and pigment dyestuff of all kinds any all can.
Said esters solvent be N-BUTYL ACETATE, vinyl acetic monomer, acetic acid defend ester any.
Said alcoholic solvent be dehydrated alcohol, methyl alcohol, Virahol, n-propyl alcohol any all can.
The present invention makes full use of that contained metallics has extremely strong change luminous reflectance illumination effect in the radium-shine printing ink, tool is high temperature resistant to send coloured light characteristics changeable with low temperature and with illumination is different, it is good to select for use with itself and pigment solvent phase mixcibility, finely dispersed ester, alcoholic solvent medium, overcome the defective that existing radium-shine printing ink can only print, be coated with and can not spray, and it is better with the base material connectivity, make mirror surface illumination more sufficient, extremely strong reflection illumination effect is arranged, and the present invention has also overcome radium-shine printing ink and has mixed easily to produce to go out in acid, alkali and subtract the deficiency that its matter is imitated.Compared with prior art its use range is more extensive, and construction cost is lower.It is applicable to industrial machinery product, all kinds of traffic appliance, vehicle, various household electrical appliance, furniture and various finishing material.
The every index of product of the present invention meets national coating technology requirement, after testing,
1 grade of paint film cross-hatching of sticking power
50 ℃ of no abnormal variations of 120h of water tolerance
Shock-resistance 5cm 5cm
Snappiness 15mm 15mm
80 ℃ of no abnormal variations of 120h of thermotolerance
60 ℃ of-40 ℃ of no abnormal variations of 2 cycles of temperature-change resistance
The objective of the invention is as can be known to realize from above-mentioned situation.
Embodiment
Embodiment 1, gets the raw materials ready by following component and weight ratio:
Get radium-shine printing ink 10 grams of GX-5202, CAB cellulose acetate color chips coloured pigment 2000 grams, dehydrated alcohol 7900 grams are standby, place container to mix above-mentioned each raw material and get final product in 10 minutes.
Embodiment 2, get the raw materials ready by following component and weight ratio:
Get radium-shine printing ink 100 grams of GX-5201, water soluble acrylic acid color chips coloured pigment 3800 grams, anhydrous methanol 6100 grams, m-70 laking agent 5 grams are standby, place container to mix above-mentioned each raw material and get final product in 5 minutes.
Embodiment 3, get the raw materials ready by following component and weight ratio:
Get radium-shine printing ink 50 grams of GX-5302, vinyl chloride vinegar color chips coloured pigment 100 grams, Virahol 9850 grams, m-70 laking agent 1 gram, thickening material 52 grams are standby, place container to mix above-mentioned each raw material and get final product in 8 minutes.
Embodiment 4, get the raw materials ready by following component and weight ratio:
Get radium-shine printing ink 1000 grams of GX-5301, nitrocellulose color chips coloured pigment 100 grams, N-BUTYL ACETATE 8990 grams, thickening material 5 grams are standby, place container to mix above-mentioned each raw material and get final product in 10 minutes.
Embodiment 5, get the raw materials ready by following component and weight ratio:
Get fineness at 1 μ m-50 μ m, radium-shine printing ink 1000 grams of the GX-5303 of sheet footpath 1-2um, CAB cellulose acetate color chips coloured pigment 3800 grams, vinyl acetic monomer 5200 grams, m-70 laking agent 50 grams are standby, place container to mix above-mentioned each raw material and get final product in 6 minutes.
Embodiment 6, get the raw materials ready by following component and weight ratio:
Get fineness at 1 μ m-50 μ m, radium-shine printing ink 750 grams of the GX-5203 of sheet footpath 1-2um, CAB cellulose acetate color chips coloured pigment 2400 grams, Virahol 6850 grams are standby, place container to mix above-mentioned each raw material and get final product in 5 minutes.
Embodiment 7, get the raw materials ready by following component and weight ratio:
Get fineness at 1 μ m-50 μ m, radium-shine printing ink 750 grams of the GX-5202 of sheet footpath 1-2um, CAB cellulose acetate color chips coloured pigment 3825 grams, acetic acid are defended ester 6900 grams, and thickening material 500 grams are standby, place container to mix above-mentioned each raw material and get final product in 6 minutes.
Embodiment 8, get the raw materials ready by following component and weight ratio:
Get fineness at 1 μ m-50 μ m, radium-shine printing ink 250 grams of the GX-5201 of sheet footpath 1-2um, water soluble acrylic acid color chips 2800 grams, N-BUTYL ACETATE 6950 grams, m-70 laking agent 500 grams are standby, place container to mix above-mentioned each raw material and get final product in 7 minutes.
Embodiment 9, get the raw materials ready by following component and weight ratio:
Get fineness at 1 μ m-50 μ m, radium-shine printing ink 50 grams of the GX-5202 of sheet footpath 1-2um, vinyl chloride vinegar color chips 1000 grams, vinyl acetic monomer 8950 grams are standby, place container to mix above-mentioned each raw material and get final product in 8 minutes.
Embodiment 10, get the raw materials ready by following component and weight ratio:
Get fineness at 1 μ m-50 μ m, radium-shine printing ink 60 grams of the GX-5202 of sheet footpath 1-2um, CAB cellulose acetate color chips coloured pigment 1040 grams, vinyl acetic monomer 8900 grams are standby, place container to mix above-mentioned each raw material and get final product in 9 minutes.
Claims (7)
1, a kind of radium emanation spraying paint is mixed by following component and weight ratio:
Radium-shine printing ink GX-5202 0.1-10
Coloured pigment 1-38
Ester or alcoholic solvent 52-98.5
2, radium emanation spraying paint according to claim 1 is characterized in that: the m-70 laking agent that is added with the 0-5 weight ratio.
3, radium emanation spraying paint according to claim 1 is characterized in that: the thickening material that is added with the 0-5 weight ratio.
4, radium emanation spraying paint according to claim 1 is characterized in that: said GX-5202 degree is 1 μ m-50 μ m, sheet footpath 1-2 μ m.
5, radium emanation spraying paint according to claim 1 is characterized in that: said coloured pigment be nitrocellulose color chips, CAB cellulose acetate color chips, water soluble acrylic acid color chips, vinyl chloride vinegar color chips and pigment dyestuff of all kinds any.
6, radium emanation spraying paint according to claim 1 is characterized in that: said esters solvent be N-BUTYL ACETATE, vinyl acetic monomer, acetic acid defend ester any.
7, radium emanation spraying paint according to claim 1 is characterized in that: said alcoholic solvent be dehydrated alcohol, methyl alcohol, Virahol, n-propyl alcohol any.