CN100560275C - The production method of rectangle copper tungsten conductive nozzle - Google Patents
The production method of rectangle copper tungsten conductive nozzle Download PDFInfo
- Publication number
- CN100560275C CN100560275C CNB2008100482865A CN200810048286A CN100560275C CN 100560275 C CN100560275 C CN 100560275C CN B2008100482865 A CNB2008100482865 A CN B2008100482865A CN 200810048286 A CN200810048286 A CN 200810048286A CN 100560275 C CN100560275 C CN 100560275C
- Authority
- CN
- China
- Prior art keywords
- ignition tip
- copper
- powder
- copper bar
- alumina powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of production method of rectangle copper tungsten conductive nozzle, concrete steps are: get tungsten powder, copper powder stirs, and gasoline stirs, gasoline volatilization, oven dry is sieved, in the desired amount, compound is put into grinding tool, grinding tool is put into hydraulic press, suppress alloy sheet, the centre of alloy sheet or the monolateral copper bar of putting into equal shape are put the infiltration copper bar on it, wrapping, pack at interval piecemeal in the graphite boat, fill with alumina powder at the interval, make real, the oxygen barrier sintering is carried out in ventilation, and each boat advances with motor, release, cooling, smash alumina powder, sieve, get blank, blank becomes ignition tip by machining silk groove.With the ignition tip that the present invention produces, high temperature resistant, the work softening temperature is about 1000 ℃; The hardness height, wear-resistant, long service life, the productivity effect height, use cost is low, welding quality is high.
Description
Technical field
The present invention relates to a kind of method with copper-tungsten production rectangle ignition tip.
Background technology
In the welding procedure of submerged-arc welding and qit4 protection weldering, use ignition tip in a large number.The effect of ignition tip is that after the assurance welding wire came out by welding equipment, weld job was carried out in the mounting technique requirement not weld seam of inclined to one side not liftoff eternal aligning welded article body.Because of ignition tip is directly adjacent to the weld seam operation, welding wire constantly comes out from the centre bore of ignition tip, thus to ignition tip conduct electricity very well, high temperature resistant, anti abrasive requirement.Bad because of electric conductivity, electric current does not reach requirement, can't weld; As non-refractory, easy deformation, influence operation; Key is wear-resistant, and because of after welding wire comes out by wire-feed motor, welding wire engrail, welding wire constantly come out from the ignition tip centre bore, and is big as the aperture mill, will depart from weld seam after welding wire comes out, the quality of influence welding; After aperture mill was big, welding wire and ignition tip also can be because of loose contacts, and cause the electric current shakiness, and the electric current shakiness not only influences welding equipment, also influences welding quality.Existing usefulness alloy production ignition tip, as " a kind of chrome copper " (Chinese patent application 200610135441), use and contain the chromium that weight ratio is 0.5-2.0%, the tellurium of 0.01-1.0, all the other are chrome copper manufacturing ignition tip, the electrode cap of copper and impurity." a kind of chrome zirconium copper alloy " (Chinese patent application 200610167589) used and contained the chromium that weight ratio is 0.5-2.0, the zirconium of 0.005-0.10%, and the tellurium of 0.01-1.0, all the other are that copper and impurity chrome zirconium copper alloy are made ignition tip." combined material of a kind of aluminum oxide dispersion copper and chrome copper " (Chinese patent application 200610171397), wherein combined material is made up of aluminum oxide dispersion copper that is positioned at core and the chrome copper that is coated on described core periphery, the percent by volume of described aluminum oxide dispersion copper is 10-70%, and the volume ratio of chrome copper is 30-90%; In the manufacture method of combined material, adopt the heat extruder extrusion molding, utilize lubricated combined material blank of glass and recipient during extruding, the electric terminal of core is partly used disperse copper, and the outside good chromium-copper of cold working of using is made ignition tip etc. as blank.
Summary of the invention
The objective of the invention is at above-mentioned present situation, aim to provide a kind ofly conduct electricity very well, high temperature resistant, wear-resistant, long service life can guarantee the production method of the rectangle copper tungsten conductive nozzle of welding quality.
The implementation of the object of the invention is, the production method of rectangle copper tungsten conductive nozzle, and its concrete steps are as follows:
1) get tungsten powder 100Kg, copper powder 11 ± 3Kg puts into mixer and stirs,
2) compound that stirs is mixed No. 120 gasoline 6000 ± 50ml by 100Kg and stir again, gasoline volatilization then,
3) compound put into baking oven dry by the fire in, cross 40 mesh sieves,
4) in the desired amount, compound is put into grinding tool, grinding tool is put into hydraulic press, suppress required specification with 60 tons of pressure, the alloy sheet of thick 5mm,
5) at the centre or the monolateral copper bar of putting into equal shape of contour alloy sheet, put the infiltration copper bar of same shape more thereon, the weight of infiltration copper bar is the 25-30% of its weight, wrapping becomes the ignition tip apperance together, in the graphite boat of 310 * 90 * 200mm that packs into piecemeal then, and every interval 10 ± 0.1mm, fill with alumina powder at the interval, make real, and cover with alumina powder, graphite boat is put in the sintering furnace, under 1300 ℃ of-1400 ℃ of temperature, carry out the oxygen barrier sintering with nitrogen, each boat advances with motor, releases cooling in 1 hour, smash alumina powder, sieve, get the ignition tip blank
6) blank becomes ignition tip by machining silk groove.
The ignition tip of producing with the present invention can satisfy fully and welds requiredly, high temperature resistant, works softening temperature about 1000 ℃; Since adopt tungsten, the hardness height of tungsten own, wear-resistant, so the ignition tip of producing is wear-resistant; Be 3-15 times of present ignition tip service life.Long service life has been saved time of frequent replacing ignition tip, has alleviated working strength of workers, has improved productivity effect, has reduced use cost, has saved spending; Because of high temperature resistant, wear-resistant, can guarantee the not inclined to one side not center weld seam of liftoff alignment pieces of welding wire for a long time, guarantee the welding high-quality.
Description of drawings
Fig. 1 a, b are master, the side views with one of ignition tip of the present invention's production
Fig. 2 a, b are two master, side views of the ignition tip produced with the present invention
Fig. 3 a, b are three master, side views of the ignition tip produced with the present invention
The specific embodiment
With the plurality of specifications that the ignition tip of the present invention's production is listed just like accompanying drawing, long 40-70mm, wide 18-26mm, thick 10-16mm, silk groove radius 2-2.5mm.Adopt with tungsten powder 100Kg, copper powder 11 ± 3Kg alloy.
The concrete steps that the present invention produces are as follows:
1) get tungsten powder 100Kg, copper powder 11 ± 1Kg puts into mixer and stirs,
2) compound that stirs is mixed No. 120 gasoline 6000 ± 2ml by 100Kg and stir again, gasoline volatilization then,
3) compound is put into oven for drying, crosses 40 mesh sieves,
4) in the desired amount, compound is put into grinding tool, grinding tool is put into hydraulic press, suppress required specification with 60 tons of pressure, the alloy sheet of thick 5mm,
5) at the centre or the monolateral copper bar of putting into equal shape of contour alloy sheet, put the infiltration copper bar of same shape more thereon, the weight of infiltration copper bar is the 25-30% of its weight, wrapping becomes the ignition tip apperance together, in the graphite boat of 310 * 90 * 200mm that packs into piecemeal then, and every interval 10 ± 0.1mm, fill with alumina powder at the interval, make real, and cover with alumina powder, graphite boat is put in the sintering furnace, under 1300 ℃ of-1400 ℃ of temperature, carry out the oxygen barrier sintering with nitrogen, each boat advances with motor, releases cooling in 1 hour, smash alumina powder, sieve, get the ignition tip blank
6) blank becomes ignition tip by machining silk groove.
With reference to Fig. 1, ignition tip is a rectangle, and both sides are copper-tungsten 1, and the centre is a copper bar 2, has oval installing hole 3, alloy two outsides that semicircle silk groove 4 is arranged in the middle of the copper bar.The long 60mm of rectangle, wide 24mm, thick 12mm, silk groove radius 2mm.Ignition tip shown in two figure share, and two halves circular wire groove 4 is merged into the silk rolling hole.
With reference to Fig. 2, ignition tip is a rectangle, and both sides are copper-tungsten 1, and the centre is a copper bar 2, has circular mounting hole 5, alloy two outsides that semicircle silk groove 4 is arranged in the middle of the copper bar.The long 44mm of ignition tip, wide 20mm, thick 12mm, silk groove radius 2mm.Two ignition tips as shown in the figure share, and two halves circular wire groove 4 is merged into the silk rolling hole.
With reference to Fig. 3, Yi Bian be copper-tungsten 1, the centre is a copper bar 2, has circular mounting hole 5, alloy one side that semicircle silk groove 4 is arranged in the middle of the copper bar.Ignition tip abnormity 6 as shown in the figure, promptly alloy part 1 is a rectangle, and copper bar part 2 is a rectangle, and part is the trapezoidal of monocline face.The long 44mm of ignition tip, wide 20mm, thick 12mm, silk groove radius 2mm.Ignition tip shown in two figure share, and two halves circular wire groove 4 is merged into the silk rolling hole.
Claims (1)
1, the production method of rectangle copper tungsten conductive nozzle is characterized in that concrete steps are as follows:
1) get tungsten powder 100Kg, copper powder 11 ± 3Kg puts into mixer and stirs,
2) compound that stirs is mixed No. 120 gasoline 6000 ± 50ml by 100Kg and stir again, gasoline volatilization then,
3) compound is put into oven for drying, crosses 40 mesh sieves,
4) in the desired amount, compound is put into mould, mould is put into hydraulic press, suppress required specification with 60 tons of pressure, the alloy sheet of thick 5mm,
5) at the centre or the monolateral copper bar of putting into equal shape of contour alloy sheet, put the infiltration copper bar of same shape more thereon, the weight of infiltration copper bar is the 25-30% of its weight, wrapping becomes the ignition tip apperance together, in the graphite boat of 310 * 90 * 200mm that packs into piecemeal then, and every interval 10 ± 0.1mm, fill with alumina powder at the interval, make real, and cover with alumina powder, graphite boat is put in the sintering furnace, under 1300 ℃ of-1400 ℃ of temperature, carry out the oxygen barrier sintering with nitrogen, each boat advances with motor, releases cooling in 1 hour, smash alumina powder, sieve, get the ignition tip blank
6) blank becomes ignition tip by machining silk groove.