CN100344533C - 一种高强度炭/石墨材料的制备方法 - Google Patents
一种高强度炭/石墨材料的制备方法 Download PDFInfo
- Publication number
- CN100344533C CN100344533C CNB2005100482429A CN200510048242A CN100344533C CN 100344533 C CN100344533 C CN 100344533C CN B2005100482429 A CNB2005100482429 A CN B2005100482429A CN 200510048242 A CN200510048242 A CN 200510048242A CN 100344533 C CN100344533 C CN 100344533C
- Authority
- CN
- China
- Prior art keywords
- temperature
- coal tar
- pitch
- tar mid
- mid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
编号 | 体积密度(g/cm3) | 弯强(MPa) | 压强(MPa) | 肖氏硬度 | 电阻率(μΩ.m) | 最高处理温度(℃) | 有无浸渍 |
实施例1 | 1.874 | 71.48 | 218.05 | 88 | 23.64 | 2500 | 有 |
实施例2 | 1.821 | 67.66 | 186.26 | 83 | 24.32 | 2500 | 有 |
实施例3 | 1.865 | 69.37 | 198.25 | 75 | 24.38 | 2500 | 有 |
比较例1 | 1.506 | - | 212.12 | 84 | - | 850 | 无 |
比较例2 | 1.650 | 40.12 | 119.79 | 81 | 28.10 | 2500 | 无 |
比较例3 | 1.747 | 113.76 | 310.00 | 103 | - | 1300 | 有 |
Claims (2)