CN109705957A - Compound the formula and production method of high extreme pressure Metalworking lubricant - Google Patents
Compound the formula and production method of high extreme pressure Metalworking lubricant Download PDFInfo
- Publication number
- CN109705957A CN109705957A CN201811326550.7A CN201811326550A CN109705957A CN 109705957 A CN109705957 A CN 109705957A CN 201811326550 A CN201811326550 A CN 201811326550A CN 109705957 A CN109705957 A CN 109705957A
- Authority
- CN
- China
- Prior art keywords
- oil
- extreme pressure
- soluble
- formula
- high extreme
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of formulas for compounding high extreme pressure Metalworking lubricant, by weight, formula composition are as follows: 10# machine oil 20.0-30.0%, refined mineral oil 150SN45.0-60.0%, rapeseed oil 3.0-7.0%, oil-soluble triazole 0.1-0.5%, sulfurized lard 1.0-3.0%, synthetic ester 5.0-10.0%, chlorinated paraffin 10.0-15.0%, oil-soluble antioxidants 0.3-0.5%.
Description
Technical field
The invention belongs to Metalworking lubricant field, more specifically to a kind of high extreme pressure intermetallic composite coating of compounding is used
The formula and production method of lubricant.
Background technique
Golden intermetallic composite coating lubricating oil includes cutting oil, grinding oil, drawing oil, punching oil etc., is suitable for cast iron, alloy
The processing methods such as cutting, grinding, stretching, the punching press of the metal products such as steel, carbon steel, stainless steel, high nickel steel, heat resisting steel, mould steel,
For lubricating and cooling down machining tool and component in metal cutting process.Currently, domestic Metalworking lubricating oil technology
It is increased with external gap, product quality is irregular.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of high extreme pressure intermetallic composite coating lubrications of the higher compounding of performance
The formula of agent.
To achieve the above object, the present invention provides the following technical scheme that a kind of high extreme pressure intermetallic composite coating lubrication of compounding
The formula of agent, by weight, formula composition are as follows: 10# machine oil 20.0-30.0%, refined mineral oil 150SN 45.0-
60.0%, rapeseed oil 3.0-7.0%, oil-soluble triazole 0.1-0.5%, sulfurized lard 1.0-3.0%, synthetic ester 5.0-
10.0%, chlorinated paraffin 10.0-15.0%, oil-soluble antioxidants 0.3-0.5%.
A kind of production method compounding high extreme pressure Metalworking lubricant, by 10# machine oil, refined mineral oil 150SN, dish
Seed oil, oil-soluble triazole, sulfurized lard, synthetic ester, chlorinated paraffin, oil-soluble antioxidants sequentially add blender, and stirring is equal
Even, the speed of agitator is 700 turns/min, and whipping temp is 50 DEG C, mixing time 60min.
Compared with prior art, the beneficial effects of the present invention are: the consumption electronic product institute risen for this several years is a large amount of
The new metallic material of use, such as almag, magnesium alloy, re-optimization extreme pressure anti-wear additives, lubricant, coolant, antioxygen
Agent, antirust, anticorrosive agent, specialist additive proportion, give full play to the synergistic effect of various additives.The suitable refining mine of selection
Object oil, vegetable oil, animal oil, synthetic ester are compounded, and the requirement of use occasion, especially viscosity and mobility requirement are reached.
The integration technology that compounds of base oil and additive, both optimization compound proportion, improves product properties, especially greasy property
And cooling performance.
Specific embodiment
Embodiment one:
A kind of formula compounding high extreme pressure Metalworking lubricant, by weight, formula composition are as follows: 10# machine oil
20.0%, refined mineral oil 150SN 57.4%, rapeseed oil 4.0%, oil-soluble triazole 0.3%, sulfurized lard 2.0%, conjunction
At ester 6.0%, chlorinated paraffin 10.0%, oil-soluble antioxidants 0.3%.
Production method: by 10# machine oil 20.0%, refined mineral oil 150SN 57.4%, rapeseed oil 4.0%, oil-soluble three
Nitrogen azoles 0.3%, sulfurized lard 2.0%, synthetic ester 6.0%, chlorinated paraffin 10.0%, oil-soluble antioxidants 0.3% sequentially add
Blender stirs evenly, and the speed of agitator is 700 turns/min, and whipping temp is 50 DEG C, and mixing time 60min is to get to originally
The transparent high extreme pressure intermetallic composite coating lubricating oil of compounding of invention brown.
Embodiment two:
A kind of formula compounding high extreme pressure Metalworking lubricant, by weight, formula composition are as follows: 10# machine oil
22.0%, refined mineral oil 150SN 52.3%, rapeseed oil 4.0%, oil-soluble triazole 0.3%, sulfurized lard 4.0%, conjunction
At ester 5.0%, chlorinated paraffin 12.0%, oil-soluble antioxidants 0.4%.
Production method: by 10# machine oil 22.0%, refined mineral oil 150SN 52.3%, rapeseed oil 4.0%, oil-soluble three
Nitrogen azoles 0.3%, sulfurized lard 4.0%, synthetic ester 5.0%, chlorinated paraffin 12.0%, oil-soluble antioxidants 0.4% sequentially add
Blender stirs evenly, and the speed of agitator is 700 turns/min, and whipping temp is 50 DEG C, and mixing time 60min is to get to originally
The transparent high extreme pressure intermetallic composite coating lubricating oil of compounding of invention brown.
Embodiment three:
A kind of formula compounding high extreme pressure Metalworking lubricant, by weight, formula composition are as follows: 10# machine oil
23.0%, refined mineral oil 150SN 47.3%, rapeseed oil 5.0%, oil-soluble triazole 0.3%, sulfurized lard 4.0%, conjunction
At ester 6.0%, chlorinated paraffin 14.0%, oil-soluble antioxidants 0.4%.
Production method: by 10# machine oil 23.0%, refined mineral oil 150SN 47.3%, rapeseed oil 5.0%, oil-soluble three
Nitrogen azoles 0.3%, sulfurized lard 4.0%, synthetic ester 6.0%, chlorinated paraffin 14.0%, oil-soluble antioxidants 0.4% sequentially add
Blender stirs evenly, and the speed of agitator is 700 turns/min, and whipping temp is 50 DEG C, and mixing time 60min is to get to originally
The transparent high extreme pressure intermetallic composite coating lubricating oil of compounding of invention brown.
Embodiment 1-3 compounding lubricating oil is tested for the property, as a result as shown in the table.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (2)
1. a kind of formula for compounding high extreme pressure Metalworking lubricant, which is characterized in that by weight, formula composition
Are as follows: 10# machine oil 20.0-30.0%, refined mineral oil 150SN 45.0-60.0%, rapeseed oil 3.0-7.0%, three nitrogen of oil-soluble
Azoles 0.1-0.5%, sulfurized lard 1.0-3.0%, synthetic ester 5.0-10.0%, chlorinated paraffin 10.0-15.0%, oil-soluble antioxygen
Agent 0.3-0.5%.
2. a kind of production method for compounding high extreme pressure Metalworking lubricant, it is characterised in that: by 10# machine oil, refining mineral
Oily 150SN, rapeseed oil, oil-soluble triazole, sulfurized lard, synthetic ester, chlorinated paraffin, oil-soluble antioxidants sequentially add stirring
Machine stirs evenly, and the speed of agitator is 700 turns/min, and whipping temp is 50 DEG C, mixing time 60min.