CN109694242A - It is a kind of suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner and its production technology - Google Patents
It is a kind of suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner and its production technology Download PDFInfo
- Publication number
- CN109694242A CN109694242A CN201710943426.4A CN201710943426A CN109694242A CN 109694242 A CN109694242 A CN 109694242A CN 201710943426 A CN201710943426 A CN 201710943426A CN 109694242 A CN109694242 A CN 109694242A
- Authority
- CN
- China
- Prior art keywords
- pressure cooking
- cooking saucepan
- ceramic liner
- electric pressure
- electric cooker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner and production technology, it is the following steps are included: (1) ingredient charges, by spodumene 40-45%, kaolin 35-45%, silica flour 5-10%, AsO3Powder 3-5% is mixed into mass ratio prepares raw material, and carries out mixing treatment；(2) it is ground up, sieved, the raw material for preparing after mixing is put into ball mill grinding, done after sieving except iron processing；(3) green compact after press filt pugging, and be dried, form semi-finished product；(4) by after above-mentioned semi-finished product moisturizing glazing, loading of kiln is fired；(5) after the completion of firing, finished product, and outbound of testing are formed.The present invention is a kind of suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner.Have the advantages that thermal stability is strong, bending and compressive strength is high, water absorption rate is low etc., and its manufacture craft is simple, than metal pan more whether there is or not content of beary metal, the advantages such as healthier safety can keep the temperature for more time, is environment friendly and pollution-free.
Description
Technical field
It is specifically a kind of suitable for electric cooker, electric pressure cooking saucepan ceramic liner the present invention relates to ceramic field
Material and its production technology.
Background technique
As the improvement of people's living standards, the requirement to cook utensil is also higher and higher.Ceramic has both ring simultaneously
The minerals protecting, is pollution-free, keeping original pair of human body beneficial, will not get rusty and cause secondary pollution and like by people.So
And there are the problems such as frangible, resistance to thermal shocks is poor for traditional ceramic, therefore develop that a kind of performance is stable, anti-folding and anti-pressing system
The strong ceramic material for being adapted to kitchen appliance of number is very important.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the existing defects, and it is strong to provide a kind of High anti bending strength, thermal stability
Be suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner and its production technology.
In order to solve the above-mentioned technical problems, the present invention provides the following technical solutions:
It is a kind of suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner, it is mixed by following quality mixture ratio:
Spodumene 40-45%
Kaolin 35-45%
Silica flour 5-10%
AsO3Powder 3-5%.
Further, described a kind of suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner, it further include that it produces work
Skill, it the following steps are included:
(1) ingredient charges, and above-mentioned material is mixed into mass ratio and prepares raw material, and carries out mixing treatment；
(2) it is ground up, sieved, the raw material for preparing after mixing is put into ball mill grinding, done after sieving except iron processing；
(3) green compact after press filt pugging, and be dried, form semi-finished product；
(4) by after above-mentioned semi-finished product moisturizing glazing, loading of kiln is fired；
(5) after the completion of firing, finished product, and outbound of testing are formed.
Further, the firing temperature is 1280 DEG C -1350 DEG C.
Further, the firing temperature is 1300 DEG C -1330 DEG C.
Further, the firing atmosphere when firing is oxidizing atmosphere.
A kind of material suitable for electric cooker, electric pressure cooking saucepan ceramic liner of the present invention strong, anti-folding and anti-pressing with thermal stability
The advantages such as intensity is high, water absorption rate is low, and its manufacture craft is simple, than metal pan, more whether there is or not content of beary metal, healthier safety
Etc. advantages, can keep the temperature for more time, is environment friendly and pollution-free.
Specific embodiment
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
The present invention is a kind of suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner, by quality mixture ratio spodumene 44%,
Kaolin 43%, silica flour 8%, AsO3Powder 5%.Its production technology, comprising the following steps: (1) ingredient charges, by above-mentioned material
It is mixed into mass ratio and prepares raw material, and carry out mixing treatment；(2) it is ground up, sieved, the raw material for preparing after mixing is put into ball milling
Machine grinding is done after sieving except iron processing；(3) green compact after press filt pugging, and be dried, form semi-finished product；It (4) will be above-mentioned
After semi-finished product moisturizing glazing, loading of kiln is fired；(5) after the completion of firing, finished product, and outbound of testing are formed.It is of the present invention
Firing temperature is 1300 DEG C.Firing atmosphere when the described firing is oxidizing atmosphere.
The material property that the present invention manufactures are as follows: (1) flexural strength >=180MPa；(2) 500 thermal stability: are heated to
Heat exchange is put into 20 DEG C of water after DEG C once without slight crack；(3) water absorption rate≤1%；(4) material thermal expansion coefficient is 1.2-
1.5×10-6/℃。
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although referring to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features.It is all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (5)
1. it is a kind of suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner, it is characterized in that: it is mixed by following quality mixture ratio
It forms:
Spodumene 40-45%
Kaolin 35-45%
Silica flour 5-10%
AsO3Powder 3-5%.
2. it is according to claim 1 a kind of suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner, it further include its production
Technique, it is characterized in that: it the following steps are included:
(1) ingredient charges, and above-mentioned material is mixed into mass ratio and prepares raw material, and carries out mixing treatment；
(2) it is ground up, sieved, the raw material for preparing after mixing is put into ball mill grinding, done after sieving except iron processing；
(3) green compact after press filt pugging, and be dried, form semi-finished product；
(4) by after above-mentioned semi-finished product moisturizing glazing, loading of kiln is fired；
(5) after the completion of firing, finished product, and outbound of testing are formed.
3. a kind of production technology suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner according to claim 2,
Be characterized in: the firing temperature is 1280 DEG C -1350 DEG C.
4. a kind of production technology suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner according to claim 3,
Be characterized in: the firing temperature is 1300 DEG C -1330 DEG C.
5. a kind of production technology suitable for electric cooker, the material of electric pressure cooking saucepan ceramic liner according to claim 2,
Be characterized in: the firing atmosphere when firing is oxidizing atmosphere.