CN109517437A - 水性凹版油墨及其制备方法 - Google Patents
水性凹版油墨及其制备方法 Download PDFInfo
- Publication number
- CN109517437A CN109517437A CN201811563369.8A CN201811563369A CN109517437A CN 109517437 A CN109517437 A CN 109517437A CN 201811563369 A CN201811563369 A CN 201811563369A CN 109517437 A CN109517437 A CN 109517437A
- Authority
- CN
- China
- Prior art keywords
- water
- gravure ink
- agent
- base gravure
- byk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及化工领域，公开了一种水性凹版油墨及其制备方法，该水性凹版油墨由以下重量百分比的组分组成：水性透明颜料20‑25%，水性丙烯酸乳液30‑35%，去离子水15‑20%，水性聚氨酯树脂20‑25%，BYK分散剂1‑2%，BYK流平剂1‑1.5%，消泡剂0.5‑1%，爽滑剂0.3‑0.8%。本发明中的水性凹版油墨具有良好的印刷适应性，可适用于以铜板纸、白卡纸、转移金银卡纸及牛皮纸为基材的多种高档包装产品，适用于各种进口和国产中、高速印刷机。
Description
技术领域
本发明涉及油墨领域，特别涉及一种水性凹版油墨及其制备方法。
背景技术
印刷油墨，根据溶剂的不同，可分为有机溶剂油墨、水性油墨，其中，虽然有机溶剂油墨的附着性更佳，但其中含有的可挥发性的有机溶剂易对人体造成危害。
而水性油墨由于其无毒、环保、安全性能高，且耐候性优良，不易因日晒而变色，因此，水性油墨倍受消费者的喜爱。
然而，水性油墨较易产生气泡、颜色的维持效果差、且状态不够稳定等情况，从而造成了水性油墨在应用上的限制。
发明内容
发明目的：针对现有技术中存在的问题，本发明提供一种水性凹版油墨及其制备方法，具有良好的印刷适应性，可适用于以铜板纸、白卡纸、转移金银卡纸及牛皮纸为基材的多种高档包装产品。
技术方案：本发明提供了一种水性凹版油墨，由以下重量百分比的组分组成：水性透明颜料 20-25%；水性丙烯酸乳液 35-40%；去离子水 15-20%；水性聚氨酯树脂 20-25%；BYK分散剂 1-2%；BYK 流平剂 1-1.5%；消泡剂 0.5-1%；爽滑剂 0.3-0.8%。
优选地，所述水性透明颜料的主要成分为酞菁蓝，水分≤1%。
优选地，所述水性丙烯酸乳液由以下重量百分比的组分组成：甲基丙烯酸丁酯与甲基丙烯酸甲酯和丙烯酸的共聚物40%，二甲基乙醇胺1%，消泡剂0.1%，其余是水。
优选地，所述水性聚氨酯树脂由聚合物多元醇、聚氨酯、多异氰酸酯和亲水单体组成。
优选地，所述BYK分散剂的主要成分为高分子嵌段共聚物。
优选地，所述BYK 流平剂由以下重量百分比的组分组成：炔二醇50%，乙二醇50%。
优选地，所述消泡剂由以下重量百分比的组分组成：聚醚硅氧烷乳液20%，水80%。
本发明还提供了上述水性凹版油墨的制备方法，包括以下步骤：S1：常温下，将水性透明颜料、水性丙烯酸乳液、去离子水、BYK分散剂按照配比混合，分散均匀成色浆；S2：对所述色浆进行循环研磨至细度≤10微米，得水性色浆；S3：将所述水性色浆、水性聚氨酯树脂、去离子水、消泡剂、爽滑剂、BYK 流平剂按照比例混合，分散均匀即得水性凹版油墨。
有益效果：本发明中的水性凹版油墨选用高级进口颜料高档水性丙烯酸树脂及各种助剂混合研磨制备而成。具有良好的印刷适应性，可适用于以铜板纸、白卡纸、转移金银卡纸及牛皮纸为基材的多种高档包装产品，适用于各种进口和国产中、高速印刷机。
1、以去离子水为溶剂，不燃、不爆、不污染环境，是一种保护人体健康的绿色环保印刷油墨。
2、油墨流动性、干燥性佳、再溶性好、不返粘、不糊版、具有优异的印刷适性。
3、印刷效果：印迹清晰、网点完整、不损层次、色彩鲜艳、图案重现性佳、叠印效果佳、光泽好，耐磨擦性为不掉色。
4、油墨耐水、抗冻性好，适用冷冻包装印刷。
5、水性油墨色泽、光泽度好、耐磨性、抗水性较佳，对墨层和纸箱有很好的保护和装饰作用。
6、油墨有较好的PH值和粘度稳定性、易于储存。
7、油墨与水溶解性好，易于印刷机的清洗。
具体实施方式
下面结合具体实施例对本发明进行详细的介绍。
实施方式1：
本实施方式提供了一种水性凹版油墨，由以下重量百分比的组分组成：水性透明颜料25%，水性丙烯酸乳液 35%，去离子水 15%，水性聚氨酯树脂 21.2%，BYK分散剂 1.5%，BYK流平剂 1%，消泡剂 0.5%，爽滑剂 0.8%。
上述水性凹版油墨的制备方法如下：水性油墨的生产制备重点在于水性色浆的研磨，也是生产水性油墨过程中最复杂的一步。在常温下首先将配比将进口环保水性丙烯酸乳液、进口高档水性透明颜料、去离子水、BYK分散剂混合配制，分散均匀成色浆，分散好的色浆因粘度高且颜料颗粒大，需要使用研磨机对色浆进行至少3遍的循环研磨，细度控制在≤10微米，得水性色浆，细度合格后需要检验色浆的色相，着色力、初彻干、粘度等指标。
将上述研磨后的水性色浆与进口高档水性聚氨酯树脂、去离子水、迪高消泡剂、道康宁爽滑剂、BYK流平剂混合配制，分散均匀，得水性凹版油墨，检验其粘度、色相、初彻干、耐摩擦、附着牢度等指标，合格后包装。
实施方式2：
本实施方式提供了一种水性凹版油墨，由以下重量百分比的组分组成：水性透明颜料20%，水性丙烯酸乳液35%，去离子水17%，水性聚氨酯树脂 24.2%，BYK分散剂 1%，BYK 流平剂 1.5%，消泡剂1%，爽滑剂 0.3%。
上述水性凹版油墨的制备方法与实施方式1完全相同，此处不做赘述。
实施方式3：
本实施方式提供了一种水性凹版油墨，由以下重量百分比的组分组成：水性透明颜料22.5%，水性丙烯酸乳液32.5%，去离子水20%，水性聚氨酯树脂 20.5%，BYK分散剂 2%，BYK流平剂 1.2%，消泡剂0.7%，爽滑剂 0.6%。
上述水性凹版油墨的制备方法与实施方式1完全相同，此处不做赘述。
上述实施方式只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神实质所做的等效变换或修饰，都应涵盖在本发明的保护范围之内。
Claims (8)
1.一种水性凹版油墨，其特征在于，由以下重量百分比的组分组成：
水性透明颜料 20-25%
水性丙烯酸乳液 30-35%
去离子水 15-20%
水性聚氨酯树脂 20-25%
BYK分散剂 1-2%
BYK 流平剂 1-1.5%
消泡剂 0.5-1%
爽滑剂 0.3-0.8%。
2.根据权利要求1所述的水性凹版油墨，其特征在于，所述水性透明颜料的主要成分为酞菁蓝，水分≤1%。
3.根据权利要求1所述的水性凹版油墨，其特征在于，所述水性丙烯酸乳液由以下重量百分比的组分组成：甲基丙烯酸丁酯与甲基丙烯酸甲酯和丙烯酸的共聚物40%，二甲基乙醇胺1%，消泡剂0.1%，其余是水。
4.根据权利要求1所述的水性凹版油墨，其特征在于，所述水性聚氨酯树脂由聚合物多元醇、聚氨酯、多异氰酸酯和亲水单体组成。
5.根据权利要求1所述的水性凹版油墨，其特征在于，所述BYK分散剂的主要成分为高分子嵌段共聚物。
6.根据权利要求1所述的水性凹版油墨，其特征在于，所述BYK 流平剂由以下重量百分比的组分组成：炔二醇50%，乙二醇50%。
7.根据权利要求1所述的水性凹版油墨，其特征在于，所述消泡剂由以下重量百分比的组分组成：聚醚硅氧烷乳液20%，水80%。
8.一种如权利要求1至7中任一项所述的水性凹版油墨的制备方法，其特征在于，包括以下步骤：
S1：常温下，将水性透明颜料、水性丙烯酸乳液、去离子水、BYK分散剂按照配比混合，分散均匀成色浆；
S2：对所述色浆进行循环研磨至细度≤10微米，得水性色浆；
S3：将所述水性色浆、水性聚氨酯树脂、去离子水、消泡剂、爽滑剂、BYK 流平剂按照比例混合，分散均匀即得水性凹版油墨。