CN109370412A - A kind of environment-friendly water-based polyurethane coating - Google Patents

A kind of environment-friendly water-based polyurethane coating Download PDF

Info

Publication number
CN109370412A
CN109370412A CN201811237903.6A CN201811237903A CN109370412A CN 109370412 A CN109370412 A CN 109370412A CN 201811237903 A CN201811237903 A CN 201811237903A CN 109370412 A CN109370412 A CN 109370412A
Authority
CN
China
Prior art keywords
environment
based polyurethane
friendly water
polyurethane coating
sodium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811237903.6A
Other languages
Chinese (zh)
Inventor
郭平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hanshan County Leader Innovative Materials Technology Co Ltd
Original Assignee
Hanshan County Leader Innovative Materials Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hanshan County Leader Innovative Materials Technology Co Ltd filed Critical Hanshan County Leader Innovative Materials Technology Co Ltd
Priority to CN201811237903.6A priority Critical patent/CN109370412A/en
Publication of CN109370412A publication Critical patent/CN109370412A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of environment-friendly water-based polyurethane coatings, it is related to technical field of aqueous paint, is made of following component: four silanol sodium salt modified polyurethane emulsions, nanometer calcium carbonate, diatom ooze, hollow glass micropearl, trimethyl silicane potassium alcoholate, tertiary ethylene carbonate, inorganic salts powder, wetting agent, defoaming agent, dispersing agent, thickener;Environment-friendly water-based polyurethane coating prepared by the present invention has excellent abrasion resistance, stain resistant and artificial ageing resistance performance.

Description

A kind of environment-friendly water-based polyurethane coating
Technical field
The invention belongs to technical field of aqueous paint, and in particular to a kind of environment-friendly water-based polyurethane coating.
Background technique
Oil paint is due to itself containing solvent at present, and when use will use the big of containing benzene, alcohols, esters or ketone Organic solvent diluting is measured, the health hazard of pollution and human body to environment is very big, and is inflammable and explosive product, to production and construction There are latent fire hazards in place, higher and higher to the needs of water paint but aqueous with the raising that people require quality of life Although the coating feature of environmental protection is good, hardness is low after solidification, and resistance to tearing is poor.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of environment-friendly water-based polyurethane coating is provided.
The present invention is achieved by the following technical solutions:
A kind of environment-friendly water-based polyurethane coating, is made of following component by weight: four silanol sodium salt modified polyurethane emulsions 93-98, nanometer calcium carbonate 18-25, diatom ooze 35-39, hollow glass micropearl 5.2-6.4, trimethyl silicane potassium alcoholate 0.12-0.15, Tertiary ethylene carbonate 3-6, inorganic salts powder 1.8-2.5, wetting agent 0.6-1, defoaming agent 0.5-1.5, dispersing agent 0.5-1.2, increase Thick dose of 0.5-1.
Further, the four silanols sodium salt modified polyurethane emulsion the preparation method comprises the following steps:
(1) in organic solvent by silane, sodium hydroxide, deionized water dissolving, anti-with the stirring of 150r/min revolving speed at 79 DEG C It after answering 1.5 hours, is cooled to room temperature, with 1500r/min revolving speed stirring 6 hours, then through revolving removing solvent, four sodium silanolates is made Salt, it is spare by vacuum drying;
(2) after mixing plant polyatomic alcohol and diisocyanate, it is added in reaction kettle, is then added into reaction kettle organic molten Agent stirs 40min with 200r/min revolving speed at 80 DEG C, then adds dibutyl tin dilaurate, and heat preservation carries out anti-at 80 DEG C It answers 3 hours, obtains performed polymer mixed liquor, hydrophilic chain extender and hydroxypropyl acrylate, four sodium silanolates are added into performed polymer mixed liquor Salt carries out polymerization reaction, and polymeric reaction temperature is 78 DEG C, and the reaction time is 5 hours, obtains condensate mixed liquor, mixes to condensate Liquid adds rare earth chloride, stirs evenly, and stands 1 hour, is then neutralized to neutrality with triethylamine again, then adds deionized water shearing Emulsify to obtain polyaminoester emulsion, remove the organic solvent in polyaminoester emulsion to get.
Further, step (1) silane, sodium hydroxide, deionized water mixing molar ratio are 1.2:2.5:1.8.
Further, step (1) and step (2) organic solvent are n,N-Dimethylformamide.
Further, step (2) plant polyatomic alcohol and diisocyanate mixing molar ratio are 1:1.
Further, step (2) the dibutyl tin dilaurate additive amount is the 0.5% of plant polyatomic alcohol quality.
Further, step (2) hydrophilic chain extender and hydroxypropyl acrylate, four silanol sodium salts and plant polyatomic alcohol are mixed Conjunction molar ratio is 1.5:80::0.5:2.8.
Further, step (2) the rare earth chloride additive amount is the 0.08% of condensate mixed liquor quality, the chlorination Rare earth is cerium chloride.
Further, the inorganic salts powder is that sodium citrate and aluminum aluminum sulfate are mixed by 3:1 mass ratio, is soaked Agent is propylene glycol, and defoaming agent is organic silicon defoamer, and dispersing agent is polyethylene glycol 200, and thickener is sodium cellulose glycolate.
The utility model has the advantages that the present invention is using four silanol sodium salt modified polyurethane emulsions as basic film forming matter, what is contained is a large amount of Active group, the not only good dispersion between filler, but also hardness of film is high after solidifying, tearing-resistant performance is fabulous, can The surface tension for reducing coating film enables coating to occur film cissing phenomenon with soaking substrate, reduction well, prevent due to quilt Protection is unclean and keeps coating uneven;By cooperateing with the effect of each ingredient, respective deficiency can be not only made up, filming performance is excellent It is different, and can effectively reduce adjacent inter-chain action, increasing gap, flexility is excellent, and tearing-resistant performance is good, and pollution-free, It is free from environmental pollution;Nanometer calcium carbonate and diatom ooze can enter inside above-mentioned film forming layer, and with active group inside film forming matter It preferably combines, under the action of with four silanol sodium salt modified polyurethane emulsion solidification process, is combined between other components, Gu Change very high density, hardness further enhances, and has excellent stain resistant.The present invention passes through with four silanol sodium salt modified polyurethanes Lotion makes the inside and outside rate of drying of coating obtained by the present invention reach high unity as basic film forming matter, while hardness, wear-resisting Property and adhesive force further enhance, have excellent artificial weathering ageing resistance's energy.Gained paint film of the invention is plentiful, has good Decoration functions and protection of environment function, all have preferable effect in smell, environmental protection, aspect of performance, smell is pure and fresh.The present invention Water paint does not injure human body, can effective traditional water paint wall basic level is insecure causes to be coated on wall Cracking that coating occurs, the problem of falling off, can be avoided and repeatedly overhaul, have high economic benefit, can be widely applied for Field of constructional ornament.
Specific embodiment
Embodiment 1
A kind of environment-friendly water-based polyurethane coating, is made of following component by weight: four silanol sodium salt modified polyurethane emulsions 93, nanometer calcium carbonate 18, diatom ooze 35, hollow glass micropearl 5.2, trimethyl silicane potassium alcoholate 0.12, tertiary ethylene carbonate 3, inorganic Salt powder 1.8, wetting agent 0.6, defoaming agent 0.5, dispersing agent 0.5, thickener 0.5.
Further, the four silanols sodium salt modified polyurethane emulsion the preparation method comprises the following steps:
(1) in organic solvent by silane, sodium hydroxide, deionized water dissolving, anti-with the stirring of 150r/min revolving speed at 79 DEG C It after answering 1.5 hours, is cooled to room temperature, with 1500r/min revolving speed stirring 6 hours, then through revolving removing solvent, four sodium silanolates is made Salt, it is spare by vacuum drying;
(2) after mixing plant polyatomic alcohol and diisocyanate, it is added in reaction kettle, is then added into reaction kettle organic molten Agent stirs 40min with 200r/min revolving speed at 80 DEG C, then adds dibutyl tin dilaurate, and heat preservation carries out anti-at 80 DEG C It answers 3 hours, obtains performed polymer mixed liquor, hydrophilic chain extender and hydroxypropyl acrylate, four sodium silanolates are added into performed polymer mixed liquor Salt carries out polymerization reaction, and polymeric reaction temperature is 78 DEG C, and the reaction time is 5 hours, obtains condensate mixed liquor, mixes to condensate Liquid adds rare earth chloride, stirs evenly, and stands 1 hour, is then neutralized to neutrality with triethylamine again, then adds deionized water shearing Emulsify to obtain polyaminoester emulsion, remove the organic solvent in polyaminoester emulsion to get.
Further, step (1) silane, sodium hydroxide, deionized water mixing molar ratio are 1.2:2.5:1.8.
Further, step (1) and step (2) organic solvent are n,N-Dimethylformamide.
Further, step (2) plant polyatomic alcohol and diisocyanate mixing molar ratio are 1:1.
Further, step (2) the dibutyl tin dilaurate additive amount is the 0.5% of plant polyatomic alcohol quality.
Further, step (2) hydrophilic chain extender and hydroxypropyl acrylate, four silanol sodium salts and plant polyatomic alcohol are mixed Conjunction molar ratio is 1.5:80::0.5:2.8.
Further, step (2) the rare earth chloride additive amount is the 0.08% of condensate mixed liquor quality, the chlorination Rare earth is cerium chloride.
Further, the inorganic salts powder is that sodium citrate and aluminum aluminum sulfate are mixed by 3:1 mass ratio, is soaked Agent is propylene glycol, and defoaming agent is organic silicon defoamer, and dispersing agent is polyethylene glycol 200, and thickener is sodium cellulose glycolate.
Embodiment 2
A kind of environment-friendly water-based polyurethane coating, is made of following component by weight: four silanol sodium salt modified polyurethane emulsions 98, nanometer calcium carbonate 25, diatom ooze 39, hollow glass micropearl 6.4, trimethyl silicane potassium alcoholate 0.15, tertiary ethylene carbonate 6, inorganic Salt powder 2.5, wetting agent 1, defoaming agent 1.5, dispersing agent 1.2, thickener 1.
Further, the four silanols sodium salt modified polyurethane emulsion the preparation method comprises the following steps:
(1) in organic solvent by silane, sodium hydroxide, deionized water dissolving, anti-with the stirring of 150r/min revolving speed at 79 DEG C It after answering 1.5 hours, is cooled to room temperature, with 1500r/min revolving speed stirring 6 hours, then through revolving removing solvent, four sodium silanolates is made Salt, it is spare by vacuum drying;
(2) after mixing plant polyatomic alcohol and diisocyanate, it is added in reaction kettle, is then added into reaction kettle organic molten Agent stirs 40min with 200r/min revolving speed at 80 DEG C, then adds dibutyl tin dilaurate, and heat preservation carries out anti-at 80 DEG C It answers 3 hours, obtains performed polymer mixed liquor, hydrophilic chain extender and hydroxypropyl acrylate, four sodium silanolates are added into performed polymer mixed liquor Salt carries out polymerization reaction, and polymeric reaction temperature is 78 DEG C, and the reaction time is 5 hours, obtains condensate mixed liquor, mixes to condensate Liquid adds rare earth chloride, stirs evenly, and stands 1 hour, is then neutralized to neutrality with triethylamine again, then adds deionized water shearing Emulsify to obtain polyaminoester emulsion, remove the organic solvent in polyaminoester emulsion to get.
Further, step (1) silane, sodium hydroxide, deionized water mixing molar ratio are 1.2:2.5:1.8.
Further, step (1) and step (2) organic solvent are n,N-Dimethylformamide.
Further, step (2) plant polyatomic alcohol and diisocyanate mixing molar ratio are 1:1.
Further, step (2) the dibutyl tin dilaurate additive amount is the 0.5% of plant polyatomic alcohol quality.
Further, step (2) hydrophilic chain extender and hydroxypropyl acrylate, four silanol sodium salts and plant polyatomic alcohol are mixed Conjunction molar ratio is 1.5:80::0.5:2.8.
Further, step (2) the rare earth chloride additive amount is the 0.08% of condensate mixed liquor quality, the chlorination Rare earth is cerium chloride.
Further, the inorganic salts powder is that sodium citrate and aluminum aluminum sulfate are mixed by 3:1 mass ratio, is soaked Agent is propylene glycol, and defoaming agent is organic silicon defoamer, and dispersing agent is polyethylene glycol 200, and thickener is sodium cellulose glycolate.
Embodiment 3
A kind of environment-friendly water-based polyurethane coating, is made of following component by weight: four silanol sodium salt modified polyurethane emulsions 95, nanometer calcium carbonate 22, diatom ooze 36, hollow glass micropearl 5.8, trimethyl silicane potassium alcoholate 0.13, tertiary ethylene carbonate 5, inorganic Salt powder 2.1, wetting agent 0.8, defoaming agent 0.9, dispersing agent 0.6, thickener 0.8.
Further, the four silanols sodium salt modified polyurethane emulsion the preparation method comprises the following steps:
(1) in organic solvent by silane, sodium hydroxide, deionized water dissolving, anti-with the stirring of 150r/min revolving speed at 79 DEG C It after answering 1.5 hours, is cooled to room temperature, with 1500r/min revolving speed stirring 6 hours, then through revolving removing solvent, four sodium silanolates is made Salt, it is spare by vacuum drying;
(2) after mixing plant polyatomic alcohol and diisocyanate, it is added in reaction kettle, is then added into reaction kettle organic molten Agent stirs 40min with 200r/min revolving speed at 80 DEG C, then adds dibutyl tin dilaurate, and heat preservation carries out anti-at 80 DEG C It answers 3 hours, obtains performed polymer mixed liquor, hydrophilic chain extender and hydroxypropyl acrylate, four sodium silanolates are added into performed polymer mixed liquor Salt carries out polymerization reaction, and polymeric reaction temperature is 78 DEG C, and the reaction time is 5 hours, obtains condensate mixed liquor, mixes to condensate Liquid adds rare earth chloride, stirs evenly, and stands 1 hour, is then neutralized to neutrality with triethylamine again, then adds deionized water shearing Emulsify to obtain polyaminoester emulsion, remove the organic solvent in polyaminoester emulsion to get.
Further, step (1) silane, sodium hydroxide, deionized water mixing molar ratio are 1.2:2.5:1.8.
Further, step (1) and step (2) organic solvent are n,N-Dimethylformamide.
Further, step (2) plant polyatomic alcohol and diisocyanate mixing molar ratio are 1:1.
Further, step (2) the dibutyl tin dilaurate additive amount is the 0.5% of plant polyatomic alcohol quality.
Further, step (2) hydrophilic chain extender and hydroxypropyl acrylate, four silanol sodium salts and plant polyatomic alcohol are mixed Conjunction molar ratio is 1.5:80::0.5:2.8.
Further, step (2) the rare earth chloride additive amount is the 0.08% of condensate mixed liquor quality, the chlorination Rare earth is cerium chloride.
Further, the inorganic salts powder is that sodium citrate and aluminum aluminum sulfate are mixed by 3:1 mass ratio, is soaked Agent is propylene glycol, and defoaming agent is organic silicon defoamer, and dispersing agent is polyethylene glycol 200, and thickener is sodium cellulose glycolate.
Comparative example 1: it is only that four silanol sodium salt modified polyurethane emulsions replace with unmodified polyurethane with the difference of embodiment 1 Lotion, using application number: the polyaminoester emulsion of 201410413410.9 preparations.
Comparative example 2: it is only that with the difference of embodiment 1 and four silanol sodium salt modified polyurethane emulsions is replaced with into application number: 201110251188.3 modified polyurethane emulsion.
Examination criteria: it is detected by standard GB/T/T 9755-2001 exterior wall coating material of synthetic resin emulsion method, specifically Correlation data is as shown in table 1 below:
Table 1
Embodiment mean value Comparative example 1 Comparative example 2
Alkali resistance (48h) It is without exception There is exception There is exception
Abrasion resistance/time 2863 2098 2215
Stain resistant (white light color/%≤15) 10 22 19
Resistance to artificial weathering aging (600h) It is not blistering not peel off flawless Blistering, which is peeled off, crackle Crackle has not been peeled off in blistering
As can be seen from Table 1, environment-friendly water-based polyurethane coating prepared by the present invention have excellent abrasion resistance, stain resistant and Artificial ageing resistance performance.

Claims (9)

1. a kind of environment-friendly water-based polyurethane coating, which is characterized in that be made by weight of following component: four silanol sodium salts change Property polyaminoester emulsion 93-98, nanometer calcium carbonate 18-25, diatom ooze 35-39, hollow glass micropearl 5.2-6.4, trimethyl silanol Potassium 0.12-0.15, tertiary ethylene carbonate 3-6, inorganic salts powder 1.8-2.5, wetting agent 0.6-1, defoaming agent 0.5-1.5, dispersion Agent 0.5-1.2, thickener 0.5-1.
2. a kind of environment-friendly water-based polyurethane coating as described in claim 1, which is characterized in that the four silanols sodium salt is modified poly- Urethane emulsion preparation method are as follows:
(1) in organic solvent by silane, sodium hydroxide, deionized water dissolving, anti-with the stirring of 150r/min revolving speed at 79 DEG C It after answering 1.5 hours, is cooled to room temperature, with 1500r/min revolving speed stirring 6 hours, then through revolving removing solvent, four sodium silanolates is made Salt, it is spare by vacuum drying;
(2) after mixing plant polyatomic alcohol and diisocyanate, it is added in reaction kettle, is then added into reaction kettle organic molten Agent stirs 40min with 200r/min revolving speed at 80 DEG C, then adds dibutyl tin dilaurate, and heat preservation carries out anti-at 80 DEG C It answers 3 hours, obtains performed polymer mixed liquor, hydrophilic chain extender and hydroxypropyl acrylate, four sodium silanolates are added into performed polymer mixed liquor Salt carries out polymerization reaction, and polymeric reaction temperature is 78 DEG C, and the reaction time is 5 hours, obtains condensate mixed liquor, mixes to condensate Liquid adds rare earth chloride, stirs evenly, and stands 1 hour, is then neutralized to neutrality with triethylamine again, then adds deionized water shearing Emulsify to obtain polyaminoester emulsion, remove the organic solvent in polyaminoester emulsion to get.
3. a kind of environment-friendly water-based polyurethane coating as claimed in claim 2, which is characterized in that step (1) silane, hydrogen-oxygen Change sodium, deionized water mixing molar ratio is 1.2:2.5:1.8.
4. a kind of environment-friendly water-based polyurethane coating as claimed in claim 2, which is characterized in that step (1) and step (2) are described Organic solvent is N,N-dimethylformamide.
5. a kind of environment-friendly water-based polyurethane coating as claimed in claim 2, which is characterized in that step (2) described plant is polynary Pure and mild diisocyanate mixing molar ratio is 1:1.
6. a kind of environment-friendly water-based polyurethane coating as claimed in claim 2, which is characterized in that step (2) described tin dilaurate Dibutyl tin additive amount is the 0.5% of plant polyatomic alcohol quality.
7. a kind of environment-friendly water-based polyurethane coating as claimed in claim 2, which is characterized in that step (2) the hydrophilic chain extension It is 1.5:80::0.5:2.8 that agent and hydroxypropyl acrylate, four silanol sodium salts, which mix molar ratio with plant polyatomic alcohol,.
8. a kind of environment-friendly water-based polyurethane coating as claimed in claim 2, which is characterized in that step (2) described rare earth chloride Additive amount is the 0.08% of condensate mixed liquor quality, and the rare earth chloride is cerium chloride.
9. a kind of environment-friendly water-based polyurethane coating as described in claim 1, which is characterized in that the inorganic salts powder is lemon Sour sodium and aluminum aluminum sulfate are mixed by 3:1 mass ratio, and wetting agent is propylene glycol, and defoaming agent is organic silicon defoamer, dispersion Agent is polyethylene glycol 200, and thickener is sodium cellulose glycolate.
CN201811237903.6A 2018-10-23 2018-10-23 A kind of environment-friendly water-based polyurethane coating Withdrawn CN109370412A (en)