CN109082973A - A kind of curly wire lawn plastic cement race track production method - Google Patents
A kind of curly wire lawn plastic cement race track production method Download PDFInfo
- Publication number
- CN109082973A CN109082973A CN201811089981.6A CN201811089981A CN109082973A CN 109082973 A CN109082973 A CN 109082973A CN 201811089981 A CN201811089981 A CN 201811089981A CN 109082973 A CN109082973 A CN 109082973A
- Authority
- CN
- China
- Prior art keywords
- surface layer
- plastic cement
- parts
- millimeters
- race track
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of curly wire lawn plastic cement race track production methods, the present invention solves the prior art, and there are disadvantages following steps: S1, sorting, base polyurethane prepolymer for use as, admixtured polyether, scrap tire rubber, EPDM rubber grain or PU particle, pigment, auxiliary agent, filler, strong environmental protection antiskid particles, sandstone, S2, base is laid with, by excavating construction ground at runway spill, total depth is up to 300 millimeters, width is carried out according to standard, S3, topping laying, it uniformly paves 5 millimeters in the top surface surface layer glue and EPDM of base by 1 to 7 proportion, S4, mixed raw material is mated formation, surface layer mixed raw material is made in the above stirring and pours into base's spill runway, it is rolled simultaneously using weight roller, S5, mat formation on surface layer, to sum up after the completion of step, the surface layer upper surface coating strong environmental protection paved after the cooling period is prevented Sliding stratum granulosum, S6, surface layer are mated formation mixed proportion, 70 parts of strong environmental protection antiskid particles layer and 13 parts of virgin rubber containing EPDM, and finally progress quality testing and drainage construction can normally come into operation.
Description
Technical field
The present invention relates to sporting equipment technical field more particularly to a kind of curly wire lawn plastic cement race track production methods.
Background technique
Plastic cement race track is also known as round-the-clock athletics tracks, it by base polyurethane prepolymer for use as, admixtured polyether, scrap tire rubber,
EPDM rubber grain or PU particle, pigment, auxiliary agent, filler composition.Plastic cement race track is with flatness is good, compression strength is high, hardness bullet
Property appropriate, stable physical property characteristic, be conducive to the performance of sportsman's speed and technology, effectively improve sports achievement, drop
Low tumble injury rate.Plastic cement race track is made of materials such as polyurethane rubbers, has certain elasticity and color, has certain resist
UV resistance and ageing-resistant power are best all-weather outdoor athletic ground terrace materials generally acknowledged in the world.
Polyurethane plastic is moderate, bright in colour with elasticity, anti-skid wearable, place cleaning, easy maintenance, can effectively avoid
Sportsman's damage significantly improves the features such as sports achievement, generally uses in the sports and training of countries in the world.
It is laid with plastic cement race track along with the development of sports cause in China and has become major small and medium-sized cities itself hair
Open up indispensable one of hardware.Existing polyurethane plastic production technology is complicated, high production cost.It is therefore desirable to propose one
Kind curly wire lawn plastic cement race track production method.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of curly wire lawn plastic cement proposed is run
Road production method.
To achieve the goals above, present invention employs following technical solutions:
1, a kind of curly wire lawn plastic cement race track production method, comprising the following steps:
S1, sorting, base polyurethane prepolymer for use as, admixtured polyether, scrap tire rubber, EPDM rubber grain or PU particle, help pigment
Agent, filler, strong environmental protection antiskid particles, sandstone.
S2, base are laid with, and by excavating construction ground at runway spill, total depth is up to 300 millimeters, and width is according to mark
Standard carries out, and bottom construction carries out scrap tire rubber using 200 millimeters of overall thickness and the pure scrap tire rubber of black pads paving layer by layer, often
Layer matches spice by 1 to 8 using glue particle between layers and paves 5 mm of thickness with a thickness of 50 millimeters.
S3, topping laying uniformly pave 5 millimeters in the top surface surface layer glue and EPDM of base by 1 to 7 proportion, until glue
Water is parched applying again again and be brushed one times, and and so on 3 times, can be laid with surface layer, topping laying material is according to base polyurethane prepolymer for use as 20-
30 parts, 5-10 parts of admixtured polyether, EPDM rubber grain or 10-20 parts of PU particle, 10-15 parts of pigment, 10-15 parts of auxiliary agent, filler
20-30 parts 350 degrees Celsius of continuous heating of progress reactor tank, while catalyst is added in reactor tank, it is stirred continuously reactor tank 45
Minute surface layer mixed raw material produced above.
S4, mixed raw material are mated formation, and surface layer mixed raw material is made in the above stirring and pours into base's spill runway, while using weight
Roller rolls, and stands 24 hours after raw material to be mixed is cooling, can be prepared by elastic surface layer.
S5, surface layer are mated formation, and to sum up after the completion of step, the surface layer upper surface coating strong environmental protection paved after the cooling period is prevented
Sliding stratum granulosum.
S6, surface layer are mated formation mixed proportion, 70 parts of strong environmental protection antiskid particles layer and 13 parts of virgin rubber containing EPDM, and polyurethane is without molten
17 parts of agent Environment-friendlyglue glue are uniformly mixed, and are put into agitator tank, while catalyst is added, and are uniformly paved on after high-temperature stirring reaction
In above-mentioned surface layer, to its natural cooling.
S7, detection-phase, above-mentioned steps are earnestly handled by cutting machine after the completion, runway are uniformly cut into several
Block is crossed after solidification, and solvent-free plastic cement race track construction is completed, and finally progress quality testing and drainage construction can normally put into and make
With.
Further, the pure scrap tire rubber of the black.Particle size 2-4 mm dia, no powder impurity, colored
Grain specification 1-3 mm dia, virgin rubber containing EPDM 13%, the solvent-free Environment-friendlyglue glue of polyurethane, the pure white sticky virgin rubber of appearance.
Further, the EPDM colorful surface layer particle is constructed thickness 5-6 millimeters.
Further, the glue material proportion；German BASF mi33.33, polyethers 66.66%, using high speed dispersion
Thermosensitive response, color is pure white, viscosity virgin rubber.
Further, runway recess lowest point is loaded using sandstone before the base is laid with, and specific sand fraction is 7:3,
First part stone is laid in lowest point, by vibrating disk by its ram-jolt, then sand is overlying on its surface thickness uniformly with Specific construction
It is required that formulate, generally 100 millimeters of stone thickness, 50 millimeters of sand thickness.
Further, the filler is polystyrene foamed plastics.
Compared with prior art, the beneficial effects of the present invention are:
1. plastic cement race track has, flatness is good, compression strength is high, elastic appropriate, stable physical property the characteristic of hardness, has
Conducive to the performance of sportsman's speed and technology, sports achievement is effectively improved, reduces tumble injury rate.Plastic cement race track is by polyurethane rubber
The materials such as glue composition, there is certain elasticity and color, there is certain anti-uv-ray and ageing-resistant power is in the world
Generally acknowledged best all-weather outdoor athletic ground terrace material.
2. filler be polystyrene foamed plastics, have it is light-weight, nontoxic, have certain elasticity, can be with mold
Molding, cheap, water imbibition very little, lower temperature resistance is good, and resistance to molten jelly property is good, and it is larger to occupy volume.
3. surface micelle uses damascene structures, guarantee that track systems have excellent weatherability and anti-spikes energy of rupture
Power, using profession from branching mechanical execution, surface is without clever gap and more smooth, material selection EPDM micelle and polyurethane glue
Not making, surface layer uses coloured EPDM micelle, and with height uvioresistant resistance, make the runway without the misgivings of colour fading,
It is different from traditional runway, it is non-toxic and tasteless even if under burning sun is exposed to the sun, be conducive to the environment for safeguarding periphery, it is strong conducive to body
Health.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
A kind of embodiment 1: curly wire lawn plastic cement race track production method, comprising the following steps:
S1, sorting, base polyurethane prepolymer for use as, admixtured polyether, scrap tire rubber, EPDM rubber grain or PU particle, help pigment
Agent, filler, strong environmental protection antiskid particles, sandstone.
S2, base are laid with, and by excavating construction ground at runway spill, total depth is up to 300 millimeters, and width is according to mark
Standard carries out, and bottom construction carries out scrap tire rubber using 200 millimeters of overall thickness and the pure scrap tire rubber of black pads paving layer by layer, often
Layer matches spice by 1 to 8 using glue particle between layers and paves 5 mm of thickness with a thickness of 50 millimeters.
S3, topping laying uniformly pave 5 millimeters in the top surface surface layer glue and EPDM of base by 1 to 7 proportion, until glue
Water is parched applying again again and be brushed one times, and and so on 3 times, can be laid with surface layer, topping laying material according to:
350 degrees Celsius of reactor tank continuous heating are carried out, while adding catalyst in reactor tank, is stirred continuously reactor tank 45
Minute surface layer mixed raw material produced above.
S4, mixed raw material are mated formation, and surface layer mixed raw material is made in the above stirring and pours into base's spill runway, while using weight
Roller rolls, and stands 24 hours after raw material to be mixed is cooling, can be prepared by elastic surface layer.
S5, surface layer are mated formation, and to sum up after the completion of step, the surface layer upper surface coating strong environmental protection paved after the cooling period is prevented
Sliding stratum granulosum.
S6, surface layer are mated formation mixed proportion, 70 parts of strong environmental protection antiskid particles layer and 13 parts of virgin rubber containing EPDM, and polyurethane is without molten
17 parts of agent Environment-friendlyglue glue are uniformly mixed, and are put into agitator tank, while catalyst is added, and are uniformly paved on after high-temperature stirring reaction
In above-mentioned surface layer, to its natural cooling.
S7, detection-phase, above-mentioned steps are earnestly handled by cutting machine after the completion, runway are uniformly cut into several
Block is crossed after solidification, and solvent-free plastic cement race track construction is completed, and finally progress quality testing and drainage construction can normally put into and make
With.
A kind of embodiment 2: curly wire lawn plastic cement race track production method, comprising the following steps:
S1, sorting, base polyurethane prepolymer for use as, admixtured polyether, scrap tire rubber, EPDM rubber grain or PU particle, help pigment
Agent, filler, strong environmental protection antiskid particles, sandstone.
S2, base are laid with, and by excavating construction ground at runway spill, total depth is up to 300 millimeters, and width is according to mark
Standard carries out, and bottom construction carries out scrap tire rubber using 200 millimeters of overall thickness and the pure scrap tire rubber of black pads paving layer by layer, often
Layer matches spice by 1 to 8 using glue particle between layers and paves 5 mm of thickness with a thickness of 50 millimeters.
S3, topping laying uniformly pave 5 millimeters in the top surface surface layer glue and EPDM of base by 1 to 7 proportion, until glue
Water is parched applying again again and be brushed one times, and and so on 3 times, can be laid with surface layer, topping laying material according to
350 degrees Celsius of reactor tank continuous heating are carried out, while adding catalyst in reactor tank, is stirred continuously reactor tank 45
Minute surface layer mixed raw material produced above.
S4, mixed raw material are mated formation, and surface layer mixed raw material is made in the above stirring and pours into base's spill runway, while using weight
Roller rolls, and stands 24 hours after raw material to be mixed is cooling, can be prepared by elastic surface layer.
S5, surface layer are mated formation, and to sum up after the completion of step, the surface layer upper surface coating strong environmental protection paved after the cooling period is prevented
Sliding stratum granulosum.
S6, surface layer are mated formation mixed proportion, 70 parts of strong environmental protection antiskid particles layer and 13 parts of virgin rubber containing EPDM, and polyurethane is without molten
17 parts of agent Environment-friendlyglue glue are uniformly mixed, and are put into agitator tank, while catalyst is added, and are uniformly paved on after high-temperature stirring reaction
In above-mentioned surface layer, to its natural cooling.
S7, detection-phase, above-mentioned steps are earnestly handled by cutting machine after the completion, runway are uniformly cut into several
Block is crossed after solidification, and solvent-free plastic cement race track construction is completed, and finally progress quality testing and drainage construction can normally put into and make
With.
A kind of embodiment 3: curly wire lawn plastic cement race track production method, comprising the following steps:
S1, sorting, base polyurethane prepolymer for use as, admixtured polyether, scrap tire rubber, EPDM rubber grain or PU particle, help pigment
Agent, filler, strong environmental protection antiskid particles, sandstone.
S2, base are laid with, and by excavating construction ground at runway spill, total depth is up to 300 millimeters, and width is according to mark
Standard carries out, and bottom construction carries out scrap tire rubber using 200 millimeters of overall thickness and the pure scrap tire rubber of black pads paving layer by layer, often
Layer matches spice by 1 to 8 using glue particle between layers and paves 5 mm of thickness with a thickness of 50 millimeters.
S3, topping laying uniformly pave 5 millimeters in the top surface surface layer glue and EPDM of base by 1 to 7 proportion, until glue
Water is parched applying again again and be brushed one times, and and so on 3 times, can be laid with surface layer, topping laying material according to
350 degrees Celsius of reactor tank continuous heating are carried out, while adding catalyst in reactor tank, is stirred continuously reactor tank 45
Minute surface layer mixed raw material produced above.
S4, mixed raw material are mated formation, and surface layer mixed raw material is made in the above stirring and pours into base's spill runway, while using weight
Roller rolls, and stands 24 hours after raw material to be mixed is cooling, can be prepared by elastic surface layer.
S5, surface layer are mated formation, and to sum up after the completion of step, the surface layer upper surface coating strong environmental protection paved after the cooling period is prevented
Sliding stratum granulosum.
S6, surface layer are mated formation mixed proportion, 70 parts of strong environmental protection antiskid particles layer and 13 parts of virgin rubber containing EPDM, and polyurethane is without molten
17 parts of agent Environment-friendlyglue glue are uniformly mixed, and are put into agitator tank, while catalyst is added, and are uniformly paved on after high-temperature stirring reaction
In above-mentioned surface layer, to its natural cooling.
S7, detection-phase, above-mentioned steps are earnestly handled by cutting machine after the completion, runway are uniformly cut into several
Block is crossed after solidification, and solvent-free plastic cement race track construction is completed, and finally progress quality testing and drainage construction can normally put into and make
With.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of curly wire lawn plastic cement race track production method, which comprises the following steps:
S1, sorting, base polyurethane prepolymer for use as, admixtured polyether, scrap tire rubber, EPDM rubber grain or PU particle, pigment, auxiliary agent are filled out
Fill agent, strong environmental protection antiskid particles, sandstone.
S2, base are laid with, by excavating construction ground at runway spill, total depth up to 300 millimeters, width according to standard into
Row, bottom construction carries out scrap tire rubber using 200 millimeters of overall thickness and the pure scrap tire rubber of black pads paving, every thickness layer by layer
Degree is 50 millimeters, matches spice by 1 to 8 using glue particle between layers and paves 5 mm of thickness.
S3, topping laying uniformly pave 5 millimeters in the top surface surface layer glue and EPDM of base by 1 to 7 proportion, until glue is dry
It applies and brushes one times again again thoroughly, and so on 3 times, surface layer can be laid with, topping laying material is according to base polyurethane prepolymer for use as 20-30
Part, 5-10 parts of admixtured polyether, EPDM rubber grain or 10-20 parts of PU particle, 10-15 parts of pigment, 10-15 parts of auxiliary agent, filler 20-
30 parts 350 degrees Celsius of continuous heating of progress reactor tank, while catalyst is added in reactor tank, it is stirred continuously reactor tank 45 minutes
Surface layer mixed raw material produced above.
S4, mixed raw material are mated formation, and surface layer mixed raw material is made in the above stirring and pours into base's spill runway, while being ground using weight roller
Pressure stands 24 hours after raw material to be mixed is cooling, can be prepared by elastic surface layer.
S5, surface layer are mated formation, to sum up after the completion of step, anti-skidding of surface layer upper surface coating strong environmental protection will paving after the cooling period
Granulosa.
S6, surface layer are mated formation mixed proportion, 70 parts of strong environmental protection antiskid particles layer and 13 parts of virgin rubber containing EPDM, the solvent-free ring of polyurethane
It protects 17 parts of glue to be uniformly mixed, be put into agitator tank, while catalyst is added, be uniformly paved on after high-temperature stirring reaction above-mentioned
In surface layer, to its natural cooling.
S7, detection-phase, above-mentioned steps are earnestly handled by cutting machine after the completion, and runway is uniformly cut into several pieces,
It crosses after solidification, solvent-free plastic cement race track construction is completed, and finally carrying out quality testing and drainage construction can normally come into operation.
2. a kind of curly wire lawn plastic cement race track production method according to claim 1, which is characterized in that the pure wheel of black
Tire rubber particle.Particle size 2-4 mm dia, no powder impurity, color grains specification 1-3 mm dia, virgin rubber containing EPDM
13%, the solvent-free Environment-friendlyglue glue of polyurethane, the pure white sticky virgin rubber of appearance.
3. a kind of curly wire lawn plastic cement race track production method according to claim 1, which is characterized in that the EPDM is colored
Surface layer particle is constructed thickness 5-6 millimeters.
4. a kind of curly wire lawn plastic cement race track production method according to claim 1, which is characterized in that the glue material
Proportion；German BASF mi33.33, polyethers 66.66%, using high speed dispersion thermosensitive response, color is pure white, viscosity virgin rubber.
5. a kind of curly wire lawn plastic cement race track production method according to claim 1, which is characterized in that the base is laid with
Preceding runway recess lowest point is loaded using sandstone, and specific sand fraction is 7:3, and first part stone is laid in lowest point, passes through vibration
Disk is by its ram-jolt, then sand is uniformly overlying on to its surface thickness and is formulated with Specific construction requirement, generally stone thickness 100 milli
Rice, 50 millimeters of sand thickness.
6. a kind of curly wire lawn plastic cement race track production method according to claim 1, which is characterized in that the filler is
Polystyrene foamed plastics.