CN108656265A - A kind of bamboo wood rolls the preparation method for discongesting machining bamboo beam - Google Patents
A kind of bamboo wood rolls the preparation method for discongesting machining bamboo beam Download PDFInfo
- Publication number
- CN108656265A CN108656265A CN201810452734.1A CN201810452734A CN108656265A CN 108656265 A CN108656265 A CN 108656265A CN 201810452734 A CN201810452734 A CN 201810452734A CN 108656265 A CN108656265 A CN 108656265A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- yellow
- time
- fluffer
- run
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The preparation method for discongesting machining bamboo beam, including step are rolled the invention discloses a kind of bamboo wood：(1) bamboo particle pretreatment：By bamboo wood hacking at bamboo chip；(2) bamboo chip is entered into feed inlet, bamboo chip, which is (3) entered feed rolls, goes ring, flattening；It rolls fluffer yellow bamboo face discongest for the first time；(4) the brittle layer on tabasheer surface layer is removed using the yellow circular shaft knife to run at high speed；(5) bamboo chip is flattened, roll fluffer and yellow bamboo face is discongested for the second time；(6) bamboo blueness and wax coat are removed using the yellow circular shaft knife to run at high speed；(7) bamboo chip is flattened, roll fluffer and bamboo strip discongest for the first time；(8) bamboo blueness and wax coat are removed using the yellow circular shaft knife to run at high speed is secondary；(9) bamboo chip is flattened, roll fluffer and bamboo strip is discongested for the second time；(10) the brittle layer on tabasheer surface layer is removed for the second time using the yellow circular shaft knife to run at high speed；(11) two sides is rolled again respectively through discongesting roller, discongest after form loose reticular fibre beam；(12) carbonization is dried in reticular fibre beam.
Description
Technical field
The present invention relates to the manufacture fields of bamboo wood, more particularly to a kind of bamboo beam preparation method.
Background technology
The Recombined bamboo produced at present is being prepared with bamboo beam, and quality of the bamboo beam when discongesting determines to a certain extent
The quality of Recombined bamboo quality.
The existing type bamboo fluffer that rolls is the preferable one kind for producing bamboo beam, and mainly industrialization degree is higher, bamboo
The advantages that material utilization rate is high, but due to there is no the bamboo with wax coat for removing major part green during preparing bamboo beam and brittleness
Bamboo beam is made during impregnation in high tabasheer, and adhesive very well, cannot be penetrated into fully inside bamboo beam and bamboo bundle fiber
It goes, main cause is the blueness of bamboo wood, the silica contained by yellow face, is formd using closing that carbohydrate is bone simultaneously doped silicon type organic
Layer, it is difficult to impregnation, make impregnation resin content be not achieved as defined in require and lack of homogeneity, brought to the quality of product it is unstable, especially
It is that Recombined bamboo product is mainly used for exporting, leads to that export requirement is not achieved；
Invention content
The present invention provides a kind of processing method for the preparation bamboo beam can guarantee Recombined bamboo product quality.
To achieve the above object, the present invention is implemented by the following technical solutions：
A kind of bamboo wood rolls the preparation method for discongesting machining bamboo beam, including step：
(1) bamboo particle pretreatment：By bamboo wood hacking at the bamboo chip of wide 20-60mm；
(2) bamboo chip is entered into feed inlet,
(3) bamboo chip is entered into feed rolls and go ring, flattening；It rolls fluffer simultaneously yellow bamboo face discongest for the first time；
(4) the brittle layer on tabasheer surface layer is removed using the yellow circular shaft knife to run at high speed；
(5) bamboo chip is flattened, roll fluffer and yellow bamboo face is discongested for the second time；
(6) bamboo blueness and wax coat are removed using the yellow circular shaft knife to run at high speed；
(7) bamboo chip is flattened, roll fluffer and bamboo strip discongest for the first time；
(8) bamboo blueness and wax coat are removed using the yellow circular shaft knife to run at high speed is secondary；
(9) bamboo chip is flattened, roll fluffer and bamboo strip is discongested for the second time；
(10) the brittle layer on tabasheer surface layer is removed for the second time using the yellow circular shaft knife to run at high speed；
(11) two sides is rolled again respectively through discongesting roller, discongest after form loose reticular fibre beam；
(12) reticular fibre beam is sent into the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon is 160-190
DEG C, 2-4 hours heating times, the carbonization of reticular fibre beam, carbonizing degree is 5%-30%.
Preferably, the part for removing bamboo blueness is thickness 0.5-1mm；Remove the brittle layer on tabasheer surface layer
Thickness 0.2-0.5mm.
The beneficial effects of the invention are as follows：
The present invention is exactly and to pass through repeatedly flattening through removing ring, removing green and tabasheer the epidermis of bamboo, repeatedly discongest, this
Sample raw material is disposable to be out just processed into qualified bamboo bundle fiber after feed inlet is entered, and the bamboo removed it is green and bamboo
Yellow epidermis is thin, both ensure that the tabasheer high with the bamboo blueness of wax coat and brittleness for removing and influencing product quality, improves
Utilization rate of bamboo, has saved manpower, energy consumption and bamboo resource, properties of product be apparently higher than and better than existing product quality.
Specific implementation mode
Embodiments of the present invention are further described with reference to embodiment, but are not limitation of the invention.
A kind of bamboo wood rolls the preparation method for discongesting machining bamboo beam, including step：
(1) bamboo particle pretreatment：By bamboo wood hacking at the bamboo chip of wide 20-60mm；
(2) bamboo chip is entered into feed inlet,
(3) bamboo chip is entered into feed rolls and go ring, flattening；It rolls fluffer simultaneously yellow bamboo face discongest for the first time；
(4) the brittle layer on tabasheer surface layer is removed using the yellow circular shaft knife to run at high speed；
(5) bamboo chip is flattened, roll fluffer and yellow bamboo face is discongested for the second time；
(6) bamboo blueness and wax coat are removed using the yellow circular shaft knife to run at high speed；
(7) bamboo chip is flattened, roll fluffer and bamboo strip discongest for the first time；
(8) remove that bamboo is green and wax coat, the part for removing bamboo blueness are using the yellow circular shaft knife to run at high speed is secondary
Thickness 0.5-1mm；Remove the thickness 0.2-0.5mm of the brittle layer on tabasheer surface layer；
(9) bamboo chip is flattened, roll fluffer and bamboo strip is discongested for the second time；
(10) the brittle layer on tabasheer surface layer is removed for the second time using the yellow circular shaft knife to run at high speed；
(11) two sides is rolled again respectively through discongesting roller, discongest after form loose reticular fibre beam；
(12) reticular fibre beam is sent into the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon is 160-190
DEG C, 2-4 hours heating times, the carbonization of reticular fibre beam, carbonizing degree is 5%-30%.
The above described is only a preferred embodiment of the present invention, not making any form to technical scheme of the present invention
On limitation.Every essence according to the present invention is to any simple modification, equivalent change and modification made by above example,
It falls within the scope of protection of the present invention.
Claims (2)
1. a kind of bamboo wood rolls the preparation method for discongesting machining bamboo beam, which is characterized in that including step：
(1) bamboo particle pretreatment：By bamboo wood hacking at the bamboo chip of wide 20-60mm；
(2) bamboo chip is entered into feed inlet,
(3) bamboo chip is entered into feed rolls and go ring, flattening；It rolls fluffer simultaneously yellow bamboo face discongest for the first time；
(4) the brittle layer on tabasheer surface layer is removed using the yellow circular shaft knife to run at high speed；
(5) bamboo chip is flattened, roll fluffer and yellow bamboo face is discongested for the second time；
(6) bamboo blueness and wax coat are removed using the yellow circular shaft knife to run at high speed；
(7) bamboo chip is flattened, roll fluffer and bamboo strip discongest for the first time；
(8) bamboo blueness and wax coat are removed using the yellow circular shaft knife to run at high speed is secondary；
(9) bamboo chip is flattened, roll fluffer and bamboo strip is discongested for the second time；
(10) the brittle layer on tabasheer surface layer is removed for the second time using the yellow circular shaft knife to run at high speed；
(11) two sides is rolled again respectively through discongesting roller, discongest after form loose reticular fibre beam；
(12) reticular fibre beam is sent into the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon is 160-190 DEG C,
2-4 hours heating times, the carbonization of reticular fibre beam, carbonizing degree are 5%-30%.
2. the preparation method of bamboo beam as described in claim 1, it is characterised in that：The part for removing bamboo blueness is thickness
0.5-1mm；Remove the thickness 0.2-0.5mm of the brittle layer on tabasheer surface layer.