CN108582336A - A kind of manufacturing method of composite board of small pieces of bamboo reinforcement - Google Patents
A kind of manufacturing method of composite board of small pieces of bamboo reinforcement Download PDFInfo
- Publication number
- CN108582336A CN108582336A CN201810497549.4A CN201810497549A CN108582336A CN 108582336 A CN108582336 A CN 108582336A CN 201810497549 A CN201810497549 A CN 201810497549A CN 108582336 A CN108582336 A CN 108582336A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- particle
- wood
- small pieces
- composite board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of manufacturing method of composite board of small pieces of bamboo reinforcement, method and step is as follows：Appropriate bamboo wood and bamboo branch item, bamboo and wood processing remaining material or straw are chosen as raw material；Bamboo branch item or bamboo and wood processing remaining material or straw are ground into particle；Particle stacks ageing, dry carbonization；Selection sieve pore specification is 0.5cm, the sieve of 0.5~1cm specifications, and particle is sieved, is graded stackings by thickness, is weighed, glued, resin added is 25~35%；The thin bamboo strip is split into bamboo wood hacking, drying to moisture content is 8~12%；Bamboo slights predrying after gluing；Bamboo is slightd and is woven into bamboo reinforcement net；Coarse particles are filled in bamboo reinforcement net areola by assembly, and disentegrated particles are covered in bamboo reinforcement is online, lower surface；Blank is pressed under room temperature in advance；The preset backing plate on hot press, preset fixed width on backing plate determine slab；Blank is put into fixed width, determines the space that slab surrounds by hot pressing, and upper and lower surface lays finish coat, carries out hot pressing, is pressed into composite board of small pieces of bamboo reinforcement.
Description
Technical field
Bamboo reinforcement net made of bamboo wood and bamboo and wood processing remaining material or straw etc. particles heat are utilized the present invention relates to a kind of
The manufacturing method of molded composite board of small pieces of bamboo reinforcement, belongs to field of plate manufacture.
Background technology
Bamboo wood has the advantages that intensity is big, hardness is high, resourceful and can replace timber, and bamboo branch item, bamboo processing are surplus
The particles such as remaining particle or straw have the characteristics that fillibility is good, dilatancy is uniform, sound-insulating heat-insulation property is good, thus the two is being made
It is used widely in board industry.The wood-based plate produced currently with bamboo wood, particle is had by its structure and processing technology point：It is glued
Plate class, laminate class and flakeboard class.Bamboo wood is split gluing after piece, is hot pressed into plate by the first two kind plank using bamboo wood as primary raw material
Material, intensity, hardness are preferable, but that there are consumption of raw materials amounts is big, processing request is high, interiors of products gap is more, density is small, thickness error
The defects of big, the number of turnover is less when being used as building template, and surface is rougher, tends not to meet building surface
Flatness requirement.The latter is cold-pressed or is hot pressed into plank using particle as primary raw material, by particle, and bamboo wood consumption is few, and cost is relatively low, production
Product density is big, and flatness is high, but there are the smaller defect of product mechanical strength, cannot meet as building template, truck board and
The performance requirement of the larger bamboo wood board of other loads, reuse rate are low.The bamboo wood board of existing method manufacture, density and strong
Degree is difficult to improve again, and thickness error phenomenon is difficult to avoid that.
Invention content
The technical problem to be solved in the present invention and the technical assignment of proposition are to overcome defect existing for existing product, provide one
Kind high intensity, the manufacturing method of high density, the good composite board of small pieces of bamboo reinforcement of flatness.It is to utilize bamboo reinforcement net made of bamboo wood
It is produced full as raw material by improving plate construction and manufacturing method with the bamboo and wood processing particles such as remaining material or straw
Foot is as building template, the composite board of small pieces of bamboo reinforcement of truck board and the larger bamboo composite board material performance requirement of other loads.
To achieve the above object, the present invention is implemented by the following technical solutions：
A kind of manufacturing method of composite board of small pieces of bamboo reinforcement, method and step are as follows：
Appropriate bamboo wood and bamboo branch item, bamboo and wood processing remaining material or straw are chosen as raw material；
Bamboo branch item or bamboo and wood processing remaining material or straw are ground into particle by 1-1；
1-2 particles stack ageing, and particle is placed in the dry machine of dried disinfecting carbon, the dry machine heating of dried disinfecting carbon by dry carbonization
Temperature be 160-190 DEG C, 2-4 hours heating times, particle carbonization, carbonizing degree be 5%-30%；
It is 0.5cm that 1-3, which selects sieve pore specification, the sieve of 0.5~1cm specifications, and particle is sieved, is graded heap by thickness
It puts, is weighed, glued, resin added is 25~35%；
Bamboo wood hacking is split the thin bamboo strip by 2-1, and drying to moisture content is 8~12%；
2-2 bamboos slight predrying after gluing；
2-3, which slights bamboo, is woven into bamboo reinforcement net；
Coarse particles are filled in bamboo reinforcement net areola by 3-1 assemblies, and disentegrated particles are covered in bamboo reinforcement is online, lower surface；
It is pressed into blank in advance under 3-2 room temperature；
4-1 preset backing plates on hot press, preset fixed width on backing plate determine slab；
Blank is put into fixed width, determines the space that slab surrounds by 4-2 hot pressing, and upper and lower surface lays finish coat, carries out hot pressing,
Hot pressing temperature is 100~160 DEG C, and pressure is 10~60Mpa, is pressed into composite board of small pieces of bamboo reinforcement.
Preferably, it is 0.5~4.0mm that the bamboo, which slights thickness, width is 0.5~2.5mm, and track and column braiding is at groined type bamboo
Muscle net, 5 × 5~250 × 250mm of sizing grid.
Preferably, described group of blank process is with finish coat, bamboo mat or wood chip, particle, groined type bamboo reinforcement net, particle, bamboo mat
Or the sequence of wood chip, finishing material lays raw material.
Preferably, one or more layers can be arranged in the groined type bamboo reinforcement net in described group of blank process.
Preferably, the glue kind of the gluing is one kind of modified phenolic glue or modified urea-formaldehyde glue, waterproof is added in when gluing
Agent, waterproofing agent dosage are 3~5%.
The beneficial effects of the invention are as follows：
The present invention uses the particle of abundance, reduces production cost, makes to be taken as fuel wood or discarded raw material in the past
It re-uses, substantially increases the comprehensive utilization ratio of resource；It is reasonable in design.Due to utilizing bamboo wood bamboo reinforcement net and particle easily
In conjunction with characteristic, manufactured plate product has been compatible with the good characteristic of bamboo plywood and flakeboard, has high intensity, high hard
The features such as degree, density is big, high-flatness, physico-mechanical properties and exterior quality are good, high as building template reuse rate,
After being first cold-pressed hot pressing process reduce " bubblings " phenomenon of bamboo board class product, product qualification rate height, plank thickness is uniform.
Specific implementation mode
Embodiments of the present invention are further described with reference to embodiment, but are not limitation of the invention.
Embodiment 1
1) prepare raw material：Bamboo wood, the bamboo wood for making bamboo reinforcement net can be moso bamboos, and other bamboo kinds also can be selected.Moso bamboo is logical
Normal life in 5 years (3 degree) is more suitable, and other bamboo kind triennials are more suitable；Select bamboo branch item or bamboo and wood processing remaining material or plant straw
It is one or more in stalk.
2) bamboo branch item or bamboo and wood processing remaining material or straw are crushed through cal rolling.
3) ageing is stacked, particle stacks ageing, and particle is placed in the dry machine of dried disinfecting carbon, dried disinfecting carbon by dry carbonization
The temperature of dry machine heating is 160 DEG C, 2 hours heating times, particle carbonization, carbonizing degree 5%；.
4) particle after dry is sieved, and grades stacking by thickness, and the plank with 122 × 244 × 1.2cm specifications is
Example, using 28 kilograms of particles, density is 0.8~1.2g/cm3.
5) it weighed, glued, resin added is 25~35%.Glue kind is one kind of modified phenolic glue or modified urea-formaldehyde glue.
6) moso bamboo hacking：It is split into 1.5~4.0mm of thickness, the bamboo chip of wide 10~30mm.
7) bamboo chip drying chamber is placed on to dry to moisture content 8~12%.
8) predrying after gluing bamboo chip.Glue kind is one kind of modified phenolic glue or modified urea-formaldehyde glue.
9) divide track and column braiding at the groined type net of the hollow squares mesh of (3~15 × 3~15) cm bamboo chip.
10) assembly；Bamboo reinforcement is online, lower surface lays quantitative particle, quantitative particle is put by surface layer fines, intermediate coarse fodder
It sets, i.e., what particle was thicker is filled in bamboo reinforcement net areola, thinner to be covered in that bamboo reinforcement is online, lower surface；With finishing paper+bamboo mat or
The sequence of art piece+particle+groined type bamboo reinforcement net+particle+bamboo mat or wood chip+paper, uniform assembly symmetrical above and below.According to actual needs
Specification, groined type bamboo reinforcement net can lay 2 layers or multilayer.
11) precompressed：To being put into preformer precompressed through the good blank of assembly.
12) hot pressing；The steel backing plate of the preset surfacing on hot press, preset fixed width on backing plate determine slab；By blank
It is put into fixed width, determines the space that slab (can adjust size as needed) surrounds, upper and lower surface lays finish coat, carries out heat
Pressure, hot pressing temperature are 100~160 DEG C, and pressure is 10~60Mpa, is pressed into composite board of small pieces of bamboo reinforcement.
13) finished product trimming：The plank suppressed is modified, Burr removal is removed, reaches required specification.
Its structure of the composite board of small pieces of bamboo reinforcement produced according to above-mentioned operation is that center is bamboo reinforcement net, (4), from the inside to surface
Symmetrical lay is particle (3), bamboo mat or wood chip (2), finish coat (1), and product has high intensity, high rigidity, density big, high smooth
The good characteristics such as degree, physico-mechanical properties are good and exterior quality is outstanding, reusable multiple, can meet as building mould
The performance requirement of plate, truck board and the larger bamboo wood board of other loads.
The above described is only a preferred embodiment of the present invention, not making any form to technical scheme of the present invention
On limitation.Every essence according to the present invention is to any simple modification, equivalent change and modification made by above example,
It falls within the scope of protection of the present invention.
Claims (5)
1. a kind of manufacturing method of composite board of small pieces of bamboo reinforcement, it is characterised in that method and step is as follows：
Appropriate bamboo wood and bamboo branch item, bamboo and wood processing remaining material or straw are chosen as raw material；
Bamboo branch item or bamboo and wood processing remaining material or straw are ground into particle by 1-1；
1-2 particles stack ageing, and particle is placed in the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon by dry carbonization
Degree is 160-190 DEG C, 2-4 hours heating times, particle carbonization, and carbonizing degree is 5%-30%；
It is 0.5cm that 1-3, which selects sieve pore specification, the sieve of 0.5~1cm specifications, and particle is sieved, is graded stacking by thickness,
It weighed, glued, resin added is 25~35%；
Bamboo wood hacking is split the thin bamboo strip by 2-1, and drying to moisture content is 8~12%；
2-2 bamboos slight predrying after gluing；
2-3, which slights bamboo, is woven into bamboo reinforcement net；
Coarse particles are filled in bamboo reinforcement net areola by 3-1 assemblies, and disentegrated particles are covered in bamboo reinforcement is online, lower surface；
It is pressed into blank in advance under 3-2 room temperature；
4-1 preset backing plates on hot press, preset fixed width on backing plate determine slab；
Blank is put into fixed width, determines the space that slab surrounds by 4-2 hot pressing, and upper and lower surface lays finish coat, carries out hot pressing, hot pressing
Temperature is 100~160 DEG C, and pressure is 10~60Mpa, is pressed into composite board of small pieces of bamboo reinforcement.
2. the manufacturing method of composite board of small pieces of bamboo reinforcement according to claim 1, Preferable scheme is that the bamboo slights thickness
Degree is 0.5~4.0mm, and width is 0.5~2.5mm, track and column braiding at groined type bamboo reinforcement net, sizing grid 5 × 5~250 ×
250mm。
3. the manufacturing method of composite board of small pieces of bamboo reinforcement according to claim 2, it is characterised in that described group of blank process with
The sequence lay raw material of finish coat, bamboo mat or wood chip, particle, groined type bamboo reinforcement net, particle, bamboo mat or wood chip, finishing material.
4. the manufacturing method of composite board of small pieces of bamboo reinforcement according to claim 3, it is characterised in that in described group of blank process
Groined type bamboo reinforcement net one or more layers can be set.
5. the manufacturing method of composite board of small pieces of bamboo reinforcement according to claim 4, it is characterised in that the glue kind of the gluing
For one kind of modified phenolic glue or modified urea-formaldehyde glue, waterproofing agent is added in when gluing, and waterproofing agent dosage is 3~5%.