CN108503750A - 眼用镜片、人工晶状体及眼用镜片制作方法 - Google Patents
眼用镜片、人工晶状体及眼用镜片制作方法 Download PDFInfo
- Publication number
- CN108503750A CN108503750A CN201710099752.1A CN201710099752A CN108503750A CN 108503750 A CN108503750 A CN 108503750A CN 201710099752 A CN201710099752 A CN 201710099752A CN 108503750 A CN108503750 A CN 108503750A
- Authority
- CN
- China
- Prior art keywords
- hydrogel
- eye lens
- aggressiveness
- silicone
- pigment additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种眼用镜片，包括基体及混合于该基体中的色素添加剂，所述色素添加剂使所述基体整体呈红色。还提供一种人工水晶体及一种上述眼用镜片的制作方法。
Description
技术领域
本发明涉及一种眼用镜片、人工晶状体及眼用镜片制作方法。
背景技术
眼用镜片、人工晶状体因其美观、轻便、稳定等特点应用较为广泛。然而，有色眼用镜片、人工晶状体更容易被看到从而更容易被佩戴，即具有更好的能见度和对比度，从而有较强的可操作性，目前的有色眼用镜片、人工晶状体一般为蓝色或绿色，惟，蓝色或绿色的眼用镜片对缓解眼睛疲劳并无特别的效果。
发明内容
有鉴于此，有必要提供一种包含红色色素的眼用镜片、人工晶状体及眼用镜片制作方法，所述包含红色色素的眼用镜片、人工晶状体及眼用镜片制作方法不仅具有好的可操作性，还能缓解眼睛疲劳。
一种眼用镜片，包括基体及混合于该基体中的色素添加剂，所述色素添加剂使所述基体整体呈红色。
一种人工水晶体，包括基体及混合于该基体中的色素添加剂，所述色素添加剂使所述基体整体呈红色。
一种眼用镜片的制作方法，包括步骤：提供一水凝胶前聚体或硅水凝胶前聚体；提供一色素添加剂，将所述色素添加剂混合入所述水凝胶前聚体或硅水凝胶前聚体，得到一包含色素添加剂的混合物；在紫外光条件下使所述包含色素添加剂的混合物发生聚合反应，制得水凝胶或硅水凝胶；将水凝胶或硅水凝胶先后置于溶剂及去离子水中溶胀，得到眼用镜片；其中，所述色素添加剂使所述眼用镜片整体呈红色。
相比于现有技术，本技术方案提供的眼用镜片、人工晶状体、眼用镜片的制作方法，具有较好的能见度和对比度，从右有较强的可操作性，并且可以提高视觉深度、减少眼睛疲劳，还能使佩戴者的光敏、畏光等症状得到改善，并能使退行性视网膜疾病患者生活质量得到显著改善。
附图说明
无
主要元件符号说明
无
如下具体实施方式将进一步说明本发明。
具体实施方式
本发明较佳实施方式提供一种眼用镜片或人工晶状体(IOLs)，其包括基体以及混合于该基体中的色素添加剂，所述色素添加剂使所述基体整体呈红色。
本实施方式中，所述色素添加剂在所述眼用镜片或人工晶状体中的质量含量优选为0.004％至5％。
本实施方式中，所述色素添加剂选用通过美国食品药品管理局(FDA，Food andDrug Administration)认证的色素。
所述色素添加剂可以使所述基体整体呈现大红色、深红色、砖红色、棕红色或粉红色等，并不限于本案。
本实施方式中，所述色素添加剂至少包含一种红色色素，所述红色色素为FDA认证的红色色素，如C.I.(颜色指数，Color Index)活性红11，C.I.活性红180，或D&C(药品和化妆品，Drug and Cosmetics)红17号等。
在其他实施方式中，所述色素添加剂还可以包含FDA认证的其他颜色的色素，用于对红色色素的颜色进行调整，以得到所需的红色的眼用镜片或人工晶状体，如：为所述基体整体呈现砖红色，可使所述色素添加剂还包括一黄色色素，如C.I.活性黄15、C.I.活性黄86或D&C黄色10号。
所述眼用镜片可以为水凝胶镜片或硅水凝胶镜片。
在本实施方式中，当所述眼用镜片或人工晶状体对应为水凝胶镜片或水凝胶人工晶状体时，所述基体为水凝胶；当所述眼用镜片或人工晶状体对应为硅水凝胶镜片或硅水凝胶人工晶状体时，所述基体为硅水凝胶。
具体地，当所述基体为水凝胶时，所述基体由水凝胶前聚体在紫外光(UV光)的照射下发生聚合反应后形成，优选聚合反应的时间为10分钟至30分钟。所述水凝胶前聚体包括亲水性单体、光引发剂及交联剂。所述至少一种色素可以在所述水凝胶前聚体发生共聚前加入，在所述水凝胶前聚体发生共聚后，所述至少一种色素形成于所述基体的分子间隙，从而，使所述眼用镜片或人工晶状体整体呈现红色。
其中，所述亲水性单体优选为丙烯酸基(CR'H＝CRCOX)单体，R是H或CH3，R'是H，CH3或烷基(alkly)，X为O，N或亲水性基团；所述亲水性单体更优选为2-羟乙基甲基丙烯酸酯(HEMA)、N-，N-二甲基丙烯酰胺(DMA)、甲基丙烯酸(MAA)、N-乙烯基吡咯烷酮(NVP)、聚乙二醇甲基丙烯酸酯(PEGMA)及磺基甜菜碱甲基丙烯酸甲酯(SBMA)中的一种或几种；所述亲水性单体在所述水凝胶前聚体中的质量占比优选为75％至99.99％。所述交联剂优选为乙二醇二甲基丙烯酸酯(EGDMA)、三羟甲基丙烷三甲基丙烯酸酯(TMPTMA)、N，N'-亚甲基双(MBAA)中的一种或几种；所述交联剂在所述水凝胶前聚体中的质量占比优选为0.5％至23％。所述引发剂优选为Irgacure-1173(I1173，化工行业标准型号)；所述引发剂在所述水凝胶前聚体中的质量占比优选为0.01％至19％。
所述水凝胶前聚体还包括溶剂；所述溶剂优选为水、乙醇或己醇；所述溶剂在所述水凝胶前聚体中的质量占比优选为0％至48％。
当所述基体为硅水凝胶时，所述基体由硅水凝胶前聚体在紫外光(UV光)的照射下发生聚合反应后形成，优选聚合反应的时间为10分钟至30分钟。所述硅水凝胶前聚体包括亲水性单体、含硅单体、光引发剂及交联剂。所述至少一种色素可以在所述硅水凝胶前聚体发生共聚前加入，在所述硅水凝胶前聚体发生共聚后，所述至少一种色素形成于所述基体的分子间隙，从而，使所述眼用镜片或人工晶状体整体呈现红色。
其中，所述亲水性单体优选为丙烯酸基(CR'H＝CRCOX)单体，R是H或CH3，R'是H，CH3或烷基(alkly)，X为O，N或亲水性基团；所述亲水性单体更优选为2-羟乙基甲基丙烯酸酯(HEMA)、N-，N-二甲基丙烯酰胺(DMA)、甲基丙烯酸(MAA)、N-乙烯基吡咯烷酮(NVP)、聚乙二醇甲基丙烯酸酯(PEGMA)及磺基甜菜碱甲基丙烯酸甲酯(SBMA)中的一种或几种；所述含硅单体优选包括三羟甲基氨基甲烷(TRIS)、3-(三甲氧基甲硅烷基)丙基丙烯酸酯(MSMA，3-(trimethoxysilyl)propyl methacrylate)及聚二甲基硅氧烷(PDMS)中的一种或几种；其中，所述亲水性单体与所述含硅单体的总量在所述硅水凝胶前聚体中的质量占比优选为55％至99.95％。所述交联剂优选为乙二醇二甲基丙烯酸酯(EGDMA)、三羟甲基丙烷三甲基丙烯酸酯(TMPTMA)、N，N'-亚甲基双(MBAA)中的一种或几种；所述交联剂在所述硅水凝胶前聚体中的质量占比优选为0.1％至34％。所述引发剂优选为Irgacure-1173(I1173，化工行业标准型号)；所述引发剂在所述硅水凝胶前聚体中的质量占比优选为0.03％至18％。
所述硅水凝胶前聚体还包括溶剂；所述溶剂优选为水、乙醇或己醇。所述溶剂在所述硅水凝胶前聚体中的质量占比优选为1.5％至52.5％。
本技术方案还提供一种眼用镜片的制作方法，包括步骤：
S1，提供一上述的水凝胶前聚体或硅水凝胶前聚体，并将其混合，得到一混合物。
在本实施方式中，当所述眼用镜片或人工晶状体对应为水凝胶镜片或水凝胶人工晶状体时，所述基体为水凝胶；当所述眼用镜片或人工晶状体对应为硅水凝胶镜片或硅水凝胶人工晶状体时，所述基体为硅水凝胶。
具体地，当所述基体为水凝胶时，所述基体由水凝胶前聚体在紫外光的照射下发生聚合反应后形成，优选聚合反应的时间为10分钟至30分钟。所述水凝胶前聚体包括亲水性单体、光引发剂及交联剂。所述至少一种色素可以在所述水凝胶前聚体发生共聚前加入，在所述水凝胶前聚体发生共聚后，所述至少一种色素形成于所述基体的分子间隙，从而，使所述眼用镜片或人工晶状体整体呈现红色。
其中，所述亲水性单体优选为丙烯酸基单体，R是H或CH3，R'是H，CH3或烷基，X为O，N或亲水性基团；所述亲水性单体更优选为HEMA、DMA、MAA、NVP、PEGMA及SBMA中的一种或几种；所述亲水性单体在所述水凝胶前聚体中的质量占比优选为75％至99.99％。所述交联剂优选为EGDMA、TMPTMA、MBAA中的一种或几种；所述交联剂在所述水凝胶前聚体中的质量占比优选为0.5％至23％。所述引发剂优选为I1173；所述引发剂在所述水凝胶前聚体中的质量占比优选为0.01％至19％。
所述水凝胶前聚体还包括溶剂；所述溶剂优选为水、乙醇或己醇；所述溶剂在所述水凝胶前聚体中的质量占比优选为0％至48％。
当所述基体为硅水凝胶时，所述基体由硅水凝胶前聚体在紫外光的照射下发生聚合反应后形成，优选聚合反应的时间为10分钟至30分钟。所述硅水凝胶前聚体包括亲水性单体、含硅单体、光引发剂及交联剂。所述至少一种色素可以在所述硅水凝胶前聚体发生共聚前加入，在所述硅水凝胶前聚体发生共聚后，所述至少一种色素形成于所述基体的分子间隙，从而，使所述眼用镜片或人工晶状体整体呈现红色。
其中，所述亲水性单体优选为丙烯酸基(CR'H＝CRCOX)单体，R是H或CH3，R'是H，CH3或烷基(alkly)，X为O，N或亲水性基团；所述亲水性单体更优选为HEMA、DMA、MAA、NVP、PEGMA及SBMA中的一种或几种；所述含硅单体优选包括TRIS、MSMA或PDMS中的一种或几种；其中，所述亲水性单体与所述含硅单体的总量在所述硅水凝胶前聚体中的质量占比优选为55％至99.95％。所述交联剂优选为EGDMA、TMPTMA、MBAA中的一种或几种；所述交联剂在所述硅水凝胶前聚体中的质量占比优选为0.01％至34％。所述引发剂优选为I1173；所述引发剂在所述硅水凝胶前聚体中的质量占比优选为0.03％至18％。
所述硅水凝胶前聚体还包括溶剂；所述溶剂优选为水、乙醇或己醇。所述溶剂在所述硅水凝胶前聚体中的质量占比优选为1.5％至52.5％。
S2，将一色素添加剂添加至所述混合物中。
本实施方式中，所述色素添加剂选用通过FDA认证的色素。
所述色素添加剂可以使所述基体整体呈现大红色、深红色、砖红色、棕红色或粉红色等，并不限于本案。
本实施方式中，所述色素添加剂至少包含一种红色色素，所述红色色素为FDA认证的红色色素，如C.I.活性红11，C.I.活性红180，或D&C红17号等。
在其他实施方式中，所述色素添加剂还可以包含FDA认证的其他颜色的色素，用于对红色色素的颜色进行调整，以得到所需的红色的眼用镜片或人工晶状体，如：为所述基体整体呈现砖红色，可使所述色素添加剂还包括一黄色色素，如C.I.活性黄15、C.I.活性黄86或D&C黄色10号。
S3，将添加色素添加剂后的所述混合物倒入至一模具中，在紫外光条件下使所述混合物发生聚合反应，制得水凝胶或硅水凝胶，其中，聚合反应的时间为10分钟至30分钟；
S4，将水凝胶或硅水凝胶先后置于溶剂及去离子水中溶胀，得到眼用镜片或人工水晶体。
本实施方式中，所述溶剂为质量分数为50％左右的乙醇溶液。
本实施方式中，所述色素添加剂在所述眼用镜片或人工晶状体中的质量含量优选为0.004％至5％。
下面通过实施例来对本发明进行具体说明。
实施例1
眼用镜片的制备方法包括：提供HEMA、NVP、TRIS、I1173、MSMA、EGDMA、乙醇及C.I.活性红11并将其混合均匀，得到混合溶液；将所述混合溶液置于隐形镜片制作模具中并在紫外光(365纳米左右)下照射10分钟，使混合物发生聚合反应形成硅水凝胶镜片；该硅水凝胶镜片先后经50％的乙醇及去离子水水化后即为含色素添加剂的呈红色的眼用镜片。
其中，所述混合溶液中HEMA的质量百分含量为9.9％，NVP的质量百分含量为23％，TRIS的质量百分含量为30％，I1173的质量百分含量为0.66％，MSMA的质量百分含量为2.6％，EGDMA的质量百分含量为0.66％，C.I.活性红11的质量百分含量为0.03％，乙醇的质量百分含量为33％。
实施例2
眼用镜片的制备方法包括：提供HEMA、NVP、MAA、I1173、EGDMA、乙醇并将其混合均匀，得到凝胶前聚体；及提供C.I.活性红11及C.I.活性黄15，并将其混合成砖色的色素添加剂；将所述色素添加剂加入到所述凝胶前聚体中得到一混合溶液；将所述混合溶液置于隐形镜片制作模具中并在紫外光(365纳米左右)下照射15分钟，使混合物发生聚合反应形成水凝胶镜片；该水凝胶镜片先后经50％的乙醇及去离子水水化后即为含色素添加剂的呈砖红色的眼用镜片。
其中，所述混合溶液中，HEMA的质量百分含量为63.07％，NVP的质量百分含量为10.77％，MAA的质量百分含量为2.5％，I1173的质量百分含量为0.03％，EGDMA的质量百分含量为0.23％，C.I.活性红11与C.I.活性黄15合计的质量百分含量为0.32％，乙醇的质量百分含量为23.08％。
实施例3
由实施例1的方法得到的眼用镜片，其中，C.I.活性红11在形成的眼用镜片中的质量百分含量为0.019％。
实施例4
由实施例2的方法得到的眼用镜片，其中，色素添加剂包括C.I.活性红11与C.I.活性黄15，色素添加剂在形成的眼用镜片中的质量百分含量为0.28％。
经验证，本技术方案提供的眼用镜片、人工晶状体、眼用镜片的制作方法，具有较好的能见度和对比度，从右有较强的可操作性，并且可以提高视觉深度、减少眼睛疲劳，还能使佩戴者的光敏、畏光等症状得到改善，并能使退行性视网膜疾病患者生活质量得到显著改善。
可以理解的是，对于本领域的普通技术人员来说，可以根据本发明的技术构思做出其它各种相应的改变与变形，而所有这些改变与变形都应属于本发明权利要求的保护范围。
Claims (20)
1.一种眼用镜片，包括基体及混合于该基体中的色素添加剂，所述色素添加剂使所述基体整体呈红色。
2.如权利要求1所述的眼用镜片，其特征在于，所述色素添加剂在所述眼用镜片中的质量含量为0.004％至5％。
3.如权利要求1所述的眼用镜片，其特征在于，所述色素添加剂至少包括一红色色素。
4.如权利要求1项所述的眼用镜片，其特征在于，所述红色色素为C.I.活性红11，C.I.活性红180，或D&C红17号。
5.如权利要求3所述的眼用镜片，其特征在于，所述色素添加剂还包括一黄色色素。
6.如权利要求5所述的眼用镜片，其特征在于，所述黄色色素为C.I.活性黄15、C.I.活性黄86或D&C黄色10号。
7.如权利要求1所述的眼用镜片，其特征在于，所述基体为水凝胶，所述基体由水凝胶前聚体在紫外光的照射下发生聚合反应后形成，所述水凝胶前聚体包括亲水性单体、光引发剂及交联剂；所述亲水性单体为丙烯酸基单体，R是H或CH3，R'是H，CH3或烷基，X为O，N或亲水性基团。
8.如权利要求7所述的眼用镜片，其特征在于，所述亲水性单体选自2-羟乙基甲基丙烯酸酯、N-，N-二甲基丙烯酰胺、甲基丙烯酸、N-乙烯基吡咯烷酮、聚乙二醇甲基丙烯酸酯及磺基甜菜碱甲基丙烯酸甲酯中的一种或几种。
9.如权利要求7所述的眼用镜片，其特征在于，所述亲水性单体在所述水凝胶前聚体中的质量占比为75％至99.99％。
10.如权利要求7所述的眼用镜片，其特征在于，所述交联剂选自乙二醇二甲基丙烯酸酯、三羟甲基丙烷三甲基丙烯酸酯、N，N'-亚甲基双中的一种或几种，所述交联剂在所述水凝胶前聚体或所述硅水凝胶前聚体中的质量占比为0.5％至23％。
11.如权利要求1所述的眼用镜片，其特征在于，所述基体为硅水凝胶，所述基体由硅水凝胶前聚体在紫外光的照射下发生聚合反应后形成，所述硅水凝胶前聚体包括亲水性单体、含硅单体、光引发剂及交联剂；所述亲水性单体为丙烯酸基单体，R是H或CH3，R'是H，CH3或烷基，X为O，N或亲水性基团；所述含硅单体选自三羟甲基氨基甲烷、3-(三甲氧基甲硅烷基)丙基丙烯酸酯、聚二甲基硅氧烷中的一种或几种。
12.如权利要求11所述的眼用镜片，其特征在于，所述亲水性单体选自2-羟乙基甲基丙烯酸酯、N-，N-二甲基丙烯酰胺、甲基丙烯酸、N-乙烯基吡咯烷酮、聚乙二醇甲基丙烯酸酯及磺基甜菜碱甲基丙烯酸甲酯中的一种或几种。
13.如权利要求11所述的眼用镜片，其特征在于，所述亲水性单体与所述含硅单体的总量在所述硅水凝胶前聚体中的质量占比为55％至99.95％。
14.如权利要求11所述的眼用镜片，其特征在于，所述交联剂选自乙二醇二甲基丙烯酸酯、三羟甲基丙烷三甲基丙烯酸酯、N，N'-亚甲基双中的一种或几种，所述交联剂在所述水凝胶前聚体或所述硅水凝胶前聚体中的质量占比为0.1％至34％。
15.一种人工水晶体，包括基体及混合于该基体中的色素添加剂，所述色素添加剂使所述基体整体呈红色。
16.如权利要求15所述的人工水晶体，其特征在于，所述色素添加剂在所述人工水晶体中的质量含量为0.004％至5％。
17.如权利要求15所述的人工水晶体，其特征在于，所述基体为水凝胶或硅水凝胶。
18.一种眼用镜片的制作方法，包括步骤：提供一水凝胶前聚体或硅水凝胶前聚体；提供一色素添加剂，将所述色素添加剂混合入所述水凝胶前聚体或硅水凝胶前聚体，得到一包含色素添加剂的混合物；在紫外光条件下使所述包含色素添加剂的混合物发生聚合反应，制得水凝胶或硅水凝胶；将水凝胶或硅水凝胶先后置于溶剂及去离子水中溶胀，得到眼用镜片；其中，所述色素添加剂使所述眼用镜片整体呈红色。
19.如权利要求18所述的眼用镜片的制作方法，其特征在于，所述色素添加剂在所述眼用镜片中的质量含量为0.004％至5％。
20.如权利要求18所述的眼用镜片的制作方法，其特征在于，所述聚合反应的时间为10至30分钟。