CN108218237A - A kind of preparation method of devitrified glass - Google Patents
A kind of preparation method of devitrified glass Download PDFInfo
- Publication number
- CN108218237A CN108218237A CN201810081806.6A CN201810081806A CN108218237A CN 108218237 A CN108218237 A CN 108218237A CN 201810081806 A CN201810081806 A CN 201810081806A CN 108218237 A CN108218237 A CN 108218237A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- glass
- preparation
- tio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of preparation method of devitrified glass, raw material includes following component according to weight percent：Li216 20 parts by weight of O, Al2O318 22 parts by weight, SiO250 60 parts by weight, B2O338 parts by weight, 26 parts by weight of MgO, TiO226 parts by weight, Ce2O31 parts by weight, 1 parts by weight of 1 parts by weight of BaF2 and AlF3；Wherein TiO2As Nucleating Agent；The preparation method includes the following steps：1）Glass raw material is fitted into crucible and is ground uniformly, oxygen, high temperature melting are passed through in Muffle furnace, heat preservation treats that glass metal melting is uniform, and taking-up is cast in stainless-steel sheet, pours into glass blocks；2）Glass blocks is put into annealing furnace and is kept the temperature, is made annealing treatment, carries out rib and crystallization at a certain temperature.The present invention improves the chemical stability of glass, good in optical property, high refractive index by rationally adjusting glass formula.
Description
Technical field
The present invention relates to a kind of preparation methods of devitrified glass, belong to optical element field.
Background technology
Devitrified glass refers to add in certain nucleation substances in glass, passes through the hands such as heat treatment, light irradiation or chemical treatment
Section, is equably precipitated a large amount of tiny crystals in glass, forms the multiphase complex of fine and close crystallite phase and glass phase.Pass through
Number of species, size of crystallite etc. is controlled, transparent glass-ceramics can be obtained, the devitrified glass that the coefficient of expansion is zero, table
Surface strengthening devitrified glass, different color or machinable glass ceramics.
Existing devitrified glass, stability and optical property are not good enough, it is impossible to meet the needs of users.
Invention content
The purpose of the present invention is to overcome the deficiencies of the prior art, provides a kind of preparation method of devitrified glass.
The preparation method of the devitrified glass of the present invention, raw material include following component according to weight percent：Li2O 16-20
Parts by weight, Al2O318-22 parts by weight, SiO250-60 parts by weight, B2O33-8 parts by weight, MgO 2-6 parts by weight, TiO2 2-
6 parts by weight, Ce2O31 parts by weight, 1 parts by weight of 1 parts by weight of BaF2 and AlF3；Wherein TiO2As Nucleating Agent；
The preparation method includes the following steps：
1）Glass raw material is fitted into crucible and is ground uniformly, oxygen, high temperature melting are passed through in Muffle furnace, glass metal is treated in heat preservation
Melting is uniform, and taking-up is cast in stainless-steel sheet, pours into glass blocks；
2）Glass blocks is put into annealing furnace and is kept the temperature, is made annealing treatment, carries out rib and crystallization at a certain temperature.
Preferably,
In the preparation method of the devitrified glass, raw material includes following component according to weight percent：Li218 parts by weight of O,
Al2O320 parts by weight, SiO255 parts by weight, B2O35 parts by weight, 4 parts by weight of MgO, TiO24 parts by weight, Ce2O31 weight
Part, 1 parts by weight of 1 parts by weight of BaF2 and AlF3.
The present invention improves the chemical stability of glass, good in optical property, refractive index by rationally adjusting glass formula
It is high.
Specific embodiment
Embodiment 1
The preparation method of the devitrified glass of the present invention, raw material include following component according to weight percent：Li216 parts by weight of O,
Al2O318 parts by weight, SiO250 parts by weight, B2O33 parts by weight, 2 parts by weight of MgO, TiO24 parts by weight, Ce2O31 weight
Part, 1 parts by weight of 1 parts by weight of BaF2 and AlF3；Wherein TiO2As Nucleating Agent；
The preparation method includes the following steps：
1）Glass raw material is fitted into crucible and is ground uniformly, oxygen, high temperature melting are passed through in Muffle furnace, glass metal is treated in heat preservation
Melting is uniform, and taking-up is cast in stainless-steel sheet, pours into glass blocks；
2）Glass blocks is put into annealing furnace and is kept the temperature, is made annealing treatment, carries out rib and crystallization at a certain temperature.
Embodiment 2
The preparation method of the devitrified glass of the present invention, raw material include following component according to weight percent：Li220 parts by weight of O,
Al2O322 parts by weight, SiO260 parts by weight, B2O38 parts by weight, 6 parts by weight of MgO, TiO22 parts by weight, Ce2O31 weight
Part, 1 parts by weight of 1 parts by weight of BaF2 and AlF3；Wherein TiO2As Nucleating Agent；
The preparation method is the same as that of Example 1 for embodiment 2.
Embodiment 3
The preparation method of the devitrified glass of the present invention, raw material include following component according to weight percent：Li218 parts by weight of O,
Al2O320 parts by weight, SiO255 parts by weight, B2O35 parts by weight, 4 parts by weight of MgO, TiO26 parts by weight, Ce2O31 weight
Part, 1 parts by weight of 1 parts by weight of BaF2 and AlF3；Wherein TiO2As Nucleating Agent；
The preparation method is the same as that of Example 1 for embodiment 3.
Claims (2)
1. a kind of preparation method of devitrified glass, which is characterized in that raw material includes following component according to weight percent：Li2O
16-20 parts by weight, Al2O318-22 parts by weight, SiO250-60 parts by weight, B2O33-8 parts by weight, MgO 2-6 parts by weight,
TiO22-6 parts by weight, Ce2O31 parts by weight, 1 parts by weight of 1 parts by weight of BaF2 and AlF3；Wherein TiO2As Nucleating Agent；
The preparation method includes the following steps：
1）Glass raw material is fitted into crucible and is ground uniformly, oxygen, high temperature melting are passed through in Muffle furnace, glass metal is treated in heat preservation
Melting is uniform, and taking-up is cast in stainless-steel sheet, pours into glass blocks；
2）Glass blocks is put into annealing furnace and is kept the temperature, is made annealing treatment, carries out rib and crystallization at a certain temperature.
2. the preparation method of devitrified glass according to claim 1, which is characterized in that raw material includes according to weight percent
Following component：Li218 parts by weight of O, Al2O320 parts by weight, SiO255 parts by weight, B2O35 parts by weight, 4 parts by weight of MgO,
TiO24 parts by weight, Ce2O31 parts by weight, 1 parts by weight of 1 parts by weight of BaF2 and AlF3.