CN108047886A - A water-based transparent primer for loose putty - Google Patents
A water-based transparent primer for loose putty Download PDFInfo
- Publication number
- CN108047886A CN108047886A CN201711420891.6A CN201711420891A CN108047886A CN 108047886 A CN108047886 A CN 108047886A CN 201711420891 A CN201711420891 A CN 201711420891A CN 108047886 A CN108047886 A CN 108047886A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- putty
- glue
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
技术领域technical field
本发明涉及装修油漆技术领域，具体为一种疏松腻子用水性透明底漆。The invention relates to the technical field of decoration paints, in particular to a water-based transparent primer for loose putty.
背景技术Background technique
装修又称装潢或装饰。是指在一定区域和范围内进行的，包括水电施工、墙体、地板、天花板、景观等所实现的，依据一定设计理念和美观规则形成的一整套施工方案和设计方案。Decoration is also called decoration or decoration. It refers to a complete set of construction schemes and design schemes that are carried out in a certain area and range, including hydropower construction, walls, floors, ceilings, landscapes, etc., and formed according to certain design concepts and aesthetic rules.
小到家具摆放和门的朝向，大到房间配饰和灯具的定制处理，都是装修的体现。装修和装饰不同，装饰是对生活用品或生活环境进行艺术加工的手法。加强审美效果，并提高其功能、经济价值和社会效益，并以环保为设计理念。完美的装饰应与客体的功能紧密结合，适应制作工艺，发挥物质材料的性能，并具有良好的艺术效果。From furniture placement and door orientation to custom-made room accessories and lamps, they are all manifestations of decoration. Decoration is different from decoration. Decoration is a means of artistic processing of daily necessities or living environment. Strengthen the aesthetic effect, and improve its function, economic value and social benefits, and take environmental protection as the design concept. Perfect decoration should be closely combined with the function of the object, adapt to the production process, give full play to the performance of material materials, and have a good artistic effect.
现代装修过程中开发商为追求最大利益，油漆工为追求最佳打磨性，腻子中的胶体添加量严重不足，有的甚至不加，腻子胶质不足，最直接的表现就是腻子层疏松，表面粉化，涂刷面漆时耗漆量大，流平性差，成膜后表面粗糙，难以形成致密的漆膜，用户搬新居后不久，墙面即会出现漆膜起皮、起泡、脱落、开裂等现象。In the process of modern decoration, in order to pursue the maximum benefit and the painters to pursue the best sandability, the amount of colloid added in the putty is seriously insufficient, and some even do not add it. The most direct manifestation of the lack of putty colloid is that the putty layer is loose and the surface Chalking, a large amount of paint is consumed when painting the topcoat, poor leveling, rough surface after film formation, and it is difficult to form a dense paint film. Soon after the user moves to a new house, the paint film will appear peeling, blistering, and peeling off on the wall , cracking and so on.
发明内容Contents of the invention
本发明的目的在于提供一种疏松腻子用水性透明底漆，以解决上述背景技术中提出的现代装修过程中开发商为追求最大利益，油漆工为追求最佳打磨性，腻子中的胶体添加量严重不足，有的甚至不加，腻子胶质不足，最直接的表现就是腻子层疏松，表面粉化，涂刷面漆时耗漆量大，流平性差，成膜后表面粗糙，难以形成致密的漆膜，用户搬新居后不久，墙面即会出现漆膜起皮、起泡、脱落、开裂等现象的问题。The purpose of the present invention is to provide a water-based transparent primer for loose putty, to solve the problem that in the modern decoration process proposed in the above-mentioned background technology, the developer is pursuing the maximum benefit, the painter is pursuing the best sandability, the amount of colloid added in the putty Seriously insufficient, some even do not add, lack of putty colloid, the most direct manifestation is that the putty layer is loose, the surface is pulverized, the paint consumption is large when painting the topcoat, the leveling property is poor, the surface is rough after film formation, and it is difficult to form dense Shortly after the user moves to a new residence, problems such as peeling, blistering, peeling, and cracking of the paint film will appear on the wall.
为实现上述目的，本发明提供如下技术方案：一种疏松腻子用水性透明底漆，该疏松腻子用水性透明底漆的原材料组成包括A料和B料，所述A料包括：水性乳液、防腐剂和消泡剂，所述B料包括：渗透胶液和防水胶，所述水性乳液、渗透胶液、防水胶、防腐剂和消泡剂按照质量比重分别为：水性乳液(70-90)份、渗透胶液(3-10)份、防水胶(3-10)份、防腐剂(2-5)份、消泡剂(2-5)份。In order to achieve the above object, the present invention provides the following technical scheme: a water-based transparent primer for loose putty, the raw material composition of the water-based transparent primer for loose putty includes material A and material B, and the material A includes: water-based emulsion, anti-corrosion agent and defoamer, the B material includes: penetrating glue and waterproof glue, and the water-based emulsion, penetrating glue, waterproof glue, preservative and defoamer are respectively according to mass proportion: water-based emulsion (70-90) Parts, penetrating glue (3-10) parts, waterproof glue (3-10) parts, preservative (2-5) parts, defoamer (2-5) parts.
优选的，所述水性乳液为水性环氧树脂乳液与水性丙烯酸乳液的混合液。Preferably, the aqueous emulsion is a mixture of aqueous epoxy resin emulsion and aqueous acrylic emulsion.
优选的，所述水性环氧树脂乳液与水性丙烯酸乳液的质量占比为1.2：0.8。Preferably, the mass ratio of the water-based epoxy resin emulsion to the water-based acrylic emulsion is 1.2:0.8.
优选的，所述渗透胶液为烷基苯磺酸钠与烷基硫酸酯钠的混合液，所述烷基苯磺酸钠与烷基硫酸酯钠的质量所占比重相同。Preferably, the osmotic glue is a mixture of sodium alkylbenzene sulfonate and sodium alkyl sulfate, and the mass proportions of sodium alkylbenzene sulfonate and sodium alkyl sulfate are the same.
优选的，所述防水胶为聚氨酯胶。Preferably, the waterproof glue is polyurethane glue.
优选的，所述防腐剂为苯甲酸、苯甲酸钠和山梨酸的混合液剂。Preferably, the preservative is a mixed solution of benzoic acid, sodium benzoate and sorbic acid.
优选的，所述消泡剂为聚二甲基硅氧烷和乙二醇硅氧烷的混合产物，所述二甲基硅氧烷和乙二醇硅氧烷的所占质量比重为1：2。Preferably, the defoamer is a mixed product of polydimethylsiloxane and ethylene glycol siloxane, and the mass proportion of dimethyl siloxane and ethylene glycol siloxane is 1: 2.
与现有技术相比，本发明的有益效果是：该疏松腻子用水性透明底漆，使用后，表面防水性能较好，通过渗透胶液的加入，使得底漆能够更好的深入腻子层中，从而填充其中的空缺部分，从根本上解决腻子脱落的问题，使用环保材料，对室内空气的污染相对较小。Compared with the prior art, the beneficial effect of the present invention is: the water-based transparent primer for the loose putty has better surface waterproof performance after use, and the primer can be better penetrated into the putty layer by adding penetrating glue , so as to fill the vacant part of it, fundamentally solve the problem of putty falling off, use environmentally friendly materials, and cause relatively little pollution to indoor air.
附图说明Description of drawings
图1为本发明实施例一原料配比图；Fig. 1 is a raw material ratio diagram of embodiment one of the present invention;
图2为本发明实施例二原料配比图；Fig. 2 is the raw material ratio figure of embodiment two of the present invention;
图3为本发明实施例三原料配比图。Fig. 3 is the raw material ratio diagram of the third embodiment of the present invention.
具体实施方式Detailed ways
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.
本发明提供一种技术方案：一种疏松腻子用水性透明底漆，该疏松腻子用水性透明底漆的原材料组成包括A料和B料，所述A料包括：水性乳液、防腐剂和消泡剂，所述B料包括：渗透胶液和防水胶，所述水性乳液、渗透胶液、防水胶、防腐剂和消泡剂按照质量比重分别为：水性乳液(70-90)份、渗透胶液(3-10)份、防水胶(3-10)份、防腐剂(2-5)份、消泡剂(2-5)份。The invention provides a technical solution: a water-based transparent primer for loose putty, the raw material composition of the water-based transparent primer for loose putty includes material A and material B, and the material A includes: water-based emulsion, preservative and defoaming agent, the B material includes: osmotic glue and waterproof glue, and the water-based emulsion, osmotic glue, waterproof glue, preservative and defoamer are respectively according to mass proportion: aqueous emulsion (70-90) parts, osmotic glue Liquid (3-10) parts, waterproof glue (3-10) parts, preservative (2-5) parts, defoamer (2-5) parts.
其中，所述水性乳液为水性环氧树脂乳液与水性丙烯酸乳液的混合液，所述水性环氧树脂乳液与水性丙烯酸乳液的质量占比为1.2：0.8，所述渗透胶液为烷基苯磺酸钠与烷基硫酸酯钠的混合液，所述烷基苯磺酸钠与烷基硫酸酯钠的质量所占比重相同，所述防水胶为聚氨酯胶，所述防腐剂为苯甲酸、苯甲酸钠和山梨酸的混合液剂，所述消泡剂为聚二甲基硅氧烷和乙二醇硅氧烷的混合产物，所述二甲基硅氧烷和乙二醇硅氧烷的所占质量比重为1：2。Wherein, the water-based emulsion is a mixture of water-based epoxy resin emulsion and water-based acrylic emulsion, the mass ratio of the water-based epoxy resin emulsion and water-based acrylic emulsion is 1.2:0.8, and the penetrating glue is alkyl benzene sulfonate The mixed solution of sodium sulfonate and sodium alkylsulfate, the mass proportion of sodium alkylbenzenesulfonate and sodium alkylsulfate is the same, the waterproof glue is polyurethane glue, and the preservative is benzoic acid, benzene A mixed solution of sodium formate and sorbic acid, the antifoaming agent is a mixed product of polydimethylsiloxane and ethylene glycol siloxane, the dimethyl siloxane and ethylene glycol siloxane The mass ratio is 1:2.
实施例一Embodiment one
(如图1)原材料按照质量比重分别为：水性乳液70份、渗透胶液10份、防水胶10份、防腐剂5份、消泡剂5份。(As shown in Figure 1) The raw materials are: 70 parts of water-based emulsion, 10 parts of penetrating glue, 10 parts of waterproof glue, 5 parts of preservative, and 5 parts of defoaming agent according to the mass proportion.
本实施方案的胶液占比较高、粘性较大，适用于腻子膏较为松散的墙体，能够很好的填充腻子膏疏松的空隙部分。The glue in this embodiment has a relatively high proportion and high viscosity, and is suitable for walls with loose putty paste, and can well fill the loose gaps of the putty paste.
实施例二Embodiment two
(如图2)原材料按照质量比重分别为：水性乳液80份、渗透胶液6.5份、防水胶6.5份、防腐剂3.5份、消泡剂3.5份。(As shown in Figure 2) The raw materials are: 80 parts of water-based emulsion, 6.5 parts of penetrating glue, 6.5 parts of waterproof glue, 3.5 parts of preservative, and 3.5 parts of defoaming agent according to the mass proportion.
本实施方案的胶液与水性乳液的比重适中，既需要粘接腻子层，又需要提高底漆的表面效果，适用于腻子膏较光滑度和紧密程度一般的墙体。The specific gravity of the glue solution and the water-based emulsion in this embodiment is moderate, and it is necessary to bond the putty layer and improve the surface effect of the primer. It is suitable for walls with average smoothness and compactness of the putty paste.
实施例三Embodiment three
(如图3)原材料按照质量比重分别为：水性乳液90份、渗透胶液3份、防水胶3份、防腐剂2份、消泡剂2份。(As shown in Figure 3) The raw materials are: 90 parts of water-based emulsion, 3 parts of penetrating glue, 3 parts of waterproof glue, 2 parts of preservative, and 2 parts of defoaming agent according to the mass proportion.
本实施方案的胶液所占比重相对较低，使得底漆的外漆面质量较高，适用于腻子膏较为紧实的墙体。The proportion of glue in this embodiment is relatively low, so that the quality of the outer paint surface of the primer is high, and it is suitable for walls with relatively tight putty paste.
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。Although the embodiments of the present invention have been shown and described, those skilled in the art can understand that various changes, modifications and substitutions can be made to these embodiments without departing from the principle and spirit of the present invention. and modifications, the scope of the invention is defined by the appended claims and their equivalents.
Claims (7)