CN107927921B - Magnetic therapy underwear - Google Patents
Magnetic therapy underwear Download PDFInfo
- Publication number
- CN107927921B CN107927921B CN201711477134.2A CN201711477134A CN107927921B CN 107927921 B CN107927921 B CN 107927921B CN 201711477134 A CN201711477134 A CN 201711477134A CN 107927921 B CN107927921 B CN 107927921B
- Authority
- CN
- China
- Prior art keywords
- weight
- fabric
- parts
- stirring
- magnetic therapy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a magnetic therapy underwear, wherein magnets are sewn at positions of human acupuncture points corresponding to the magnetic therapy underwear. The magnetic therapy underwear of the invention can utilize a magnetic field with certain intensity to act on the acupuncture points of the human body to carry out magnetic therapy health care and disease treatment, effectively absorb and discharge sweat after the wearer sweats during sports, keep the skin of the wearer dry and comfortable and prevent the wearer from suffering from diseases, and has good antibacterial, quick-drying, antistatic and washing resistance properties and good comprehensive performance. Can meet the requirements of people on wearing comfort, functionality and practicability, and has good market prospect, economic benefit and social benefit.
Description
Technical Field
The invention relates to a magnetic therapy underwear.
Background
The magnetic therapy is also called magnetic point therapy or magnetic field therapy. As the name suggests, magnetic therapy is to use a magnetic field with a certain intensity to act on certain parts of a human body to treat diseases. As early as more than 2000 years ago, ancient workers in China used magnetism to treat diseases. In the spring and autumn warring state, ancient famous medical magpie of China has been tried for magnet therapy; the characteristics of magnetite are recorded in the book of Shen nong Ben Cao Jing in the early stage of West Han dynasty: can be used for treating pain, arthralgia due to pungent and cold taste of Magnetitum, rheumatism, and arthralgia. There are many other descriptions that follow, and magnetite is used as a part of decoction or patent medicine. Until Ming Dynasty Li Shizhen, Magnetitum powder and various ointments are mixed to make into topical medicine. The proved recipe for treating nerve deafness and tinnitus by using magnetite is recommended by people in Qing Dynasty. In addition, there is a record in the medical book "ge zhi jing yuan": the people who benefit sleep, like the magnet, are used as the basin pillow, and the pillow is used for keeping the people away from dizziness and keeping the people constant, so that the health care effect is achieved.
Tianchi acupoint:
tianchi acupoint is located in the fourth intercostal space of the chest, 1 cun lateral to the nipple. On the other hand, "two cun behind the breast" in the same body and cun as the latter "(Wang Bing from Huang Di Nei Jing Su Wen & Qi Fu Lun); "one inch after breast, the fifth part below it" is an integration of acupuncture and moxibustion.
Tianchi acupoint significance: the high-temperature water vapor transported outside the pericardium is condensed into water passing through the ground and is transported downwards along the channels. Characteristics of qi and blood: the qi and blood substance is high-temperature water vapor in the upper part of the body. The operation rule is as follows: the heat-dissipating cold descending from the ground circulates downward through the pericardium. Specificity: the point of intersection between hand jueyin and foot shaoyang. The efficacy and the effect are as follows: the Tianchi point has the functions of regulating qi, relieving chest stuffiness, clearing heat, dissipating stagnation, promoting blood circulation, removing blood stasis, relieving chest stuffiness and regulating qi.
Tianchi acupoint is very important for modern women, especially for women living in large cities. Tianchi acupoint is the first acupoint of the pericardium channel, one inch above the nipple, and between the fifth rib, which is also the high-lying region of breast cancer, and deep qi and blood obstruction is one of the causes of cancer, and Tianchi acupoint is often massaged to dredge local qi and blood, so that self-kneading and massaging the Tianchi acupoint can prevent breast cancer.
The pressure of life of the women in the large city is large and many, the women are more likely to suffer from breast cancer, the incidence of the breast cancer is generally in great relation with the damage of bad emotion to go deep into the heart, the Tianchi point is a happy point of the women, the heart and the chest of the women can be widened by frequently rubbing the point, the qi is not easy to generate, the people can live long without generating the qi, and the breast cancer can be prevented because the bad emotion can be relieved by frequently rubbing the point. It is better to perform an-rou on this acupoint in combination with an-rou on Taichong acupoint, Jianjing acupoint and Qimen acupoint.
Tianchi point is mainly used for treating vexation, fullness in chest, hypochondriac pain, scrofula, swelling and pain in armpit, etc.; circulatory diseases: angina pectoris, epicardial inflammation; gynecological system diseases: mastitis, insufficient milk secretion; diseases of the surgical system: lymphoid tuberculosis, axillary lymphadenitis; and (3) the other: intercostal neuralgia, cerebral congestion, etc.
The edible sinus acupoint:
the food sinus is subordinate to the spleen meridian of foot taiyin. In the 5 th intercostal space, the anterior serratus muscle, there are intercostal medial and lateral muscles in the deep layer; there are thoracic lateral artery and vein; thoracic abdominal wall artery and vein; the 5 th intercostal nerve lateral cutaneous branch is distributed. It is commonly used to treat stomach qi failing to descend.
And (4) feeding the antrum. Food and stomach are affected by five cereals, spleen and earth. The sinuses, orifices and uterus. The point name means that water flows through the spleen meridian and falls into the spleen in the triple energizer. The substance in this acupoint is the water of the local meridians from the abdominal sorrow, and there are more spleen-earth substances which flow with the water of the local meridians, but the gaps in the local acupoints are connected with the spleen, and the spleen-earth substances return to the spleen with the flowing water of the local meridians, so the name is.
The function and the effect are as follows: the spleen is returned to spleen via qi and blood on body surface.
The main treatment is as follows: 1. distending pain in the chest and hypochondrium; 2. syndrome of stomach-qi failing to descend, such as belching, regurgitation, abdominal distention, etc.; 3. edema.
Breast root acupoints:
the Rugen acupoint is most likely to be various gynecological diseases for female friends in modern life, and is common for many female friends, and the Rugen acupoint can help women to solve gynecological diseases, so that the condition of the Rugen acupoint is
The breast root part, as the name implies, is the position of the heart below the breast and to the left of the breast root acupoint, and after hitting the heart, the breast root part can impact the heart and even cause shock.
Firstly, the points, namely the breast root points, are found right below the chest, the breast root points can be found along the lower part of the front surface of the breast by the thumbs of the two hands, then the breast root points on the two sides are pressed, but the force is not too strong, the deep breathing can be realized by matching the pressing frequency, the best pressing is realized before the sleep every night, the pressing frequency is about 20 times, and the excessive pressing is not suitable.
Since the breast root points have a plurality of advantages and can be used for health care through massaging the breast root points, the breast root points are frequently massaged, which is known by a plurality of people, and the breast root points are really beneficial, the breast can be enlarged firstly, the regrowth and the development of the breast can be stimulated through pressing the breast root points, and the long-term massage has obvious effect. Secondly, the breast distending pain can be relieved, the breast distending pain condition of women in the lactation period is often caused, the breast distending pain can be relieved by massaging the breast root acupuncture points, the breast hypogalactia condition in the lactation period can be treated, and the mastitis disease caused by the leucocytosis in the mammary gland can be relieved. Can also be used for treating respiratory diseases, and can be used for treating cough, asthma, chronic bronchitis and the like caused by obstructed respiratory tract due to the specificity of the part and great association with the respiratory organs.
Disclosure of Invention
The invention aims to provide a magnetic therapy underwear which has the magnetic therapy health care effect.
The technical scheme is as follows:
a magnetic therapy underwear fabric is an antibacterial moisture permeable fabric.
A magnet therapy underwear is characterized in that magnets are sewn at positions of human acupuncture points corresponding to the magnet therapy underwear.
The human body acupuncture point is one or more of Tianchi acupuncture point, Rugen acupuncture point and antral acupuncture point.
The preparation method of the antibacterial moisture permeable fabric comprises the following steps:
(1) using a circular knitting machine to perform knitting and weaving on 35-40 parts by weight of cotton fibers, 58-63 parts by weight of modal fibers and 2-5 parts by weight of spandex to obtain a fabric;
(2) adding 5-15 parts by weight of polyacrylate emulsion, 0.2-0.5 part by weight of citric acid, 2-5 parts by weight of carboxymethyl chitosan, 0.2-0.5 part by weight of rosmarinic acid and 0.3-0.7 part by weight of surfactant into 85-95 parts by weight of water, and uniformly mixing by stirring at the rotation speed of 200-;
(3) and (3) soaking the fabric in the antibacterial finishing liquid, taking out the fabric after soaking, and drying to obtain the antibacterial moisture-permeable fabric.
Preferably, the preparation method of the antibacterial moisture permeable fabric comprises the following steps:
(1) using a circular knitting machine to perform knitting and weaving on 35-40 parts by weight of cotton fibers, 58-63 parts by weight of modal fibers and 2-5 parts by weight of spandex to obtain a fabric;
(2) adding 5-15 parts by weight of polyacrylate emulsion, 0.2-0.5 part by weight of citric acid, 2-5 parts by weight of modified carboxymethyl chitosan, 0.2-0.5 part by weight of rosmarinic acid and 0.3-0.7 part by weight of surfactant into 85-95 parts by weight of water, and uniformly mixing by stirring at the rotation speed of 200 plus 500 rpm for 15-25min to obtain an antibacterial finishing liquid;
(3) and (3) soaking the fabric in the antibacterial finishing liquid, taking out the fabric after soaking, and drying to obtain the antibacterial moisture-permeable fabric.
The preparation method of the modified carboxymethyl chitosan comprises the following steps: adding 1-5g carboxymethyl chitosan into 95-105g water at a rotation speed of 200-500 rpm, stirring for 5-15min, adding 0.2-0.7g cordycepin at a temperature of 30-50 ℃ at a rotation speed of 200-500 rpm, stirring for 15-25min, adding 25-35g sodium tripolyphosphate aqueous solution with a concentration of 2-5mg/mL at a temperature of 30-50 ℃ at a rotation speed of 200-500 rpm, stirring for 15-25min, adding 2-6g silver nitrate aqueous solution with a concentration of 0.1-0.5mol/L at a rotation speed of 200-500 rpm, stirring for 15-25min, adding 2-6g sodium hydroxide aqueous solution with a concentration of 0.1-0.5mol/L at a rotation speed of 200-500 rpm, stirring for 15-25min, spray drying to obtain the final product.
The impregnation temperature is 35-55 deg.C, and the impregnation time is 20-40 min.
The mass ratio of the fabric to the antibacterial finishing liquid is 1: (10-30).
The drying temperature is 60-80 ℃ and the drying time is 4-9 h.
The surfactant is lauric acid imidazoline quaternary ammonium salt and/or N-alkylamino-2-perfluoroalkyl imidazoline quaternary ammonium salt. In one embodiment of the present invention, the surfactant is composed of 65 to 75 wt% of N-ethylamino-2-perfluorononanylimidazoline quaternary ammonium salt and 25 to 35 wt% of lauric acid imidazoline quaternary ammonium salt.
The technical effects are as follows:
the magnetic therapy underwear of the invention can utilize a magnetic field with certain intensity to act on the acupuncture points of the human body to carry out magnetic therapy health care and disease treatment, effectively absorb and discharge sweat after the wearer sweats during sports, keep the skin of the wearer dry and comfortable and prevent the wearer from suffering from diseases, and has good antibacterial, quick-drying, antistatic and washing resistance properties and good comprehensive performance. Can meet the requirements of people on wearing comfort, functionality and practicability, and has good market prospect, economic benefit and social benefit.
Drawings
Fig. 1 is a schematic diagram of the positions corresponding to the acupuncture points on the underwear.
Detailed Description
Surface charge density test: the test is carried out by adopting a C method (a charge surface density method) in the national standard GB/T12703-1991 textile static test method.
Moisture absorption and sweat releasing performance test: the method adopts the evaluation part 1 of the moisture absorption quick drying property of the textile in the national standard GB/T21655.1-2008: single item combination test method.
Drapability testing: the method is carried out by referring to FZ/T01045-1996, and the test instrument adopts a fabric draping performance tester with the model number YG811E provided by Wuhan national instruments Co., Ltd; before the test, the antibacterial moisture permeable fabric is subjected to humidity conditioning for 24 hours under the conditions that the temperature is 20 ℃ and the relative humidity is 65%. The drapability of the fabric is an important index of the wearability of the fabric, and the garment with good drapability can form a smooth curved surface shape and can be properly attached to a human body to provide visual comfort for people.
Citric acid in the examples, CAS number: 77-92-9.
In the examples, the cotton fibers are fine cotton wool, and the specification is as follows: 1.8dtex 30 mm.
In the examples, modal fibers were produced by austria lanjing, and the product specifications were as follows: 1.3dtex 38 mm.
In the examples, the spandex was produced by Shantou Honghuo yarn textile Co., Ltd., spandex filament, 70D.
Examples rosmarinic acid, CAS No.: 20283-92-5.
Examples carboxymethyl chitosan, CAS No.: 83512-85-0, available from Wan Xin Biotech Co., Ltd, Hunan, at a food grade.
Examples cordycepin, CAS No.: 73-03-0, provided by Seieniko Biotech, Inc., having a purity of 98 wt.%.
Examples sodium tripolyphosphate, CAS number: 7758-29-4, available from Hua aviation chemical technology, Inc., Suzhou.
Examples silver nitrate, CAS number: 7761-88-8.
Examples sodium hydroxide, CAS number: 1310-73-2.
In the examples, the lauric acid imidazoline quaternary ammonium salt is prepared according to section 1.1 in a study on corrosion inhibition performance of synthesis of lauric acid imidazoline quaternary ammonium salt, which is published in Shanghai, Lisan and Ruiyehan.
Examples N-ethylamino-2-perfluorononane imidazoline quaternary ammonium salt was prepared as shown in example 1 in Chinese patent application No. 201110002735.4.
In the examples, the polyacrylate emulsion is prepared by the method shown in example 1 in Chinese patent with reference to application number 201310478426.3.
Example 1
The magnetic therapy underwear fabric is an antibacterial moisture permeable fabric, and magnets are sewn at positions of human acupuncture points corresponding to the magnetic therapy underwear.
The human body acupuncture points are Tianchi acupuncture point, Rugen acupuncture point and edible sinus acupuncture point.
The preparation method of the antibacterial moisture permeable fabric comprises the following steps:
(1) blending 36 parts by weight of cotton fiber and 61 parts by weight of modal fiber into blended yarn, and then using a weft knitting circular knitting machine to perform knitting and weaving on the blended yarn and 3 parts by weight of spandex to obtain plain woven fabric, wherein the gram weight of the fabric is 160 g/square meter;
(2) adding 10 parts by weight of polyacrylate emulsion, 0.3 part by weight of citric acid, 3.5 parts by weight of carboxymethyl chitosan, 0.3 part by weight of rosmarinic acid and 0.5 part by weight of N-ethylamino-2-perfluorononane imidazoline quaternary ammonium salt into 90 parts by weight of deionized water, stirring at the rotating speed of 300 revolutions per minute for 20min, and uniformly mixing to obtain an antibacterial finishing liquid;
(3) soaking the fabric in the antibacterial finishing liquid for 30min at the soaking temperature of 45 ℃, wherein the mass ratio of the fabric to the antibacterial finishing liquid is 1: 20, taking out after dipping, and drying for 7h at the temperature of 65 ℃ to obtain the antibacterial moisture permeable fabric.
Example 2
The magnetic therapy underwear fabric is an antibacterial moisture permeable fabric, and magnets are sewn at positions of human acupuncture points corresponding to the magnetic therapy underwear.
The human body acupuncture points are Tianchi acupuncture point, Rugen acupuncture point and edible sinus acupuncture point.
The preparation method of the antibacterial moisture permeable fabric comprises the following steps:
(1) blending 36 parts by weight of cotton fiber and 61 parts by weight of modal fiber into blended yarn, and then using a weft knitting circular knitting machine to perform knitting and weaving on the blended yarn and 3 parts by weight of spandex to obtain plain woven fabric, wherein the gram weight of the fabric is 160 g/square meter;
(2) adding 10 parts by weight of polyacrylate emulsion, 0.3 part by weight of citric acid, 3.5 parts by weight of modified carboxymethyl chitosan, 0.3 part by weight of rosmarinic acid and 0.5 part by weight of N-ethylamino-2-perfluorononane imidazoline quaternary ammonium salt into 90 parts by weight of deionized water, stirring at the rotating speed of 300 revolutions per minute for 20min, and uniformly mixing to obtain an antibacterial finishing liquid;
(3) soaking the fabric in the antibacterial finishing liquid for 30min at the soaking temperature of 45 ℃, wherein the mass ratio of the fabric to the antibacterial finishing liquid is 1: 20, taking out after dipping, and drying for 7h at the temperature of 65 ℃ to obtain the antibacterial moisture permeable fabric.
The preparation method of the modified carboxymethyl chitosan comprises the following steps: adding 3g of carboxymethyl chitosan into 100g of water, stirring for 10min at the rotating speed of 300 revolutions per minute, adding 0.4g of cordycepin, stirring for 20min at the temperature of 40 ℃ at the rotating speed of 300 revolutions per minute, adding 30g of sodium tripolyphosphate aqueous solution with the concentration of 3mg/mL, stirring for 20min at the temperature of 40 ℃ at the rotating speed of 300 revolutions per minute, adding 3g of silver nitrate aqueous solution with the concentration of 0.2mol/L, stirring for 20min at the rotating speed of 300 revolutions per minute, adding 3g of sodium hydroxide aqueous solution with the concentration of 0.2mol/L, and stirring for 20min at the rotating speed of 300 revolutions per minute to obtain a reaction solution; spray drying the reaction solution, wherein the parameters of the spray drying are that the inlet air temperature is 175 ℃, the outlet air temperature is 80 ℃, and the hot air speed is 3.5m3And/min, the feeding speed is 35mL/min, and the rotating speed of an atomizer is 180r/min, so that the modified carboxymethyl chitosan is obtained.
Example 3
The magnetic therapy underwear fabric is an antibacterial moisture permeable fabric, and magnets are sewn at positions of human acupuncture points corresponding to the magnetic therapy underwear.
The human body acupuncture points are Tianchi acupuncture point, Rugen acupuncture point and edible sinus acupuncture point.
The preparation method of the antibacterial moisture permeable fabric comprises the following steps:
(1) blending 36 parts by weight of cotton fiber and 61 parts by weight of modal fiber into blended yarn, and then using a weft knitting circular knitting machine to perform knitting and weaving on the blended yarn and 3 parts by weight of spandex to obtain plain woven fabric, wherein the gram weight of the fabric is 160 g/square meter;
(2) adding 10 parts by weight of polyacrylate emulsion, 0.3 part by weight of citric acid, 3.5 parts by weight of modified carboxymethyl chitosan, 0.3 part by weight of rosmarinic acid and 0.5 part by weight of N-ethylamino-2-perfluorononane imidazoline quaternary ammonium salt into 90 parts by weight of deionized water, stirring at the rotating speed of 300 revolutions per minute for 20min, and uniformly mixing to obtain an antibacterial finishing liquid;
(3) soaking the fabric in the antibacterial finishing liquid for 30min at the soaking temperature of 45 ℃, wherein the mass ratio of the fabric to the antibacterial finishing liquid is 1: 20, taking out after dipping, and drying for 7h at the temperature of 65 ℃ to obtain the antibacterial moisture permeable fabric.
The preparation method of the modified carboxymethyl chitosan comprises the following steps: adding 3g of carboxymethyl chitosan into 100g of water, stirring for 10min at the rotating speed of 300 revolutions per minute, adding 0.4g of cordycepin, stirring for 20min at the temperature of 40 ℃ at the rotating speed of 300 revolutions per minute, adding 30g of sodium tripolyphosphate aqueous solution with the concentration of 3mg/mL, stirring for 20min at the temperature of 40 ℃ at the rotating speed of 300 revolutions per minute to obtain a reaction solution; spray drying the reaction solution, wherein the parameters of the spray drying are that the inlet air temperature is 175 ℃, the outlet air temperature is 80 ℃, and the hot air speed is 3.5m3And/min, the feeding speed is 35mL/min, and the rotating speed of an atomizer is 180r/min, so that the modified carboxymethyl chitosan is obtained.
Example 4
The magnetic therapy underwear fabric is an antibacterial moisture permeable fabric, and magnets are sewn at positions of human acupuncture points corresponding to the magnetic therapy underwear.
The human body acupuncture points are Tianchi acupuncture point, Rugen acupuncture point and edible sinus acupuncture point.
The preparation method of the antibacterial moisture permeable fabric comprises the following steps:
(1) blending 36 parts by weight of cotton fiber and 61 parts by weight of modal fiber into blended yarn, and then using a weft knitting circular knitting machine to perform knitting and weaving on the blended yarn and 3 parts by weight of spandex to obtain plain woven fabric, wherein the gram weight of the fabric is 160 g/square meter;
(2) adding 10 parts by weight of polyacrylate emulsion, 0.3 part by weight of citric acid, 3.5 parts by weight of modified carboxymethyl chitosan, 0.3 part by weight of rosmarinic acid and 0.5 part by weight of imidazoline laurate quaternary ammonium salt into 90 parts by weight of deionized water, stirring at the rotating speed of 300 revolutions per minute for 20min, and uniformly mixing to obtain an antibacterial finishing liquid;
(3) soaking the fabric in the antibacterial finishing liquid for 30min at the soaking temperature of 45 ℃, wherein the mass ratio of the fabric to the antibacterial finishing liquid is 1: 20, taking out after dipping, and drying for 7h at the temperature of 65 ℃ to obtain the antibacterial moisture permeable fabric.
The preparation method of the modified carboxymethyl chitosan comprises the following steps: adding 3g of carboxymethyl chitosan into 100g of water, stirring for 10min at the rotating speed of 300 revolutions per minute, adding 0.4g of cordycepin, stirring for 20min at the temperature of 40 ℃ at the rotating speed of 300 revolutions per minute, adding 30g of sodium tripolyphosphate aqueous solution with the concentration of 3mg/mL, stirring for 20min at the temperature of 40 ℃ at the rotating speed of 300 revolutions per minute, adding 3g of silver nitrate aqueous solution with the concentration of 0.2mol/L, stirring for 20min at the rotating speed of 300 revolutions per minute, adding 3g of sodium hydroxide aqueous solution with the concentration of 0.2mol/L, and stirring for 20min at the rotating speed of 300 revolutions per minute to obtain a reaction solution; spray drying the reaction solution, wherein the parameters of the spray drying are that the inlet air temperature is 175 ℃, the outlet air temperature is 80 ℃, and the hot air speed is 3.5m3And/min, the feeding speed is 35mL/min, and the rotating speed of an atomizer is 180r/min, so that the modified carboxymethyl chitosan is obtained.
Example 5
The magnetic therapy underwear fabric is an antibacterial moisture permeable fabric, and magnets are sewn at positions of human acupuncture points corresponding to the magnetic therapy underwear.
The human body acupuncture points are Tianchi acupuncture point, Rugen acupuncture point and edible sinus acupuncture point.
The preparation method of the antibacterial moisture permeable fabric comprises the following steps:
(1) blending 36 parts by weight of cotton fiber and 61 parts by weight of modal fiber into blended yarn, and then using a weft knitting circular knitting machine to perform knitting and weaving on the blended yarn and 3 parts by weight of spandex to obtain plain woven fabric, wherein the gram weight of the fabric is 160 g/square meter;
(2) adding 10 parts by weight of polyacrylate emulsion, 0.3 part by weight of citric acid, 3.5 parts by weight of modified carboxymethyl chitosan, 0.3 part by weight of rosmarinic acid, 0.15 part by weight of lauric acid imidazoline quaternary ammonium salt and 0.35 part by weight of N-ethylamino-2-perfluorononane imidazoline quaternary ammonium salt into 90 parts by weight of deionized water, stirring at the rotating speed of 300 revolutions per minute for 20min, and uniformly mixing to obtain an antibacterial finishing liquid;
(3) soaking the fabric in the antibacterial finishing liquid for 30min at the soaking temperature of 45 ℃, wherein the mass ratio of the fabric to the antibacterial finishing liquid is 1: 20, taking out after dipping, and drying for 7h at the temperature of 65 ℃ to obtain the antibacterial moisture permeable fabric. The performance test result of the antibacterial moisture permeable fabric is as follows: the moisture permeability is 9098g/m2D, coefficient of drape of 6.03%, unwashed surface charge density of 1.7 μ C/m2。
The preparation method of the modified carboxymethyl chitosan comprises the following steps: adding 3g of carboxymethyl chitosan into 100g of water, stirring for 10min at the rotating speed of 300 revolutions per minute, adding 0.4g of cordycepin, stirring for 20min at the temperature of 40 ℃ at the rotating speed of 300 revolutions per minute, adding 30g of sodium tripolyphosphate aqueous solution with the concentration of 3mg/mL, stirring for 20min at the temperature of 40 ℃ at the rotating speed of 300 revolutions per minute, adding 3g of silver nitrate aqueous solution with the concentration of 0.2mol/L, stirring for 20min at the rotating speed of 300 revolutions per minute, adding 3g of sodium hydroxide aqueous solution with the concentration of 0.2mol/L, and stirring for 20min at the rotating speed of 300 revolutions per minute to obtain a reaction solution; spray drying the reaction solution, wherein the parameters of the spray drying are that the inlet air temperature is 175 ℃, the outlet air temperature is 80 ℃, and the hot air speed is 3.5m3And/min, the feeding speed is 35mL/min, and the rotating speed of an atomizer is 180r/min, so that the modified carboxymethyl chitosan is obtained.
Test example 1
The antibacterial moisture-permeable fabric prepared in the examples 1 to 4 is subjected to performance tests, and specific results are shown in table 1.
Table 1: test result table
The magnetic therapy underwear of the invention can utilize a magnetic field with certain intensity to act on the acupuncture points of the human body to carry out magnetic therapy health care and disease treatment, effectively absorb and discharge sweat after the wearer sweats during sports, keep the skin of the wearer dry and comfortable and prevent the wearer from suffering from diseases, and has good antibacterial, quick-drying, antistatic and washing resistance properties and good comprehensive performance. Can meet the requirements of people on wearing comfort, functionality and practicability, and has good market prospect, economic benefit and social benefit.
Claims (6)
1. A magnetic therapy underwear is characterized in that the magnetic therapy underwear fabric is an antibacterial moisture permeable fabric;
the preparation method of the antibacterial moisture permeable fabric comprises the following steps:
(1) using a circular knitting machine to perform knitting and weaving on 35-40 parts by weight of cotton fibers, 58-63 parts by weight of modal fibers and 2-5 parts by weight of spandex to obtain a fabric;
(2) adding 5-15 parts by weight of polyacrylate emulsion, 0.2-0.5 part by weight of citric acid, 2-5 parts by weight of modified carboxymethyl chitosan, 0.2-0.5 part by weight of rosmarinic acid and 0.3-0.7 part by weight of surfactant into 85-95 parts by weight of water, and uniformly mixing by stirring at the rotation speed of 200 plus 500 rpm for 15-25min to obtain an antibacterial finishing liquid;
(3) dipping the fabric in an antibacterial finishing liquid, taking out the fabric after dipping and drying to obtain an antibacterial moisture-permeable fabric;
the preparation method of the modified carboxymethyl chitosan comprises the following steps: adding 1-5g carboxymethyl chitosan into 95-105g water at a rotation speed of 200-500 rpm, stirring for 5-15min, adding 0.2-0.7g cordycepin at a temperature of 30-50 ℃ at a rotation speed of 200-500 rpm, stirring for 15-25min, adding 25-35g sodium tripolyphosphate aqueous solution with a concentration of 2-5mg/mL at a temperature of 30-50 ℃ at a rotation speed of 200-500 rpm, stirring for 15-25min, adding 2-6g silver nitrate aqueous solution with a concentration of 0.1-0.5mol/L at a rotation speed of 200-500 rpm, stirring for 15-25min, adding 2-6g sodium hydroxide aqueous solution with a concentration of 0.1-0.5mol/L at a rotation speed of 200-500 rpm, stirring for 15-25min, spray drying to obtain;
the surfactant consists of 65-75 wt% of N-ethylamino-2-perfluorononane imidazoline quaternary ammonium salt and 25-35 wt% of lauric acid imidazoline quaternary ammonium salt.
2. The magnetotherapeutic undergarment according to claim 1, wherein magnets are sewn in positions corresponding to acupuncture points of a human body.
3. The magnetotherapeutic undergarment of claim 2, wherein the body acupuncture points are one or more of Tianchi acupuncture point, Rugen acupuncture point, and Shi Kong acupuncture point.
4. The magnetotherapeutic undergarment according to claim 1, wherein the impregnation is carried out at a temperature of 35-55 ℃ for 20-40 min.
5. The magnetic therapy underwear of claim 1, wherein the mass ratio of the fabric to the antibacterial finishing liquid is 1: (10-30).
6. The magnetotherapeutic undergarment of claim 1, wherein the drying temperature is 60-80 ℃ and the drying time is 4-9 hours.