CN107903480A - A kind of stretch-proof polyethylene film and preparation method thereof - Google Patents
A kind of stretch-proof polyethylene film and preparation method thereof Download PDFInfo
- Publication number
- CN107903480A CN107903480A CN201710978994.8A CN201710978994A CN107903480A CN 107903480 A CN107903480 A CN 107903480A CN 201710978994 A CN201710978994 A CN 201710978994A CN 107903480 A CN107903480 A CN 107903480A
- Authority
- CN
- China
- Prior art keywords
- parts
- stretch
- polyethylene
- temperature
- low density
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of stretch-proof polyethylene film, it is made by the raw material of following parts by weight：15 25 parts of low density polyethylene (LDPE), 50 70 parts of linear low density polyethylene, 5 15 parts of metallocene PE, 10 15 parts of polyethylene terephthalate, 37 parts of trimethylol-propane trimethacrylate, 5 12 parts of zinc stearate, 14 18 parts of oxidized polyethylene wax, 12 16 parts of ammonium polyphosphate, 36 parts of nano silicon dioxide, 328 0.2 0.4 parts of 14 parts of silane coupling agent, 38 parts of glass fibre, 6 10 parts of irgasfos 168 and ultra-violet absorber.Intensity, toughness, the tensile resistance of stretch-proof polyethylene film of the present invention are excellent.Present invention also offers the preparation method of the stretch-proof polyethylene film.
Description
Technical field
The invention belongs to polythene material technical field, more particularly to a kind of stretch-proof polyethylene film and its preparation side
Method.
Background technology
Plastic film, for packing and as coating layer.Plastics package and plastic packet product are commercially shared
Share is increasing, and particularly composite plastic flexible package, oneself is through being widely used in the fields such as food, medicine, chemical industry.
Polyethylene film is a kind of colourless, tasteless, odorless, translucent avirulent insulating materials, a large amount of to be used as packaging
Bag, food bag, can also make various containers.The characteristics of polyethylene film has moisture resistance, and penetrability is small, but existing be packed for
Polyethylene film, resilience and tensile strength have much room for improvement.
Metallocene PE is a kind of novel thermoplastic plastics, and metallocene-polyolefin has than original homopolymerization or copolyalkenamer
More excellent performance, the plastic film made of metallocene polyethylene material, has relatively low fusing point and obvious melting zone, and
Conventional polyethylene is substantially better than in toughness, transparency, thermal viscosity, heat-sealing temperature, low smell etc..
The content of the invention
For above-mentioned technical problem, it is an object of the invention to provide a kind of stretch-proof polyethylene film, to improve its time
Elasticity and stretch-resistance, present invention also offers the preparation method of the stretch-proof polyethylene film.
The technical solution adopted by the present invention is：
A kind of stretch-proof polyethylene film, is made by the raw material of following parts by weight：15-25 parts of low density polyethylene (LDPE), linearly
50-70 parts of low density polyethylene (LDPE), 5-15 parts of metallocene PE, 10-15 parts of polyethylene terephthalate, trihydroxy methyl third
3-7 parts of alkane trimethyl acrylic ester, 5-12 parts of zinc stearate, 14-18 parts of oxidized polyethylene wax, 12-16 parts of ammonium polyphosphate, nanometer
3-6 parts of silica, 1-4 parts of silane coupling agent, 3-8 parts of glass fibre, 6-10 parts of irgasfos 168 and ultra-violet absorber
3280.2-0.4 part.
Stretch-proof polyethylene film of the present invention, wherein, it is made by the raw material of following parts by weight：Low density polyethylene (LDPE)
20 parts, 60 parts of linear low density polyethylene, 10 parts of metallocene PE, 10 parts of polyethylene terephthalate, trihydroxy methyl
5 parts of propane trimethyl acrylic ester, 8 parts of zinc stearate, 15 parts of oxidized polyethylene wax, 14 parts of ammonium polyphosphate, nano silicon dioxide 4
3280.2 parts of part, 3 parts of silane coupling agent, 4 parts of glass fibre, 7 parts of irgasfos 168 and ultra-violet absorber.
Stretch-proof polyethylene film of the present invention, wherein, the silane coupling agent is gamma-aminopropyl-triethoxy silicon
One kind in alkane and γ-(the third oxygen of 2,3- epoxies) propyl trimethoxy silicane.
Stretch-proof polyethylene film of the present invention obtains preparation method, comprises the following steps：
(1) glass fibre is shredded, obtains glass fibre of the length in below 0.5mm；
(2) low density polyethylene (LDPE), linear low density polyethylene, metallocene PE and polyethylene terephthalate are weighed
Ester and stirrer for mixing, and heat while stirring uniformly to 240-270 DEG C, stop heating after keeping the temperature 4-5h；
(3) and then in the mixer ammonium polyphosphate is added, nano silicon dioxide, silane coupling agent, glass fibre, resists
Oxygen agent 168 and ultra-violet absorber 328, stir evenly, and controlled at 260-280 DEG C, keep the temperature 0.5-1h, mixed
Material；
(4) mixture obtained by step (3) is extruded through double screw extruder, its Zhong-1 block temperature is 160-170 DEG C, 2nd area
Temperature is 165-175 DEG C, and three area's temperature are 175-190 DEG C, and four area's temperature are 180-200 DEG C, obtain coarse fodder, casting film-forming is cold
But pack afterwards.
The preparation method of stretch-proof polyethylene film of the present invention, wherein, casting temperature is in the step (4)
175-200℃。
Beneficial effect of the present invention：
Stretch-proof polyethylene film of the present invention, by metallocene PE, polyethylene terephthalate and
The synergistic effect of glass fibre and other each components, makes the film of preparation have excellent intensity, toughness, tensile resistance.
The preparation method of the stretch-proof polyethylene film of the present invention, technique is simple and convenient to operate, production efficiency is high, is held
Easily implement industrialization, can be produced with common plastics inflation film manufacturing machine.
Embodiment
Embodiment 1
A kind of stretch-proof polyethylene film, is made by the raw material of following parts by weight：20 parts of low density polyethylene (LDPE), it is linear low close
Spend 60 parts of polyethylene, 10 parts of metallocene PE, 10 parts of polyethylene terephthalate, trimethylol propane trimethyl propylene
5 parts of acid esters, 8 parts of zinc stearate, 15 parts of oxidized polyethylene wax, 14 parts of ammonium polyphosphate, 4 parts of nano silicon dioxide, silane coupling agent 3
3280.2 parts of part, 4 parts of glass fibre, 7 parts of irgasfos 168 and ultra-violet absorber, the silane coupling agent is γ-aminopropyl three
Ethoxysilane.
Stretch-proof polyethylene film described in the present embodiment obtains preparation method, comprises the following steps：
(1) glass fibre is shredded, obtains glass fibre of the length in below 0.5mm；
(2) low density polyethylene (LDPE), linear low density polyethylene, metallocene PE and polyethylene terephthalate are weighed
Ester and stirrer for mixing, and heat while stirring uniformly to 260 DEG C, stop heating after keeping the temperature 4h；
(3) and then in the mixer ammonium polyphosphate is added, nano silicon dioxide, silane coupling agent, glass fibre, resists
Oxygen agent 168 and ultra-violet absorber 328, stir evenly, and controlled at 265 DEG C, keep the temperature 0.5h, obtain mixture；
(4) mixture obtained by step (3) is extruded through double screw extruder, its Zhong-1 block temperature is 160-170 DEG C, 2nd area
Temperature is 165-175 DEG C, and three area's temperature are 175-190 DEG C, and four area's temperature are 180-200 DEG C, obtain coarse fodder, casting film-forming is cold
But pack afterwards, casting temperature is 175-200 DEG C.
Embodiment 2
A kind of stretch-proof polyethylene film, is made by the raw material of following parts by weight：15 parts of low density polyethylene (LDPE), it is linear low close
Spend 70 parts of polyethylene, 5 parts of metallocene PE, 15 parts of polyethylene terephthalate, trimethylol propane trimethyl propylene
7 parts of acid esters, 5 parts of zinc stearate, 18 parts of oxidized polyethylene wax, 12 parts of ammonium polyphosphate, 6 parts of nano silicon dioxide, silane coupling agent 4
3280.2 parts of part, 3 parts of glass fibre, 10 parts of irgasfos 168 and ultra-violet absorber, the silane coupling agent is γ-(2,3- rings
The third oxygen of oxygen) propyl trimethoxy silicane.
Stretch-proof polyethylene film described in the present embodiment obtains preparation method, comprises the following steps：
(1) glass fibre is shredded, obtains glass fibre of the length in below 0.5mm；
(2) low density polyethylene (LDPE), linear low density polyethylene, metallocene PE and polyethylene terephthalate are weighed
Ester and stirrer for mixing, and heat while stirring uniformly to 240 DEG C, stop heating after keeping the temperature 4h；
(3) and then in the mixer ammonium polyphosphate is added, nano silicon dioxide, silane coupling agent, glass fibre, resists
Oxygen agent 168 and ultra-violet absorber 328, stir evenly, and controlled at 280 DEG C, keep the temperature 1h, obtain mixture；
(4) mixture obtained by step (3) is extruded through double screw extruder, its Zhong-1 block temperature is 160-170 DEG C, 2nd area
Temperature is 165-175 DEG C, and three area's temperature are 175-190 DEG C, and four area's temperature are 180-200 DEG C, obtain coarse fodder, casting film-forming is cold
But pack afterwards, casting temperature is 175-200 DEG C.
Embodiment 3
A kind of stretch-proof polyethylene film, is made by the raw material of following parts by weight：25 parts of low density polyethylene (LDPE), it is linear low close
Spend 50 parts of polyethylene, 15 parts of metallocene PE, 10 parts of polyethylene terephthalate, trimethylol propane trimethyl propylene
3 parts of acid esters, 12 parts of zinc stearate, 14 parts of oxidized polyethylene wax, 16 parts of ammonium polyphosphate, 3 parts of nano silicon dioxide, silane coupling agent
1 part, 8 parts of glass fibre, 3280.4 parts of 6 parts of irgasfos 168 and ultra-violet absorber, the silane coupling agent is γ-aminopropyl
Triethoxysilane.
Stretch-proof polyethylene film described in the present embodiment obtains preparation method, comprises the following steps：
(1) glass fibre is shredded, obtains glass fibre of the length in below 0.5mm；
(2) low density polyethylene (LDPE), linear low density polyethylene, metallocene PE and polyethylene terephthalate are weighed
Ester and stirrer for mixing, and heat while stirring uniformly to 270 DEG C, stop heating after keeping the temperature 5h；
(3) and then in the mixer ammonium polyphosphate is added, nano silicon dioxide, silane coupling agent, glass fibre, resists
Oxygen agent 168 and ultra-violet absorber 328, stir evenly, and controlled at 260 DEG C, keep the temperature 0.5h, obtain mixture；
(4) mixture obtained by step (3) is extruded through double screw extruder, its Zhong-1 block temperature is 160-170 DEG C, 2nd area
Temperature is 165-175 DEG C, and three area's temperature are 175-190 DEG C, and four area's temperature are 180-200 DEG C, obtain coarse fodder, casting film-forming is cold
But pack afterwards, casting temperature is 175-200 DEG C.
The performance test of stretch-proof polyethylene film prepared by the present embodiment 1-3 is as shown in table 1 below.
1 performance test data table of table
| Embodiment 1 | Embodiment 2 | Embodiment 3 | |
| Resilience (%) | 81 | 80 | 79 |
| Tensile strength (MPa) | 29.8 | 28.6 | 28.1 |
As it can be seen from table 1 the resilience of stretch-proof polyethylene film made from embodiment 1-3 between 79-81%, is drawn
Intensity is stretched between 22.4-26.8MPa.In addition, the flat appearance of film, without perforation, crack-free, resilience is good, tensile strength
Height, can be widely used in packaging field.
Embodiment described above is only that the preferred embodiment of the present invention is described, not to the model of the present invention
Enclose and be defined, on the premise of design spirit of the present invention is not departed from, technical side of the those of ordinary skill in the art to the present invention
The various modifications and improvement that case is made, should all fall into the protection domain that claims of the present invention determines.
Claims (5)
- A kind of 1. stretch-proof polyethylene film, it is characterised in that：It is made by the raw material of following parts by weight：Low density polyethylene (LDPE) 15- 25 parts, 50-70 parts of linear low density polyethylene, 5-15 parts of metallocene PE, 10-15 parts of polyethylene terephthalate, 3-7 parts of trimethylol-propane trimethacrylate, 5-12 parts of zinc stearate, 14-18 parts of oxidized polyethylene wax, ammonium polyphosphate 12-16 parts, 3-6 parts of nano silicon dioxide, 1-4 parts of silane coupling agent, 3-8 parts of glass fibre, 6-10 parts of irgasfos 168 and ultraviolet 3280.2-0.4 parts of light absorbers.
- 2. stretch-proof polyethylene film according to claim 1, it is characterised in that：It is made by the raw material of following parts by weight： 20 parts of low density polyethylene (LDPE), 60 parts of linear low density polyethylene, 10 parts of metallocene PE, polyethylene terephthalate 10 Part, 5 parts of trimethylol-propane trimethacrylate, 8 parts of zinc stearate, 15 parts of oxidized polyethylene wax, 14 parts of ammonium polyphosphate, receives 3280.2 parts of 4 parts of silica of rice, 3 parts of silane coupling agent, 4 parts of glass fibre, 7 parts of irgasfos 168 and ultra-violet absorber.
- 3. stretch-proof polyethylene film according to claim 1 or 2, it is characterised in that：The silane coupling agent is γ-ammonia Propyl-triethoxysilicane and γ-(the third oxygen of 2,3- epoxies) propyl trimethoxy silicane.
- 4. the stretch-proof polyethylene film described in claim 1-3 any one obtains preparation method, it is characterised in that：Including following Step：(1) glass fibre is shredded, obtains glass fibre of the length in below 0.5mm；(2) weigh low density polyethylene (LDPE), linear low density polyethylene, metallocene PE and polyethylene terephthalate with Stirrer for mixing, and heat while stirring uniformly to 240-270 DEG C, stop heating after keeping the temperature 4-5h；(3) and then in the mixer ammonium polyphosphate, nano silicon dioxide, silane coupling agent, glass fibre, antioxidant are added 168 and ultra-violet absorber 328, stir evenly, and controlled at 260-280 DEG C, keep the temperature 0.5-1h, obtain mixture；(4) mixture obtained by step (3) is extruded through double screw extruder, its Zhong-1 block temperature is 160-170 DEG C, two area's temperature For 165-175 DEG C, three area's temperature are 175-190 DEG C, and four area's temperature are 180-200 DEG C, obtain coarse fodder, casting film-forming, after cooling Packaging.
- 5. the preparation method of stretch-proof polyethylene film according to claim 4, it is characterised in that：In the step (4) Casting temperature is 175-200 DEG C.