CN107686331A - 一种用于生产太阳能瓦的轻质陶瓷基材配方 - Google Patents

一种用于生产太阳能瓦的轻质陶瓷基材配方 Download PDF

Info

Publication number
CN107686331A
CN107686331A CN201710823045.2A CN201710823045A CN107686331A CN 107686331 A CN107686331 A CN 107686331A CN 201710823045 A CN201710823045 A CN 201710823045A CN 107686331 A CN107686331 A CN 107686331A
Authority
CN
China
Prior art keywords
parts
base material
major ingredient
ceramics base
composite reactive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710823045.2A
Other languages
English (en)
Inventor
万锦标
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710823045.2A priority Critical patent/CN107686331A/zh
Publication of CN107686331A publication Critical patent/CN107686331A/zh
Pending legal-status Critical Current

Abstract

本发明克服了现有技术存在的不足，提供了一种用于生产太阳能瓦的轻质陶瓷基材配方，为了解决上述技术问题，本发明采用的技术方案为：一种用于生产太阳能瓦的轻质陶瓷基材配方，包括主料、长石、石英和复合活性成分，其中，主料为25～35份，长石为45～55份，石英为15～25份，复合活性成分为10～15份，所述复合活性成分包括碳化硅、碳酸镁和碳酸锂；所述主料包括页岩、粘土和高岭土，所述页岩、粘土和高岭土按1：1：1混合配置主料，所述复合活性料为碳化硅、碳酸镁和碳酸锂中的任意一种，或为多种组合；本发明可广泛应用于轻质陶瓷基材领域。

Description

一种用于生产太阳能瓦的轻质陶瓷基材配方
技术领域
本发明一种用于生产太阳能瓦的轻质陶瓷基材配方，属于轻质陶瓷基材技术领域。
背景技术
目前太阳能发电薄膜一般设置在玻璃夹层内进行利用，但玻璃基材不仅成本高，而且重量大，生产和安装均极为不便。
发明内容
本发明克服了现有技术存在的不足，提供了一种用于生产太阳能瓦的轻质陶瓷基材配方，降低了陶瓷砖的重量，并与太阳能发电薄膜结合，达到一物两用的目的，不仅将太阳能发电板的重量大大减小，而且生产和安装的成本均极低。
为了解决上述技术问题，本发明采用的技术方案为：一种用于生产太阳能瓦的轻质陶瓷基材配方，包括主料、长石、石英和复合活性成分，其中，主料为25～35份，长石为45～55份，石英为15～25份，复合活性成分为10～15份，所述复合活性成分包括碳化硅、碳酸镁和碳酸锂。
所述主料包括页岩、粘土和高岭土。
所述页岩、粘土和高岭土按1：1：1混合配置主料。
所述复合活性料为碳化硅、碳酸镁和碳酸锂中的任意一种，或为多种组合。
本发明与现有技术相比具有的有益效果是：根据本发明生产出的产品坯体里有细微均匀的闭合孔，不但具有不透水、隔热功能，而且重量大大减轻，相同规格和厚度的情况下与传统工艺相比重量要轻二分之一以上，让产品重量大幅减轻的情况下，将轻质的陶瓷基材作为基层，用特种透明玻璃将太阳能发电薄膜压在基层上，可作为建筑材料覆盖到房顶，达到一物两用的目的，不仅将太阳能发电板的重量大大减小，而且生产和安装的成本均极低。
具体实施方式
本发明一种用于生产太阳能瓦的轻质陶瓷基材配方，包括主料、长石、石英和复合活性成分，其中，主料为25～35份，长石为45～55份，石英为15～25份，复合活性成分为10～15份，所述复合活性成分包括碳化硅、碳酸镁和碳酸锂。
所述主料包括页岩、粘土和高岭土。
所述页岩、粘土和高岭土按1：1：1混合配置主料。
所述复合活性料为碳化硅、碳酸镁和碳酸锂中的任意一种，或为多种组合。
根据本发明生产出的产品坯体里有细微均匀的闭合孔，不但具有不透水、隔热功能，而且重量大大减轻，相同规格和厚度的情况下与传统工艺相比重量要轻二分之一以上，让产品重量大幅减轻的情况下，将轻质的陶瓷基材作为基层，用特种透明玻璃将太阳能发电薄膜压在基层上，可作为建筑材料覆盖到房顶，达到一物两用的目的，不仅将太阳能发电板的重量大大减小，而且生产和安装的成本均极低。
由于单位产品消耗的原料大幅下降，产品烧成时间缩短，流水线生产速度得以迅速提升，日均产量较传统陶瓷瓦提高四分之一以上，这样就大大的降低了生产成本，产品经济效益显著。而比较于其他材料（比如：玻璃等）成本更低。
通过在产品内部引进透明太阳能薄膜发电系统，让产品具备了新能源环保发电功能，实现传统建筑装修风格和现代环保节能的完美结合。
实施例一
本发明一种用于生产太阳能瓦的轻质陶瓷基材配方，包括主料、长石、石英和复合活性成分，其中，主料为页岩、粘土和高岭土的混合物共计35份，长石为55份，石英为25份，复合活性成分为碳化硅、碳酸镁和碳酸锂的混合物共计15份。
实施例二
本发明一种用于生产太阳能瓦的轻质陶瓷基材配方，包括主料、长石、石英和复合活性成分，其中，主料为粘土和高岭土的混合物共计30份，长石为50份，石英为20份，复合活性成分为碳酸镁和碳酸锂的混合物共计13份。
实施例三
本发明一种用于生产太阳能瓦的轻质陶瓷基材配方，包括主料、长石、石英和复合活性成分，其中，主料为高岭土共25份，长石为45份，石英为15份，复合活性成分为碳酸镁共10份。
实施例四
本发明一种用于生产太阳能瓦的轻质陶瓷基材配方，包括主料、长石、石英和复合活性成分，其中，主料为页岩和粘土的混合物共计20份，长石为45份，石英为18份，复合活性成分为碳化硅和碳酸镁的混合物共计12份。
上面结合实施例对本发明作了详细说明，但是本发明并不限于上述实施例，在本领域普通技术人员所具备的知识范围内，还可以在不脱离本发明宗旨的前提下作出各种变化。

Claims (4)

1.一种用于生产太阳能瓦的轻质陶瓷基材配方，其特征在于：包括主料、长石、石英和复合活性成分，其中，主料为25～35份，长石为45～55份，石英为15～25份，复合活性成分为10～15份，所述复合活性成分包括碳化硅、碳酸镁和碳酸锂。
2.根据权利要求1所述的一种用于生产太阳能瓦的轻质陶瓷基材配方，其特征在于：所述主料包括页岩、粘土和高岭土。
3.根据权利要求2所述的一种用于生产太阳能瓦的轻质陶瓷基材配方，其特征在于：所述页岩、粘土和高岭土按1：1：1混合配置主料。
4.根据权利要求1所述的一种用于生产太阳能瓦的轻质陶瓷基材配方，其特征在于：所述复合活性料为碳化硅、碳酸镁和碳酸锂中的任意一种，或为多种组合。
CN201710823045.2A 2017-09-13 2017-09-13 一种用于生产太阳能瓦的轻质陶瓷基材配方 Pending CN107686331A (zh)