CN107628769A - A kind of resistant automatically cleaning sliver paint - Google Patents
A kind of resistant automatically cleaning sliver paint Download PDFInfo
- Publication number
- CN107628769A CN107628769A CN201710861842.XA CN201710861842A CN107628769A CN 107628769 A CN107628769 A CN 107628769A CN 201710861842 A CN201710861842 A CN 201710861842A CN 107628769 A CN107628769 A CN 107628769A
- Authority
- CN
- China
- Prior art keywords
- parts
- automatically cleaning
- sliver
- resistant automatically
- sliver paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of resistant automatically cleaning sliver paint of the present invention, it is characterised in that include the component of following parts by weight：Acrylic emulsion：20 30 parts；Sliver：35 55 parts；Nano titanium oxide：5 18 parts；Polytetrafluoroethylene (PTFE)：3 10 parts；Defoamer：28 parts；Dispersant：15 parts；Thickener：15 parts；Water：30 44 parts.The resistant automatically cleaning sliver paint, surface is not easy adhering dust, dirt, while the organic matter on surface can be decomposed under light illumination, and resistant automatically cleaning effect is good, service life length.
Description
Technical field
The present invention relates to a kind of resistant automatically cleaning sliver paint.
Background technology
At present, the decorative paint species of in the market is various, and sliver paint is one kind therein, because sliver paint has well
Decorative effect, commercially attract attention extensively, existing sliver paint there are two kinds of major classes, and one kind is made using natural rock
Sliver paint, another kind of is the sliver paint made using artificial synthesized sliver.The sliver paint that artificial synthesized sliver makes, it is only suitable
Conjunction is closely seen, is far seen, is difficult to the effect for finding out sliver and texture, without the sensation of true stone, is prepared using existing process and still can not
Reach the effect of rock, the light degree of its heat insulation effect, durability and color can not all be compared with natural rock；Using natural rock
Standby sliver paint made of stones, building decoration can be made more to be bonded naturally, more graceful, steady, style effect, then, in natural sliver
In the preparation process of paint, raw material, formula, no fabrication process condition, the using effect of natural sliver paint is all had influence on.But
The resistant sex chromosome mosaicism of such product is difficult to solve always in the market, and sliver paint surface is easily stained with some dusts, dirt, shadow
Ring the attractive in appearance of entirety.
The content of the invention
To solve above-mentioned problem, it is an object of the invention to provide a kind of resistant automatically cleaning sliver paint.It is described resistance to
Dirty automatically cleaning sliver paint, surface is not easy adhering dust, dirt, while the organic matter on surface can be decomposed under light illumination,
Resistant automatically cleaning effect is good, service life length.
To reach above-mentioned purpose, the technical scheme is that：
A kind of resistant automatically cleaning sliver paint, include the component of following parts by weight：Acrylic emulsion：20-30 parts；Sliver：35-55
Part；Nano titanium oxide：5-18 parts；Polytetrafluoroethylene (PTFE)：3-10 parts；Defoamer：2-8 parts；Dispersant：1-5 parts；Thickener：1-5
Part；Water：30-44 parts.
Further, the component of following parts by weight is included：Acrylic emulsion：20-26 parts；Sliver：41-55 parts；Nanometer
Titanium dioxide：5-13 parts；Polytetrafluoroethylene (PTFE)：6-10 parts；Defoamer：5-8 parts；Dispersant：3-5 parts；Thickener：1-4 parts；Water：
36-44 parts.
Further, the component of following parts by weight is included：Acrylic emulsion：22 parts；Sliver：46 parts；Nanometer titanium dioxide
Titanium：9 parts；Polytetrafluoroethylene (PTFE)：8 parts；Defoamer：6 parts；Dispersant：4 parts；Thickener：3 parts；Water：37 parts.
Further, the particle diameter of the nano titanium oxide is 20-40nm.
Further, the defoamer is dimethicone or tributyl phosphate.
Further, the dispersant is OPE.
Further, the thickener is methyl diphenylene diisocyanate type urethane, the alkali solubility third of hydrophobically modified
Olefin(e) acid based polymer or its combination.
The beneficial effects of the present invention are：
（1）A kind of resistant automatically cleaning sliver paint provided by the invention, containing nano titanium oxide, there is nano titanium oxide light to urge
Change activity so that the organic matter of sliver paint surface attachment is decomposed under light illumination, can be removed after rain-out, and resistant is made
With strong；
（2）A kind of resistant automatically cleaning sliver paint provided by the invention, it is dispersed after sliver paint is dried containing polytetrafluoroethylene (PTFE)
On surface so that dust, dirt are not easy adhesion and sliver paint surface, fundamentally reduce the attachment of dust, dirt；
（3）A kind of environment-friendly dry powder sliver paint provided by the invention, there is outstanding anti-dry and cracked and with wall adhesive force, use
Effect is good.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, it is further detailed with reference to embodiments
Describe in detail bright.
Embodiment 1
A kind of resistant automatically cleaning sliver paint, include the component of following parts by weight：Acrylic emulsion：20 parts；Sliver：35 parts；Receive
Rice titanium dioxide：10 parts；Polytetrafluoroethylene (PTFE)：3 parts；Defoamer：4 parts；Dispersant：5 parts；Thickener：3 parts；Water：30 parts.
Embodiment 2
A kind of resistant automatically cleaning sliver paint, include the component of following parts by weight：Acrylic emulsion：24 parts；Sliver：40 parts；Receive
Rice titanium dioxide：5 parts；Polytetrafluoroethylene (PTFE)：10 parts；Defoamer：2 parts；Dispersant：4 parts；Thickener：2 parts；Water：33 parts.
Embodiment 3
A kind of resistant automatically cleaning sliver paint, include the component of following parts by weight：Acrylic emulsion：22 parts；Sliver：46 parts；Receive
Rice titanium dioxide：9 parts；Polytetrafluoroethylene (PTFE)：8 parts；Defoamer：6 parts；Dispersant：4 parts；Thickener：3 parts；Water：37 parts.
Embodiment 4
A kind of resistant automatically cleaning sliver paint, include the component of following parts by weight：Acrylic emulsion：30 parts；Sliver：55 parts；Receive
Rice titanium dioxide：11 parts；Polytetrafluoroethylene (PTFE)：7 parts；Defoamer：8 parts；Dispersant：1 part；Thickener：1 part；Water：44 parts.
Embodiment 5
A kind of resistant automatically cleaning sliver paint, include the component of following parts by weight：Acrylic emulsion：27 parts；Sliver：42 parts；Receive
Rice titanium dioxide：18 parts；Polytetrafluoroethylene (PTFE)：5 parts；Defoamer：5 parts；Dispersant：3 parts；Thickener：5 parts；Water：36 parts.
The resistant automatically cleaning sliver paint, surface is not easy adhering dust, dirt, while can have under light illumination to surface
Machine thing is decomposed, and resistant automatically cleaning effect is good, service life length.
It should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the technology of invention
Scheme is modified or equivalent substitution, and without departing from the scope of technical solution of the present invention, it all should cover the power in the present invention
In sharp claimed range.
Claims (7)
1. a kind of resistant automatically cleaning sliver paint, it is characterised in that include the component of following parts by weight：Acrylic emulsion：20-30
Part；Sliver：35-55 parts；Nano titanium oxide：5-18 parts；Polytetrafluoroethylene (PTFE)：3-10 parts；Defoamer：2-8 parts；Dispersant：1-5
Part；Thickener：1-5 parts；Water：30-44 parts.
2. a kind of resistant automatically cleaning sliver paint according to claim 1, it is characterised in that include the group of following parts by weight
Point：Acrylic emulsion：20-26 parts；Sliver：41-55 parts；Nano titanium oxide：5-13 parts；Polytetrafluoroethylene (PTFE)：6-10 parts；Defoaming
Agent：5-8 parts；Dispersant：3-5 parts；Thickener：1-4 parts；Water：36-44 parts.
3. a kind of resistant automatically cleaning sliver paint according to claim 1, it is characterised in that include the group of following parts by weight
Point：Acrylic emulsion：22 parts；Sliver：46 parts；Nano titanium oxide：9 parts；Polytetrafluoroethylene (PTFE)：8 parts；Defoamer：6 parts；It is scattered
Agent：4 parts；Thickener：3 parts；Water：37 parts.
A kind of 4. resistant automatically cleaning sliver paint according to claim 1, it is characterised in that the grain of the nano titanium oxide
Footpath is 20-40nm.
5. a kind of resistant automatically cleaning sliver paint according to claim 1, it is characterised in that the defoamer is dimethyl-silicon
Oil or tributyl phosphate.
6. a kind of resistant automatically cleaning sliver paint according to claim 1, it is characterised in that the dispersant is the poly- second of oxidation
Alkene wax.
7. a kind of resistant automatically cleaning sliver paint according to claim 1, it is characterised in that the thickener is diphenylmethyl
Alkane diisocyanate type urethane, alkali-soluble acrylic's polymer of hydrophobically modified or its combination.