CN107604194A - A kind of wire feed powder feeding coupling device based on arc deposited metal-base composites - Google Patents

A kind of wire feed powder feeding coupling device based on arc deposited metal-base composites Download PDF

Info

Publication number
CN107604194A
CN107604194A CN201711049482.XA CN201711049482A CN107604194A CN 107604194 A CN107604194 A CN 107604194A CN 201711049482 A CN201711049482 A CN 201711049482A CN 107604194 A CN107604194 A CN 107604194A
Authority
CN
China
Prior art keywords
powder feeding
coupling device
wire feed
base composites
device based
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201711049482.XA
Other languages
Chinese (zh)
Other versions
CN107604194B (en
Inventor
孙建新
肖海峰
王乐平
李怀君
彭道衡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hubei University of Automotive Technology
Original Assignee
Hubei University of Automotive Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hubei University of Automotive Technology filed Critical Hubei University of Automotive Technology
Priority to CN201711049482.XA priority Critical patent/CN107604194B/en
Publication of CN107604194A publication Critical patent/CN107604194A/en
Application granted granted Critical
Publication of CN107604194B publication Critical patent/CN107604194B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites; including welding gun protection sleeve (1), functional sleeve (2), powder feeding injection nozzle (3) and powder feeding conduit (10); the functional sleeve (2) is wrapped in the surface of the welding gun protection sleeve (1); the powder feeding conduit (10) is loaded on the side of the functional sleeve (2); the powder feeding injection nozzle (3) is connected on the powder feeding conduit (10), and the coupling device coordinates electrode gas shielded arc welding gun to use.The device can both avoid particle during powder feeding from passing through arc space over long distances, can shorten the solid-liquid contact time of particle and liquid metal again, so as to prevent the grain dissolution in metal-base composites preparation process and the generation of harmful chemicals reacting phenomenon.

Description

A kind of wire feed powder feeding coupling device based on arc deposited metal-base composites
Technical field
The invention belongs to technical field of composite materials, is related to particles reiforced metal-base composition preparation facilities, specifically relates to A kind of and wire feed powder feeding coupling device based on arc deposited metal-base composites.
Background technology
Particles reiforced metal-base composition is due to good combination property, cost-effective, in Aero-Space, defence and military, vapour The fields such as vehicle device car have major application potentiality.Conventional particles enhancing metal-base composites using stirring casting, powder metallurgy, Prepared by the methods of high energy beam cladding, the preparation temperature and longer solid-liquid that not only efficiency is low, manufacturing cost is high and higher connect The tactile time will cause particle to produce harmful chemicals reaction with metallic matrix, so as to reduce the comprehensive of particles reiforced metal-base composition Close performance.The particularly exploitation of 3D increases material manufacturing technologies, the manufacturing technology of particles reiforced metal-base composition is proposed newly Requirement.The manufacturing cost of arc deposited metal-base composites is cheap, and manufacture efficiency is high, is applicable not only to traditional metal surface Complex intensifying, and be adapted to particles reiforced metal-base composition 3D increasing material manufacturings.The electric arc of coaxial wire feed side powder feeding sinks Product method, during particles reiforced metal-base composition is prepared, it can effectively prevent that particles by heat is serious and dissolves With the phenomenon of harmful chemicals reaction, it is adapted to industrialized production and application.The coupling distance and angle of wire feed powder feeding are for manufactured Particles reiforced metal-base composition quality influences very big.The metal of different physicochemical characteristic and different process processes and enhancing Grain differs to the coupling distance and angle requirement of wire feed powder feeding.
At present, on the market and the wire feed powder feeding adjusting means that can retrieve is mainly for laser melting and coating technique, and mainly Suitable for coaxial wire feed powder feeding, it is impossible to solve the problems such as powder dissolving and harmful chemicals reaction, be not suitable for arc deposition and prepare Particles reiforced metal-base composition, more precisely, being not suitable for and supporting gold of the manufacture based on arc deposition of arc welding gun Metal-matrix composite material.Such as Chinese invention patent Publication No. CN104195542A, publication date 2014.12.10, innovation and creation name A kind of referred to as patent of invention of " adjusting means of combining nozzle ", it which disclose a kind of regulation wire feed of suitable laser melting coating The device of powder feeding axiality, its purposes and purpose are different from the present invention.
The content of the invention
The technical problems to be solved by the invention are:Grain dissolution in preparation process be present and have in metal-base composites Evil chemical reaction phenomenon, greatly reduce the performance of prepared composite.
For above-mentioned technical problem, the invention provides a kind of wire feed powder feeding based on arc deposited metal-base composites Coupling device, protect the welding gun protection sleeve of weldering to be designed transformation to conventional fused pole, and with its supporting side that can be adjusted Side powder feeding injection nozzle, the device can both avoid particle during powder feeding from passing through arc space over long distances, and can shorten particle again With the solid-liquid time of contact of liquid metal, so as to prevent the grain dissolution and harmful in metal-base composites preparation process Learn reacting phenomenon.
Therefore, present invention employs following technical scheme:
A kind of wire feed powder feeding coupling device based on arc deposited metal-base composites, including welding gun protection sleeve, work( Energy set, powder feeding injection nozzle and powder feeding conduit, the functional sleeve are wrapped in the surface of the welding gun protection sleeve, and the powder feeding is led Pipe is loaded on the side of the functional sleeve, and the powder feeding injection nozzle is connected on the powder feeding conduit, and the coupling device is matched somebody with somebody Electrode gas shielded arc welding gun is closed to use.
Further, the surface of welding gun protection sleeve is provided with transmission groove and guide key groove, the transmission groove and Guide key groove is respectively positioned at the both sides of welding gun protection sleeve.
Further, the side of the functional sleeve is positioned in guide key groove using guide pin, the opposite side of functional sleeve Fastened using bolt.
Further, the both sides of the functional sleeve are respectively equipped with longitudinally adjust valve and angular adjustment valve, the angular adjustment Valve is located at this side of powder feeding injection nozzle.
As a preferred embodiment, the longitudinally adjust valve is provided with gear, the gear engages with transmission groove, turn longitudinal direction Regulating valve can be enclosed on dynamic to backhaul on welding gun protection sleeve with driving function.
As a preferred embodiment, the angular adjustment valve is provided with neck and trip bolt, rotating angle regulating valve can be adjusted Save the angle of powder feeding injection nozzle and welding gun protection sleeve.
Further, one end of the powder feeding injection nozzle is provided with the mouth that dusts, and the other end is connected with powder feeding conduit using screw thread Connect, in neck of the powder feeding conduit loaded on angular adjustment valve.
Further, the material of the powder feeding conduit is copper or copper alloy.
Further, the flexibility of the powder feeding injection nozzle be 20 ° -40 °, the mouth that dusts of powder feeding injection nozzle it is transversal Face is circular hole or slit.
Further, the material of the powder feeding injection nozzle is red copper or ceramics.
Compared with prior art, the beneficial effects of the invention are as follows:
(1) it can both avoid particle during powder feeding from passing through arc space over long distances, particle and liquid metal can be shortened again Solid-liquid time of contact, so as to prevent the grain dissolution and harmful chemicals reacting phenomenon in metal-base composites preparation process Occur.
(2) simple in construction, flexible design is easy to use.
(3) manufacturing cost is low, and manufacture efficiency is high, is adapted to industrialized production and application.
Brief description of the drawings
Fig. 1 is a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites provided by the present invention Overall structure diagram.
Fig. 2 is in a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites provided by the present invention The structural representation of functional sleeve.
Fig. 3 is in a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites provided by the present invention The structural representation of longitudinally adjust valve.
Fig. 4 is in a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites provided by the present invention The structural representation of angular adjustment valve.
Fig. 5 is in a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites provided by the present invention The structural representation of the mouth that dusts of powder feeding injection nozzle.
Description of reference numerals:1st, welding gun protection sleeve;2nd, functional sleeve;3rd, powder feeding injection nozzle;4th, it is driven groove;5th, it is oriented to Keyway;6th, longitudinally adjust valve;7th, angular adjustment valve;8th, guide pin;9th, bolt;10th, powder feeding conduit;11st, gear;12nd, neck; 13rd, trip bolt;14th, dust mouth.
Embodiment
Below in conjunction with the accompanying drawings and specific embodiment describes the present invention in detail, and specific embodiment therein and explanation be only For explaining the present invention, but it is not as a limitation of the invention.
As shown in figure 1, the invention discloses a kind of wire feed powder feeding based on arc deposited metal-base composites to couple dress Put, including welding gun protection sleeve 1, functional sleeve 2, powder feeding injection nozzle 3 and powder feeding conduit 10, the functional sleeve 2 are wrapped in described Welding gun protects the surface of sleeve 1, and the powder feeding conduit 10 is loaded on the side of the functional sleeve 2, and the powder feeding injection nozzle 3 connects It is connected on the powder feeding conduit 10, the coupling device coordinates electrode gas shielded arc welding gun to use.
Wherein, the surface of the welding gun protection sleeve 1 is provided with transmission groove 4 and guide key groove 5, the transmission He of groove 4 Guide key groove 5 is respectively positioned at the both sides of welding gun protection sleeve 1.
As shown in Fig. 2 the side of the functional sleeve 2 is positioned in guide key groove 5 using guide pin 8, functional sleeve 2 it is another Side is fastened using bolt 9.The both sides of the functional sleeve 2 are respectively equipped with longitudinally adjust valve 6 and angular adjustment valve 7, the angle Regulating valve 7 is located at this side of powder feeding injection nozzle 3.
As shown in figure 3, the longitudinally adjust valve 6 is provided with gear 11, the gear 11 engages with transmission groove 4, turn Longitudinally adjust valve 6 can be covered 2 with driving function and be moved back and forth on welding gun protection sleeve 1.
As shown in figure 4, the angular adjustment valve 7 is provided with neck 12 and trip bolt 13, rotating angle regulating valve 7 can be with Adjust the angle of powder feeding injection nozzle 3 and welding gun protection sleeve 1.
One end of the powder feeding injection nozzle 3 is provided with the mouth 14 that dusts, and the other end is used with powder feeding conduit 10 and is threadedly coupled, institute State in neck 12 of the powder feeding conduit 10 loaded on angular adjustment valve 7.
The flexibility of the powder feeding injection nozzle 3 is 20 ° -40 °, and the cross section of the mouth 14 that dusts of powder feeding injection nozzle 3 is Circular hole or slit, as shown in Figure 5.
The material of the powder feeding conduit 10 is copper or copper alloy.The material of the powder feeding injection nozzle 3 be red copper or Ceramics.
Pass through a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites provided by the present invention Adjustment effect, the wire feed powder feeding coupling angle, θ during arc deposited metal-base composites are can be controlled in the range of 10 ° -60 ° Change.
The better embodiment of the present invention is the foregoing is only, is not intended to limit the invention, it is all the present invention's Any modification, equivalent substitution and improvement made within spirit and spirit etc., it should be included in the protection model of the present invention Within enclosing.

Claims (10)

1. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites, including welding gun protection sleeve (1), work( (2), powder feeding injection nozzle (3) and powder feeding conduit (10) can be covered, it is characterised in that:The functional sleeve (2) is wrapped in the welding gun The surface of sleeve (1) is protected, the powder feeding conduit (10) is loaded on the side of the functional sleeve (2), the powder feeding injection nozzle (3) it is connected on the powder feeding conduit (10), the coupling device coordinates electrode gas shielded arc welding gun to use.
2. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites according to claim 1, its It is characterised by:The surface of the welding gun protection sleeve (1) is provided with transmission groove (4) and guide key groove (5), the transmission groove (4) and guide key groove (5) is respectively positioned at the both sides of welding gun protection sleeve (1).
3. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites according to claim 2, its It is characterised by:The side of the functional sleeve (2) is positioned in guide key groove (5) using guide pin (8), functional sleeve (2) it is another Side is fastened using bolt (9).
4. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites according to claim 3, its It is characterised by:The both sides of the functional sleeve (2) are respectively equipped with longitudinally adjust valve (6) and angular adjustment valve (7), the angular adjustment Valve (7) is located at powder feeding injection nozzle (3) this side.
5. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites according to claim 4, its It is characterised by:The longitudinally adjust valve (6) is provided with gear (11), and the gear (11) is engaged with transmission groove (4), and turn is indulged It can be moved back and forth to regulating valve (6) with driving function set (2) on welding gun protection sleeve (1).
6. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites according to claim 4 or 5, It is characterized in that:The angular adjustment valve (7) is provided with neck (12) and trip bolt (13), and rotating angle regulating valve (7) can To adjust the angle of powder feeding injection nozzle (3) and welding gun protection sleeve (1).
7. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites according to claim 6, its It is characterised by:One end of the powder feeding injection nozzle (3) is provided with the mouth (14) that dusts, and the other end uses screw thread with powder feeding conduit (10) Connection, neck (12) of the powder feeding conduit (10) loaded on angular adjustment valve (7) are interior.
8. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites according to claim 7, its It is characterised by:The material of the powder feeding conduit (10) is copper or copper alloy.
9. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites according to claim 8, its It is characterised by:The flexibility of the powder feeding injection nozzle (3) is 20 ° -40 °, the horizontal stroke of the mouth that dusts (14) of powder feeding injection nozzle (3) Section is circular hole or slit.
10. a kind of wire feed powder feeding coupling device based on arc deposited metal-base composites according to claim 9, its It is characterised by:The material of the powder feeding injection nozzle (3) is red copper or ceramics.
CN201711049482.XA 2017-10-31 2017-10-31 Wire and powder feeding coupling device based on arc deposition metal matrix composite Active CN107604194B (en)