CN107587136A - A kind of brass polish cream of viscosity stabilization - Google Patents
A kind of brass polish cream of viscosity stabilization Download PDFInfo
- Publication number
- CN107587136A CN107587136A CN201710593272.0A CN201710593272A CN107587136A CN 107587136 A CN107587136 A CN 107587136A CN 201710593272 A CN201710593272 A CN 201710593272A CN 107587136 A CN107587136 A CN 107587136A
- Authority
- CN
- China
- Prior art keywords
- viscosity stabilization
- component
- thickener
- polish cream
- brass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to metal surface clean technologies field, is specifically related to a kind of brass polish cream of viscosity stabilization.It is made up of abrasive material, organic solvent, thickener, Ludox, Ludox stabilizer, essence and water.The brass polish cream of viscosity stabilization is prepared by special preparation technology, for the surface cleaning of the large-scale copper class ornaments such as hotel, hotel, reaches mirror effect.
Description
Technical field
The present invention relates to metal surface clean technologies field, is specifically related to a kind of brass polish cream of viscosity stabilization
Background technology
Copper and its alloy polishing are also known as bright dipped finish, substantially have three acid cleanings and are cleaned containing chromium, three acid formula speed
Degree is fast, and pickling light extraction bright property is good, therefore application surface is most wide.But the disadvantage of three acid formulas is strong reaction, is soaked in workpiece
Enter the moment of polishing fluid, i.e., can produce the largely tobacco with pungent taste, pollution air, poison environment, influence worker's health.
And cleaned containing chromium in inorganic agent used and contain Cr6+, hexavalent chromium compound belongs to extremely toxic and carcinogenicity material, has mutagenesis.
European Union successively promulgates in January, 2003《On limiting the instruction using some harmful substances in electronic and electrical equipment》And
《Instructed on waste electronic andelectrical equipment》, it is desirable to each member state works out corresponding standard regulation in before the part of in August, 2004 have
The specific requirement of evil material, such as lead, Cr VI.It, which is sought unity of standard, put into effect in 2005 and was forced from 1 day July in 2006 real
OK.
Such cleaning agent is liquid simultaneously, needs soaking and washing, clear for the surface of the large-scale copper class ornaments such as hotel, hotel
It is clean to have certain difficulty, it is even more impossible for large-scale statue in bronze, therefore, it is necessary to develop a kind of brass polish cream of stabilization, simplification is clear
Clean technique, mirror effect is can reach by wiping by hand, the cleaning for the ornaments of large-scale copper has certain application market.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to a kind of brass polish cream of stabilization is provided, by abrasive material, You Jirong
Agent, thickener, Ludox, Ludox stabilizer, essence and water composition.Viscosity stabilization is prepared by special preparation technology
Brass polish cream, for the surface cleaning of the large-scale copper class ornaments such as hotel, hotel, minute surface effect is just can reach only by simple wiping
Fruit.
To achieve the above object, present invention employs following technical scheme：
A kind of brass polish cream of viscosity stabilization, it is characterised in that be made up of the raw material of following parts by weight：
Described thickener includes：Component (a) is in carboxymethyl cellulose, methylcellulose, hydroxyethyl cellulose
It is a kind of；Component (b) is selected from polyvinyl alcohol.The weight ratio of the component (a) and the component (b) is 5:5~9:1.
The alcoholysis degree of component polyvinyl alcohol in the thickener is 60-90%, degree of polymerization 500-3000.
Described Ludox is 40-60nm cataloids selected from particle diameter.
Described Ludox stabilizer is selected from KBM-602.
The one kind of described organic solvent in ethanol, ethylene glycol, glycol monoethyl ether, ethylene glycol monobutyl ether.
The preparation method of the brass polish cream of described viscosity stabilization, it is characterised in that：
(1) first the component (b) of the thickener component (a) of weighing and 50% is incorporated in water, is heated to 60 DEG C, 800-
10-20min is stirred under 1000rpm, it is standby to obtain viscosity stabilization, uniform solubilizer solution A.
(2) under 800-1000rpm stirrings, it is stable that abrasive material, Ludox, Ludox are sequentially added in thickener soln A
Agent, organic solvent and essence, stirring at normal temperature uniformly obtain mixture B.Often plus a kind of raw material must assure that and add again after being well mixed
Enter another raw material.
(3) in the case where 800-1000rpm is stirred, it is molten that remaining 50% component (b) thickener is added into mixture B
Liquid carries out viscosity fine setting, and obtains the product.
The application process of the brass polish cream of described viscosity stabilization：Take out part brass polish cream to be applied on clean rag, by hand
Mode is wiped on the surface of copper, is wiped with clean step remove unnecessary dosage component afterwards.
The present invention prepares the brass polish cream of viscosity stabilization by special preparation technology, is answered using two kinds of different thickeners
With stable brass polish cream is prepared, mode of operation is simple and convenient, and mirror effect is can reach by simple wiping, for hotel, guest
The oily certain market of the surface cleaning of the large-scale copper class ornaments such as shop.
Embodiment
Below with reference to embodiment, the present invention is described in detail.But embodiment content is only to this hair
Bright example and explanation, affiliated those skilled in the art do various repair to described specific embodiment
Change or supplement or substituted using similar mode, design without departing from invention or surmount defined in the claims
Scope, protection scope of the present invention all should be belonged to.
Thickener soln A preparation：
| Total amount/g | Component (a) | Dosage/g | 50% component (b) | Dosage/g | |
| Thickener A1 | 0.5 | Carboxymethyl cellulose | 0.25 | Polyvinyl alcohol | 0.125 |
| Thickener A2 | 2 | Methylcellulose | 1.8 | Polyvinyl alcohol | 0.1 |
| Thickener A3 | 3 | Hydroxyethyl cellulose | 2.7 | Polyvinyl alcohol | 1.5 |
Preparation method：First the component (b) of the thickener component (a) of metering and 50% is incorporated in water, is heated to 60 DEG C,
10-20min is stirred under 800-1000rpm, it is standby to obtain viscosity stabilization, uniform solubilizer solution A.
Embodiment preparation method：
(1) under 800-1000rpm stirrings, it is stable that abrasive material, Ludox, Ludox are sequentially added in thickener soln A
Agent, organic solvent and essence, stirring at normal temperature uniformly obtain mixture B.Often plus a kind of raw material must assure that and add again after being well mixed
Enter another raw material.
(3) in the case where 800-1000rpm is stirred, it is molten that remaining 50% component (b) thickener is added into mixture B
Liquid carries out viscosity fine setting, and obtains the product.
Performance test：According to the copper surface after wiping, surface cleanliness and brightness are estimated, respectively according to such as the following grading
Row judges：
1 grade of surface free from dust and oxide skin, reach mirror effect
2 grades of surface free from dust and oxide skin, but brightness is not good enough
3 grades of surfaces are poor without greasy dirt, visible a small amount of selective oxidation skin, brightness
4 grades of surfaces do not clean up, hence it is evident that visible oxide skin, brightness are poor
| Embodiment | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Grade | 1 | 1 | 1 |
Claims (8)
1. a kind of brass polish cream of viscosity stabilization, it is characterised in that be made up of the raw material of following parts by weight：
。
2. the brass polish cream of viscosity stabilization as claimed in claim 1, it is characterised in that：Described thickener includes：Component (a) is selected
One kind from carboxymethyl cellulose, methylcellulose, hydroxyethyl cellulose；Component (b) is selected from polyvinyl alcohol.
3. the brass polish cream of the viscosity stabilization as described in claim 1 or 2, it is characterised in that：Described group in the thickener
It is 5 to divide (a) and the weight ratio of the component (b):5~9:1.
4. the brass polish cream of the viscosity stabilization as described in claim 1 and 2, it is characterised in that：Component in the thickener is gathered
The alcoholysis degree of vinyl alcohol is 60-90%, degree of polymerization 500-3000.
5. the brass polish cream of viscosity stabilization as claimed in claim 1, it is characterised in that：Described Ludox is 40- selected from particle diameter
60nm cataloids.
6. the brass polish cream of viscosity stabilization as claimed in claim 1, it is characterised in that：Described Ludox stabilizer is selected from KBM-
602。
7. the brass polish cream of viscosity stabilization as claimed in claim 1, it is characterised in that：Described organic solvent is selected from ethanol, second
One kind in glycol, glycol monoethyl ether, ethylene glycol monobutyl ether.
A kind of 8. preparation method of the brass polish cream of viscosity stabilization as described in claim 1-7, it is characterised in that：
(1) first the component (b) of the thickener component (a) of weighing and 50% is incorporated in water, is heated to 60 DEG C, 800-
10-20min is stirred under 1000rpm, it is standby to obtain viscosity stabilization, uniform solubilizer solution A.
(2) under 800-1000rpm stirrings, abrasive material, Ludox is sequentially added in thickener soln A, Ludox stabilizer, is had
Solvent and essence, stirring at normal temperature uniformly obtain mixture B.Often plus a kind of raw material must assure that and be added in addition after being well mixed
A kind of raw material.
(3) in the case where 800-1000rpm is stirred, remaining 50% component (b) thickener soln is added into mixture B and is entered
Row viscosity is finely tuned, and obtains the product.