CN107540953A - Injector for medical purpose polypropylene resin composite and preparation method thereof - Google Patents
Injector for medical purpose polypropylene resin composite and preparation method thereof Download PDFInfo
- Publication number
- CN107540953A CN107540953A CN201610489861.XA CN201610489861A CN107540953A CN 107540953 A CN107540953 A CN 107540953A CN 201610489861 A CN201610489861 A CN 201610489861A CN 107540953 A CN107540953 A CN 107540953A
- Authority
- CN
- China
- Prior art keywords
- injector
- medical purpose
- polypropylene resin
- resin composite
- purpose polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to processing of high molecular material technical field, and in particular to a kind of injector for medical purpose polypropylene resin composite and preparation method thereof.Injector for medical purpose is made up with polypropylene resin composite of the following raw material：Homopolymerization PP, random copolymerization PP, crushing-resistant copolymerization transparent PP, antioxidant, acid-acceptor, lubricant, nucleator.The present invention obtains a kind of transparent polypropylene composition of high rigid-tough balance by the screening of three kinds of polypropylene base resins and the application of adjuvant system.Said composition can meet medical standard requirement, for the production of injector for medical purpose, simultaneously can be used for the production that injection produces other transparent articles such as transparent cutlery box, parcel tray.Due to higher rigid-tough balance and the transparency, improving the quality and durability of product.
Description
Technical field
The invention belongs to processing of high molecular material technical field, and in particular to a kind of injector for medical purpose acrylic resin group
Compound and preparation method thereof.
Background technology
At present, polypropylene is the main raw material(s) for producing Dispoable medical syringe.Injector for medical purpose is required with polypropylene
Meet specified in YY/T 0242-2007 to the requirements such as polypropylene physical and mechanical properties, biological property, chemical property, mesh
Preceding prior art can produce the acrylic resin for meeting the requirement of above standard, but in production injector for medical purpose actual use
In, be present the problem of toughness deficiency in existing acrylic resin, show：The syringe of production occurs brokenly in transport and in
The phenomenon split, especially the phenomenon is even more serious at low temperature, have impact on normal use.To solve the problems, such as toughness deficiency, note
Emitter factory can typically add toughening material such as POP, POE, SEBS, metallocene PE, propylene-based elastomeric etc. in polypropylene
Toughness reinforcing is carried out, but the toughener introduced makes rigid, the transparent reduction of material, while another non-PP introduced material is
The control of syringe products wholesomeness brings very unfavorable factor.
Based on problem above, a kind of new composition based on polypropylene is developed, meets injector for medical purpose to firm
The requirement of property, toughness, the transparency and medical standard is extremely urgent.
The content of the invention
It is an object of the invention to provide a kind of injector for medical purpose polypropylene resin composite, has higher rigidity-toughness balanced
Property and the transparency, improve the quality and durability of product；Invention also provides injector for medical purpose acrylic resin group
The preparation method of compound, it is scientific and reasonable, simple and easy.
Injector for medical purpose polypropylene resin composite of the present invention, is made up of the raw material of following parts by weight：
The MFR of described homopolymerization PP is 10-60g/10min, and bending modulus is more than 1600MPa.
Described random copolymerization PP is that ethylene-propylene random copolymer or propene-1-butene random copolymer, comonomer contain
3-3.5% is measured, MFR 8-40g/10min, 1mm prints mist degree is less than 10%.
The MFR of described crushing-resistant copolymerization transparent PP is 8-30g/10min, ethylene contents 4-6%, and simply supported beam notch shock is strong
Spend 10kJ/m2More than, 1mm prints mist degree is less than 13%.
Described antioxidant is one kind in Hinered phenols antioxidant, phosphite antioxidant or composite antioxidant.Dosage
For 0.1-0.3 parts, preferably 0.2 part.
Described composite antioxidant is the compound of antioxidant 1010 and irgasfos 168, and both mass ratioes are 1:1.
Described acid-acceptor is stearate, including calcium stearate, zinc stearate, odium stearate etc., preferably calcium stearate,
It is abbreviated as Cast.
Described lubricant is one kind in glycerin monostearate, fatty acid metal salts, fatty acid amide or wax, preferably singly
Tristerin, its sour glycerine ester of chemical entitled list 18 (alkane), abbreviation monoglyceride GMS.
Described nucleator is phosphoric acid salt nucleator or Sorbitol Nucleator, and dosage is 0.3-0.4 parts, preferably 0.35
Part.
Injector for medical purpose of the present invention stirs mixed after being raw material weighing with the preparation method of polypropylene resin composite
Close, through double-screw extruding pelletizing, produce.
The present invention compared with prior art, has the advantages that：
The present invention is obtained a kind of high strong and unyielding flat by the screening of three kinds of polypropylene base resins and the application of adjuvant system
The transparent polypropylene composition of weighing apparatus property.Said composition can meet the requirement of medical standard, for the production of injector for medical purpose, simultaneously
It can also be used for the production that injection produces other transparent articles such as transparent cutlery box, parcel tray.Due to higher rigid-tough balance
And the transparency, improve the quality and durability of product.
Embodiment
The present invention is described further with reference to embodiments.
Antioxidant used in following examples, comparative example is the 1 of 1010,168:1 built agent, dosage are 0.2 part.Institute
The nucleator used is Sorbitol Nucleator, and dosage is 0.35 part.The acid-acceptor used is calcium stearate, dosage 0.05
Part.The lubricant used is glycerin monostearate, 0.05 part of dosage.
Embodiment 1-3 raw materials form and behavior pattern is shown in Table 1.
Preparation method of composition described in invention：It is stirred after resin in above auxiliary agent and table is weighed by proportioning, after
Said composition is obtained through double-screw extruding pelletizing.
Performance test methods in table：
Melt mass flow rate (MFR) is carried out by GB/T 3682-2000；
Simply supported beam notch impact strength is tested by GB/T 1043.1-2008；
The modulus of elasticity in static bending is carried out by GB/T 9341-2008；
Rockwell hardness is carried out according to GB/T 3398.2-2008；
Mist degree is carried out according to GB/T 2410-2008；
Separating force is carried out according to GB/T 1962-2001.
The embodiment 1-3 raw materials of table 1 form and performance
The embodiment 4-6 raw materials of table 2 form and performance
By the whole resin based on polypropylene of the composition prepared by the present invention it can be seen from embodiment 1-6, ensure
Unicity and wholesomeness of the product on molecular structure composition.And prepare composition have good rigid-tough balance and
The transparency and hardness etc., so as to ensure that the transparent outward appearance of syringe products, separating force test request and mechanicalness
Can require etc..
Contrast is for example shown in table 3, table 4, wherein used polypropylene is identical with embodiment.
The comparative example 1-3 raw materials of table 3 form and performance
The comparative example 4-6 raw materials of table 4 form and performance
From comparative example 1-6 can be seen that composition prepared by comparative example can toughness, rigidity, hardness, the transparency, point
From power etc. existing defects.
Claims (10)
1. a kind of injector for medical purpose polypropylene resin composite, it is characterised in that be made up of the raw material of following parts by weight：
2. injector for medical purpose polypropylene resin composite according to claim 1, it is characterised in that described homopolymerization PP
MFR be 10-60g/10min, bending modulus is more than 1600MPa.
3. injector for medical purpose polypropylene resin composite according to claim 1, it is characterised in that described is random common
Poly- PP is ethylene-propylene random copolymer or propene-1-butene random copolymer, co-monomer content 3-3.5%, MFR 8-
40g/10min, 1mm print mist degree are less than 10%.
4. injector for medical purpose polypropylene resin composite according to claim 1, it is characterised in that described anti-impact is total to
The MFR of poly- transparent PP is 8-30g/10min, ethylene contents 4-6%, simply supported beam notch impact strength 10kJ/m2More than, 1mm samples
Piece mist degree is less than 13%.
5. injector for medical purpose polypropylene resin composite according to claim 1, it is characterised in that described antioxidant
It is one kind in Hinered phenols antioxidant, phosphite antioxidant or composite antioxidant.
6. injector for medical purpose polypropylene resin composite according to claim 5, it is characterised in that described is compound anti-
Oxygen agent is the compound of antioxidant 1010 and irgasfos 168, and both mass ratioes are 1:1.
7. injector for medical purpose polypropylene resin composite according to claim 1, it is characterised in that described acid-acceptor
For stearate.
8. injector for medical purpose polypropylene resin composite according to claim 1, it is characterised in that described lubricant
For one kind in glycerin monostearate, fatty acid metal salts, fatty acid amide or wax.
9. injector for medical purpose polypropylene resin composite according to claim 1, it is characterised in that described nucleator
For phosphoric acid salt nucleator or Sorbitol Nucleator.
10. a kind of preparation method of any described injector for medical purpose polypropylene resin composites of claim 1-9, its feature
It is stirred after being raw material weighing, through double-screw extruding pelletizing, produces.