CN107418337A - Water-based sand streak paint and preparation method thereof - Google Patents
Water-based sand streak paint and preparation method thereof Download PDFInfo
- Publication number
- CN107418337A CN107418337A CN201710728730.7A CN201710728730A CN107418337A CN 107418337 A CN107418337 A CN 107418337A CN 201710728730 A CN201710728730 A CN 201710728730A CN 107418337 A CN107418337 A CN 107418337A
- Authority
- CN
- China
- Prior art keywords
- water
- sand streak
- based sand
- paint
- streak paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of coatings, and in particular to a kind of water-based sand streak paint and preparation method thereof.Counted using the gross mass of the water-based sand streak paint as 100%, the water-based sand streak enamel-cover includes the composition of following weight/mass percentage composition：Aqueous acrylic emulsion 45 50%；Clear glass sand 32 38%；Blanc fixe 4 8%；Aqueous black paste 5 6%；Coalescents 2 2.5%；Dry film mould inhibitor 0.1 0.5%；Dispersant 0.3 0.5%；Defoamer 0.3 0.4%；PH conditioning agents 0.2 0.25%；First auxiliary rheological agents 0.2 0.25%；Second auxiliary rheological agents 0.2 0.25%；Water 0.4 3.8%.Water-based sand streak paint smell is low, hardness is high for this, adhesive force is good, has good weatherability, to workmen's non-hazardous, can be widely used for the field that sound equipment surface and decorative panel etc. want application sand streak effect.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of water-based sand streak paint and preparation method thereof.
Background technology
Sand streak paint is matt after a kind of spraying and touches up the paint kind of site operation with frosted texture, and it is household or life day
Articles for use provide diversified painting effect.Traditional solvent-borne type sand streak paint, with its excellent mechanical performance, splendid adhesive force
And chemical resistance, and it is cheap the advantages that, it is occupied critical role in Coating Market, can be widely applied to sound equipment, dress
The fields such as plaque；But solvent-borne type sand streak paint can discharge a large amount of solvents in the production and use process, it has to health
Harm, not environmentally, and smell is big in construction, is not easy to be received by workmen.
At present, aqueous wooden ware sand streak paint is mostly one pack system on the market, as common aqueous wooden ware sand streak paint, its multi-purpose sand
Prepared by line powder, and sand streak powder footpath is small, oil absorption is big, and price costly, and needs to spray and could repeatedly reached during its use
To ideal effect, it is difficult to compared favourably with traditional solvent-borne type woodenware sand streak paint product.
The content of the invention
It is an object of the invention to overcome the above-mentioned deficiency of prior art, there is provided a kind of water-based sand streak paint and its preparation side
Method, it is intended to solve existing water-based sand streak paint spraying effect is undesirable and technical problem that cost is high.
For achieving the above object, the technical solution adopted by the present invention is as follows：
One aspect of the present invention provides a kind of water-based sand streak paint, is counted using the gross mass of the water-based sand streak paint as 100%, described
Water-based sand streak enamel-cover includes the composition of following weight/mass percentage composition：
Water-based sand streak paint provided by the invention is using aqueous acrylic emulsion as matrix, using clear glass sand as packing material,
Simultaneously add blanc fixe, aqueous black paste, coalescents, dry film preservative, dispersant, defoamer and PH conditioning agents and
The various adjuvants such as auxiliary rheological agents, by being acted synergistically between each component so that the water-based sand streak paint is finally crosslinked shape after drying
Into paint film there is the performance that drying varniss speed is fast, hardness is high, and take into account good adhesive force, weatherability；The water-based sand
Line paint is easy for construction, and smell is low, to workmen's non-hazardous, excellent performance, can be widely used for sound equipment surface and decorative panel etc.
Field.
Another aspect of the present invention provides a kind of preparation method of water-based sand streak paint, comprises the following steps：
Each component materials are weighed respectively according to the composition contained by above-mentioned water-based sand streak paint and its content；
The dry film mould inhibitor, the dispersant and the coalescents are added in the aqueous acrylic emulsion
The mixing treatment of row first, obtain the first batch mixing thing；
The blanc fixe and the defoamer are added in the first batch mixing thing and carry out the second mixing treatment, is obtained
Second batch mixing thing；
The aqueous black paste, the PH conditioning agents, first auxiliary rheological agents and second auxiliary rheological agents are added
The 3rd mixing treatment is carried out into the second batch mixing thing, obtains the 3rd batch mixing thing；
The clear glass sand and the water are added to the 4th mixing treatment of progress in the 3rd batch mixing thing, obtained described
Water-based sand streak paint.
The preparation method technique of water-based sand streak paint provided by the invention is simple, only need to be according to formula without special equipment
Each component is subjected to mixing addition in four times by step so that each component is sufficiently mixed uniformly, and the preparation method cost is low, is adapted to
Industrialized production；And the water-based sand streak paint smell of this method preparation is low, hardness is high, adhesive force is good, has good weatherability,
To workmen's non-hazardous, the field that sound equipment surface and decorative panel etc. want application sand streak effect can be widely used for.
Embodiment
In order that technical problems, technical solutions and advantageous effects to be solved by the present invention are more clearly understood, below in conjunction with
Embodiment, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only explaining
The present invention, it is not intended to limit the present invention.
On the one hand, the embodiments of the invention provide a kind of water-based sand streak paint, using the gross mass of the water-based sand streak paint as
100% meter, the water-based sand streak enamel-cover include the composition of following weight/mass percentage composition：
Water-based sand streak paint provided in an embodiment of the present invention is using aqueous acrylic emulsion as matrix, using clear glass sand as filling
Material, while add blanc fixe, aqueous black paste, coalescents, dry film preservative, dispersant, defoamer and PH and adjust
The various adjuvants such as agent and auxiliary rheological agents are saved, by being acted synergistically between each component so that finally crosslinking is dry for the water-based sand streak paint
The paint film formed after dry has the performance that drying varniss speed is fast, hardness is high, and takes into account good adhesive force, weatherability；Should
Water-based sand streak paint is easy for construction, and smell is low, to workmen's non-hazardous, has excellent spraying property and splendid sand streak to stack effect
Fruit, it can be widely used for the fields such as sound equipment surface and decorative panel.
Further, in water-based sand streak paint provided in an embodiment of the present invention, aqueous acrylic emulsion is selfing bipropenyl
Yogurt liquid, and its solids content is 44-46% (i.e. 45 ± 1wt%).Quality of the aqueous acrylic emulsion in water-based sand streak paint
Percentage composition can be 45%, 48% and 50%.The aqueous acrylic emulsion of the solids content has extremely strong encapsulation to filler,
Especially suitable for high PVC system so that the water-based sand streak paint film of the embodiment of the present invention has remarkable hardness, good flexible
The advantages that property and chemical resistance.
Further, in water-based sand streak paint provided in an embodiment of the present invention, clear glass sand is a kind of sand borosilicate
The clear glass microballon that raw material processes from strand, particle diameter are 60 mesh, its smooth appearance, rounding, glass transparent free from admixture.Transparent glass
The weight/mass percentage composition of glass sand can be 32%, 35%, 37% or 38%.The clear glass sand hardness is high, and high-speed stirred will not be broken
Bad surface effect, easily scattered, the splendid fillibility of imparting paint film and stacking property.
Further, in water-based sand streak paint provided in an embodiment of the present invention, blanc fixe has high chemistry to be a kind of
The chemical raw material of stability and high structural strength, and particle diameter is 1250 mesh, blanc fixe weight/mass percentage composition can be 4%, 6%
Or 8%.Blanc fixe oil absorption under the particle diameter is low, can be uniformly dispersed among emulsion, is remarkably improved emulsion to transparent
The parcel performance of glass sand, and structural strength is good, cheap, appropriate addition can reduce cost.
Further, in water-based sand streak paint provided in an embodiment of the present invention, aqueous black paste is that a kind of tinting strength, tinting power is high
Water-based ultra-dispersed carbon black color slurry, the BK9007-SB products produced such as section's enlightening.Aqueous black paste weight/mass percentage composition can be 5% or
6%.The water-based ultra-dispersed carbon black color slurry is fast light and weather resistance is excellent, possesses higher cost benefit.
Further, in water-based sand streak paint provided in an embodiment of the present invention, coalescents are that propane diols ethers film forming helps
Agent, such as dipropylene.The weight/mass percentage composition of coalescents can be 2% or 2.5%.The preferable coalescents can make this
After the water-based sand streak paint spraying of inventive embodiments, fast filming.
Further, in water-based sand streak paint provided in an embodiment of the present invention, dispersant is that ammonium polyacrylate salt disperses
Agent.Such dispersant efficiency is higher, is advantageous to the stably dispersing of powder in water-based sand streak paint.The quality percentage of dispersant contains
Amount is chosen as 0.3%, 0.4% and 1.0%.
Further, in water-based sand streak paint provided in an embodiment of the present invention, defoamer is the hydrophobic in polyethylene glycol
The defoamer of the mixing species defoamer of solid and brokenly bubble polysiloxanes, such as the model BYK 024 of German Bi Ke chemical productions.
The weight/mass percentage composition of defoamer can be 0.3% and 0.4%.The preferable defoamer can quickly the bubble in elimination system and
Bubble caused by scattered powder, improves sand streak paint workability.
Further, in water-based sand streak paint provided in an embodiment of the present invention, dry film mould inhibitor is done for isothiazolinone
Film mould inhibitor and/or benzimidazole dry film mould inhibitor, it is a kind of mildew and algae without formaldehyde and organic volatile (VOC)
Agent, such as the mildew and algae agent for the model ACTICIDE EPW that Sol THOR companies produce.The quality percentage of dry film preservative contains
Amount can be 0.1%, 0.4 and 0.5%.The preferable dry film preservative can thoroughly prevent that mould and algae are raw on coating paint film
It is long, it is mould proof particularly suitable for dry film.
Further, in water-based sand streak paint provided in an embodiment of the present invention, PH conditioning agents are 2- amino-2-methyls -1-
Aqueous propanol solution, while wherein containing 95% 2-amino-2-methyl-1-propanol and 5% water, as DOW Chemical produces
AMP- products.PH conditioning agents weight/mass percentage composition can be 0.2% and 0.25%.The preferable PH conditioning agents can also improve filler profit
It is wet, promote to disperse, prevent filler from re-uniting.
Further, in water-based sand streak paint provided in an embodiment of the present invention, the first auxiliary rheological agents are that anion alkali soluble is swollen
Association thickener, i.e., a kind of cross-linked type macromolecule emulsion-type alkali swollen thickener containing acidic-group, as ROHM AND HAAS is given birth to
The model ASE-60 of production thickener, the weight/mass percentage composition of the first auxiliary rheological agents can be 0.2% and 0.25%.This is preferable
First auxiliary rheological agents can effectively improve low sheraing (Brookfield) viscosity, coating system is had higher pseudoplastic behavior.And
Second auxiliary rheological agents are preferably non-ionic polyurethane association thickener, such as the thickening for the model DSX 3290 that section rather produces
Agent, the weight/mass percentage composition of the second auxiliary rheological agents can be 0.25% and 0.3%, and it is steady that second auxiliary rheological agents can improve coating storage
It is qualitative, make its gloss and water resistance more preferably.
On the other hand, the embodiment of the present invention additionally provides a kind of preparation method of water-based sand streak paint, and it comprises the following steps：
S01：Each component materials are weighed respectively according to the composition contained by above-mentioned water-based sand streak paint and its content；
S02：Dry film mould inhibitor, dispersant and coalescents therein are added in aqueous acrylic emulsion and carry out first
Mixing treatment, obtain the first batch mixing thing；
S03：Blanc fixe and defoamer are added in above-mentioned first batch mixing thing and carry out the second mixing treatment, obtains second
Batch mixing thing；
S04：Aqueous black paste, PH conditioning agents, the first auxiliary rheological agents and the second auxiliary rheological agents are added into above-mentioned second to mix
The 3rd mixing treatment is carried out in material, obtains the 3rd batch mixing thing；
S05：Clear glass sand and water are added to the 4th mixing treatment of progress in above-mentioned 3rd batch mixing thing, obtain water-based sand streak
Paint.
The preparation method technique of above-mentioned water-based sand streak paint provided in an embodiment of the present invention is simple, without special equipment, only
Each component need to be subjected to mixing addition in four times by step according to formula so that each component is sufficiently mixed uniformly, the preparation method
Cost is low, is adapted to industrialized production；And the water-based sand streak paint smell of this method preparation is low, hardness is high, adhesive force is good, has very
Good weatherability, to workmen's non-hazardous, can be widely used for the neck that sound equipment surface and decorative panel etc. want application sand streak effect
Domain.
Further, in above-mentioned steps S02, the first mixing treatment is that process is：400-500 revs/min, stir 10-
15 minutes；In above-mentioned steps S03, the process of the second mixing treatment is：800-1000 revs/min, stir 15-20 minutes；
In above-mentioned steps S04, the process of the 3rd mixing treatment is：1000-1200 revs/min, stir 10-15 minutes；In above-mentioned steps
In S05, the process of the 4th mixing treatment is：1000-1200 revs/min, stir 5-10 minutes.Under the conditions of the technological parameter,
Each component can be more well mixed.
It is of the invention successively to carry out test of many times, it is further detailed as reference pair invention progress now to lift A partial experiment result
Thin description, is described in detail with reference to specific embodiment.
Embodiment 1
A kind of water-based sand streak paint, the formula for preparing the water-based sand streak paint are shown in Table embodiment 1 in 1.The water-based sand streak paint
Preparation method comprises the following steps：
S11：Each component materials are weighed respectively according to the composition contained by the water-based sand streak paint of embodiment 1 in table 1 and its content.
S12：Dry film mould inhibitor, dispersant and coalescents therein are added in aqueous acrylic emulsion and carry out first
Mixing treatment, obtain the first batch mixing thing；Wherein, the first mixing treatment is that process is：400-500 revs/min, stir 10-15 minutes.
S13：Blanc fixe and defoamer are added in above-mentioned first batch mixing thing and carry out the second mixing treatment, obtains second
Batch mixing thing；Wherein, the process of the second mixing treatment is：800-1000 revs/min, stir 15-20 minutes.
S14：Aqueous black paste, PH conditioning agents, the first auxiliary rheological agents and the second auxiliary rheological agents are added into above-mentioned second to mix
The 3rd mixing treatment is carried out in material, obtains the 3rd batch mixing thing；Wherein, the process of the 3rd mixing treatment is：1000-1200 revs/min
Clock, stir 10-15 minutes.
S15：Clear glass sand and water are added to the 4th mixing treatment of progress in above-mentioned 3rd batch mixing thing, obtain water-based sand streak
Paint；Wherein, the process of the 4th mixing treatment is：1000-1200 revs/min, stir 5-10 minutes.
Embodiment 2
A kind of water-based sand streak paint, the formula for preparing the water-based sand streak paint are shown in Table embodiment 2 in 1.The water-based sand streak paint
Preparation method comprises the following steps：
S21：Each component materials are weighed respectively according to the composition contained by the water-based sand streak paint of embodiment 2 in table 1 and its content.
S22：Dry film mould inhibitor, dispersant and coalescents therein are added in aqueous acrylic emulsion and carry out first
Mixing treatment, obtain the first batch mixing thing；Wherein, the first mixing treatment is that process is：400-500 revs/min, stir 10-15 minutes.
S23：Blanc fixe and defoamer are added in above-mentioned first batch mixing thing and carry out the second mixing treatment, obtains second
Batch mixing thing；Wherein, the process of the second mixing treatment is：800-1000 revs/min, stir 15-20 minutes.
S24：Aqueous black paste, PH conditioning agents, the first auxiliary rheological agents and the second auxiliary rheological agents are added into above-mentioned second to mix
The 3rd mixing treatment is carried out in material, obtains the 3rd batch mixing thing；Wherein, the process of the 3rd mixing treatment is：1000-1200 revs/min
Clock, stir 10-15 minutes.
S25：Clear glass sand and water are added to the 4th mixing treatment of progress in above-mentioned 3rd batch mixing thing, obtain water-based sand streak
Paint；Wherein, the process of the 4th mixing treatment is：1000-1200 revs/min, stir 5-10 minutes.
Embodiment 3
A kind of water-based sand streak paint, the formula for preparing the water-based sand streak paint are shown in Table embodiment 3 in 1.The water-based sand streak paint
Preparation method comprises the following steps：
S31：Each component materials are weighed respectively according to the composition contained by the water-based sand streak paint of embodiment 3 in table 1 and its content.
S32：Dry film mould inhibitor, dispersant and coalescents therein are added in aqueous acrylic emulsion and carry out first
Mixing treatment, obtain the first batch mixing thing；Wherein, the first mixing treatment is that process is：400-500 revs/min, stir 10-15 minutes.
S33：Blanc fixe and defoamer are added in above-mentioned first batch mixing thing and carry out the second mixing treatment, obtains second
Batch mixing thing；Wherein, the process of the second mixing treatment is：800-1000 revs/min, stir 15-20 minutes.
S34：Aqueous black paste, PH conditioning agents, the first auxiliary rheological agents and the second auxiliary rheological agents are added into above-mentioned second to mix
The 3rd mixing treatment is carried out in material, obtains the 3rd batch mixing thing；Wherein, the process of the 3rd mixing treatment is：1000-1200 revs/min
Clock, stir 10-15 minutes.
S35：Clear glass sand and water are added to the 4th mixing treatment of progress in above-mentioned 3rd batch mixing thing, obtain water-based sand streak
Paint；Wherein, the process of the 4th mixing treatment is：1000-1200 revs/min, stir 5-10 minutes.
Comparative example 1
A kind of water-based sand streak paint, the formula for preparing the water-based sand streak paint are shown in Table comparative example 1 in 1.The water-based sand streak paint
Preparation method comprises the following steps：
S41：Each component materials are weighed respectively according to the composition contained by the water-based sand streak paint of comparative example 1 in table 1 and its content.
S42：Dry film mould inhibitor, dispersant and coalescents therein are added in aqueous acrylic emulsion and carry out first
Mixing treatment, obtain the first batch mixing thing；Wherein, the first mixing treatment is that process is：400-500 revs/min, stir 10-15 minutes.
S43：Blanc fixe and defoamer are added in above-mentioned first batch mixing thing and carry out the second mixing treatment, obtains second
Batch mixing thing；Wherein, the process of the second mixing treatment is：800-1000 revs/min, stir 15-20 minutes.
S44：Aqueous black paste, PH conditioning agents and the second auxiliary rheological agents are added in above-mentioned second batch mixing thing and carry out the 3rd
Mixing treatment, obtain the 3rd batch mixing thing；Wherein, the process of the 3rd mixing treatment is：1000-1200 revs/min, 10-15 points of stirring
Clock.
S45：Clear glass sand and water are added to the 4th mixing treatment of progress in above-mentioned 3rd batch mixing thing, obtain water-based sand streak
Paint；Wherein, the process of the 4th mixing treatment is：1000-1200 revs/min, stir 5-10 minutes.
Table 1
Performance test
Carry out performance test to water-based sand streak paint made from above-described embodiment 1-3 and comparative example 1, related test event and
The data of test result are as shown in table 2.Meanwhile by water-based sand streak paint made from embodiments of the invention 1 and commercially available one-component water
Under equal conditions Construction Comparison, its performance comparison data result are as shown in table 3 for property woodenware sand streak paint.
Table 2
As can be seen from the above Table 2, the water-based sand streak paint that prepared by 1-3 of the embodiment of the present invention passes through the collaboration between each component
Effect, goes out that rifle is smooth, and sand does not rebound during spraying so that sand is uniform on the paint film that final crosslinking is formed after drying, the water-based sand streak
It is high to paint hardness, there is excellent wearability, humidity resistance.Wherein, by comparative example 1 compared with embodiment 1~3, can be apparent from
Dry film mould inhibitor, the first auxiliary rheological agents are to sprayability, weatherability and the storage stability of the water-based sand streak paint of the embodiment of the present invention
Deng important.For comparative example 1 because dry film mould inhibitor dosage is small, artificial weathering ageing resistance and humidity resistance are poor, cause
The easy mouldy loss of gloss of paint film；And comparative example 1 causes to paint sample sprayability, poor storage stability again due to no first auxiliary rheological agents,
Go out rifle to have some setbacks, sand bounce-back is serious, and upper sand amount is few.And embodiment 1~3, due to enough dry film mould inhibitors, the first auxiliary rheological agents,
Protect the excellent dry film mildew resistance of positive product while there is good construction, storage stability performance, do not influence product other performances
Meanwhile significantly improve paint film impact resistance and weatherability.
Table 3
As shown in Table 3, the water-based sand streak paint that prepared by the present invention, its artificial weathering ageing resistance, humidity resistance and sprayability
Certain commercially available single-component water-based woodenware sand streak paint product is substantially better than, and the dry and hard time is shorter, wearability is more preferable, and combination property is excellent
It is different.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
All any modification, equivalent and improvement made within refreshing and principle etc., should be included in the scope of the protection.
Claims (10)
1. a kind of water-based sand streak paint, it is characterised in that counted using the gross mass of the water-based sand streak paint as 100%, the water-based sand
Line enamel-cover includes the composition of following weight/mass percentage composition：
2. water-based sand streak paint as claimed in claim 1, it is characterised in that the solids content of the aqueous acrylic emulsion is
44-46wt%.
3. water-based sand streak paint as claimed in claim 1, it is characterised in that the coalescents are that propane diols ethers film forming helps
Agent；And/or
The aqueous black paste is water-based ultra-dispersed carbon black slurry.
4. water-based sand streak paint as claimed in claim 1, it is characterised in that the dry film mould inhibitor is isothiazolinone dry film
Mould inhibitor and/or benzimidazole dry film mould inhibitor.
5. water-based sand streak paint as claimed in claim 1, it is characterised in that the dispersant is that ammonium polyacrylate salt disperses
Agent；And/or
The defoamer is the hydrophobic solid and the mixture of brokenly bubble polysiloxanes in polyethylene glycol.
6. water-based sand streak paint as claimed in claim 1, it is characterised in that the PH conditioning agents are 2- amino-2-methyls -1- third
Alcohol solution, and the mass fraction of 2-amino-2-methyl-1-propanol is in the 2-amino-2-methyl-1-propanol aqueous solution
94-96%.
7. water-based sand streak paint as claimed in claim 1, it is characterised in that first auxiliary rheological agents are formed for anion alkali soluble is swollen
Thickener；And/or
Second auxiliary rheological agents are non-ionic polyurethane association thickener.
8. water-based sand streak paint as claimed in claim 1, it is characterised in that the particle diameter of the clear glass sand is 60 mesh；And/or
The particle diameter of the blanc fixe is 1250 mesh.
9. a kind of preparation method of water-based sand streak paint, it is characterised in that comprise the following steps：
It is former that each composition is weighed respectively according to the composition contained by the water-based sand streak paint described in claim any one of 1-8 and its content
Material；
The dry film mould inhibitor, the dispersant and the coalescents are added in the aqueous acrylic emulsion and carry out
One mixing treatment, obtain the first batch mixing thing；
The blanc fixe and the defoamer are added in the first batch mixing thing and carry out the second mixing treatment, obtains second
Batch mixing thing；
The aqueous black paste, the PH conditioning agents, first auxiliary rheological agents and second auxiliary rheological agents are added to institute
The 3rd mixing treatment of progress in the second batch mixing thing is stated, obtains the 3rd batch mixing thing；
The clear glass sand and the water are added to the 4th mixing treatment of progress in the 3rd batch mixing thing, obtained described water-based
Sand streak paint.
10. the preparation method of water-based sand streak paint as claimed in claim 9, it is characterised in that first mixing treatment was
Cheng Wei：400-500 revs/min, stir 10-15 minutes；And/or
The process of second mixing treatment is：800-1000 revs/min, stir 15-20 minutes；And/or
The process of 3rd mixing treatment is：1000-1200 revs/min, stir 10-15 minutes；And/or
The process of 4th mixing treatment is：1000-1200 revs/min, stir 5-10 minutes.