CN107301887A - A kind of silver-colored conductive silver paste composition of the novel solar battery back of the body and preparation method - Google Patents
A kind of silver-colored conductive silver paste composition of the novel solar battery back of the body and preparation method Download PDFInfo
- Publication number
- CN107301887A CN107301887A CN201710338701.XA CN201710338701A CN107301887A CN 107301887 A CN107301887 A CN 107301887A CN 201710338701 A CN201710338701 A CN 201710338701A CN 107301887 A CN107301887 A CN 107301887A
- Authority
- CN
- China
- Prior art keywords
- silver
- solar battery
- silver paste
- novel solar
- paste composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of silver-colored conductive silver paste composition of novel solar battery back of the body, including：78% 82% silver powder, 8% 12% bisphenol A type epoxy resins, 1% 3% acid anhydride type curing agents, 0 1% methyl miaow sound of crying or vomiting, 4% 6% butyl acetates, 1% 2% reactive diluent, tetraethyl titanate, 0 1% polyamide waxes.The silver paste compositions conductive performance that the present invention is prepared is good, and adhesive ability is strong, and printing performance is good, with low cost, and the conductor paste has the compatibility with baseplate material, dielectric material, is conducive to environmental protection.
Description
Technical field
The present invention relates to technical field of solar batteries, particularly a kind of silver-colored conductive silver paste combination of the novel solar battery back of the body
Thing and preparation method thereof.
Background technology
At present, with the quickening of world energy consumption speedup, non-renewable energy resources have been gradually decreased, and the mankind are entering
In sector-style energy, water energy, the quick exploitation of nuclear energy and solar energy, wherein developing environmental protection the most, effectively and money especially with solar energy
Source is abundant, and crystal silicon solar photoelectricity development of projects main at present is the rapidest.Wherein, the main component of the back silver paste of application
Include function phase silver powder, inorganic binder (such as glass powder, oxide powder), organic binder bond, other solvent and
Additive.There are 2 shortcomings in the silver powder that current back of the body silver is taken, one is to use micro silver powder, i.e. silver powder to be generally micro nanometer silver more
Powder, the slurry fineness being made is larger, coarse, causes that the film layer in printing process is thicker, and compactness is bad, produces hole, print
Brush performance is bad, and then influences electric conductivity, and two be that silver powder content is higher, and the consumption to noble silver is larger, so that crystal silicon
Solar photovoltaic device industrial production cost is increased, therefore in this case, a kind of low silver of exploitation contains high performance crystal silicon too
Sun can carry on the back silver conductive paste and just be particularly important.
The content of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of silver-colored conductive silver paste of novel solar battery back of the body
Composition and preparation method thereof, the silver paste compositions conductive performance that the application is prepared is good, and adhesive ability is strong, and printing performance is good,
It is with low cost, and the conductor paste has the compatibility with baseplate material, dielectric material, is conducive to environmental protection.
The purpose of the present invention is achieved through the following technical solutions：
A kind of silver-colored conductive silver paste composition of the novel solar battery back of the body, includes the raw material of following mass percent：
78%-82% silver powder, 8%-12% bisphenol A type epoxy resins, 1%-3% acid anhydride type curing agents, 0-1% methyl miaows
Sound of crying or vomiting, 4%-6% butyl acetates, 1%-2% reactive diluents, tetraethyl titanate, 0-1% polyamide waxes.
Further, in the preferred embodiment of the invention, it also includes solvent, and the solvent includes the molten acid anhydride acetic acid of butyl
Ester, butyl acetate, diethylene glycol ether acetate, isophorone.
Further, in the preferred embodiment of the invention, it also includes titanium dioxide and bismuth oxide.
A kind of preparation method of the silver-colored conductive silver paste composition of the novel solar battery back of the body, comprises the following steps：
S1, by 78%-82% silver powder, 8%-12% bisphenol A type epoxy resins, 1%-3% acid anhydride type curing agents, 0-1%
Methyl miaow sound of crying or vomiting, 4%-6% butyl acetates, 1%-2% reactive diluents, tetraethyl titanate, 0-1% polyamide waxes be well mixed,
It is placed in 145-155 DEG C of baking oven drying 1.5-2.5h；
S2, by dried material and the molten acid anhydride acetic acid esters of butyl, butyl acetate, diethylene glycol ether acetic acid
Ester, isophorone, titanium dioxide and bismuth oxide mixing, then roll after slurry 25 times with three-roll grinder that to obtain fineness be below 12mm's
Back side silver paste.
The beneficial effects of the invention are as follows：
The silver paste compositions conductive performance that the present invention is prepared is good, and adhesive ability is strong, and printing performance is good, with low cost, and
The conductor paste has the compatibility with baseplate material, dielectric material, is conducive to environmental protection.
Brief description of the drawings
Fig. 1 is the process chart of preparation method of the present invention.
Embodiment
Illustrate embodiments of the present invention below by way of specific instantiation, those skilled in the art can be by this specification
Disclosed content understands other advantages and effect of the present invention easily.The present invention can also pass through specific realities different in addition
The mode of applying is embodied or practiced, the various details in this specification can also based on different viewpoints with application, without departing from
Various modifications or alterations are carried out under the spirit of the present invention.It should be noted that, in the case where not conflicting, following examples and implementation
Feature in example can be mutually combined.
It should be noted that the diagram provided in following examples only illustrates the basic structure of the present invention in a schematic way
Think, then in schema only display with relevant component in the present invention rather than according to component count, shape and the size during actual implement
Draw, it is actual when implementing, and kenel, quantity and the ratio of each component can be a kind of random change, and its assembly layout kenel
It is likely more complexity.
A kind of silver-colored conductive silver paste composition of the novel solar battery back of the body, includes the raw material of following mass percent：
78%-82% silver powder, 8%-12% bisphenol A type epoxy resins, 1%-3% acid anhydride type curing agents, 0-1% methyl miaows
Sound of crying or vomiting, 4%-6% butyl acetates, 1%-2% reactive diluents, tetraethyl titanate, 0-1% polyamide waxes.
Further, in the preferred embodiment of the invention, it also includes solvent, and the solvent includes the molten acid anhydride acetic acid of butyl
Ester, butyl acetate, diethylene glycol ether acetate, isophorone.
Further, in the preferred embodiment of the invention, it also includes titanium dioxide and bismuth oxide.
A kind of preparation method of the silver-colored conductive silver paste composition of the novel solar battery back of the body, comprises the following steps：
S1, by 78%-82% silver powder, 8%-12% bisphenol A type epoxy resins, 1%-3% acid anhydride type curing agents, 0-1%
Methyl miaow sound of crying or vomiting, 4%-6% butyl acetates, 1%-2% reactive diluents, tetraethyl titanate, 0-1% polyamide waxes be well mixed,
It is placed in 145-155 DEG C of baking oven drying 1.5-2.5h；
S2, by dried material and the molten acid anhydride acetic acid esters of butyl, butyl acetate, diethylene glycol ether acetic acid
Ester, isophorone, titanium dioxide and bismuth oxide mixing, then roll after slurry 25 times with three-roll grinder that to obtain fineness be below 12mm's
Back side silver paste.
Embodiment described above only expresses the embodiment of the present invention, and it describes more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.
Claims (4)
1. a kind of silver-colored conductive silver paste composition of the novel solar battery back of the body, it is characterised in that include the original of following mass percent
Material：
78%-82% silver powder, 8%-12% bisphenol A type epoxy resins, 1%-3% acid anhydride type curing agents, 0-1% methyl miaows sound of crying or vomiting,
4%-6% butyl acetates, 1%-2% reactive diluents, tetraethyl titanate, 0-1% polyamide waxes.
2. a kind of novel solar battery carries on the back silver-colored conductive silver paste composition according to claim 1, it is characterised in that it is also wrapped
Solvent is included, the solvent includes the molten acid anhydride acetic acid esters of butyl, butyl acetate, diethylene glycol ether acetate, different Fo Er
Ketone.
3. a kind of novel solar battery carries on the back silver-colored conductive silver paste composition according to claim 1, it is characterised in that it is also wrapped
Include titanium dioxide and bismuth oxide.
4. a kind of preparation method of the silver-colored conductive silver paste composition of the novel solar battery back of the body, it is characterised in that comprise the following steps：
S1, by 78%-82% silver powder, 8%-12% bisphenol A type epoxy resins, 1%-3% acid anhydride type curing agents, 0-1% methyl
Miaow sound of crying or vomiting, 4%-6% butyl acetates, 1%-2% reactive diluents, tetraethyl titanate, 0-1% polyamide waxes be well mixed, juxtaposition
1.5-2.5h is dried in 145-155 DEG C of baking oven；
S2, by dried material and the molten acid anhydride acetic acid esters of butyl, butyl acetate, diethylene glycol ether acetate, different
Phorone, titanium dioxide and bismuth oxide mixing, then with three-roll grinder roll slurry 25 times after obtain the back side that fineness is below 12mm
Silver paste.