CN107232988A - A kind of stainless steel pan surface treatment method - Google Patents
A kind of stainless steel pan surface treatment method Download PDFInfo
- Publication number
- CN107232988A CN107232988A CN201710479744.XA CN201710479744A CN107232988A CN 107232988 A CN107232988 A CN 107232988A CN 201710479744 A CN201710479744 A CN 201710479744A CN 107232988 A CN107232988 A CN 107232988A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- steel pan
- mesh
- powder
- treatment method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to metallic article technical field, there is provided a kind of stainless steel pan surface treatment method, following steps：Clear water cleaning, drying, air gun cleaning, sandblasting, spraying and solidification, the ceramic paint include the component of following weight：The dicalcium powder of 600 800 mesh, the talcum powder of 700 900 mesh, the whitening powder of 800 900 mesh, the modified starch of 600 1200 mesh, cellulose ether, inorganic adhesive, percentage by weight shared by each component is：Dicalcium powder 40 50%, talcum powder 35 50%, whitening powder 2 5%, modified starch 1 5%, cellulose ether 1 3%, inorganic adhesive 1 3%, the modified starch preparation method is specially：Under stirring operation, powdered modified starch is mixed with adhesive, compound is inserted in forming machine, then gained compound is soaked and whole grain, the product of required shape is pressurizeed at a temperature of 20 50 DEG C；The weight of adhesive is the 1 5% of modified starch weight.The present invention has the advantages that technique is simple, processing cost is low and effect is good.
Description
Technical field
The invention belongs to metallic article technical field, in particular it relates to a kind of stainless steel pan surface treatment method.
Background technology
Traditional stainless steel pan is general in surface treatment all to be handled using polishing mode.
The ceramic lacquer craftwork of new technology-interior painting of stainless steel pan surface treatment has broken traditional pan surface treatment,
The demand to environmental protection is catered to.But for the square roasting basin of stainless steel（Ceramic paint）, add from product design, mold design
The each side such as work, production technology are formulated, special equipment configuration are more complicated than circular pan, and technical difficulty is high, is mainly reflected in following
Aspect：If square pot, pan has 4 angles and development has straight type, oblique type, and this extension to material requires very severe
Carve, a block of material is uniformly extended, it is necessary to when on the design fit dimension of concave-convex mold, stretching on pressure and time control
There is very high requirement.The fastness that the multiple bottom of square pot is bonded takes special process to heat, dedicated templates positioning ensure pot body, aluminium sheet,
The protective plate Trinity, coupled position is without a bit error.Undercoating strictly controls cleannes and crude degree in pot, to spray stream
Face is applied in primary coat when waterline heating-up temperature, baking time and coating spraying and apply three layers, not the thickness and the uniformity of sizing, strictly
Grasp.Polishing, which will be carried out, is surface-treated the process that up to standard and mirror is thrown, it is ensured that outer pot wants burnishing.
The content of the invention
For defect of the prior art, it is an object of the invention to provide a kind of stainless steel pan surface treatment method, tool
Have the advantages that technique is simple, processing cost is low and effect is good.
A kind of stainless steel pan surface treatment method provided according to the present invention, in stainless steel pan surface spraying ceramics
Paint, specifically includes following steps：Clear water cleaning, drying, air gun cleaning, sandblasting, spraying and solidification, the ceramic paint include
The component of following weight：Dicalcium powder, the talcum powder of 700-900 mesh, the whitening powder of 800-900 mesh, the 600-1200 of 600-800 mesh
Purpose modified starch, cellulose ether, inorganic adhesive, percentage by weight shared by each component is：Dicalcium powder 40-50%, talcum powder
35-50%, whitening powder 2-5%, modified starch 1-5%, cellulose ether 1-3%, inorganic adhesive 1-3%, the modified starch
Preparation method is specially：Under stirring operation, powdered modified starch is mixed with adhesive, compound is inserted into forming machine
In, then gained compound is soaked and whole grain, the product of required shape is pressurizeed at a temperature of 20-50 DEG C；Adhesive
Weight is the 1-5% of modified starch weight.
Preferably, the ceramic paint includes bottom and surface layer, and thickness is respectively bottom 36-45um, surface layer 4-6um.
Preferably, the sandblasting uses the corundum or aluminum oxide of 90-110 mesh, and surface sand layer thickness is 13-15 μm, table
Face average roughness Ra is 2.6-3.3 μm.
Preferably, it is described before spraying, stainless steel pan is preheated.
Preferably, it is described to make stainless-steel pan preheating up to 60 DEG C.
Preferably, the solidification includes at least 5min that first volatilized at 40-80 DEG C, is then warming up to 180-200 DEG C and permanent
Temperature solidification 20-25min.
Preferably, the use clear water is washed 2-3 times.
Preferably, the temperature of the drying is 60-80 DEG C.
Compared with prior art, the present invention has following beneficial effect：
（1）The present invention provides a kind of stainless steel pan surface treatment method, and present treatment technique is in preposition processing procedure, using clear
Water cleaning, drying, air gun cleaning, in advance remove the impurity on pan surface, beneficial to later stage spraying process, with technique letter
The single, advantage that processing cost is low and effect is good；
（2）The preparation method of modified starch of the present invention, with following advantage, because product is wetted, dust is not had and is flown
Raise, it is to avoid cause dust pollution, environmental protection；Product be extruded it is blocking after, be difficult crushing, can directly pack, being scattered not had
Grain powder, it is to avoid cause to waste while also functioning to the effect for reducing pollution；, can in transportation after product is extruded together
It is neat to stack, crushing is difficult, space-consuming is reduced；
（3）Sandblasting of the present invention uses diamond dust, diamond dust also known as it is pure be clear crystal.Density, hardness is very big, about Mohs
9.5 degree.General is colourless powder particle.After grinding, grounds travel can be made, can polishing paper processed, again can emery wheel and whetslate processed
Friction surface.It is placed on by sand and appropriate carbon in electric furnace and strengthens hot be made.Natural emery also known as garnet, are silicate
Class mineral.Sort, be machined by waterpower, the grinding-material that the method such as sieving and grading is made.Sandblasting is carried out using diamond dust
The impurity of stainless steel surfaces can be removed, beneficial to spraying process below.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.It should be understood that these embodiments are merely to illustrate the present invention
Rather than limitation the scope of the present invention.
Embodiment 1
A kind of stainless steel pan surface treatment method that the present embodiment is provided, in stainless steel pan surface spraying ceramic paint, specifically
Comprise the following steps：Clear water cleaning, drying, air gun cleaning, sandblasting, spraying and solidification, the ceramic paint include following weight
The component of amount：The dicalcium powder of 800 mesh, the talcum powder of 700 mesh, the whitening powder of 900 mesh, the modified starch of 600 mesh, cellulose ether,
Inorganic adhesive, percentage by weight shared by each component is：Dicalcium powder 50%, talcum powder 35%, whitening powder 5%, modified starch
1%th, cellulose ether 3%, inorganic adhesive 1%, the modified starch preparation method is specially：Under stirring operation, by powder
Shape modified starch is mixed with adhesive, and compound is inserted in forming machine, then gained compound is soaked and whole grain, 50
The product of required shape is pressurizeed at a temperature of DEG C；The weight of adhesive is the 1% of modified starch weight.
Preferably, the ceramic paint includes bottom and surface layer, and thickness is respectively bottom 45um, surface layer 4um.Bottom
More than the adhesion effect that surface layer can increase ware.
Preferably, the sandblasting uses the corundum or aluminum oxide of 110 mesh, and surface sand layer thickness is 13 μm, table
Face average roughness Ra is 3.3 μm.Using diamond dust, diamond dust also known as it is pure be clear crystal.Density, hardness is very big, about
It is 9.5 degree of Mohs.General is colourless powder particle.After grinding, grounds travel can be made, can polishing paper processed, again can emery wheel processed
With the friction surface of whetslate.It is placed on by sand and appropriate carbon in electric furnace and strengthens hot be made.Natural emery also known as garnet, be
Silicates mineral.Sort, be machined by waterpower, the grinding-material that the method such as sieving and grading is made.Entered using diamond dust
Row sandblasting can remove the impurity of stainless steel surfaces, beneficial to spraying process below.
Preferably, it is described before spraying, stainless steel pan is preheated.Beneficial to japanning.
Preferably, it is described to make stainless-steel pan preheating up to 60 DEG C.Beneficial to japanning.
Preferably, the solidification includes at least 5min that first volatilized at 80 DEG C, is then warming up to 180 DEG C and permanent
Temperature solidification 25min.
Preferably, the use clear water is washed 3 times.The impurity on pan surface is fully washed off, beneficial to finishing operations
Carry out.
Preferably, the temperature of the drying is 60 DEG C.
Embodiment 2
A kind of stainless steel pan surface treatment method that the present embodiment is provided, in stainless steel pan surface spraying ceramic paint, specifically
Comprise the following steps：Clear water cleaning, drying, air gun cleaning, sandblasting, spraying and solidification, the ceramic paint include following weight
The component of amount：The dicalcium powder of 600 mesh, the talcum powder of 900 mesh, the whitening powder of 800 mesh, the modified starch of 1200 mesh, cellulose ether,
Inorganic adhesive, percentage by weight shared by each component is：Dicalcium powder 40%, talcum powder 50%, whitening powder 2%, modified starch
5%th, cellulose ether 1%, inorganic adhesive 3%, the modified starch preparation method is specially：Under stirring operation, by powder
Shape modified starch is mixed with adhesive, and compound is inserted in forming machine, then gained compound is soaked and whole grain, 20
The product of required shape is pressurizeed at a temperature of DEG C；The weight of adhesive is the 5% of modified starch weight.
Preferably, the ceramic paint includes bottom and surface layer, and thickness is respectively bottom 36um, surface layer 6um.Bottom
More than the adhesion effect that surface layer can increase ware.
Preferably, the sandblasting uses the corundum of 90 mesh, and surface sand layer thickness is 15 μm, surface average roughness
It is 2.6 μm to spend Ra.Using diamond dust, diamond dust also known as it is pure be clear crystal.Density, hardness is very big, about Mohs 9.5
Degree.General is colourless powder particle.After grinding, grounds travel can be made, can polishing paper processed, again can emery wheel and whetslate processed rub
Wipe surface.It is placed on by sand and appropriate carbon in electric furnace and strengthens hot be made.Natural emery also known as garnet, are silicates ore deposit
Thing.Sort, be machined by waterpower, the grinding-material that the method such as sieving and grading is made.Carrying out sandblasting using diamond dust can remove
The impurity of stainless steel surfaces is removed, beneficial to spraying process below.
Preferably, it is described before spraying, stainless steel pan is preheated.Beneficial to japanning.
Preferably, it is described to make stainless-steel pan preheating up to 60 DEG C.Beneficial to japanning.
Preferably, the solidification includes at least 5min that first volatilized at 40 DEG C, is then warming up to 200 DEG C and permanent
Temperature solidification 20min.
Preferably, the use clear water is washed 2 times.The impurity on pan surface is fully washed off, beneficial to finishing operations
Carry out.
Preferably, the temperature of the drying is 80 DEG C.
Embodiment 3
A kind of stainless steel pan surface treatment method that the present embodiment is provided, in stainless steel pan surface spraying ceramic paint, specifically
Comprise the following steps：Clear water cleaning, drying, air gun cleaning, sandblasting, spraying and solidification, the ceramic paint include following weight
The component of amount：The dicalcium powder of 700 mesh, the talcum powder of 800 mesh, the whitening powder of 850 mesh, the modified starch of 900 mesh, cellulose ether,
Inorganic adhesive, percentage by weight shared by each component is：Dicalcium powder 45%, talcum powder 38%, whitening powder 4%, modified starch
3%th, cellulose ether 2%, inorganic adhesive 2%, the modified starch preparation method is specially：Under stirring operation, by powder
Shape modified starch is mixed with adhesive, and compound is inserted in forming machine, then gained compound is soaked and whole grain, 40
The product of required shape is pressurizeed at a temperature of DEG C；The weight of adhesive is the 4% of modified starch weight.
Preferably, the ceramic paint includes bottom and surface layer, and thickness is respectively bottom 43um, surface layer 5um.Bottom
More than the adhesion effect that surface layer can increase ware.
Preferably, the sandblasting uses the corundum or aluminum oxide of 95 mesh, and surface sand layer thickness is 14 μm, surface
Average roughness Ra is 2.8 μm.Using diamond dust, diamond dust also known as it is pure be clear crystal.Density, hardness is very big, is about
9.5 degree of Mohs.General is colourless powder particle.After grinding, grounds travel can be made, can polishing paper processed, again can emery wheel processed and
The friction surface of whetslate.It is placed on by sand and appropriate carbon in electric furnace and strengthens hot be made.Natural emery also known as garnet, are silicon
Barbiturates mineral.Sort, be machined by waterpower, the grinding-material that the method such as sieving and grading is made.Carried out using diamond dust
Sandblasting can remove the impurity of stainless steel surfaces, beneficial to spraying process below.
Preferably, it is described before spraying, stainless steel pan is preheated.Beneficial to japanning.
Preferably, it is described to make stainless-steel pan preheating up to 60 DEG C.Beneficial to japanning.
Preferably, the solidification includes at least 5min that first volatilized at 46 DEG C, is then warming up to 190 DEG C and permanent
Temperature solidification 24min.
Preferably, the use clear water is washed 3 times.The impurity on pan surface is fully washed off, beneficial to finishing operations
Carry out.
Preferably, the temperature of the drying is 70 DEG C.
Embodiment 4
A kind of stainless steel pan surface treatment method that the present embodiment is provided, in stainless steel pan surface spraying ceramic paint, specifically
Comprise the following steps：Clear water cleaning, drying, air gun cleaning, sandblasting, spraying and solidification, the ceramic paint include following weight
The component of amount：The dicalcium powder of 700 mesh, the talcum powder of 750 mesh, the whitening powder of 850 mesh, the modified starch of 700 mesh, cellulose ether,
Inorganic adhesive, percentage by weight shared by each component is：Dicalcium powder 48%, talcum powder 37%, whitening powder 3%, modified starch
3%th, cellulose ether 2%, inorganic adhesive 2%, the modified starch preparation method is specially：Under stirring operation, by powder
Shape modified starch is mixed with adhesive, and compound is inserted in forming machine, then gained compound is soaked and whole grain, 26
The product of required shape is pressurizeed at a temperature of DEG C；The weight of adhesive is the 4% of modified starch weight.
Preferably, the ceramic paint includes bottom and surface layer, and thickness is respectively bottom 39um, surface layer 5um.
Preferably, the sandblasting uses the corundum or aluminum oxide of 98 mesh, and surface sand layer thickness is 14 μm, surface
Average roughness Ra is 3.1 μm.
Preferably, it is described before spraying, stainless steel pan is preheated.
Preferably, it is described to make stainless-steel pan preheating up to 60 DEG C.
Preferably, the solidification includes at least 5min that first volatilized at 44 DEG C, is then warming up to 190 DEG C and permanent
Temperature solidification 22min.
Preferably, the use clear water is washed 2 times.
Preferably, the temperature of the drying is 63 DEG C.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of stainless steel pan surface treatment method, it is characterised in that：In stainless steel pan surface spraying ceramic paint, specific bag
Include following steps：Clear water cleaning, drying, air gun cleaning, sandblasting, spraying and solidification, the ceramic paint include following weight
Component：The dicalcium powder of 600-800 mesh, the talcum powder of 700-900 mesh, the whitening powder of 800-900 mesh, the modification of 600-1200 mesh
Starch, cellulose ether, inorganic adhesive, percentage by weight shared by each component is：Dicalcium powder 40-50%, talcum powder 35-50%,
Whitening powder 2-5%, modified starch 1-5%, cellulose ether 1-3%, inorganic adhesive 1-3%, the modified starch preparation method
Specially：Under stirring operation, powdered modified starch is mixed with adhesive, compound is inserted in forming machine, then to institute
Obtain compound to be soaked and whole grain, the product of required shape is pressurizeed at a temperature of 20-50 DEG C；The weight of adhesive is modification
The 1-5% of starch weight.
2. stainless steel pan surface treatment method according to claim 1, it is characterised in that：The ceramic paint includes bottom
And surface layer, thickness is respectively bottom 36-45um, surface layer 4-6um.
3. stainless steel pan surface treatment method according to claim 1, it is characterised in that：The sandblasting uses 90-110
Purpose corundum or aluminum oxide, surface sand layer thickness are 13-15 μm, and surface average roughness Ra is 2.6-3.3 μm.
4. stainless steel pan surface treatment method according to claim 1, it is characterised in that：It is described before spraying, to not
Rust steel pan is preheated.
5. stainless steel pan surface treatment method according to claim 4, it is characterised in that：It is described to preheat stainless-steel pan
Up to 60 DEG C.
6. stainless steel pan surface treatment method according to claim 5, it is characterised in that：The solidification includes first existing
Volatilize at least 5min at 40-80 DEG C, is then warming up to 180-200 DEG C and isothermal curing 20-25min.
7. stainless steel pan surface treatment method according to claim 1, it is characterised in that：The use clear water washes 2-3
It is secondary.
8. stainless steel pan surface treatment method according to claim 1, it is characterised in that：The temperature of the drying is
60-80℃。