CN106760283A - The preparation method of ornamental glass fibre prickling plate - Google Patents

The preparation method of ornamental glass fibre prickling plate Download PDF

Info

Publication number
CN106760283A
CN106760283A CN201611148030.2A CN201611148030A CN106760283A CN 106760283 A CN106760283 A CN 106760283A CN 201611148030 A CN201611148030 A CN 201611148030A CN 106760283 A CN106760283 A CN 106760283A
Authority
CN
China
Prior art keywords
glass fibre
decoration
plate
prickling
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611148030.2A
Other languages
Chinese (zh)
Inventor
周致中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUXI CITY MINGJIANG INSULATION MATERIAL CO Ltd
Original Assignee
WUXI CITY MINGJIANG INSULATION MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI CITY MINGJIANG INSULATION MATERIAL CO Ltd filed Critical WUXI CITY MINGJIANG INSULATION MATERIAL CO Ltd
Priority to CN201611148030.2A priority Critical patent/CN106760283A/en
Publication of CN106760283A publication Critical patent/CN106760283A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of preparation method of ornamental glass fibre prickling plate, belong to heat preservation technology field.It passes through to be chopped, shredding compacting and heat treatment are obtained product decoration glass fibre acupuncture board.Ornamental glass fibre prickling plate prepared by the present invention has the advantages that insulation, decoration, sound insulation, sound-absorbing, waterproof, fire-retardant, mould proof, mothproof, scrubbing resistance simultaneously, and surface recombination bunting and insulation quilt are integrated using needling process.Inner wall of building is fixed on support member once complete inside holding and decoration use.Save man hour of labour and substantial amounts of organic binder bond.

Description

The preparation method of ornamental glass fibre prickling plate
Technical field
The present invention relates to a kind of preparation method of ornamental glass fibre prickling plate, belong to heat preservation technology field.
Background technology
Insulation material generally refers to material of the thermal conductivity factor less than or equal to 0.2.Insulation material have developed rapidly, industry and Good heat preservation technology and material are used in building, can often be played a multiplier effect.One ton of ore deposit is often used in building Thing cotton insulating product, can save one ton of oil for 1 year.
In current indoor heat insulating and decorative overlay material, it is made up of two parts respectively：Building inside holding is by building Company undertakes, and is repaired on the basis of heat insulating inner wall layer by decoration corporation after building payment, then with substantial amounts of organic Ornamental wall covering fabric is covered in insulation layer surface by binding agent.Technology above has used substantial amounts of binding agent, typically often puts down Square 0.5 ~ 1kg of rice, it is not only time-consuming but also take material.
The content of the invention
It is an object of the present invention to overcome the above deficiencies, there is provided a kind of preparation side of ornamental glass fibre prickling plate Method.
According to the technical scheme that the present invention is provided, the preparation method of ornamental glass fibre prickling plate, step is as follows：
（1）It is chopped：In mass ratio 8 ~ 10：1 prepares alkali-free glass fibre yarn and polypropylene fibre, and it is chopped；Wherein without Alkali containing glass fibre yarn is cut into the short silk of 50 ~ 70mm, and polypropylene fibre is cut into the short silk of 50 ~ 70mm, both are well mixed；
（2）Shredding is suppressed：To step（1）Gained composite fibre carries out shredding with opener, then is combed into by carding machine uniform thin Layer, then carry out lapping repeatedly, compacting, needing machine is counter pierces, finally on its surface, covering contains the decoration embryo cloth of polyester fiber, then carries out Positive thorn, cutting is batched coiled；
（3）Heat treatment：By step（2）Gained raw material in heat-treatment furnace with 140 ~ 180 DEG C carry out elastic cure process 5 ~ 10min；Using printing technology, pattern needed for the surface printing in decorative panel obtains final product product decoration glass fibre acupuncture board.
A diameter of 8 ~ 10 μm of the alkali-free glass fibre yarn；Polypropylene fibre diameter is below 5 μm.
Beneficial effects of the present invention：The present invention prepare ornamental glass fibre prickling plate simultaneously have insulation, decoration, every The advantages of sound, sound-absorbing, waterproof, fire-retardant, mould proof, mothproof, scrubbing resistance, using needling process by surface recombination bunting and insulation quilt It is integrated.Inner wall of building is fixed on support member once complete inside holding and decoration use.Save man hour of labour and a large amount of Organic binder bond.
Specific embodiment
The preparation method of the ornamental glass fibre prickling plate of embodiment 1, step is as follows：
（1）It is chopped：In mass ratio 9：1 prepares alkali-free glass fibre yarn and polypropylene fibre, and it is chopped；Wherein alkali-free glass Glass silvalin is cut into the short silk of 50mm, and polypropylene fibre is cut into the short silk of 50mm, both are well mixed；
（2）Shredding is suppressed：To step（1）Gained composite fibre carries out shredding with opener, then is combed into by carding machine uniform thin Layer, then carry out lapping repeatedly, compacting, needing machine is counter pierces, finally on its surface, covering contains the decoration embryo cloth of polyester fiber, then carries out Positive thorn, cutting is batched coiled；
（3）Heat treatment：By step（2）Gained raw material carries out elastic cure process 10min in heat-treatment furnace with 140 DEG C；Using Printing technology, pattern needed for the surface printing in decorative panel.
A diameter of 8 μm of the alkali-free glass fibre yarn；Polypropylene fibre diameter is below 5 μm.
It is as follows that embodiment 1 prepares products obtained therefrom ornamental glass fibre prickling plate technique index：Appearance and size：600mm wide, Thick 5mm, 5m long；Density：<1400g/m2)；Thermal conductivity factor：0.042W/m·K；Physical and chemical performance：Acid and alkali-resistance；Hygroscopicity：0.1g/ m2；Water imbibition：< 1%；Tensile strength：150KPa（75*230*20）；Acoustic absorptivity：0.1~0.2.
The preparation method of the ornamental glass fibre prickling plate of embodiment 2, step is as follows：
（1）It is chopped：In mass ratio 10：1 prepares alkali-free glass fibre yarn and polypropylene fibre, and it is chopped；Wherein alkali-free Glass fiber yarn is cut into the short silk of 70mm, and polypropylene fibre is cut into the short silk of 70mm, both are well mixed；
（2）Shredding is suppressed：To step（1）Gained composite fibre carries out shredding with opener, then is combed into by carding machine uniform thin Layer, then carry out lapping repeatedly, compacting, needing machine is counter pierces, finally on its surface, covering contains the decoration embryo cloth of polyester fiber, then carries out Positive thorn, cutting is batched coiled；
（3）Heat treatment：By step（2）Gained raw material carries out elastic cure process 5min in heat-treatment furnace with 180 DEG C；Using print Flower process, pattern needed for the surface printing in decorative panel.
A diameter of 10 μm of the alkali-free glass fibre yarn；Polypropylene fibre diameter is below 5 μm.
It is as follows that embodiment 2 prepares products obtained therefrom ornamental glass fibre prickling plate technique index：Appearance and size：800mm wide, Thick 10mm, 10m long；Density：<1600g/m2；Thermal conductivity factor：0.042+0.00017W/m·K；Physical and chemical performance：Acid and alkali-resistance；Moisture absorption Property：0.1g/m2；Water imbibition：<1%；Tensile strength：150KPa（75*230*20）；Acoustic absorptivity：0.1~0.2.
The preparation method of the ornamental glass fibre prickling plate of embodiment 3, step is as follows：
（1）It is chopped：In mass ratio 9：1 prepares alkali-free glass fibre yarn and polypropylene fibre, and it is chopped；Wherein alkali-free glass Glass silvalin is cut into the short silk of 60mm, and polypropylene fibre is cut into the short silk of 60mm, both are well mixed；
（2）Shredding is suppressed：To step（1）Gained composite fibre carries out shredding with opener, then is combed into by carding machine uniform thin Layer, then carry out lapping repeatedly, compacting, needing machine is counter pierces, finally on its surface, covering contains the decoration embryo cloth of polyester fiber, then carries out Positive thorn, cutting is batched coiled；
（3）Heat treatment：By step（2）Gained raw material carries out elastic cure process 8min in heat-treatment furnace with 160 DEG C；Using print Flower process, pattern needed for the surface printing in decorative panel.
A diameter of 9 μm of the alkali-free glass fibre yarn；Polypropylene fibre diameter is below 5 μm.
It is as follows that embodiment 3 prepares products obtained therefrom ornamental glass fibre prickling plate technique index：Appearance and size：700mm wide, Thick 8mm, 8m long；Density：<1500g/m2)；Thermal conductivity factor：0.042+0.00015W/m·K；Physical and chemical performance：Acid and alkali-resistance；Moisture absorption Property：0.1g/m2；Water imbibition：<1%；Tensile strength：150KPa（75*230*20）；Acoustic absorptivity：0.1~0.2.

Claims (2)

1. the preparation method of ornamental glass fibre prickling plate, it is characterized in that step is as follows：
（1）It is chopped：In mass ratio 8 ~ 10：1 prepares alkali-free glass fibre yarn and polypropylene fibre, and it is chopped；Wherein without Alkali containing glass fibre yarn is cut into the short silk of 50 ~ 70mm, and polypropylene fibre is cut into the short silk of 50 ~ 70mm, both are well mixed；
（2）Shredding is suppressed：To step（1）Gained composite fibre carries out shredding with opener, then is combed into by carding machine uniform thin Layer, then carry out lapping repeatedly, compacting, needing machine is counter pierces, finally on its surface, covering contains the decoration embryo cloth of polyester fiber, then carries out Positive thorn, cutting is batched coiled；
（3）Heat treatment：By step（2）Gained raw material in heat-treatment furnace with 140 ~ 180 DEG C carry out elastic cure process 5 ~ 10min；Using printing technology, pattern needed for the surface printing in decorative panel obtains final product product decoration glass fibre acupuncture board.
2. the preparation method of ornamental glass fibre prickling plate as claimed in claim 1, it is characterized in that：The alkali-free glass fibre Yarn diameter is 8 ~ 10 μm；Polypropylene fibre diameter is below 5 μm.
CN201611148030.2A 2016-12-13 2016-12-13 The preparation method of ornamental glass fibre prickling plate Pending CN106760283A (en)