CN106637623A - 200D jacquard fabric for outer-cover of automobile interior decoration - Google Patents
200D jacquard fabric for outer-cover of automobile interior decoration Download PDFInfo
- Publication number
- CN106637623A CN106637623A CN201610977900.0A CN201610977900A CN106637623A CN 106637623 A CN106637623 A CN 106637623A CN 201610977900 A CN201610977900 A CN 201610977900A CN 106637623 A CN106637623 A CN 106637623A
- Authority
- CN
- China
- Prior art keywords
- temperature
- fabric
- needle
- dye vat
- speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of process technology of automobile lining, in particular to a 200D jacquard fabric for outer-cover of automobile interior decoration, which comprises the following technology: the first step, weaving a fabric; the second step, water washing a dye vat for pretreatment; the third step, shaping for aftertreatment. The 200D jacquard fabric for outer-cover of automobile interior decoration has the advantages that the 200D jacquard fabric can make the basic fabric meet the requirements of tension, tear and tensile strength of a static load through changing the traditional knitting technology needles and the shaping technology for aftertreatment, but also reduce the weight and thickness and the use cost.
Description
Technical field
The present invention relates to inner lining of automobile Technology field, is particularly used for the 200D jacquard weaves of automotive trim epidermis
Cloth.
Background technology
Automotive trim (Automotive Interior) is primarily referred to as the used automobile product of automotive interior repacking, relates to
And to the every aspect of automotive interior, such as automobile steering wheel cover, automobile cushion, automatic foot-mat, automobile perfume, automobile pendant,
Internal goods of furniture for display rather than for use, containing box etc. are all automotive trim products.Automotive trim described in our country, in fact in English
Interiors System.Because this partial automobile parts has certain dicoration, so common at present in the industry turn over
Translate and be all called " automotive trim ".But from English " Interiors ", we it is known that, this parts thereof not only only has
Decoration function, the feature, safety and engineering attribute involved by them is very abundant.Wherein automotive trim table
Dermatome must have specific pulling force, tear and static load tensile strength according to different automobile types, and other specific physical property are required,
In Japanese auto project interior trim epidermis, need to such as reach physical property requirement and quality is qualified, the base fabric for using must will reach corresponding
Physical property standard specification, traditional handicraft appears in when meeting pulling force, tear and the physical property such as static load tensile strength and requiring, exists
Grammes per square metre lays particular stress on, thickness is bigger than normal, the higher situation of corresponding production cost.
Based on above reason, the new base fabric for automotive trim epidermis is needed to be devised, by changing to raw material
Enter, weaving process, the lifting of postfinishing process, develop meet Japanese auto project interior trim epidermis base fabric pulling force, tear and
While static load tensile strength, have in grammes per square metre and thickness and be significantly improved, reduce the cost of client, i.e., for automobile
The 200D tmaterials of interior trim epidermis.
The content of the invention
In order to solve the technical problem that above-mentioned existing facecloth technique is present, the present invention is provided to automotive trim epidermis
200D tmaterials.
The technical solution adopted for the present invention to solve the technical problems is：
For the 200D tmaterials of automotive trim epidermis, including following technique：
The first step：Fabric is weaved.
Raw material：200D/96F DTY low stretch yarns；
Weaving board size：30 inches of diameter；
Knitting needle：Pin number is 18 pins/inch, and total needle amount is 1740 pieces；
Yarn is long：First and third ... the four ten one a length of 18cm/50 pins of road yarn, second, four ... four ten two road yarns are a length of
18.5cm/50 pins, 12 one group of tunnels, by that analogy.
Pricking with needle technique：
The mode of pricking with needle be ABCD, BADC, ABDC, by that analogy.
Second step：Pre-treatment dye vat is washed；
1) fabric enters dye vat；
2) dye vat temperature is set as 120 DEG C, and the speed that heats up is 2 DEG C/min, and temperature retention time is 30 minutes, and temperature retention time is arrived, and is opened
Begin to lower the temperature, cooling speed is 3 DEG C/min, and to room temperature cylinder is gone out；
3) cleaning machine is cleaned 2 times；
4) processed is carried out with dewaterer；
3rd step：Post processing is shaped；
1) punishment in advance is processed, and is carried out from fire retardant 509 or hydrophilic silicone oil finishing agent or stiffening agent SST according to order demand
Material process.
2) heat treatment, Uneven Width width is set as 172cm during sizing, and oven temperature is 190 DEG C, and rotation speed of fan is 1000
Rev/min, speed is 30M/ minutes, overfeeding 16 of shaping, and shape thickness 0.48-0.52mm.
3) finished product clot is processed.
The invention has the beneficial effects as follows：The present invention be by changing traditional knitting pricking with needle and Final finishing setting process,
Make epidermis base fabric to meet pulling force, tear and static load tensile strength to require, reduction grammes per square metre and thickness can be reached again.Reduce
Use cost.
Description of the drawings
With reference to the accompanying drawings and examples the present invention is further described.
Fig. 1 is the knitting flow chart making of facecloth in the present invention；
Fig. 2 is pre-treatment dye vat washing process schematic diagram of the present invention；
Fig. 3 is post processing sizing schematic flow sheet of the present invention.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, it is right below in conjunction with drawings and Examples
The present invention is further elaborated.It should be appreciated that specific embodiment described herein is only to explain the present invention, and
It is not used in the restriction present invention.
As shown in Figure 1-Figure 3, the 200D tmaterials for automotive trim epidermis of the present invention, including following technique：
The first step：Fabric is weaved.
Raw material：200D/96F DTY low stretch yarns；
Weaving board size：30 inches of diameter；
Knitting needle：Pin number is 18 pins/inch, and total needle amount is 1740 pieces；
Yarn is long：First and third ... the four ten one a length of 18cm/50 pins of road yarn, second, four ... four ten two road yarns are a length of
18.5cm/50 pins, 12 one group of tunnels, by that analogy.
Pricking with needle technique：
The mode of pricking with needle be ABCD, BADC, ABDC, by that analogy.
Second step：Pre-treatment dye vat is washed；
1) fabric enters dye vat；
2) dye vat temperature is set as 120 DEG C, and the speed that heats up is 2 DEG C/min, and temperature retention time is 30 minutes, and temperature retention time is arrived, and is opened
Begin to lower the temperature, cooling speed is 3 DEG C/min, and to room temperature cylinder is gone out；
3) cleaning machine is cleaned 2 times；
4) processed is carried out with dewaterer；
3rd step：Post processing is shaped；
1) punishment in advance is processed, and is carried out from fire retardant 509 or hydrophilic silicone oil finishing agent or stiffening agent SST according to order demand
Material process.
2) heat treatment, Uneven Width width is set as 172cm during sizing, and oven temperature is 190 DEG C, and rotation speed of fan is 1000
Rev/min, speed is 30M/ minutes, overfeeding 16 of shaping, and shape thickness 0.48-0.52mm.
3) finished product clot is processed.
Ultimate principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not restricted to the described embodiments, the simply explanation described in above-described embodiment and description this
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes
Change and improvement is both fallen within scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (1)
1. the 200D tmaterials of automotive trim epidermis are used for, it is characterised in that including following technique：
The first step：Fabric is weaved.
Raw material：200D/96F DTY low stretch yarns；
Weaving board size：30 inches of diameter；
Knitting needle：Pin number is 18 pins/inch, and total needle amount is 1740 pieces；
Yarn is long：First and third ... the four ten one a length of 18cm/50 pins of road yarn, second, four ... the four ten two a length of 18.5cm/50 of road yarn
Pin, 12 one group of tunnels, by that analogy.
Pricking with needle technique：
The mode of pricking with needle be ABCD, BADC, ABDC, by that analogy.
Second step：Pre-treatment dye vat is washed；
1) fabric enters dye vat；
2) dye vat temperature is set as 120 DEG C, and the speed that heats up is 2 DEG C/min, and temperature retention time is 30 minutes, and temperature retention time is arrived, and starts drop
Temperature, cooling speed is 3 DEG C/min, and to room temperature cylinder is gone out；
3) cleaning machine is cleaned 2 times；
4) processed is carried out with dewaterer；
3rd step：Post processing is shaped；
1) punishment in advance is processed, and is carried out at punishment in advance from fire retardant 509 or hydrophilic silicone oil finishing agent or stiffening agent SST according to order demand
Reason.
2) heat treatment, Uneven Width width is set as 172cm during sizing, and oven temperature is 190 DEG C, and rotation speed of fan is 1000 revs/min
Clock, speed is 30M/ minutes, overfeeding 16 of shaping, and shape thickness 0.48-0.52mm.
3) finished product clot is processed.