CN106542049A - A kind of impacting type quickly casts anchor release device - Google Patents
A kind of impacting type quickly casts anchor release device Download PDFInfo
- Publication number
- CN106542049A CN106542049A CN201611167951.3A CN201611167951A CN106542049A CN 106542049 A CN106542049 A CN 106542049A CN 201611167951 A CN201611167951 A CN 201611167951A CN 106542049 A CN106542049 A CN 106542049A
- Authority
- CN
- China
- Prior art keywords
- cooled
- air
- arc crotch
- metal coating
- resistance metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The release device the invention discloses a kind of impacting type quickly casts anchor, including fixed seat, fixed seat is rectangular structure, U-shaped hole is offered along fixed seat length direction one end, in U-shaped hole, arc crotch is set, fixed seat, arc crotch are sequentially passed through by bearing pin makes arc crotch rotate by axis of bearing pin, and chain lock chambers of casting anchor are formed between arc crotch and fixed seat；Be provided with the buckle that can be rotated in fixed seat centre position, arc crotch away from bearing pin one end be clasped.
Description
Technical field
The present invention relates to release device of casting anchor, specifically a kind of impacting type quickly casts anchor release device.
Background technology
With developing rapidly for ship, on many ships, simple and fast need to be set up on the basis of existing anchor-handling equipment
Release device, for some inland rivers and intercoastal specific ship type, the towing gear that casts anchor outfit is relatively low, without supporting hydraulic system
Actually used situation it is more, be badly in need of a kind of simple quick anchoring apparatus, improve work efficiency.
The content of the invention
The technical problem to be solved is, for the shortcoming of above prior art, proposes that a kind of impacting type is quick
Cast anchor release device, make simple, operating aspect, be easy to carry, cast anchor quick, use range extensively, improve work efficiency, drop
Low cost, long service life are safe and reliable.
In order to solve above-mentioned technical problem, the technical scheme is that what is be accomplished by：A kind of impacting type
Quickly cast anchor release device, including fixed seat, fixed seat is rectangular structure, offers U-shaped along fixed seat length direction one end
Hole, arranges arc crotch in U-shaped hole, and sequentially passing through fixed seat, arc crotch by bearing pin makes arc crotch with bearing pin as axis
Rotate, between arc crotch and fixed seat, form chain lock chambers of casting anchor；
Be provided with the buckle that can be rotated in fixed seat centre position, arc crotch away from bearing pin one end be clasped.
So, by technical scheme, arc crotch freely can be rotated, when need pinning cast anchor chain when, only
Then buckle is bitten arc crotch one end, and then locks the chain that casts anchor, realized quick through chain lock chambers of casting anchor by the chain that will need to cast anchor
Anchor is pinned, only buckle need to be tapped with external force when needing to cast anchor, make arc crotch depart to fall buckle and be capable of achieving quickly to cast anchor, greatly
Work efficiency is improve greatly, the simple structure, easy to operate, low cost.
The technical scheme that further limits of the present invention is：
Aforesaid impacting type quickly casts anchor release device, and buckle is rectangular configuration, and buckle centre position offers card apertured, buckle
It is connected with fixed seat by connecting rod, such setting structure is simple, easy to process, cost-effective.
Aforesaid impacting type quickly casts anchor release device, offers installing hole away from one end of U-shaped hole in fixed seat, installs
Hole is directly Φ 50-80mm, so can be capable of achieving fixed seat through installing hole by steel wire and fix, it is to avoid seat fixation is outer
Power is dragged away, improves the safety and reliability of the device.
Aforesaid impacting type quickly casts anchor release device, and the component of coating is by mass percentage：C：0.16%, Co：
0.63%, Ti：0.21%, Cu：0.75%, Cr：4.72%, Ni：0.12%, V：0.22%, balance of Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1140 DEG C, be incubated 5h, be then air cooled to 820
DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C, using water-cooled
Steel plate is cooled to into 320 DEG C with the cooldown rate of 18 DEG C/s, room temperature is then air cooled to；
Step（2）：Then arc crotch and buckle are heated to 550 DEG C by configuration rub resistance metal coating powder, equal to its surface
Even spraying rub resistance metal coating, after thickness is 0.5mm, keeps 3h, is then air cooled to room temperature.
Aforesaid impacting type quickly casts anchor release device, and the component of coating is by mass percentage：C：0.19%, Co：
0.65%, Ti：0.23%, Cu：0.77%, Cr：4.79%, Ni：0.15%, V：0.24%, balance of Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1160 DEG C, be incubated 7h, be then air cooled to 830
DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C, using water-cooled
Steel plate is cooled to into 330 DEG C with the cooldown rate of 18 DEG C/s, room temperature is then air cooled to；
Step（2）：Then arc crotch and buckle are heated to 560 DEG C by configuration rub resistance metal coating powder, equal to its surface
Even spraying rub resistance metal coating, after thickness is 0.8mm, keeps 4h, is then air cooled to room temperature.
Aforesaid impacting type quickly casts anchor release device, and the component of coating is by mass percentage：C：0.17%, Co：
0.64%, Ti：0.22%, Cu：0.76%, Cr：4.75%, Ni：0.13%, V：0.23%, balance of Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1150 DEG C, be incubated 6h, be then air cooled to 825
DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C, using water-cooled
Steel plate is cooled to into 325 DEG C with the cooldown rate of 18 DEG C/s, room temperature is then air cooled to；
Step（2）：Then arc crotch and buckle are heated to 556 DEG C by configuration rub resistance metal coating powder, equal to its surface
Even spraying rub resistance metal coating, after thickness is 0.7mm, keeps 3.5h, is then air cooled to room temperature.
The invention has the beneficial effects as follows：Arc crotch freely can be rotated, when need pinning cast anchor chain when, only will need to cast anchor
Then buckle is bitten arc crotch one end, and then locks the chain that casts anchor through chain lock chambers of casting anchor by chain, realizes quick pinning anchor,
Only buckle need to be tapped with external force when needing to cast anchor, make arc crotch depart to fall buckle and be capable of achieving quickly to cast anchor, greatly improve
Work efficiency, the simple structure, easy to operate, low cost；Arrange installing hole can be capable of achieving through installing hole by steel wire
Fixed seat is fixed, it is to avoid seat fixation is dragged away by external force, improves the safety and reliability of the device.
Description of the drawings
Fig. 1 is the front view of the present invention；
Fig. 2 is the structural representation of buckle in the present invention；
Fig. 3 is the structural representation of fixed seat in the present invention；
Wherein：1- fixed seats, 2-U shapes hole, 3- arc crotches, 4- bearing pins, 5- buckles, 6- card apertured, 7- connecting rods, 8- installing holes,
9- casts anchor chain lock chambers.
Specific embodiment
The present invention is described in further detail below：
Embodiment 1
A kind of impacting type that the present embodiment is provided quickly casts anchor release device, including fixed seat 1, and fixed seat 1 is rectangular structure,
U-shaped hole 2 is offered along 1 length direction one end of fixed seat, arc crotch 3 is set in U-shaped hole 2, fixation is sequentially passed through by bearing pin 4
Seat 1, arc crotch 3 makes arc crotch 3 rotate by axis of bearing pin 4, and the chain lock that casts anchor is formed between arc crotch 3 and fixed seat 1
Tight chamber 9；
The buckle 5 that can be rotated is provided with 1 centre position of fixed seat, arc crotch 3 is coordinated with buckle 5 away from one end of bearing pin 4；Card
5 are detained for rectangular configuration, 5 centre position of buckle offers card apertured 6, and buckle 5 is connected with fixed seat 1 by connecting rod 7；In fixed seat
1 offers installing hole 8 away from one end of U-shaped hole 2, and installing hole 8 is directly Φ 50mm, can so pass through steel wire through installing hole
It is capable of achieving fixed seat to fix, it is to avoid seat fixation is dragged away by external force, improves the safety and reliability of the device.
The component of its floating coat is by mass percentage：C：0.16%, Co：0.63%, Ti：0.21%, Cu：0.75%, Cr：
4.72%, Ni：0.12%, V：0.22%, balance of Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1140 DEG C, be incubated 5h, be then air cooled to 820
DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C, using water-cooled
Steel plate is cooled to into 320 DEG C with the cooldown rate of 18 DEG C/s, room temperature is then air cooled to；
Step（2）：Then arc crotch and buckle are heated to 550 DEG C by configuration rub resistance metal coating powder, equal to its surface
Even spraying rub resistance metal coating, after thickness is 0.5mm, keeps 3h, is then air cooled to room temperature.
Embodiment 2
A kind of impacting type that the present embodiment is provided quickly casts anchor release device, the structure as the structure in embodiment 1, wherein
The component of coating is by mass percentage：C：0.19%, Co：0.65%, Ti：0.23%, Cu：0.77%, Cr：4.79%, Ni：
0.15%, V：0.24%, balance of Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1160 DEG C, be incubated 7h, be then air cooled to 830
DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C, using water-cooled
Steel plate is cooled to into 330 DEG C with the cooldown rate of 18 DEG C/s, room temperature is then air cooled to；
Step（2）：Then arc crotch and buckle are heated to 560 DEG C by configuration rub resistance metal coating powder, equal to its surface
Even spraying rub resistance metal coating, after thickness is 0.8mm, keeps 4h, is then air cooled to room temperature.
Embodiment 3
A kind of impacting type that the present embodiment is provided quickly casts anchor release device, the structure as the structure in embodiment 1, wherein
The component of coating is by mass percentage：C：0.17%, Co：0.64%, Ti：0.22%, Cu：0.76%, Cr：4.75%, Ni：
0.13%, V：0.23%, balance of Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1150 DEG C, be incubated 6h, be then air cooled to 825
DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C, using water-cooled
Steel plate is cooled to into 325 DEG C with the cooldown rate of 18 DEG C/s, room temperature is then air cooled to；
Step（2）：Then arc crotch and buckle are heated to 556 DEG C by configuration rub resistance metal coating powder, equal to its surface
Even spraying rub resistance metal coating, after thickness is 0.7mm, keeps 3.5h, is then air cooled to room temperature.
Above example technological thought only to illustrate the invention, it is impossible to which protection scope of the present invention is limited with this, it is every
According to technological thought proposed by the present invention, any change done on the basis of technical scheme, the scope of the present invention is each fallen within
Within.
Claims (6)
1. a kind of impacting type quickly casts anchor release device, it is characterised in that：Including fixed seat（1）, the fixed seat（1）For rectangular
Body structure, along the fixed seat（1）Length direction one end offers U-shaped hole（2）, in the U-shaped hole（2）Arc crotch is set
（3）, by bearing pin（4）Sequentially pass through fixed seat（1）, arc crotch（3）Make arc crotch（3）With bearing pin（4）Rotate for axis,
The arc crotch（3）With fixed seat（1）Between formed and cast anchor chain lock chambers（9）；
In the fixed seat（1）Centre position is provided with the buckle that can be rotated（5）, the arc crotch（3）Away from bearing pin（4）One
End and buckle（5）Coordinate；
The arc crotch is coated with one layer of rub resistance metal coating with snap surface, and the component of the coating is by mass percentage
For：C：0.16-0.19%, Co：0.63-0.65%, Ti：0.21-0.23%, Cu：0.75-0.77%, Cr：4.72-4.79%, Ni：
0.12-0.15%, V：0.22-0.24%, balance of Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1140-1160 DEG C, be incubated 5-7h, then air cooling
To 820-830 DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C,
Adopt water-cooled and steel plate is cooled to into 320-330 DEG C with the cooldown rate of 18 DEG C/s, be then air cooled to room temperature；
Step（2）：Then arc crotch and buckle are heated to 550-560 DEG C, Xiang Qibiao by configuration rub resistance metal coating powder
Face even application rub resistance metal coating, after thickness is 0.5-0.8mm, keeps 3-4h, is then air cooled to room temperature.
2. impacting type according to claim 1 quickly casts anchor release device, it is characterised in that：The buckle（5）For rectangle
Structure, the buckle（5）Centre position offers card apertured（6）, the buckle（5）By connecting rod（7）With fixed seat（1）Even
Connect.
3. impacting type according to claim 1 quickly casts anchor release device, it is characterised in that：In the fixed seat（1）Far
From U-shaped hole（2）One end offer installing hole（8）, the installing hole（8）Directly be Φ 50-80mm.
4. impacting type according to claim 1 quickly casts anchor release device, it is characterised in that：The component of the coating presses matter
Measuring percentage ratio is：C：0.16%, Co：0.63%, Ti：0.21%, Cu：0.75%, Cr：4.72%, Ni：0.12%, V：0.22%, it is remaining
Measure as Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1140 DEG C, be incubated 5h, be then air cooled to 820
DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C, using water-cooled
Steel plate is cooled to into 320 DEG C with the cooldown rate of 18 DEG C/s, room temperature is then air cooled to；
Step（2）：Then arc crotch and buckle are heated to 550 DEG C by configuration rub resistance metal coating powder, equal to its surface
Even spraying rub resistance metal coating, after thickness is 0.5mm, keeps 3h, is then air cooled to room temperature.
5. impacting type according to claim 1 quickly casts anchor release device, it is characterised in that：The component of the coating presses matter
Measuring percentage ratio is：C：0.19%, Co：0.65%, Ti：0.23%, Cu：0.77%, Cr：4.79%, Ni：0.15%, V：0.24%, it is remaining
Measure as Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1160 DEG C, be incubated 7h, be then air cooled to 830
DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C, using water-cooled
Steel plate is cooled to into 330 DEG C with the cooldown rate of 18 DEG C/s, room temperature is then air cooled to；
Step（2）：Then arc crotch and buckle are heated to 560 DEG C by configuration rub resistance metal coating powder, equal to its surface
Even spraying rub resistance metal coating, after thickness is 0.8mm, keeps 4h, is then air cooled to room temperature.
6. impacting type according to claim 1 quickly casts anchor release device, it is characterised in that：The component of the coating presses matter
Measuring percentage ratio is：C：0.17%, Co：0.64%, Ti：0.22%, Cu：0.76%, Cr：4.75%, Ni：0.13%, V：0.23%, it is remaining
Measure as Fe and inevitable impurity；
The handling process of the rub resistance metal coating, concrete technology are as follows：
Step（1）：By arc crotch with snap through high-frequency quenching stove heat to 1150 DEG C, be incubated 6h, be then air cooled to 825
DEG C, combined with water-cooled using air-cooled, first adopt the air-cooled cooldown rate with 15 DEG C/s that steel plate is cooled to 620 DEG C, using water-cooled
Steel plate is cooled to into 325 DEG C with the cooldown rate of 18 DEG C/s, room temperature is then air cooled to；
Step（2）：Then arc crotch and buckle are heated to 556 DEG C by configuration rub resistance metal coating powder, equal to its surface
Even spraying rub resistance metal coating, after thickness is 0.7mm, keeps 3.5h, is then air cooled to room temperature.