CN106515185A - Method for manufacturing tempered glass and tempered glass manufactured by adopting method - Google Patents
Method for manufacturing tempered glass and tempered glass manufactured by adopting method Download PDFInfo
- Publication number
- CN106515185A CN106515185A CN201610920995.2A CN201610920995A CN106515185A CN 106515185 A CN106515185 A CN 106515185A CN 201610920995 A CN201610920995 A CN 201610920995A CN 106515185 A CN106515185 A CN 106515185A
- Authority
- CN
- China
- Prior art keywords
- glass
- self
- carrying
- safety glass
- raw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing tempered glass. The method comprises the following steps: (S1) slicing glass: slicing white glass according to required shapes so as to form raw glass sheets, and carrying out edging on edges of the raw glass sheets so as to remove burrs; (S2) carrying out tempering: carrying out tempering operation on the raw glass sheets in a tempering furnace, so as to form raw tempered glass sheets; (S3) carrying out doubling: carrying out doubling on edge portions of corresponding two raw tempered glass sheets so as to form a glass cavity between the corresponding two raw tempered glass sheets; (S4) carrying out thermal-discoloration aquagel pouring: pouring thermal-discoloration aquagel into glass cavities formed in the step (S3), and carrying out sealing so as to close inner sides of the glass cavities; and (S5) carrying out self-cleaned film coating: coating one-sided raw tempered glass sheet surfaces with self-cleaned films, so as to form self-cleaned film layers. According to the method, through arranging thermal-discoloration layers, the temperature of a control panel can be displayed, and thus, scalding during use is avoided.
Description
Technical field
The present invention relates to a kind of manufacture method of safety glass and the safety glass made using the method.
Background technology
The kitchen range top of domestic would generally arrange safety glass as guidance panel, compare the convenient cleaning of other structures, together
When, also more attractive in appearance, structure is firmer.But during due to use, easily viscous tack coat stain, cleans very inconvenient.Together
When, during use, the kitchen range top is heated, and can occur warming phenomenon simultaneously, as the existing kitchen range top is not provided with temperature prompt
Information, user can not understand the temperature of kitchen range top operating board in time, and operation is easily scalded when not noting.
The content of the invention
It is an object of the invention to provide a kind of manufacture method of safety glass and the safety glass made using the method,
The problem of prior art presence can be improved, by arranging thermochromic layer, can realize showing control panel temperature, it is to avoid
Scald.
The present invention is achieved through the following technical solutions：
A kind of manufacture method of safety glass, comprises the following steps：
S1：Glass slice：By white glass section in needing shape to form original sheet glass, edging is carried out to original sheet glass edge
Remove Burr removal；
S2：Tempering：Original sheet glass is put into annealing furnace carries out tempering operations, forms safety glass original piece；
S3：Doubling：By 2 safety glass original piece edge doublings, make to form glass sky between 2 safety glass original pieces
Chamber；
S4：Perfusion thermo-color hydrogel：Glass sky intra-bladder instillation thermo-color hydrogel in step s3, and seal, make
Close on the inside of glass cavity；
S5：Coating self-cleaning film：In unilateral safety glass original piece surface-coated self-cleaning film, self-cleaning film layer is formed.
Further, for the present invention is better achieved, described self-cleaning film layer is the self-cleaning film layer of hydrophilic.
Further, for the present invention is better achieved, described thermo-color hydrogel is hydroxypropyl methyl cellulose, hydroxypropyl
The hydrogel that base cellulose is mixed with inorganic salt.
Further, for the present invention is better achieved, described white glass thickness is 4-6.
Further, for the present invention is better achieved, in step s 4, in the glass cavity in the middle part of safety glass original piece
Arranging hollow cylindrical through hole is used for installing switch element.
The invention also discloses a kind of safety glass, successively including self-cleaning film layer, 2 toughened glass layers, at described 2
Thermo-color hydrogel is provided between toughened glass layer, on the inside of the edge of the toughened glass layer described in 2 is provided with binding agent,
Fluid sealant is coated with the toughened glass layer outer ledge described in 2, element is provided between the toughened glass layer described in 2
Installing hole.
The present invention compared with prior art, has the advantages that：
(1) safety glass prepared by the present invention can change light transmittance according to temperature, such that it is able to facilitate user according to face
Color discrimination temperature, wall are scalded；
(2) safety glass prepared by the present invention can conveniently clean surface blot, and cleaning operation is simple.
Description of the drawings
In order to be illustrated more clearly that the technical scheme of the embodiment of the present invention, below by to be used attached needed for embodiment
Figure is briefly described, it will be appreciated that the following drawings illustrate only certain embodiments of the present invention, thus be not construed as it is right
The restriction of scope, for those of ordinary skill in the art, on the premise of not paying creative work, can be with according to this
A little accompanying drawings obtain other related accompanying drawings.
Fig. 1 is 2 overall structure diagram of the embodiment of the present invention.
Wherein：101. self-cleaning film layers, 102. toughened glass layers, 103. hot heating hydrogels, 104. binding agents, 105. sealings
Glue, 106. element installing holes.
Specific embodiment
The present invention is described in further detail with reference to specific embodiment, but embodiments of the present invention are not limited to
This.
Embodiment 1：
A kind of manufacture method of safety glass, comprises the following steps：
S1：Glass slice：By white glass section in needing shape to form original sheet glass, edging is carried out to original sheet glass edge
Remove Burr removal；
S2：Tempering：Original sheet glass is put into annealing furnace carries out tempering operations, forms safety glass original piece；
S3：Doubling：By 2 safety glass original piece edge doublings, make to form glass sky between 2 safety glass original pieces
Chamber；
S4：Perfusion thermo-color hydrogel：Glass sky intra-bladder instillation thermo-color hydrogel in step s3, and seal, make
Close on the inside of glass cavity；
S5：Coating self-cleaning film：In unilateral safety glass original piece surface-coated self-cleaning film, self-cleaning film layer is formed.
Preferably, in the present embodiment, described self-cleaning film layer is the self-cleaning film layer of hydrophilic.
It is further preferred that in the present embodiment, described thermo-color hydrogel is hydroxypropyl methyl cellulose, hydroxypropyl fibre
The hydrogel that dimension element is mixed with inorganic salt.Preferably, the minimum critical compatible temperature of described thermo-color hydrogel is
30～33 DEG C.
It is further preferred that in this enforcement, described white glass thickness is 4-6.
Preferably, installation elements for convenience, in the present embodiment, in step s 4, the glass in the middle part of safety glass original piece
Arranging hollow cylindrical through hole in glass cavity is used for installing switch element.
Embodiment 2：
As shown in figure 1, the present invention is on the basis of embodiment 1, a kind of safety glass is also disclosed, successively including self-cleaning film
101,2 toughened glass layer 102 of layer, are provided with thermo-color hydrogel 103, between 2 described toughened glass layers 102 2
Binding agent 104 is provided with the inside of the edge of the toughened glass layer 102 described in piece, in 102 outer side edges of toughened glass layer described in 2
Edge is coated with fluid sealant 105, between the toughened glass layer 102 described in 2 is provided with element installing hole 106.
Embodiment 3：
In the present embodiment, described self-cleaning film layer is electrodeless self-cleaning coat, and which needs to be coated in preparation process in advance
Glass surface.The 5mm ultra-clear glasses original piece of certain size is cut first, after the cleaning of Jing edgings, original sheet glass is carried out into tempering,
After tempering, one layer of pvb film is coated between two panels safety glass original piece, seal safety glass, shape using polyester spacer bar
Into cavity, using grouting process to glass sky intra-bladder instillation heat to colour change function layer, by glass cavities seals after perfusion, and in steel
Change glass outer layer coating hydrophilic self-cleaning film layer.
The preferred embodiments of the present invention are the foregoing is only, the present invention is not limited to, for the skill of this area
For art personnel, the present invention can have various modifications and variations.It is all within the spirit and principles in the present invention, made any repair
Change, equivalent, improvement etc., should be included within the scope of the present invention.
Claims (6)
1. a kind of manufacture method of safety glass, it is characterised in that：Comprise the following steps：
S1：Glass slice：By white glass section in needing shape to form original sheet glass, edging removal is carried out to original sheet glass edge
Burr；
S2：Tempering：Original sheet glass is put into annealing furnace carries out tempering operations, forms safety glass original piece；
S3：Doubling：By 2 safety glass original piece edge doublings, make to form glass cavity between 2 safety glass original pieces；
S4：Perfusion thermo-color hydrogel：Glass sky intra-bladder instillation thermo-color hydrogel in step s3, and seal, make glass
Close on the inside of cavity；
S5：Coating self-cleaning film：In unilateral safety glass original piece surface-coated self-cleaning film, self-cleaning film layer is formed.
2. the manufacture method of a kind of safety glass according to claim 1, it is characterised in that：Described self-cleaning film layer is parent
The self-cleaning film layer of aqueouss.
3. the manufacture method of a kind of safety glass according to claim 1, it is characterised in that：Described thermo-color hydrogel
For the hydrogel that hydroxypropyl methyl cellulose, hydroxypropyl cellulose and inorganic salt are mixed.
4. the manufacture method of a kind of safety glass according to claim 1, it is characterised in that：Described white glass thickness is
4-6㎜。
5. the manufacture method of a kind of safety glass according to claim 1, it is characterised in that：In step s 4, in tempering
Arranging hollow cylindrical through hole in glass cavity in the middle part of original sheet glass is used for installing switch element.
6. a kind of safety glass, it is characterised in that：Include self-cleaning film layer (101), 2 toughened glass layers (102) successively, described
2 toughened glass layers (102) between be provided with thermo-color hydrogel (103), in the toughened glass layer (102) described in 2
Binding agent (104) is provided with the inside of edge, is coated with fluid sealant in toughened glass layer (102) outer ledge described in 2
(105), element installing hole (106) is provided between the toughened glass layer (102) described in 2.