CN106495582A - Permeable stone of a kind of cavernous body and preparation method thereof and application - Google Patents
Permeable stone of a kind of cavernous body and preparation method thereof and application Download PDFInfo
- Publication number
- CN106495582A CN106495582A CN201610933384.1A CN201610933384A CN106495582A CN 106495582 A CN106495582 A CN 106495582A CN 201610933384 A CN201610933384 A CN 201610933384A CN 106495582 A CN106495582 A CN 106495582A
- Authority
- CN
- China
- Prior art keywords
- parts
- cavernous body
- permeable stone
- permeable
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of permeable stone of cavernous body, the raw material for preparing the permeable stone of the cavernous body includes cement, quartz sand, brightener, wood fibre and water.Further, also include in yellow ground, pigment and additive one or more.The invention also discloses the permeable stone preparation method of cavernous body and application.The permeable stone water-permeable and air permeable of the cavernous body, and smooth texture, fine and closely woven, the application in terms of with good market application foreground, can be used for making sheet, make container or making false tree body；Top board, the health board of hot compress steam of surface layer, spit of fland step, night-cellar and/or the flower stand on road and/or square is can also be used for, and is used for making permeable vase and/or permeable tea set.
Description
Technical field
The present invention relates to a kind of stone, more particularly to the permeable stone of a kind of cavernous body and preparation method thereof and application.
Background technology
General stone does not possess water penetration；And some permeable stones are although permeable, but its quality is more coarse, loose,
Frangible, and affect attractive in appearance.
Content of the invention
For these reasons, the present inventor tries hard to create a kind of both permeable, and smooth texture, fine and closely woven stone.Its technology
Scheme is, a kind of permeable stone of cavernous body, prepare the permeable stone of the cavernous body raw material include cement, quartz sand, brightener,
Wood fibre and water.Wood fibre refers to plant refuse, the branch for such as pruning generation, the leaf for dropping, rice husk, stalk etc.
Garden waste and/or agricultural waste material, it is achieved that to the excellent of garden waste material regeneration resource in Process of Urban Development
Change configuration.Wood fibre plays filling effect in the permeable stone of cavernous body involved in the present invention so that cavernous body permeable stone
Block is internally formed reticulated void, so that the permeable stone of the cavernous body has the permeable and airing function as sponge.Right
In brightener, common brightener may be incorporated for the present invention on the market.
Further, the weight proportion of each raw material is：100 parts of cement, 220～380 parts of quartz sands, 2～18 parts of light
Bright dose, 3～15 parts of wood fibres and 35～48 parts of water.
In a detailed embodiment, the raw material for preparing the permeable stone of the cavernous body also includes pigment, each original
The weight proportion of material is：100 parts of cement, 220～380 parts of quartz sands, 2～18 parts of brighteners, 1～10 part of pigment, 3～15 parts of wood
Matter fiber and 35～48 parts of water.
In another embodiment, the raw material for preparing the permeable stone of the cavernous body also includes yellow ground, each described
The weight proportion of raw material is：100 parts of cement, 85～120 parts of yellow ground, 200～330 parts of quartz sand, 2～18 parts of brighteners, 3～15
Part wood fibre and 35～48 parts of water.
Further, the raw material for preparing the permeable stone of the cavernous body also includes pigment, the weight proportion of each raw material
For：100 parts of cement, 85～120 parts of yellow ground, 200～330 parts of quartz sand, 2～18 parts of brighteners, 1～10 part of pigment, 3～15 parts
Wood fibre and 35～48 parts of water.
Further, the raw material for preparing the permeable stone of the cavernous body also includes additive, the wherein cement of 100 weight portions
The additive of corresponding 0.1-15 weight portions.
Further, the additive is water reducer, reinforcing agent, air entraining agent, pumping admixture, retarder, early strength agent, rapid hardening
Agent, waterproofing agent, corrosion inhibitor, air-entrainment, swelling agent, antifreezing agent, colouring agent, adhesive, asbestos army, land plaster, dicalcium powder, slag
With one or more in rubber powder.
The preparation method that the present invention also provides a kind of permeable stone of cavernous body as above, comprises the following steps：
Step one, weigh each raw material by weight ratio, after first preparing concrete, then to the not solidified coagulation
Wood fibre and additives, stirring are added to obtain product one in soil；
Step 2, the product one for obtaining the step one insert strip mould mechanical ramming, and water seasoning 1-5 days is obtained
Arrive product two；
Step 3, the product two for obtaining the step 2 are taken out from the strip mould, are conserved through 10-28 days,
Carry out cutting into tabular, obtain product three；
Step 4, the plate face of the product three for obtaining the step 3 carry out mechanical wire-drawing shape, obtain the cavernous body
Permeable stone；
In the step one, the preparation of concrete is to be stirred cement, sandstone aggregate and water, reaction；Sandstone aggregate bag
Quartz sand is included, additives include brightener.
Further, the sandstone aggregate in the step one also includes that yellow ground, additives also include pigment and/or interpolation
Agent.
The benefit for preparing concrete in advance is：Cement prepare in hydration reaction, that is, during concrete can with molten
Weak acid and weak base reaction in liquid.If now, adding wood fibre, as wood fibre is in faintly acid, therefore can occur with cement
Reaction, so that be unfavorable for the formation of water permeability.Only when concrete has been prepared, but during ot-yet-hardened, add wooden fibre again
Dimension, is mixed, and can be prevented effectively from cement and be reacted with wood fibre.And due to wood fibre surface ratio in whipping process
Sandstone aggregate rough surface, thus wood fibre can come the bur plunder part on sandstone aggregate so as in concrete
Portion forms tiny space, enhances water penetration.Additionally, preparing concrete in advance it is also possible that the intensity of concrete and
Even property is as few as possible to be affected by wood fibre.
Preferably, the time for washing maintenance in the step 2 is 3 days.Curing time in the step 3 is 28 days.
The permeable stone of cavernous body as above that also provides of the invention is in terms of making sheet, making container or making false tree body
Application.
Especially a kind of permeable stone of cavernous body as above is used for the surface layer on laying road and/or square；Or make
Use for spit of fland step；Or for laying the top board of night-cellar and/or flower stand；Or make as the health board of hot compress steam
With.
The health board of hot compress steam when using, lie/lie prone/lie on one's side/sit/lean against on the health board by human body, vapours from
Ascension through the health board and human contact below health board, carries out hot compress.Hot compress therapy is controlled soft tissue injury disease
Occupy important position in treatment.Hot compress therapy has expansion of blood vessels, the effect for improving local blood circulation, promoting local metabolic,
It is beneficial to the recovery of disease.Muscle cramp can be also alleviated in hot compress itself, promote the absorption of inflammation and hemostasis.Medicine hot compress can also make
Medicine reaches the purpose of through disease institute by local absorption, make treatment more directly, more effective.Medicine is spread on affected part such as, is wrapped
After upper gauze, human body lies in.The temperature in affected part is directly lifted, expands veins beneath the skin, plus
Fast blood circulation, reaches elimination chronic inflammation, pain relieving, goes to swell, accelerate recovery from illness, muscle cramp of releiving, the nerve that relaxes, improve tendon
The effect of pliability.The symptom that can be suitable for includes：Chronic inflammation and pain (affected part does not have rubescent or heating symptom), example
Such as：Chronic waist cervicodynia, chronic degenerative gonitis, muscular fatigue or spasm etc..
Further, health board/health-care box of the permeable stone of a kind of cavernous body as above as moxa-moxibustion.During use
The corresponding site that Ai Zhu/moxa stick is arranged on (or in the health-care box) moxibustion, human body or human body below the health board is (such as
Hand) it is placed on the health board (or the health-care box).
And a kind of permeable stone of cavernous body as above is used for making permeable vase and/or permeable tea set.
Beneficial effect is：
1st, there is the permeable stone of cavernous body involved in the present invention the function of water-permeable and air permeable, air and moisture will not be subject to sea
The stop of the permeable stone of continuous body, so as to be used for preparing can reduce during false tree body to trees using air and moisture impact；With
And for laying road and/or square surface layer when which is rakish simultaneously causing, do not affect other seepy materials of lower floor
Effect play, be conducive to the construction in sponge city.
2nd, quartz sand quality hard, fine and smooth cause the permeable stone of cavernous body quality more preferably, good looking appearance.
3rd, in prior art the health board of steam type hot compress mainly with batten or bamboo assembling or establishment, its wood
Bar and bamboo are waterproof ventilative in itself.Therefore steam can be passed through from the space between two battens and reach human body, but
The some vapor that body is contacted with batten cannot then be reached.Similarly there are Similar Problems in the health board of bamboo establishment.The present invention
Using the permeable stone of the homogeneous cavernous body of quality as the health board of hot compress steam, solve the problem well, control curative effect
Fruit is more preferably.And the permeable stone of cavernous body is more durable in use, economical and practical.
Description of the drawings
Fig. 1 is a kind of structural representation of specific embodiment of the permeable stone of cavernous body involved in the present invention.
Specific embodiment
Below in conjunction with the drawings and specific embodiments, the invention will be further described.
Embodiment one
Fig. 1 shows a kind of specific embodiment of the permeable stone of the cavernous body of the present invention.Prepare the cavernous body permeable stone
The raw material of block includes cement, quartz sand, brightener, wood fibre and water.The weight proportion of each raw material is：100 parts of cement,
220 parts of quartz sands, 2 parts of brighteners, 3 parts of wood fibres and 35 parts of water.Wood fibre is to prune the branch for producing, the leaf for dropping
Etc. garden waste.
Embodiment two
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 280 quartz sands,
10 parts of brighteners, 10 parts of wood fibres and 40 parts of water.Wood fibre includes the agricultural waste materials such as rice husk, stalk.Remaining is with real
Apply example one.
Embodiment three
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 380 parts of quartz
Sand, 18 parts of brighteners, 15 parts of wood fibres and 48 parts of water.Wood fibre is to prune the gardens such as the branch for producing, the leaf for dropping
Discarded object.
Example IV
The raw material for preparing the permeable stone of cavernous body of the present embodiment includes cement, quartz sand, brightener, pigment, wooden fibre
Peacekeeping water.The weight proportion of each raw material is：100 parts of cement, 220 parts of quartz sand, 2 parts of brighteners, 1 part of pigment, 3 parts wooden
Fiber and 35 parts of water.Wood fibre is to prune the garden wastes such as the branch for producing, the leaf for dropping.
Embodiment five
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 380 quartz sands,
18 parts of brighteners, 10 parts of pigment, 15 parts of wood fibres and 48 parts of water.Wood fibre includes the agricultural waste materials such as rice husk, stalk.
Remaining same example IV.
Embodiment six
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 300 quartz sands,
14 parts of brighteners, 6 parts of pigment, 10 parts of wood fibres and 40 parts of water.Wood fibre includes the agricultural waste materials such as rice husk, stalk.
Remaining same example IV.
Embodiment seven
The raw material for preparing the permeable stone of cavernous body of the present embodiment includes cement, yellow ground, quartz sand, brightener, wooden fibre
Peacekeeping water.The weight proportion of each raw material is：100 parts of cement, 85 parts of yellow ground, 200 parts of quartz sands, 2 parts of brighteners, 3 parts of wood
Matter fiber and 35 parts of water.Wood fibre is to prune the garden wastes such as the branch for producing, the leaf for dropping.
Embodiment eight
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 120 parts of yellow ground,
330 parts of quartz sands, 18 parts of brighteners, 15 parts of wood fibres and 48 parts of water.Wood fibre includes the crop wastes such as rice husk, stalk
Thing.Remaining is with embodiment seven.
Embodiment nine
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 100 parts of yellow ground,
300 parts of quartz sands, 14 parts of brighteners, 10 parts of wood fibres and 40 parts of water.Wood fibre includes the crop wastes such as rice husk, stalk
Thing.Remaining is with embodiment seven.
Embodiment ten
The raw material for preparing the permeable stone of cavernous body of the present embodiment includes cement, yellow ground, quartz sand, brightener, pigment, wood
Matter fiber, water and additive.The weight proportion of each raw material is：100 parts of cement, 85 parts of yellow ground, 200 parts of quartz sands, 2 parts of light
Bright dose, 1 part of pigment, 3 parts of wood fibres, 35 parts of water and 0.1 part of additive.Wood fibre is to prune the branch of generation, drop
The garden wastes such as leaf.Additive is water reducer, reinforcing agent, air entraining agent, pumping admixture, retarder, early strength agent, accelerator, anti-
Aqua, corrosion inhibitor, air-entrainment, swelling agent, antifreezing agent, colouring agent, adhesive, asbestos army, land plaster, dicalcium powder, slag and glue
One or more in powder.
Embodiment 11
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 120 parts of yellow ground,
330 parts of quartz sands, 18 parts of brighteners, 10 parts of pigment, 15 parts of wood fibres, 48 parts of water and 15 parts of additives.Wood fibre includes
The agricultural waste materials such as rice husk, stalk.Remaining is with embodiment ten.
Embodiment 12
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 100 parts of yellow ground,
300 parts of quartz sands, 14 parts of brighteners, 7 parts of pigment, 10 parts of wood fibres, 40 parts of water and 5 parts of additives.Wood fibre includes rice
The agricultural waste materials such as shell, stalk.Remaining is with embodiment ten.
Embodiment 13
The raw material for preparing the permeable stone of cavernous body of the present embodiment includes cement, quartz sand, brightener, pigment, wooden fibre
Dimension, water and additive.The weight proportion of each raw material is：100 parts of cement, 220 parts of quartz sand, 2 parts of brighteners, 1 part of pigment,
3 parts of wood fibres, 35 parts of water and 0.1 part of additive.Wood fibre is to prune the gardens such as the branch for producing, the leaf for dropping to discard
Thing.Additive be water reducer, reinforcing agent, air entraining agent, pumping admixture, retarder, early strength agent, accelerator, waterproofing agent, corrosion inhibitor, plus
One kind in gas agent, swelling agent, antifreezing agent, colouring agent, adhesive, asbestos army, land plaster, dicalcium powder, slag and rubber powder or
Multiple.
Embodiment 14
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 380 parts of quartz
Sand, 18 parts of brighteners, 10 parts of pigment, 15 parts of wood fibres, 48 parts of water and 15 parts of additives.Wood fibre includes rice husk, stalk
Deng agricultural waste material.Remaining is with embodiment 13.
Embodiment 15
The weight proportion of each described raw material of the permeable stone of the cavernous body of the present embodiment is：100 parts of cement, 300 parts of quartz
Sand, 14 parts of brighteners, 7 parts of pigment, 10 parts of wood fibres, 40 parts of water and 5 parts of additives.Wood fibre includes rice husk, stalk etc.
Agricultural waste material.Remaining is with embodiment 13.
Embodiment 16
The permeable preparation method of cavernous body is comprised the following steps：
Step one, weigh each raw material by weight ratio, after first preparing concrete, then to the not solidified coagulation
Wood fibre and brightener, stirring is added to obtain product one in soil；
Step 2, the product one for obtaining the step one insert strip mould mechanical ramming, and water seasoning 1-5 days is obtained
Arrive product two；
Step 3, the product two for obtaining the step 2 are taken out from the strip mould, are conserved through 10-28 days,
Carry out cutting into tabular, obtain product three；
Step 4, the plate face of the product three for obtaining the step 3 carry out mechanical wire-drawing shape, obtain the cavernous body
Permeable stone；
In the step one, the preparation of concrete is to be stirred cement, sandstone aggregate and water, reaction；Sandstone aggregate bag
Quartz sand is included, additives include brightener.
Further, the sandstone aggregate in the step one also includes that yellow ground, additives also include pigment and/or interpolation
Agent.
The physical and mechanical property of the permeable stone of cavernous body in embodiment one to ten five is as shown in table 1：
The physical and mechanical property of the permeable stone of 1 cavernous body of table
| Performance | 100×200×60mm3The permeable stone of cavernous body after cured |
| Compression strength (MPa) | 10～25 |
| Coefficient of permeability (mm/h) | 30～60 |
Embodiment 17
With the permeable stone of the cavernous body of embodiment nine, as hot compress steam health board, to 5 experimenters, (wherein 2 tested
Person has more serious scapulohumeral periarthritis) carry out the hot compress steam of continuous 7 days.Once a day, every time 20 minutes.Other conditions are identical, but
The permeable stone of cavernous body is replaced using wooden health board of the prior art.
As a result：
1st, 5 experimenter's health boards that the permeable stone of expression cavernous body does more allow people comfortable.
2nd, the temperature that 5 experimenters can be stood in the health board that the permeable stone of use cavernous body does is than wooden health care
3 DEG C are averagely higher by during plate.
3rd, 2 scapulohumeral periarthritis patients represent that the health board for seeming to make of the permeable stone of cavernous body is helped to the improvement of shoulder symptom
Bigger.
Reason：During vapours reaches human body through the permeable stone of cavernous body, the permeable stone of cavernous body is first sponged
Partial heat, then it is very gentle to pass to the temperature that experiences during human body.Then the heat that the permeable stone of cavernous body absorbs is fewer and feweri,
The temperature for passing to human body is slowly rising.The rising that the human body regular hour carrys out adaptive temperature is given, so that people feel
More comfortable, and the temperature that can finally reach is higher, fomentation effect is more preferable.Wood fibre in the permeable stone of cavernous body is caused
Reticulated void helps steam radiating, on the one hand sponges partial heat, on the one hand causes steam again through reticulated void to intelligent
Body.
The preferred embodiment of the present invention described in detail above.It should be appreciated that one of ordinary skill in the art without
Need creative work just can make many modifications and variations according to the design of the present invention.Therefore, all technology in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical scheme, all should be in the protection domain being defined in the patent claims.
Claims (10)
1. the permeable stone of a kind of cavernous body, it is characterised in that the raw material for preparing the permeable stone of the cavernous body includes cement, quartz
Sand, brightener, wood fibre and water.
2. the permeable stone of cavernous body as claimed in claim 1, it is characterised in that the weight proportion of each raw material is：100 parts
Cement, 220～380 parts of quartz sands, 2～18 parts of brighteners, 3～15 parts of wood fibres and 35～48 parts of water.
3. the permeable stone of cavernous body as claimed in claim 1, it is characterised in that prepare the raw material of the permeable stone of the cavernous body
Also include that pigment, the weight proportion of each raw material are：100 parts of cement, 220～380 parts of quartz sand, 2～18 parts of brighteners, 1
～10 parts of pigment, 3～15 parts of wood fibres and 35～48 parts of water.
4. the permeable stone of cavernous body as claimed in claim 1, it is characterised in that prepare the raw material of the permeable stone of the cavernous body
Also include that yellow ground, the weight proportion of each raw material are：100 parts of cement, 85～120 parts of yellow ground, 200～330 parts of quartz sand, 2
～18 parts of brighteners, 3～15 parts of wood fibres and 35～48 parts of water.
5. the permeable stone of cavernous body as claimed in claim 4, it is characterised in that prepare the raw material of the permeable stone of the cavernous body
Also include that pigment, the weight proportion of each raw material are：100 parts of cement, 85～120 parts of yellow ground, 200～330 parts of quartz sand, 2
～18 parts of brighteners, 1～10 part of pigment, 3～15 parts of wood fibres and 35～48 parts of water.
6. the permeable stone of cavernous body as described in any one of claim 3-5, it is characterised in that prepare the cavernous body permeable stone
The raw material of block also includes additive, the wherein additive of the corresponding 0.1-15 weight portions of the cement of 100 weight portions.
7. the preparation method of the permeable stone of a kind of cavernous body as claimed in claim 1, it is characterised in that comprise the following steps：
Step one, weigh each raw material by weight ratio, after first preparing concrete, then in the not solidified concrete
Wood fibre and additives, stirring are added to obtain product one；
Step 2, the product one for obtaining the step one insert strip mould mechanical ramming, and water seasoning 1-5 days is produced
Thing two；
Step 3, the product two for obtaining the step 2 are taken out from the strip mould, are conserved through 10-28 days, are carried out
Tabular is cut into, product three is obtained；
Step 4, the plate face of the product three for obtaining the step 3 carry out mechanical wire-drawing shape, obtain the cavernous body permeable
Stone；
In the step one, the preparation of concrete is to be stirred cement, sandstone aggregate and water, reaction；The sandstone aggregate bag
Quartz sand is included, the additives include brightener.
8. application of the permeable stone of cavernous body as claimed in claim 1 in making sheet, in terms of making container or making false tree body.
9. a kind of permeable stone of cavernous body as claimed in claim 1 is used for the surface layer on laying road and/or square；Or conduct
Spit of fland step is used；Or for laying the top board of night-cellar and/or flower stand；Or use as the health board of hot compress steam.
10. a kind of permeable stone of cavernous body as claimed in claim 1 is used for making permeable vase and/or permeable tea set.