CN106400317A - Anti-microbial insect-repellent non-woven fabric and preparation method thereof - Google Patents
Anti-microbial insect-repellent non-woven fabric and preparation method thereof Download PDFInfo
- Publication number
- CN106400317A CN106400317A CN201611046696.7A CN201611046696A CN106400317A CN 106400317 A CN106400317 A CN 106400317A CN 201611046696 A CN201611046696 A CN 201611046696A CN 106400317 A CN106400317 A CN 106400317A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven fabrics
- worm
- antibacterial
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anti-microbial insect-repellent non-woven fabric and a preparation method thereof, which relate to the technical field of non-woven fabrics. The non-woven fabric is prepared from the following raw materials in parts by weight: 80 to 110 parts of polypropylene, 1 to 8 parts of anti-aging agent, 10 to 25 parts of sugarcane fiber, 12 to 25 parts of cornstalk fiber, 2 to 6 parts of filler, 10 to 16 parts of insect repellant, 2 to 7 parts of zinc stearate, 0.5 to 2.5 parts of coupling agent, 0.5 to 1.5 parts of copper sulfate, and 0.5 to 1.5 parts of borax. The non-woven fabric provided by the invention has anti-microbial and anti-parasitic effects; by using the copper sulfate and the borax, the non-woven fabric has mould proof and mothproof performance; through adding the insect repellant, the non-woven fabric has an insect repelling effect on crops, raw materials of the insect repellant can be obtained easily and are pure natural, and the insect repellant is safe and environmentally-friendly; the non-woven fabric is soaked in complex liquid, so that the anti-microbial and anti-parasitic effects of the non-woven fabric are further improved; the preparation method provided by the invention is simple, low in cost, and suitable for small, medium and large enterprises, and has favorable economic benefit.
Description
Technical field
The present invention relates to field of nonwoven fabric technology is and in particular to a kind of antibacterial, worm-expelling non-woven fabrics and preparation method thereof.
Background technology
Currently, country advocates " green agriculture " thought energetically.Traditional agricultural, while boosting agricultural yield, also gives agriculture
Industry ecological environment exerts a certain influence.The plantation process of plant typically has the stage of a nursery.Seedling bag is in nursery
Achieve fabulous effect in production, be widely used in agricultural, melon fruits and vegetables, flowers, tobacco seedling.With Seedling bag cultivation
Seedling growth cycle is short, emerge that fast, quality is good, save work(, laborsaving and low production cost, during transplanted seedling tree, do not need bag direct
Field planting, survival rate is high.Pure plastic Seedling bag breathe freely bad, bad to the growth promoter of plant, when the well developed root system of plant
Afterwards, easy disk is tied inside Seedling bag, leads to root hair to be destroyed, reduces the survival rate of nursery, and the Seedling bag abandoning was both
Can not reuse, the pollution of surrounding enviroment can be caused again.And nowadays, a kind of new nursery form still occurs, that is just
It is non-woven fabrics Seedling bag.It not only has facilitation to improving crop yield, and is again degradable and pollution-free.Cause
This, welcomed warmly by market.Non-woven fabrics Seedling bag is made by non-woven fabrics.Non-woven fabrics are currently marketed
A kind of new material, it is to be made up of fiber that orient or random, is environment-friendly materials of new generation, has protection against the tide, ventilative, soft
Tough, light weight, not combustion-supporting, easy decomposition, nontoxic nonirritant, rich color, cheap, recyclable the features such as.So
Can directly be planted in soil together with seedling.Non-woven fabrics Seedling bag breathability is better than other materials, so using nonwoven
No matter the plant of cloth Seedling bag is water absorption or breathability is all preferable, meanwhile, plant absorption nutritional labeling is also especially fast.Tradition
The effects such as non-woven fabrics do not have antibacterial, worm-expelling, can lead to seedling dead because of infection pest and disease damage.
Content of the invention
It is an object of the invention to provide a kind of low manufacture cost, survival rate of seedling are high, degradable and have antibacterial, worm-expelling
Non-woven fabrics and preparation method thereof.
In order to realize the purpose of the present invention, adopt the following technical scheme that：
A kind of antibacterial, worm-expelling non-woven fabrics, are made up of the raw material of following weight portion：
Preferably, it is made up of the raw material of following weight portion：
Preferably, it is made up of the raw material of following weight portion：
Preferably, filler is one of vermiculite power, wollastonite in powder or kieselguhr.Further, the preparation of anthelmintic
Method is：
Weigh Flos Chrysanthemi bar stem 20-40 part, Folium Artemisiae Argyi 10-15 part, Camphora 7-15 part, Cacumen Platycladi 15-25 part, Herba Houttuyniae 7- first
13 parts, Herba Menthae 15-20 part, Radix Sophorae Flavescentiss 10-35 part, by each plant material be cut into physical dimension be 2-5mm little bulk, mix homogeneously
It is placed in afterwards in 40-60 DEG C of drying room, dries and be less than 8% to water content, then the plant mixture after drying is put into pulverizer
Interior, make powder cross 200 mesh standard sieves, add suitable quantity of water in the powder, stir into a paste, finally pasty state compound is placed in
In baking oven, temperature is 45-50 DEG C, and the time is 20-30min, is cooled to 22-27 DEG C, ground 200 mesh standard sieves.
A kind of preparation method of antibacterial, worm-expelling non-woven fabrics, specifically includes following steps：
Weigh the polypropylene of corresponding weight, age resister, Caulis Sacchari sinensis fiber, cornstalk fibers, filler, anthelmintic, Hard Fat
Sour zinc, coupling agent, copper sulfate and Borax, mixing and stirring post-heating melts, and the mixture after fusing is passed through Screw Extrusion
Machine extruding is filtered, and spray webbing stretching is solidified into fiber, is thermal bonding to non-woven fabrics, finally non-woven fabrics is placed on 35-50 DEG C compound
30-60min is soaked, taking-up press dry and gets product in liquid.
Preferably, complex liquid is made up of Oleum menthae, clove oil, oil of Herba Pogostemonis, lonicera oil and medical alcohol, wherein Herba Menthae
The volume proportion of oil, clove oil, oil of Herba Pogostemonis, lonicera oil and medical alcohol is 7:3:5:5:80.
Beneficial effects of the present invention：
The non-woven fabrics of the present invention have functions that antibacterial, worm-expelling, using copper sulfate and Borax, so that non-woven fabrics is had mould proof anti-
The performance of moth；By add insect-proof agent, make non-woven fabrics have functions that anthelmintic to crops, insect-proof agent adopt Flos Chrysanthemi bar stem, Folium Artemisiae Argyi,
The compositions such as Herba Menthae, raw material is easy to get and pure natural, safety and environmental protection；Non-woven fabrics soak in complex liquid, further increase non-woven fabrics
Antibacterial, worm-expelling effect；The preparation method of the present invention is simple, and low cost, it is adaptable to large, medium and small various enterprise, has good warp
Ji benefit.
Specific embodiment
Below embodiments of the invention are elaborated, the present embodiment is carried out under premised on technical solution of the present invention
Implement, give detailed embodiment and specific operating process, but protection scope of the present invention is not limited to following enforcements
Example.
Embodiment 1
A kind of antibacterial, worm-expelling non-woven fabrics and preparation method thereof, are made up of the raw material of following weight portion：95 parts of polypropylene, anti-ageing
4 parts of agent, 15 parts of Caulis Sacchari sinensis fiber, 18 parts of cornstalk fibers, 3 parts of filler, 13 parts of anthelmintic, 4 parts of zinc stearate, coupling agent
1.5 parts, 0.5 part of copper sulfate, 0.5 part of Borax；Wherein filler is one of vermiculite power, wollastonite in powder or kieselguhr；
The preparation method of anthelmintic is：
Weigh first 20 parts of Flos Chrysanthemi bar stem, 10 parts of Folium Artemisiae Argyi, 7 parts of Camphora, 15 parts of Cacumen Platycladi, 7 parts of Herba Houttuyniae, 15 parts of Herba Menthae,
10 parts of Radix Sophorae Flavescentiss, each plant material are cut into the little bulk that physical dimension is 2-5mm, are placed in 40-60 DEG C of drying room after mix homogeneously
Interior, dry and be less than 8% to water content, then put into the plant mixture after drying in pulverizer, make powder cross 200 targets accurate
Sieve, adds suitable quantity of water in the powder, stirs into a paste, finally pasty state compound is placed in baking oven, and temperature is 45-50
DEG C, the time is 20-30min, is cooled to 22-27 DEG C, ground 200 mesh standard sieves.
A kind of preparation method of antibacterial, worm-expelling non-woven fabrics, specifically includes following steps：
Weigh the polypropylene of corresponding weight, age resister, Caulis Sacchari sinensis fiber, cornstalk fibers, filler, anthelmintic, Hard Fat
Sour zinc, coupling agent, copper sulfate and Borax, mixing and stirring post-heating melts, and the mixture after fusing is passed through Screw Extrusion
Machine extruding is filtered, and spray webbing stretching is solidified into fiber, is thermal bonding to non-woven fabrics, finally non-woven fabrics is placed on 35-50 DEG C compound
30-60min is soaked, taking-up press dry and gets product in liquid.
Further, complex liquid is made up of Oleum menthae, clove oil, oil of Herba Pogostemonis, lonicera oil and medical alcohol, wherein thin
Lotus oil, clove oil, the volume proportion of oil of Herba Pogostemonis, lonicera oil and medical alcohol are 7:3:5:5:80.
Embodiment 2
A kind of antibacterial, worm-expelling non-woven fabrics and preparation method thereof, are made up of the raw material of following weight portion：80 parts of polypropylene, anti-ageing
1 part of agent, 10 parts of Caulis Sacchari sinensis fiber, 12 parts of cornstalk fibers, 2 parts of filler, 10 parts of anthelmintic, 2 parts of zinc stearate, coupling agent
0.5 part, 0.5 part of copper sulfate, 0.5 part of Borax；Wherein filler is one of vermiculite power, wollastonite in powder or kieselguhr；
The preparation method of anthelmintic is：
Weigh first 25 parts of Flos Chrysanthemi bar stem, 13 parts of Folium Artemisiae Argyi, 8 parts of Camphora, 17 parts of Cacumen Platycladi, 10 parts of Herba Houttuyniae, 18 parts of Herba Menthae,
13 parts of Radix Sophorae Flavescentiss, each plant material are cut into the little bulk that physical dimension is 2-5mm, are placed in 40-60 DEG C of drying room after mix homogeneously
Interior, dry and be less than 8% to water content, then put into the plant mixture after drying in pulverizer, make powder cross 200 targets accurate
Sieve, adds suitable quantity of water in the powder, stirs into a paste, finally pasty state compound is placed in baking oven, and temperature is 45-50
DEG C, the time is 20-30min, is cooled to 22-27 DEG C, ground 200 mesh standard sieves.
A kind of preparation method of antibacterial, worm-expelling non-woven fabrics, specifically includes following steps：
Weigh the polypropylene of corresponding weight, age resister, Caulis Sacchari sinensis fiber, cornstalk fibers, filler, anthelmintic, Hard Fat
Sour zinc, coupling agent, copper sulfate and Borax, mixing and stirring post-heating melts, and the mixture after fusing is passed through Screw Extrusion
Machine extruding is filtered, and spray webbing stretching is solidified into fiber, is thermal bonding to non-woven fabrics, finally non-woven fabrics is placed on 35-50 DEG C compound
30-60min is soaked, taking-up press dry and gets product in liquid.
Further, complex liquid is made up of Oleum menthae, clove oil, oil of Herba Pogostemonis, lonicera oil and medical alcohol, wherein thin
Lotus oil, clove oil, the volume proportion of oil of Herba Pogostemonis, lonicera oil and medical alcohol are 7:3:5:5:80.
Embodiment 3
A kind of antibacterial, worm-expelling non-woven fabrics and preparation method thereof, are made up of the raw material of following weight portion：110 parts of polypropylene, anti-
Aging dose 8 parts, 25 parts of Caulis Sacchari sinensis fiber, 25 parts of cornstalk fibers, 6 parts of filler, 16 parts of anthelmintic, 7 parts of zinc stearate, coupling agent
2.5 parts, 1.5 parts of copper sulfate, 1.5 parts of Borax；Wherein filler is one of vermiculite power, wollastonite in powder or kieselguhr；
The preparation method of anthelmintic is：
Weigh 40 parts of Flos Chrysanthemi bar stem, 15 parts of Folium Artemisiae Argyi, 15 parts of Camphora, 25 parts of Cacumen Platycladi, 13 parts of Herba Houttuyniae, Herba Menthae 20 first
Part, 35 parts of Radix Sophorae Flavescentiss, each plant material are cut into the little bulk that physical dimension is 2-5mm, are placed in 40-60 DEG C of baking after mix homogeneously
In room, dry and be less than 8% to water content, then put into the plant mixture after drying in pulverizer, make powder cross 200 targets
Quasi- sieve, adds suitable quantity of water in the powder, stirs into a paste, finally pasty state compound is placed in baking oven, and temperature is 45-50
DEG C, the time is 20-30min, is cooled to 22-27 DEG C, ground 200 mesh standard sieves.
A kind of preparation method of antibacterial, worm-expelling non-woven fabrics, specifically includes following steps：
Weigh the polypropylene of corresponding weight, age resister, Caulis Sacchari sinensis fiber, cornstalk fibers, filler, anthelmintic, Hard Fat
Sour zinc, coupling agent, copper sulfate and Borax, mixing and stirring post-heating melts, and the mixture after fusing is passed through Screw Extrusion
Machine extruding is filtered, and spray webbing stretching is solidified into fiber, is thermal bonding to non-woven fabrics, finally non-woven fabrics is placed on 35-50 DEG C compound
30-60min is soaked, taking-up press dry and gets product in liquid.
Further, complex liquid is made up of Oleum menthae, clove oil, oil of Herba Pogostemonis, lonicera oil and medical alcohol, wherein thin
Lotus oil, clove oil, the volume proportion of oil of Herba Pogostemonis, lonicera oil and medical alcohol are 7:3:5:5:80.
Embodiment 4
A kind of antibacterial, worm-expelling non-woven fabrics and preparation method thereof, are made up of the raw material of following weight portion：90 parts of polypropylene, anti-ageing
2 parts of agent, 13 parts of Caulis Sacchari sinensis fiber, 20 parts of cornstalk fibers, 4 parts of filler, 12 parts of anthelmintic, 5 parts of zinc stearate, coupling agent
1.5 parts, 1.2 parts of copper sulfate, 0.5 part of Borax；Wherein filler is one of vermiculite power, wollastonite in powder or kieselguhr；
The preparation method of anthelmintic is：
Weigh first 35 parts of Flos Chrysanthemi bar stem, 15 parts of Folium Artemisiae Argyi, 9 parts of Camphora, 23 parts of Cacumen Platycladi, 10 parts of Herba Houttuyniae, 17 parts of Herba Menthae,
22 parts of Radix Sophorae Flavescentiss, each plant material are cut into the little bulk that physical dimension is 2-5mm, are placed in 40-60 DEG C of drying room after mix homogeneously
Interior, dry and be less than 8% to water content, then put into the plant mixture after drying in pulverizer, make powder cross 200 targets accurate
Sieve, adds suitable quantity of water in the powder, stirs into a paste, finally pasty state compound is placed in baking oven, and temperature is 45-50
DEG C, the time is 20-30min, is cooled to 22-27 DEG C, ground 200 mesh standard sieves.
A kind of preparation method of antibacterial, worm-expelling non-woven fabrics, specifically includes following steps：
Weigh the polypropylene of corresponding weight, age resister, Caulis Sacchari sinensis fiber, cornstalk fibers, filler, anthelmintic, Hard Fat
Sour zinc, coupling agent, copper sulfate and Borax, mixing and stirring post-heating melts, and the mixture after fusing is passed through Screw Extrusion
Machine extruding is filtered, and spray webbing stretching is solidified into fiber, is thermal bonding to non-woven fabrics, finally non-woven fabrics is placed on 35-50 DEG C compound
30-60min is soaked, taking-up press dry and gets product in liquid.
Further, complex liquid is made up of Oleum menthae, clove oil, oil of Herba Pogostemonis, lonicera oil and medical alcohol, wherein thin
Lotus oil, clove oil, the volume proportion of oil of Herba Pogostemonis, lonicera oil and medical alcohol are 7:3:5:5:80.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Any modification, equivalent and improvement made within god and principle etc., should be included within the scope of the present invention.
Claims (7)
1. a kind of antibacterial, worm-expelling non-woven fabrics are it is characterised in that be made up of the raw material of following weight portion：
2. a kind of antibacterial, worm-expelling non-woven fabrics according to claim 1 are it is characterised in that raw material group by following weight portion
Become：
3. a kind of antibacterial, worm-expelling non-woven fabrics according to claim 1 are it is characterised in that raw material group by following weight portion
Become：
4. a kind of antibacterial, worm-expelling non-woven fabrics according to claim 1 or 2 or 3, its feature is, filler is Vermiculitum
One of powder, wollastonite in powder or kieselguhr.
5. a kind of antibacterial, worm-expelling non-woven fabrics according to claim 1 or 2 or 3, its feature is, the preparation side of anthelmintic
Method is：
Weigh Flos Chrysanthemi bar stem 20-40 part, Folium Artemisiae Argyi 10-15 part, Camphora 7-15 part, Cacumen Platycladi 15-25 part, Herba Houttuyniae 7-13 first
Part, Herba Menthae 15-20 part, Radix Sophorae Flavescentiss 10-35 part, each plant material are cut into the little bulk that physical dimension is 2-5mm, after mix homogeneously
It is placed in 40-60 DEG C of drying room, dries and be less than 8% to water content, then the plant mixture after drying is put in pulverizer,
Make powder cross 200 mesh standard sieves, add suitable quantity of water in the powder, stir into a paste, finally pasty state compound is placed in baking
In case, temperature is 45-50 DEG C, and the time is 20-30min, is cooled to 22-27 DEG C, ground 200 mesh standard sieves.
6. a kind of preparation method of antibacterial, worm-expelling non-woven fabrics is it is characterised in that specifically include following steps：
Weigh the polypropylene of corresponding weight, age resister, Caulis Sacchari sinensis fiber, cornstalk fibers, filler, anthelmintic, zinc stearate,
Coupling agent, copper sulfate and Borax, mixing and stirring post-heating melts, and the mixture after fusing is extruded by screw extruder
Filter, spray webbing stretching is solidified into fiber, is thermal bonding to non-woven fabrics, finally non-woven fabrics are placed on leaching in 35-50 DEG C of complex liquid
Bubble 30-60min, taking-up press dry and gets product.
7. a kind of preparation method of antibacterial, worm-expelling non-woven fabrics according to claim 6 is it is characterised in that complex liquid is by Herba Menthae
Oil, clove oil, oil of Herba Pogostemonis, lonicera oil and medical alcohol composition, wherein Oleum menthae, clove oil, oil of Herba Pogostemonis, lonicera oil
Volume proportion with medical alcohol is 7:3:5:5:80.