CN106316266A - High-strength cement brick - Google Patents
High-strength cement brick Download PDFInfo
- Publication number
- CN106316266A CN106316266A CN201610735294.1A CN201610735294A CN106316266A CN 106316266 A CN106316266 A CN 106316266A CN 201610735294 A CN201610735294 A CN 201610735294A CN 106316266 A CN106316266 A CN 106316266A
- Authority
- CN
- China
- Prior art keywords
- parts
- brick
- cement brick
- cement
- strength cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength cement brick. The high-strength cement brick is prepared from, by weight, 5-9 parts of isobutyric acid branched alkyl ester, 10-12 parts of aluminum oxide, 20-30 parts of cement, 10-13 parts of gravel, 40-50 parts of vermiculite powder and 50-60 parts of coal ash. The high-strength cement brick has the advantages that adhesion is tight, and the probability that a finished product has a crack is low; the good water resistance and acid resistance and the strong anti-cracking and anti-bending strength are achieved, the brick does not deform, and the color of the brick is not faded; the color, modeling and materials can be designed as needed, and the cement brick has the advantages of being low in cost, environmentally friendly, capable of meeting the sustainable development industrial policy and the like, and can be widely applied to decorations of walls, floors, furniture surfaces and the like.
Description
Technical field
The present invention relates to cement brick technical field, especially a kind of high strength cement brick.
Background technology
Along with the development of national economy life, the material that Outdoor Design is used has been directed to iron and steel, non-ferrous metal, change
The multiple industries such as work, weaving, timber, pottery, plastics, glass.People for Outdoor Design theme tone emphasizing with weight
Depending on, it is also desirable to the new material of great individual character moderate cost again realizes.Single with regard to wall, ground decoration one, available material
Huge number, such as glaze for glazed tile, marble, granite finishing brick etc., but above-mentioned material is difficult to have new on decorative effect
Breakthrough, and cost is higher.Develop the feature cheap, functional, there is environmental protection, meet the dress of national development policy
Decorations brick material is quite necessary.Patent CN101126271A discloses a kind of cement decorative plate including surface layer and bottom；But
The contract with dry rate gap being the surface layer of this cement decorative plate and bottom is relatively big, and crack easily occurs in its finished product.
Cement brick refer to utilize flyash, cinder, gangue, mine tailings, residue of chemical industry or natural sand, tidal land mud etc. (with
One or several of upper raw material) as primary raw material, do coagulator with cement, a kind of Novel wall manufactured without high-temperature calcination
Body material.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, propose a kind of high strength cement brick, form ingenious, performance is good.
In order to realize foregoing invention purpose, the present invention provides techniques below scheme: a kind of high strength cement brick, by following heavy
Amount part composition constitute: isopropylformic acid. branched alkyl ester 5-9, aluminium oxide 10-12, cement 20-30, rubble 10-13, vermiculite power 40-50,
Flyash 50-60.
Further, the weight portion of each composition is: isopropylformic acid. branched alkyl ester 7, aluminium oxide 11, cement 25, rubble 12, trematodiasis
Stone powder 45, flyash 55.
Compared with prior art, the invention have the advantages that and closely bond, finished product occurs that the probability in crack is low；Have
Good water-fast acid resistance, stronger cracking resistance and rupture strength, indeformable, colour-fast.Its color, moulding, material can root
It is designed according to needs, there is the advantages such as low cost, environmental protection, the industrial policy meeting sustainable development.Can be widely applied to wall
The decoration of face, ground, furniture surface etc..
Detailed description of the invention
Describing the present invention below in conjunction with embodiment, the description of this part is only exemplary and explanatory, no
Reply protection scope of the present invention has any restriction effect.
Embodiment 1
A kind of high strength cement brick, is made up of following weight parts composition: isopropylformic acid. branched alkyl ester 7, aluminium oxide 11, cement 25,
Rubble 12, vermiculite power 45, flyash 55.
Embodiment 2
A kind of high strength cement brick, is made up of following weight parts composition: isopropylformic acid. branched alkyl ester 5, aluminium oxide 12, cement 20,
Rubble 13, vermiculite power 40, flyash 60.
Embodiment 3
A kind of high strength cement brick, is made up of following weight parts composition: isopropylformic acid. branched alkyl ester 9, aluminium oxide 10, cement 30,
Rubble 10, vermiculite power 50, flyash 50.
The manufacture method of the said goods is, by proportioning, each composition is stirred mixing, adds suitable quantity of water slurrying, injects mould
Tool shakes flat, condenses maintenance 3 days, the demoulding, dries.
The cement brick that the present invention prepares has high abrasion, high anti-skidding function, easily slides after decreasing the wet water of floor tile
The danger of traumatic injury.After tested, every technological standards of this product reaches requirement.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (2)
1. a high strength cement brick, it is characterised in that: it is made up of following weight parts composition: isopropylformic acid. branched alkyl ester 5-9, oxygen
Change aluminum 10-12, cement 20-30, rubble 10-13, vermiculite power 40-50, flyash 50-60.
2. high strength cement brick as claimed in claim 1, it is characterised in that: the weight portion of each composition is: isopropylformic acid. branched alkyl
Ester 7, aluminium oxide 11, cement 25, rubble 12, vermiculite power 45, flyash 55.