CN106147003A - A kind of plastic film for wrapping and preparation method thereof - Google Patents
A kind of plastic film for wrapping and preparation method thereof Download PDFInfo
- Publication number
- CN106147003A CN106147003A CN201610643549.1A CN201610643549A CN106147003A CN 106147003 A CN106147003 A CN 106147003A CN 201610643549 A CN201610643549 A CN 201610643549A CN 106147003 A CN106147003 A CN 106147003A
- Authority
- CN
- China
- Prior art keywords
- parts
- wrapping
- raw material
- plastic film
- acetylbutyrylcellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of plastic film for wrapping and preparation method thereof, described plastic film for wrapping includes that the raw material of following parts by weight is made: linear low density polyethylene resin 25 50 parts, Merlon 8 18 parts, nylon 13 25 parts, aluminum-based layered nanometer material 10 18 parts, flax fiber 27 parts, antioxidant 0.8 2.5 parts, plasticizer 0.6 1.5 parts, stabilizer 13 parts, stearic acid 39 parts, acetylbutyrylcellulose 6 12 parts, diamine propyl group polydimethylsiloxane 26 parts, 0.8 2.5 parts of Oleum Ricini wax, lubricant 1.5 4 parts.Compared with prior art, the low raw-material cost of intermediate package plastic sheeting of the present invention, each raw material components synergism makes it have preferable hot strength and rigidity, thus reaches more preferable using effect.
Description
Technical field
The invention belongs to thin film materials art, particularly to a kind of plastic film for wrapping and preparation method thereof.
Background technology
Plastic sheeting is mainly used in packaging and is used as coating layer.Plastics package and plastic packet product are commercially shared
Share increasing, particularly composite plastic flexible package, have been widely used for the fields such as food, medicine, chemical industry, wherein
Maximum with packaging for foodstuff proportion again, such as beverage packaging, quick frozen food packaging, cooking food packaging, fast food packaging
Deng, these products all bring great convenience to people's life.But the tensile resistance of existing plastic sheeting and rigidity are the most relatively
Difference, thus cause being easily broken during the foreign object carrying constant weight, and make troubles to routine use.
Summary of the invention
It is an object of the invention to provide a kind of plastic film for wrapping and preparation method thereof, resisting of this plastic film for wrapping
Stretch capability is simple compared with strong, good rigidly and preparation technology.
For achieving the above object, the present invention provides following technical scheme:
A kind of plastic film for wrapping, it includes that the raw material of following parts by weight is made: linear low density polyethylene resin
25-50 part, Merlon 8-18 part, nylon 13-25 part, aluminum-based layered nanometer material 10-18 part, flax fiber 2-7 part, antioxygen
Agent 0.8-2.5 part, plasticizer 0.6-1.5 part, stabilizer 1-3 part, stearic acid 3-9 part, acetylbutyrylcellulose 6-12 part is double
Amine propyl group polydimethylsiloxane 2-6 part, Oleum Ricini wax 0.8-2.5 part, lubricant 1.5-4 part.
Preferably, described plastic film for wrapping includes that the raw material of following parts by weight is made: linear low density polyethylene
Resin 36 parts, Merlon 11 parts, nylon 15 parts, aluminum-based layered nanometer material 12 parts, flax fiber 5.5 parts, antioxidant 1.3
Part, plasticizer 1 part, stabilizer 1.5 parts, stearic acid 7 parts, acetylbutyrylcellulose 10 parts, diamine propyl group polydimethylsiloxane 6
Part, 1.4 parts of Oleum Ricini wax, lubricant 2.3 parts.
Preferably, described plastic film for wrapping includes that the raw material of following parts by weight is made: linear low density polyethylene
Resin 42 parts, Merlon 12 parts, nylon 18 parts, aluminum-based layered nanometer material 11 parts, flax fiber 3.5 parts, antioxidant 2
Part, plasticizer 0.9 part, stabilizer 1.4 parts, stearic acid 8 parts, acetylbutyrylcellulose 8 parts, diamine propyl group polydimethylsiloxane
5 parts, 1.3 parts of Oleum Ricini wax, lubricant 2.5 parts.
Preferably, described plastic film for wrapping includes that the raw material of following parts by weight is made: linear low density polyethylene
Resin 50 parts, Merlon 10 parts, nylon 16 parts, aluminum-based layered nanometer material 16 parts, flax fiber 6 parts, antioxidant 2.2
Part, plasticizer 1 part, stabilizer 1.5 parts, stearic acid 5 parts, acetylbutyrylcellulose 9 parts, diamine propyl group polydimethylsiloxane 6
Part, 2.3 parts of Oleum Ricini wax, lubricant 3.5 parts.
The preparation method of described plastic film for wrapping, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is
12-15 minute, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Compared with prior art, the invention has the beneficial effects as follows:
Intermediate package plastic sheeting of the present invention is added with linear low density polyethylene resin, aluminum-based layered nanometer material,
The raw material such as flax fiber and acetylbutyrylcellulose, each raw material components with low cost and being made it have relatively by synergism
Good hot strength and rigidity, thus reach more preferable using effect.
Detailed description of the invention
Describe technical scheme in detail below in conjunction with embodiment, but protection domain is not limited thereto.
Embodiment one:
A kind of plastic film for wrapping, it includes that the raw material of following parts by weight is made: linear low density polyethylene resin
36 parts, Merlon 9 parts, nylon 16 parts, aluminum-based layered nanometer material 14 parts, flax fiber 5.5 parts, antioxidant 1.7 parts, increase
Mould agent 1.2 parts, stabilizer 2.2 parts, stearic acid 8 parts, acetylbutyrylcellulose 10 parts, diamine propyl group polydimethylsiloxane 4.5
Part, 2 parts of Oleum Ricini wax, lubricant 2.6 parts.
The preparation method of described plastic film for wrapping, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is
12-15 minute, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment two:
A kind of plastic film for wrapping, it includes that the raw material of following parts by weight is made: linear low density polyethylene resin
40 parts, Merlon 18 parts, nylon 23 parts, aluminum-based layered nanometer material 15 parts, flax fiber 6 parts, antioxidant 2.1 parts, increase
Mould agent 1 part, stabilizer 1.8 parts, stearic acid 9 parts, acetylbutyrylcellulose 11 parts, diamine propyl group polydimethylsiloxane 4.5 parts,
2.3 parts of Oleum Ricini wax, lubricant 3.5 parts.
The preparation method of described plastic film for wrapping, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is
12-15 minute, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment three:
A kind of plastic film for wrapping, it includes that the raw material of following parts by weight is made: linear low density polyethylene resin
36 parts, Merlon 11 parts, nylon 15 parts, aluminum-based layered nanometer material 12 parts, flax fiber 5.5 parts, antioxidant 1.3 parts,
Plasticizer 1 part, stabilizer 1.5 parts, stearic acid 7 parts, acetylbutyrylcellulose 10 parts, diamine propyl group polydimethylsiloxane 6 parts,
1.4 parts of Oleum Ricini wax, lubricant 2.3 parts.
The preparation method of described plastic film for wrapping, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is
12-15 minute, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment four:
A kind of plastic film for wrapping, it includes that the raw material of following parts by weight is made: linear low density polyethylene resin
42 parts, Merlon 12 parts, nylon 18 parts, aluminum-based layered nanometer material 11 parts, flax fiber 3.5 parts, antioxidant 2 parts, increase
Mould agent 0.9 part, stabilizer 1.4 parts, stearic acid 8 parts, acetylbutyrylcellulose 8 parts, diamine propyl group polydimethylsiloxane 5 parts,
1.3 parts of Oleum Ricini wax, lubricant 2.5 parts.
The preparation method of described plastic film for wrapping, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is
12-15 minute, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment five:
A kind of plastic film for wrapping, it includes that the raw material of following parts by weight is made: linear low density polyethylene resin
50 parts, Merlon 10 parts, nylon 16 parts, aluminum-based layered nanometer material 16 parts, flax fiber 6 parts, antioxidant 2.2 parts, increase
Mould agent 1 part, stabilizer 1.5 parts, stearic acid 5 parts, acetylbutyrylcellulose 9 parts, diamine propyl group polydimethylsiloxane 6 parts, castor
2.3 parts of Oleum Sesami wax, lubricant 3.5 parts.
The preparation method of described plastic film for wrapping, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is
12-15 minute, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment six:
A kind of plastic film for wrapping, it includes that the raw material of following parts by weight is made: linear low density polyethylene resin
42 parts, Merlon 13 parts, nylon 20 parts, aluminum-based layered nanometer material 15 parts, flax fiber 4 parts, antioxidant 1.6 parts, increase
Mould agent 0.8 part, stabilizer 1.6 parts, stearic acid 9 parts, acetylbutyrylcellulose 10 parts, diamine propyl group polydimethylsiloxane 5 parts,
2.3 parts of Oleum Ricini wax, lubricant 2 parts.
The preparation method of described plastic film for wrapping, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is
12-15 minute, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment seven:
A kind of plastic film for wrapping, it includes that the raw material of following parts by weight is made: linear low density polyethylene resin
50 parts, Merlon 18 parts, nylon 14 parts, aluminum-based layered nanometer material 14 parts, flax fiber 6 parts, antioxidant 1.7 parts, increase
Mould agent 1.3 parts, stabilizer 2 parts, stearic acid 9 parts, acetylbutyrylcellulose 12 parts, diamine propyl group polydimethylsiloxane 5.5 parts,
1.3 parts of Oleum Ricini wax, lubricant 3 parts.
The preparation method of described plastic film for wrapping, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is
12-15 minute, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment eight:
A kind of plastic film for wrapping, it includes that the raw material of following parts by weight is made: linear low density polyethylene resin
30 parts, Merlon 12 parts, nylon 24 parts, aluminum-based layered nanometer material 18 parts, flax fiber 7 parts, antioxidant 1.6 parts, increase
Mould agent 1.2 parts, stabilizer 2.3 parts, stearic acid 8 parts, acetylbutyrylcellulose 10 parts, diamine propyl group polydimethylsiloxane 4 parts,
2.4 parts of Oleum Ricini wax, lubricant 2.6 parts.
The preparation method of described plastic film for wrapping, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is
12-15 minute, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Finally illustrating, above example is only in order to illustrate technical scheme and unrestricted, although with reference to relatively
The present invention has been described in detail by good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent, and without deviating from objective and the scope of the technical program, it all should be contained in the present invention
Right in the middle of.
Claims (5)
1. a plastic film for wrapping, it is characterised in that include that the raw material of following parts by weight is made: linear low density polyethylene
Olefine resin 25-50 part, Merlon 8-18 part, nylon 13-25 part, aluminum-based layered nanometer material 10-18 part, flax fiber 2-7
Part, antioxidant 0.8-2.5 part, plasticizer 0.6-1.5 part, stabilizer 1-3 part, stearic acid 3-9 part, acetylbutyrylcellulose 6-
12 parts, diamine propyl group polydimethylsiloxane 2-6 part, Oleum Ricini wax 0.8-2.5 part, lubricant 1.5-4 part.
A kind of plastic film for wrapping the most according to claim 1, it is characterised in that include the raw material of following parts by weight
Make: linear low density polyethylene resin 36 parts, Merlon 11 parts, nylon 15 parts, aluminum-based layered nanometer material 12 parts, Caulis et Folium Lini
Fiber 5.5 parts, antioxidant 1.3 parts, plasticizer 1 part, stabilizer 1.5 parts, stearic acid 7 parts, acetylbutyrylcellulose 10 parts, double
Amine propyl group polydimethylsiloxane 6 parts, 1.4 parts of Oleum Ricini wax, lubricant 2.3 parts.
A kind of plastic film for wrapping the most according to claim 1, it is characterised in that include the raw material of following parts by weight
Make: linear low density polyethylene resin 42 parts, Merlon 12 parts, nylon 18 parts, aluminum-based layered nanometer material 11 parts, Caulis et Folium Lini
Fiber 3.5 parts, antioxidant 2 parts, plasticizer 0.9 part, stabilizer 1.4 parts, stearic acid 8 parts, acetylbutyrylcellulose 8 parts, double
Amine propyl group polydimethylsiloxane 5 parts, 1.3 parts of Oleum Ricini wax, lubricant 2.5 parts.
A kind of plastic film for wrapping the most according to claim 1, it is characterised in that include the raw material of following parts by weight
Make: linear low density polyethylene resin 50 parts, Merlon 10 parts, nylon 16 parts, aluminum-based layered nanometer material 16 parts, Caulis et Folium Lini
Fiber 6 parts, antioxidant 2.2 parts, plasticizer 1 part, stabilizer 1.5 parts, stearic acid 5 parts, acetylbutyrylcellulose 9 parts, diamine
Propyl group polydimethylsiloxane 6 parts, 2.3 parts of Oleum Ricini wax, lubricant 3.5 parts.
5. according to the preparation method of the plastic film for wrapping according to any one of claim 1-4, it is characterised in that include with
Lower step:
(1) each raw material components is weighed according to ratio of weight and number；
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing time is 12-
15 minutes, temperature controlled, for 85-90 DEG C, to obtain raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting finished product.