CN106118402A - A kind of boats and ships anti-corrosive primer - Google Patents

A kind of boats and ships anti-corrosive primer Download PDF

Info

Publication number
CN106118402A
CN106118402A CN201610565393.XA CN201610565393A CN106118402A CN 106118402 A CN106118402 A CN 106118402A CN 201610565393 A CN201610565393 A CN 201610565393A CN 106118402 A CN106118402 A CN 106118402A
Authority
CN
China
Prior art keywords
parts
raw material
boats
powder
ships
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610565393.XA
Other languages
Chinese (zh)
Inventor
张玉湘
孙巨福
戴宇钧
汪鹏程
祝盆鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianchang Julong Car and Ship Coating Co Ltd
Original Assignee
Tianchang Julong Car and Ship Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianchang Julong Car and Ship Coating Co Ltd filed Critical Tianchang Julong Car and Ship Coating Co Ltd
Priority to CN201610565393.XA priority Critical patent/CN106118402A/en
Publication of CN106118402A publication Critical patent/CN106118402A/en
Pending legal-status Critical Current

Abstract

A kind of boats and ships anti-corrosive primer, relate to chemistry painting industry preparing technical field, be made up of following raw material: acrylic resin 15 25 parts, alkyd resin 15 25 parts, chlorinated rubber 10 20 parts, chlorinated paraffin 8 10 parts, Ludox 68 parts, zinc powder 57 parts, sodio bentonite 35 parts, aluminium triphosphate 13 parts, 35 parts of modified nano montmorillonite powder, methylcellulose 13 parts, nano-organosilicon emulsion 57 parts.The invention has the beneficial effects as follows: present invention process flow process is succinct, reasonable raw material proportioning, use acrylic resin, alkyd resin as main material, coordinate chlorinated rubber, zinc powder and the use of remaining auxiliary agent, obtaining antirust paint, tolerance own is strong, difficult drop-off, good antirust property, curing rate faster, after spraying, it is ensured that boats and ships are long-term security in sea water, quickness and high efficiency, it is simple to promote and use.

Description

A kind of boats and ships anti-corrosive primer
Technical field
The present invention relates to chemistry painting industry preparing technical field, be specifically related to a kind of boats and ships anti-corrosive primer.
Background technology
Paint is that one can firmly cover at body surface, rises and protect, decorates, indicates and the chemistry of other specific uses is mixed Compound coating.China's more authoritative " coating process " book of coating circle is defined such that " coating is a kind of material, this Material can be coated in object surface by different construction technologies, formed adhere to firmly, to have some strength, continuous print solid-state thin Film.The film common name film so formed, also known as paint film or coating.
Boats and ships, the general name of various ships.Boats and ships are to navigate by water or berth to carry out in waters transporting or the vehicles of operation, External form is usually beneficial to overcome the cleanliness envelope of fluid resistance, and material is constantly updated along with scientific and technological progress, be in early days wood, bamboo, Mostly the nature materials such as fiber crops, be steel and aluminum, glass fibre, acrylic and various composite modern age, and boats and ships are long-term due to it Float on water body, and boats and ships body have to carry out antirust treatment, be typically all and use paint to realize, but owing to boats and ships exist Environment in water body is more severe, and itself has certain salt in sea water, and the most common antirust paint is not also durable, easily Corrosion comes off, the use that impact is actual.
Summary of the invention:
The technical problem to be solved is to provide a kind of formula reasonable, and production technology is simple, and performance consolidates Boats and ships anti-corrosive primer.
The technical problem to be solved realizes by the following technical solutions:
A kind of boats and ships anti-corrosive primer, it is characterised in that: it is made up of following raw material:
Acrylic resin 15-25 part, alkyd resin 15-25 part, chlorinated rubber 10-20 part, chlorinated paraffin 8-10 part, silicon are molten Glue 6-8 part, zinc powder 5-7 part, sodio bentonite 3-5 part, aluminium triphosphate 1-3 part, modified nano montmorillonite powder 3-5 part, methyl Cellulose 1-3 part, nano-organosilicon emulsion 5-7 part.
The preferred component of each raw material is: acrylic resin 20 parts, alkyd resin 20 parts, chlorinated rubber 15 parts, chlorinated paraffin 9 Part, Ludox 7 parts, zinc powder 6 parts, sodio bentonite 4 parts, aluminium triphosphate 2 parts, 4 parts of modified nano montmorillonite powder, Methyl cellulose Element 2 parts, nano-organosilicon emulsion 6 parts.
Described modified nano montmorillonite powder comprises following raw material: montmorillonite powder 15 parts, Polymeric sodium metaphosphate. 2 parts, potassium hydroxide 3 Part, Cab-O-sil 5 parts, magnetic iron powder 15 parts, hydrochloric acid 5 parts, 75 parts of water；
Preparation method is: by by montmorillonite powder in potassium permanganate solution, soak after 8-15min, taking-up is dried, then with After the mixing of remaining raw material, put in ball mill, control rotating speed 2500-3000r/min, after ball milling 12-15min, the most available.
It is a further object to provide a kind of method preparing boats and ships anti-corrosive primer of the present invention, it is characterised in that Comprise the following steps:
(1) select Scattered Kettle, aforesaid propylene acid resin, alkyd resin, chlorinated rubber and chlorinated paraffin are added thereto, stir After mixing mix homogeneously, Ludox is added thereto, after high-speed stirred 15-25min, standby；
(2), after zinc powder, sodio bentonite, aluminium triphosphate and modified nano montmorillonite powder being merged, carry out being milled to Grain fineness is 25um；
(3) methylcellulose in raw material is dissolved in nano-organosilicon emulsion, after being uniformly mixed, by step 2 Raw material be added thereto, be sufficiently stirred for, until the raw material in step 2 is substantially soluble in wherein；
(4) material in above-mentioned steps 1 is added in the raw material in step 3, the rotating speed of ball mill is controlled at 2500- 3500r/min, high speed ball milling is until fineness of the particles is less than after 20um, and discharging, packaging is the most available.
The invention has the beneficial effects as follows: present invention process flow process is succinct, reasonable raw material proportioning, use acrylic resin, alcohol Acid resin, as main material, coordinates chlorinated rubber, zinc powder and the use of remaining auxiliary agent, obtains antirust paint, and tolerance own is strong, no Easy to fall off, good antirust property, curing rate faster, after spraying, it is ensured that boats and ships are long-term security in sea water, quickness and high efficiency, it is simple to Promote and use.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot Close specific embodiment, the present invention is expanded on further.
Embodiment 1
Weigh: acrylic resin 15kg, alkyd resin 15kg, chlorinated rubber 10kg, chlorinated paraffin 8kg, Ludox 6kg, Zinc powder 5kg, sodio bentonite 3kg, aluminium triphosphate 1kg, modified nano montmorillonite powder 3kg, methylcellulose 1kg, nanometer have Machine silicon emulsion 5kg.
Embodiment 2
Weigh: acrylic resin 20kg, alkyd resin 20kg, chlorinated rubber 15kg, chlorinated paraffin 9kg, Ludox 7kg, Zinc powder 6kg, sodio bentonite 4kg, aluminium triphosphate 2kg, modified nano montmorillonite powder 4kg, methylcellulose 2kg, nanometer have Machine silicon emulsion 6kg.
The preparation method of above-described embodiment 1 or 2 is as follows:
(1) select Scattered Kettle, aforesaid propylene acid resin, alkyd resin, chlorinated rubber and chlorinated paraffin are added thereto, stir After mixing mix homogeneously, Ludox is added thereto, after high-speed stirred 15-25min, standby；
(2), after zinc powder, sodio bentonite, aluminium triphosphate and modified nano montmorillonite powder being merged, carry out being milled to Grain fineness is 25um；
(3) methylcellulose in raw material is dissolved in nano-organosilicon emulsion, after being uniformly mixed, by step 2 Raw material be added thereto, be sufficiently stirred for, until the raw material in step 2 is substantially soluble in wherein；
(4) material in above-mentioned steps 1 is added in the raw material in step 3, the rotating speed of ball mill is controlled at 2500- 3500r/min, high speed ball milling is until fineness of the particles is less than after 20um, and discharging, packaging is the most available.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and Equivalent defines.

Claims (3)

1. a boats and ships anti-corrosive primer, it is characterised in that: it is made up of following raw material:
Acrylic resin 15-25 part, alkyd resin 15-25 part, chlorinated rubber 10-20 part, chlorinated paraffin 8-10 part, Ludox 6- 8 parts, zinc powder 5-7 part, sodio bentonite 3-5 part, aluminium triphosphate 1-3 part, modified nano montmorillonite powder 3-5 part, Methyl cellulose Element 1-3 part, nano-organosilicon emulsion 5-7 part；
Preparation method is:
(1) selecting Scattered Kettle, aforesaid propylene acid resin, alkyd resin, chlorinated rubber and chlorinated paraffin are added thereto, stirring is mixed After closing uniformly, Ludox is added thereto, after high-speed stirred 15-25min, standby；
(2), after zinc powder, sodio bentonite, aluminium triphosphate and modified nano montmorillonite powder being merged, carry out being milled to granule thin Degree is 25um；
(3) methylcellulose in raw material is dissolved in nano-organosilicon emulsion, after being uniformly mixed, former by step 2 Material is added thereto, and is sufficiently stirred for, until the raw material in step 2 is substantially soluble in wherein；
(4) material in above-mentioned steps 1 is added in the raw material in step 3, the rotating speed of ball mill is controlled at 2500-3500r/ Min, high speed ball milling is until fineness of the particles is less than after 20um, and discharging, packaging is the most available.
A kind of boats and ships anti-corrosive primer the most according to claim 1, it is characterised in that the preferred component of each raw material is: third Olefin(e) acid resin 20 parts, alkyd resin 20 parts, chlorinated rubber 15 parts, chlorinated paraffin 9 parts, Ludox 7 parts, zinc powder 6 parts, sodio Peng Run 4 parts of soil, aluminium triphosphate 2 parts, 4 parts of modified nano montmorillonite powder, methylcellulose 2 parts, nano-organosilicon emulsion 6 parts.
A kind of boats and ships anti-corrosive primer the most according to claim 1, it is characterised in that: described modified nano montmorillonite powder Comprise following raw material: montmorillonite powder 15 parts, Polymeric sodium metaphosphate. 2 parts, potassium hydroxide 3 parts, Cab-O-sil 5 parts, magnetic iron powder 15 parts, hydrochloric acid 5 Part, 75 parts of water；
Preparation method is: by by montmorillonite powder in potassium permanganate solution, soak after 8-15min, taking-up is dried, then with remaining After raw material mixing, put in ball mill, control rotating speed 2500-3000r/min, after ball milling 12-15min, the most available.
CN201610565393.XA 2016-07-18 2016-07-18 A kind of boats and ships anti-corrosive primer Pending CN106118402A (en)