CN106118141A - A kind of inorganic polymeric coating with zeolite as adsorbent and preparation method - Google Patents
A kind of inorganic polymeric coating with zeolite as adsorbent and preparation method Download PDFInfo
- Publication number
- CN106118141A CN106118141A CN201610438529.0A CN201610438529A CN106118141A CN 106118141 A CN106118141 A CN 106118141A CN 201610438529 A CN201610438529 A CN 201610438529A CN 106118141 A CN106118141 A CN 106118141A
- Authority
- CN
- China
- Prior art keywords
- powder
- zeolite
- parts
- adsorbent
- inorganic polymeric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of inorganic polymeric coating with zeolite as adsorbent, being that material mixes by sierozem power, dicalcium powder, natural zeolite powder, Pulvis Talci, white cement, titanium dioxide and methylcellulose, its proportioning is as follows: sierozem power 10 20 parts, dicalcium powder 15 25 parts, zeolite powder 10 20 parts, white cement 5 15 parts, Pulvis Talci 25 35 parts, titanium dioxide 5 15 parts, cellulose 12 parts, toner are appropriate.The present invention 1, unique environmental protection characteristic, nonpoisonous and tasteless, inorganic environment-friendly；2, scalable indoor air humidity；3, zeolite has bigger specific surface area, and the internal stress field produced can be adsorbed the harmful gass such as indoor formaldehyde, be purified the air of a room；4, mushroom and bryophyte spores can be killed；5, having heat insulation, the wearability of excellence, resistance to chemical attack ability is strong；6, resistance to sassafras washes performance by force, has the resistance to water of height；7, there is excellent workability；8, by force, inner-outer wall is constructed for good weatherability, resistance to water.
Description
Technical field
The present invention relates to the decoration for building inside and outside wall, it is achieved the dry powder of the construction technologies such as blade coating, bullet painting, silk screen printing
Polymeric coatings, a kind of inorganic polymeric coating with zeolite as adsorbent and preparation method.
Background technology
Zeolite group mineral is found in 1756, is by this special (Cronstedt) research Iceland Black Warrior of Sweden's mineralogist's crown
Find in its hole during rock.It is named zeolite owing to foaming when it has fine idiomorphic crystal and blowpipe heating
(Zeolite).Natural zeolite be by original aluminum silicate material magma late, hydrothermal alteration, contact metasomatism, deposition diagenesis,
Go bad and air slaking hypergene process each stage, the mineral formed in the presence of water.Most important of which mineralizing process is middle acidity
Volcanic glass material under the effect of alkaline aqueous medium through aquation, hydrolyze, react and crystallize into Piper pulicatulum C. D C. and become.
Natural zeolite has internal structure and the Crystallochemical Properties of uniqueness so that it is have water suction, absorption, acidproof and resistance to spoke
The performance such as penetrate.A large amount of holes of zeolite crystal and passage make zeolite have the biggest specific surface area, and zeolite internal cavities has should
The field of force, and the material of surrounding is had the strongest adsorption, the harmful gas in house ornamentation can be adsorbed.
Therefore, zeolite is applied to inorganic polymeric coating, has been a good problem to study.
Summary of the invention
In order to overcome above-mentioned deficiency of the prior art, the invention provides a kind of will have intensity high, water-fast, alkaline-resisting,
The performance that fire-resistant, environmental protection etc. are excellent；Zeolite with adsorbing indoor harmful gases, can purify the effect of air as porous material simultaneously
The inorganic polymeric coating with zeolite as adsorbent and preparation method.
The object of the present invention is achieved like this:
A kind of inorganic polymeric coating with zeolite as adsorbent, by sierozem power, dicalcium powder, natural zeolite powder, Pulvis Talci, white
Cement, titanium dioxide and methylcellulose are that material mixes,
Its proportioning of described material is as follows: sierozem power 10-20 part, dicalcium powder 15-25 part, zeolite powder 10-20 part, white cement
5-15 part, Pulvis Talci 25-35 part, titanium dioxide 5-15 part, cellulose 1-2 part, toner are appropriate；
Described sierozem power is the 400 above powder body of mesh, and dicalcium powder is the 1250 above powder body of mesh, and zeolite powder is more than 1000 mesh
Powder body；
The preparation method of the described inorganic polymeric coating with zeolite as adsorbent, by sierozem power, dicalcium powder, zeolite powder,
White cement, Pulvis Talci, titanium dioxide are pressed configuration proportion and are added dry powder agitator stirring 10 minutes, make powder mix homogeneously to wrap
Dress, prepares inorganic polymeric dry powder paint；
The using method of the described inorganic polymeric coating with zeolite as adsorbent, is 0.4-0.5 according to the solid weight ratio of water
Weigh water, water can be used with powder mixing and stirring.
Actively beneficial effect: 1, unique environmental protection characteristic, nonpoisonous and tasteless, inorganic environment-friendly；2, room air can be regulated wet
Degree；3, high adsorption: zeolite has bigger specific surface area, and the internal stress field produced can be adsorbed indoor formaldehyde etc. and be had
Do harm to gas, purify the air of a room；4, mushroom and bryophyte spores can be killed, even if the most also will not rise mould for a long time
Speckle；5, having heat insulation, the wearability of excellence, resistance to chemical attack ability is strong；6, resistance to sassafras washes performance by force, has height after the construction of this product
The resistance to water of degree, available water is directly rinsed or wet rag is cleaned；7, there is excellent workability, it is possible to achieve multiple construction work
Skill；8, by force, inner-outer wall is constructed for good weatherability, resistance to water.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described further:
A kind of inorganic polymeric coating with zeolite as adsorbent, by sierozem power, dicalcium powder, natural zeolite powder, Pulvis Talci, white
Cement, titanium dioxide and methylcellulose are that material mixes,
Its proportioning of described material is as follows: sierozem power 10-20 part, dicalcium powder 15-25 part, zeolite powder 10-20 part, white cement
5-15 part, Pulvis Talci 25-35 part, titanium dioxide 5-15 part, cellulose 1-2 part, toner are appropriate；
Described sierozem power is the 400 above powder body of mesh, and dicalcium powder is the 1250 above powder body of mesh, and zeolite powder is more than 1000 mesh
Powder body；
The preparation method of the described inorganic polymeric coating with zeolite as adsorbent, by sierozem power, dicalcium powder, zeolite powder,
White cement, Pulvis Talci, titanium dioxide are pressed configuration proportion and are added dry powder agitator stirring 10 minutes, make powder mix homogeneously to wrap
Dress, prepares inorganic polymeric dry powder paint；
The using method of the described inorganic polymeric coating with zeolite as adsorbent, is 0.4-0.5 according to the solid weight ratio of water
Weigh water, water can be used with powder mixing and stirring.
Embodiment 1
Ash calcium 20 parts, triple superphosphate 15 parts, 20 parts of zeolite, white cement 5 parts, Pulvis Talci 25 parts, titanium dioxide 15 parts, hydroxypropyl methyl
Cellulose 1.5 parts, adds batch mixer, the nothing that stirring can be prepared by with zeolite as adsorbent for 10 minutes by each raw material of accurate measurement
Machine polymeric coatings.By prepared inorganic polymeric coating according to coating: water is to add water at 1: 0.4, stirs and can construct.
Embodiment 2
Sierozem power 15 parts, dicalcium powder 20 parts, 20 parts of zeolite, white cement 10 parts, Pulvis Talci 35 parts, titanium dioxide 5 parts, toner 3
Part, hydroxypropyl methyl cellulose 1 part；Each raw material of accurate measurement is added batch mixer, stirs and can be prepared by with zeolite for 10 minutes
Inorganic polymeric coating for adsorbent.By prepared inorganic polymeric coating according to coating: water is to add water at 1: 0.4, stirs i.e.
Can construct.
The inorganic polymeric colour-wash prepared can use different construction technologies according to different requirements, can be used for scratching, bullet
The construction technology such as painting, cloudy quarter, sun quarter, silk screen printing, it is achieved graceful decorative effect.
Grey calcium and white cement both materials in the present invention itself have the highest activity, are a kind of Binder Materials, ash
Calcium is a kind of air hardening cementitious materials, and white cement is a kind of hydraulic cementing materials；Formed simultaneously because zeolite is slag
The aluminium silicate mineral of a kind of rack-like structure, there is good Pozzolanic feature, ash calcium be mainly composed of calcium hydroxide, hydrogen-oxygen
Change calcium and zeolite powder in overbasic solution by OH-Erosion, its screen work columnar structure start decompose, there is following reaction；
3+Si-O-Si3++6OH-→2[SiO(OH)3]-
3+Si-O-Al3++7OH-→[SiO(OH)3]-+[Al(OH)4]-
[SiO (OH) after depolymerization3]-[Al (OH)4]-Enter solution and Ca2+In conjunction with forming hydrated calcium silicate and aquation
Calcium aluminate.Hydrated calcium silicate and drated calcium aluminate and white cement are all Binder Materials, are the inorganic filming substance matter of this product, have
The excellent performances such as intensity is high, water-fast, alkaline-resisting, fire-resistant, environmental protection；Zeolite can be with gas harmful in adsorption chamber as porous material simultaneously
Body, purifies the effect of air；
The products characteristics of the present invention: 1, unique environmental protection characteristic, nonpoisonous and tasteless, inorganic environment-friendly；2, Interior Space can be regulated
Air humidity degree；3, high adsorption: zeolite has bigger specific surface area, and the internal stress field produced can adsorb indoor formaldehyde
Etc. harmful gas, purify the air of a room；4, mushroom and bryophyte spores can be killed, even if the most also will not rise for a long time
Mildew；5, having heat insulation, the wearability of excellence, resistance to chemical attack ability is strong；6, resistance to sassafras washes performance by force, has after the construction of this product
The resistance to water of height, available water is directly rinsed or wet rag is cleaned；7, there is excellent workability, it is possible to achieve multiple construction
Technique；8, by force, inner-outer wall is constructed for good weatherability, resistance to water.
Claims (5)
1. the inorganic polymeric coating with zeolite as adsorbent, it is characterised in that: by sierozem power, dicalcium powder, natural zeolite powder,
Pulvis Talci, white cement, titanium dioxide and methylcellulose are that material mixes.
A kind of inorganic polymeric coating with zeolite as adsorbent the most according to claim 1, it is characterised in that: described thing
Expect that its proportioning is as follows: sierozem power 10-20 part, dicalcium powder 15-25 part, zeolite powder 10-20 part, white cement 5-15 part, Pulvis Talci 25-
35 parts, titanium dioxide 5-15 part, cellulose 1-2 part, toner appropriate.
A kind of inorganic polymeric coating with zeolite as adsorbent the most according to claim 1, it is characterised in that: described ash
Calcium powder is the 400 above powder body of mesh, and dicalcium powder is the 1250 above powder body of mesh, and zeolite powder is the 1000 above powder body of mesh.
4. the preparation method of the inorganic polymeric coating with zeolite as adsorbent as claimed in claim 1, it is characterised in that: by ash
Calcium powder, dicalcium powder, zeolite powder, white cement, Pulvis Talci, titanium dioxide are pressed configuration proportion and are added dry powder agitator stirring 10 minutes, make
Powder mix homogeneously can be packed, and prepares inorganic polymeric dry powder paint.
5. the using method of the inorganic polymeric coating with zeolite as adsorbent as claimed in claim 1, it is characterised in that: according to
The solid weight ratio of water is that 0.4-0.5 weighs water, can be used with powder mixing and stirring by water.