CN106116413A - A kind of high intensity anticracking plasterboard - Google Patents
A kind of high intensity anticracking plasterboard Download PDFInfo
- Publication number
- CN106116413A CN106116413A CN201610477120.XA CN201610477120A CN106116413A CN 106116413 A CN106116413 A CN 106116413A CN 201610477120 A CN201610477120 A CN 201610477120A CN 106116413 A CN106116413 A CN 106116413A
- Authority
- CN
- China
- Prior art keywords
- parts
- plasterboard
- high intensity
- anticracking
- croci
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high intensity anticracking plasterboard, be made up of the raw material of following mass fraction: Gypsum Fibrosum powder 70 80 parts, Ore tailings 38 parts, croci 68 parts, 7 11 parts of flyash, alumina silicate fibre 8 10 parts, polymer emulsion 58 parts, calcium oxide extender 8 10 parts, 8 12 parts of ultra-fine sand, glass fibre 14 18 parts, Resina persicae 59 parts, hydrolytic resin 7 11 parts, 35 45 parts of water.Intensity of the present invention is high, and anti-crack ability is strong, and material is light, economic and environment-friendly.
Description
Technical field
The present invention relates to technical field of inorganic nonmetallic materials, particularly relate to a kind of high intensity anticracking plasterboard.
Background technology
Plasterboard is a kind of material made for primary raw material with plaster of Paris, it be a kind of lightweight, intensity is higher, thick
Spend relatively thin, easy to process and sound insulation is adiabatic and the construction material of the better performances such as fire prevention, be the Novel light of current development emphatically
One of lumber.Existing plasterboard, intensity is low, crackle usually can occur in transportation, even rupture, and impact normally makes
With, bring certain economic loss.
Summary of the invention
For solving the problem of above-mentioned existence, the present invention provides a kind of intensity high, and anti-crack ability is strong, and material is light, economic and environment-friendly
High intensity anticracking plasterboard.
The present invention solves the technical scheme of above-mentioned technical problem employing: a kind of high intensity anticracking plasterboard, by following matter
The raw material of amount number is made:
Gypsum Fibrosum powder 70-80 part, Ore tailings 3-8 part, croci 6-8 part, flyash 7-11 part, alumina silicate fibre 8-10
Part, polymer emulsion 5-8 part, calcium oxide extender 8-10 part, ultra-fine sand 8-12 part, glass fibre 14-18 part, Resina persicae 5-9 part,
Hydrolytic resin 7-11 part, water 35-45 part.
Above-mentioned high intensity anticracking plasterboard, is made up of the raw material of following mass fraction:
Gypsum Fibrosum powder 75 parts, Ore tailings 5 parts, croci 7 parts, 9 parts of flyash, alumina silicate fibre 9 parts, polymer emulsion 7
Part, calcium oxide extender 9 parts, 10 parts of ultra-fine sand, glass fibre 16 parts, Resina persicae 7 parts, hydrolytic resin 9 parts, 40 parts of water.
The beneficial effects of the present invention is: intensity of the present invention is high, anti-crack ability is strong, and material is light, economic and environment-friendly.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in further details.
Embodiment 1
A kind of high intensity anticracking plasterboard, is made up of the raw material of following mass fraction:
Gypsum Fibrosum powder 70 parts, Ore tailings 3 parts, croci 6 parts, 7 parts of flyash, alumina silicate fibre 8 parts, polymer emulsion 5
Part, calcium oxide extender 8 parts, 8 parts of ultra-fine sand, glass fibre 14 parts, Resina persicae 5 parts, hydrolytic resin 7 parts, 35 parts of water.
Embodiment 2
A kind of high intensity anticracking plasterboard, is made up of the raw material of following mass fraction:
Gypsum Fibrosum powder 75 parts, Ore tailings 5 parts, croci 7 parts, 9 parts of flyash, alumina silicate fibre 9 parts, polymer emulsion 7
Part, calcium oxide extender 9 parts, 10 parts of ultra-fine sand, glass fibre 16 parts, Resina persicae 7 parts, hydrolytic resin 9 parts, 40 parts of water.
Embodiment 3
A kind of high intensity anticracking plasterboard, is made up of the raw material of following mass fraction:
Gypsum Fibrosum powder 80 parts, Ore tailings 8 parts, croci 8 parts, 11 parts of flyash, alumina silicate fibre 10 parts, polymer emulsion
8 parts, calcium oxide extender 10 parts, 12 parts of ultra-fine sand, glass fibre 18 parts, Resina persicae 9 parts, hydrolytic resin 11 parts, 45 parts of water.
Although the above-mentioned detailed description of the invention to the present invention is described, but not limit to scope
System, one of ordinary skill in the art should be understood that on the basis of technical scheme, and those skilled in the art need not pay
Go out various amendments or deformation that creative work can make still within protection scope of the present invention.
Claims (2)
1. a high intensity anticracking plasterboard, it is characterised in that: it is made up of the raw material of following mass fraction:
Gypsum Fibrosum powder 70-80 part, Ore tailings 3-8 part, croci 6-8 part, flyash 7-11 part, alumina silicate fibre 8-10
Part, polymer emulsion 5-8 part, calcium oxide extender 8-10 part, ultra-fine sand 8-12 part, glass fibre 14-18 part, Resina persicae 5-9 part,
Hydrolytic resin 7-11 part, water 35-45 part.
High intensity anticracking plasterboard the most according to claim 1, it is characterised in that: by the raw material system of following mass fraction
Become:
Gypsum Fibrosum powder 75 parts, Ore tailings 5 parts, croci 7 parts, 9 parts of flyash, alumina silicate fibre 9 parts, polymer emulsion 7
Part, calcium oxide extender 9 parts, 10 parts of ultra-fine sand, glass fibre 16 parts, Resina persicae 7 parts, hydrolytic resin 9 parts, 40 parts of water.