CN106116155A - 一种钧花釉料 - Google Patents
一种钧花釉料 Download PDFInfo
- Publication number
- CN106116155A CN106116155A CN201610513347.5A CN201610513347A CN106116155A CN 106116155 A CN106116155 A CN 106116155A CN 201610513347 A CN201610513347 A CN 201610513347A CN 106116155 A CN106116155 A CN 106116155A
- Authority
- CN
- China
- Prior art keywords
- raw material
- ancient unit
- anhydrite
- glaze
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种钧花釉料，它是由下列重量百分比的原料制备而成的：红长石30﹪，白长石20﹪，汝药5﹪，熔块10﹪，铜灰5﹪，南坡硬土10﹪，石英18﹪，氧化锡1.5﹪，氧化锌0.5﹪，对传统配方进行重新量化，自然原料配合相互作用，与化学原料在高温熔融作用下，会产生釉色整体色彩变化多样的独特艺术效果，同时色斑变化大开，极富美感，具有很好的社会和经济效益。
Description
技术领域
本发明涉及钧瓷领域，具体涉及一种钧花釉料。
背景技术
陶瓷的发展与人类的进步有着密切而久远的联系，它是人类文明的时代标志。陶瓷中的钧瓷，经理了唐、宋、元、明、清的岁月洗礼，形成了独特的艺术表现形式，钧窑有着极美的色彩，釉在窑中变化万千，并具有自然美感，今天仍为各地瓷窑所继承和仿效，并不断创新，使钧窑这枝绚丽的花朵重放异彩。
河南禹州的钧窑为北方青瓷窑系，目前仍然有着很大的成就，一般采用柴、煤、炭和天然气烧制，不同的烧制工艺产生的釉色变化也不同。外部是釉料在经过高温熔融时产生绚丽的色彩斑斓变化，原因主要在釉料的配方，这是影响钧瓷成品外色的重要因素，同时也是造成钧瓷入窑一色，出窑万彩的关键因素。
因此，本发明生产一种原料纯正，配比新颖，成品色彩绚丽的钧花釉料，具有广泛的市场前景。
发明内容
针对现有技术的不足，本发明提供一种原料纯正，配比新颖，成品色彩绚丽的钧花釉料，用来解决现有技术中的缺陷。
本发明的技术方案是这样实现：一种钧花釉料，它是由下列重量百分比的原料制备而成的：红长石29﹪至31﹪，白长石19﹪至21﹪，汝药4﹪至6﹪，熔块9﹪至11﹪，铜灰4﹪至6﹪，南坡硬土9﹪至11﹪，石英17﹪至19﹪，氧化锡1.4﹪至1.6﹪，氧化锌0.4﹪至0.6﹪。
它是由下列重量百分比的原料制备而成的：红长石30﹪，白长石20﹪，汝药5﹪，熔块10﹪，铜灰5﹪，南坡硬土10﹪，石英18﹪，氧化锡1.5﹪，氧化锌0.5﹪。
本发明具有如下的积极效果：本发明对传统配方进行重新量化，自然原料配合相互作用，与化学原料在高温熔融作用下，会产生釉色整体色彩变化多样的独特艺术效果，具有很好的社会和经济效益。
具体实施方式
实施例1：一种钧花釉料，它是由下列重量百分比的原料制备而成的：红长石30﹪，白长石20﹪，汝药5﹪，熔块10﹪，铜灰5﹪，南坡硬土10﹪，石英18﹪，氧化锡1.5﹪，氧化锌0.5﹪。
本发明对传统配方进行重新量化，自然原料配合相互作用，与化学原料在高温熔融作用下，会产生釉色整体色彩变化多样的独特艺术效果，具有很好的社会和经济效益。
实施例2：一种钧花釉料，它是由下列重量百分比的原料制备而成的：红长石29﹪，白长石21﹪，汝药6﹪，熔块9﹪，铜灰6﹪，南坡硬土9﹪，石英18﹪，氧化锡1.5﹪，氧化锌0.5﹪。
本发明对传统配方进行重新量化，自然原料配合相互作用，与化学原料在高温熔融作用下，会产生釉色整体色彩变化多样的独特艺术效果，具有很好的社会和经济效益。
长石属于硅酸盐矿物盐，其内部含量为钾元素、钠元素和钙元素等，分为黄色、白色和红色等，是釉料的主要成分，主要对于釉料的形成起到重要作用。禹州分布有众多矿藏。
汝药是河南当地出产的一种制备钧瓷釉料的石材，主要成分为二氧化硅，河南人民出版社《中国钧炉研究》一书123页有详细介绍。
熔块稳定性强，可作为釉的强溶剂。铜灰自制，主要成分一氧化铜含量98﹪。南坡硬土主要成分二氧化硅。河南人民出版社《中国钧炉研究》一书123页有详细介绍。
石英常用于钧瓷釉料中，本专利成分为15﹪，与其他成分相互配合。
氧化锌是一种常用的化学添加剂，广泛地应用于塑料、硅酸盐制品、合成橡胶、润滑油、油漆涂料、药膏、粘合剂、食品、电池、阻燃剂等产品的制作中。氧化锌的能带隙和激子束缚能较大，透明度高，有优异的常温发光性能。
氧化锡为白色、淡黄色或淡灰色四方、六方或斜方晶系粉末。熔点1630℃。
上述天然原料与化工原料配合使用，在高温熔融作用下，会产生釉色整体色彩变化多样的独特艺术效果，同时色斑变化大开，极富美感。具有很好的社会和经济效益。
Claims (2)
1.一种钧花釉料，其特征在于，它是由下列重量百分比的原料制备而成的：红长石29﹪至31﹪，白长石19﹪至21﹪，汝药4﹪至6﹪，熔块9﹪至11﹪，铜灰4﹪至6﹪，南坡硬土9﹪至11﹪，石英17﹪至19﹪，氧化锡1.4﹪至1.6﹪，氧化锌0.4﹪至0.6﹪。
2.根据权利要求1所述的钧花釉料，其特征在于，它是由下列重量百分比的原料制备而成的：红长石30﹪，白长石20﹪，汝药5﹪，熔块10﹪，铜灰5﹪，南坡硬土10﹪，石英18﹪，氧化锡1.5﹪，氧化锌0.5﹪。