CN106003333A - Wicker product anti-pest and anti-mildew method capable of enhancing wicker knitting capacity - Google Patents
Wicker product anti-pest and anti-mildew method capable of enhancing wicker knitting capacity Download PDFInfo
- Publication number
- CN106003333A CN106003333A CN201610551281.9A CN201610551281A CN106003333A CN 106003333 A CN106003333 A CN 106003333A CN 201610551281 A CN201610551281 A CN 201610551281A CN 106003333 A CN106003333 A CN 106003333A
- Authority
- CN
- China
- Prior art keywords
- wicker
- parts
- temperature
- proof
- mass fraction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wicker product anti-pest and anti-mildew method capable of enhancing wicker knitting capacity. The method includes the following steps of (1) wicker peeling, (2) softening treatment, (3) wicker knitting and (4) anti-pest and anti-mildew treatment. By the adoption of the method, all the steps are matched scientifically and reasonably, and wicker products manufactured are good in anti-pest and anti-mildew effect. Compared with the prior art, the service life under the conventional using condition can be prolonged by about 20%, and the service life under the high-humidity condition can be prolonged by over 50%. Moreover, using stability is good, anti-deformation capacity is high, and the use value is good.
Description
Technical field
The invention belongs to wicker plaiting article manufacture field, a kind of method being specifically related to wicker products Vermins-proof mildew-proof strengthening wicker braiding.
Background technology
Wicker plaiting article is China's one traditional technology, and present wicker products is commercially popular, wicker products of a great variety, has the polytypes such as seat, basket, basket, dustpan, round-bottomed basket, crate, shallow basket made of wicker or thin bamboo strips, the gaily decorated basket, bamboo strainer, food dish at domestic aspect.Export trade aspect, has formed buck basket, flower pot coat, picnic tableware basket, hanging basket, lampshade, kennel, cat litter, Bird's Nest etc. through developing and design multiple, forms the appreciation effect that low-grade goods become high-grade in foreign trade, very popular.Wicker products is with wicker as primary raw material, but wicker is the most infested, mouldy, causes knitting shortening in service life.The most infested in order to solve wicker, mouldy phenomenon, the most employing chemical agents carry out immersion treatment, but its toxicity is stronger, remain more serious, toxic residue is often caused to leak during knitting uses, affect user healthy, although people attempt using herbal mediciment to carry out immersion treatment, have a better effect, it also avoid the problem that chemical agent toxicity is stronger, but its prepared composition is complex with method, cost is the highest, it is not easy to promote, in addition, wicker products effect under conditions of humidity is higher after above two mode processes can be greatly reduced, and because being all that wicker surface is processed, once there is damage in surface, the easiest to be mouldy infested.Content of ashes in wicker is about 2%, and this type of material is the dependence composition of the fungi survivings such as trichoderma.
Summary of the invention
It is desirable to provide a kind of method of wicker products Vermins-proof mildew-proof strengthening wicker braiding.
The present invention is achieved through the following technical solutions:
A kind of method of wicker products Vermins-proof mildew-proof strengthening wicker braiding, comprises the steps:
(1) wicker peeling: harvested wicker is carried out peeling operation, then puts it into soaking and washing 20min in the salt solution that mass fraction is 3%, standby after being placed under the sun dry in the sun with clear water after being finally drawn off rinsing well 1 ~ 2 day；
(2) sofening treatment:
A. the wicker after dry in the sun is put into temperature be 140 ~ 150 DEG C, pressure be 5 ~ 6MPa, relative humidity be 70 ~ 75% vapor tight tank in, the state of normal temperature and pressure it is promptly restored to after heat-insulation pressure keeping 1h, put into after taking-up and fill in the compound enzyme aqueous solution that mass fraction is 2%, keeping aqueous temperature is 38 ~ 42 DEG C, put it into again in vapor tight tank after soaking enzymolysis 10min, processing by above-mentioned parameter condition, this is a circulation, amounts to circulation operation 3 times；Containing cellulase, tannase, pectase in described compound enzyme, the weight ratio of three is 5:1:2；
B. the wicker after being processed by operation a is put in the hydrochloric acid solution that mass fraction is 4%, heating keeps solution temperature to be 50 DEG C, immersion treatment 15min, put it in the hydrofluoric acid solution that mass fraction is 5% after taking-up, heating keeps solution temperature to be 65 DEG C, immersion treatment 15min, put it in the salpeter solution that mass fraction is 5% after taking-up, heating keeps solution temperature to be 70 DEG C, immersion treatment 15min, put in the sodium hydroxide solution that mass fraction is 7% after taking-up, heating keeps solution temperature to be 75 DEG C, immersion treatment 15min, rinse well standby after finally taking out with clear water；
C. will operation b process after wicker put into bating liquor dries after immersion treatment 2h standby；Described bating liquor is made up of the material of following weight portion: 0.5 part of trimethyl phosphate, 3 parts of Oleum Brassicae campestriss, 1.5 parts of stearic acid sodium, 2 parts of sodium bicarbonate, 1 part of epoxy modified polysiloxane, 50 parts of water；
(3) wicker braiding:
Wicker after step (2) sofening treatment is woven, after braiding, obtains semi-finished product for standby；
(4) Vermins-proof mildew-proof processes:
A. after step (3) being woven, the semi-finished product of gained soak in complex liquid, and heating keeps the temperature of complex liquid to be 55 DEG C, takes out after immersion treatment 1h, standby after rinsing well with clear water；Described complex liquid is made up of the material of following weight portion: 4 parts of diethanolamine, 5 parts of ethyl acetates, 8 parts of polyvinyl alcohol, 5 parts of Fructus Toosendan leaf extracts, 100 parts of water；
B. the semi-finished product after being processed by operation a are put into and are dried under conditions of temperature is 48 ~ 50 DEG C, get product.
Further, the time that step (3) weaves is within 2 days.
Further, step (4) described Fructus Toosendan leaf extract is the water extract of Melia azedarach L. cotyledon.
There is advantages that
(1) present invention is when sofening treatment, first wicker is carried out multiple high temp high pressure, enzymolysis processing, can the overall organizational structure of loose wicker, and tiny gap can be formed at wicker shallow-layer enzymolysis, and do not interfere with the intensity of entirety, i.e. improve its pliability and bating effect, it is beneficial to again the process of subsequent step, the most again it is carried out repeatedly, different classes of acid-alkali treatment, can effectively reduce the content of ashes in wicker, reduce the viable conditions of the funguses such as trichoderma, improve the insect protected of wicker, fungicidal properties.
(2) with complex liquid, semi-finished product wicker products is processed, the effective ingredient in complex liquid is utilized to carry out combination reaction with the material in wicker, it is filled with gap during sofening treatment, enhancing intensity and the wear resistence of entirety, the Fructus Toosendan leaf extract of interpolation can assist to improve the Vermins-proof mildew-proof characteristic of wicker further.
(3) collocation of the inventive method each step is scientific and reasonable, the wicker products insect protected, the anti-mold effect that prepare are preferable, compared with prior art, service life under its normal service condition can extend about 20%, service life under high humidity conditions can extend more than 50%, and its stability in use is preferable, anti-deformation ability is relatively strong, and use value is preferable.
Detailed description of the invention
Embodiment 1
A kind of method of wicker products Vermins-proof mildew-proof strengthening wicker braiding, comprises the steps:
(1) wicker peeling: harvested wicker is carried out peeling operation, then puts it into soaking and washing 20min in the salt solution that mass fraction is 3%, standby after being placed under the sun dry in the sun with clear water after being finally drawn off rinsing well 1 ~ 2 day；
(2) sofening treatment:
A. the wicker after dry in the sun is put into temperature be 143 DEG C, pressure be 5.7MPa, relative humidity be 73 ~ 75% vapor tight tank in, the state of normal temperature and pressure it is promptly restored to after heat-insulation pressure keeping 1h, put into after taking-up and fill in the compound enzyme aqueous solution that mass fraction is 2%, keeping aqueous temperature is 40 DEG C, put it into again in vapor tight tank after soaking enzymolysis 10min, processing by above-mentioned parameter condition, this is a circulation, amounts to circulation operation 3 times；Containing cellulase, tannase, pectase in described compound enzyme, the weight ratio of three is 5:1:2；
B. the wicker after being processed by operation a is put in the hydrochloric acid solution that mass fraction is 4%, heating keeps solution temperature to be 50 DEG C, immersion treatment 15min, put it in the hydrofluoric acid solution that mass fraction is 5% after taking-up, heating keeps solution temperature to be 65 DEG C, immersion treatment 15min, put it in the salpeter solution that mass fraction is 5% after taking-up, heating keeps solution temperature to be 70 DEG C, immersion treatment 15min, put in the sodium hydroxide solution that mass fraction is 7% after taking-up, heating keeps solution temperature to be 75 DEG C, immersion treatment 15min, rinse well standby after finally taking out with clear water；
C. will operation b process after wicker put into bating liquor dries after immersion treatment 2h standby；Described bating liquor is made up of the material of following weight portion: 0.5 part of trimethyl phosphate, 3 parts of Oleum Brassicae campestriss, 1.5 parts of stearic acid sodium, 2 parts of sodium bicarbonate, 1 part of epoxy modified polysiloxane, 50 parts of water；
(3) wicker braiding:
Wicker after step (2) sofening treatment is woven, after braiding, obtains semi-finished product for standby；
(4) Vermins-proof mildew-proof processes:
A. after step (3) being woven, the semi-finished product of gained soak in complex liquid, and heating keeps the temperature of complex liquid to be 55 DEG C, takes out after immersion treatment 1h, standby after rinsing well with clear water；Described complex liquid is made up of the material of following weight portion: 4 parts of diethanolamine, 5 parts of ethyl acetates, 8 parts of polyvinyl alcohol, 5 parts of Fructus Toosendan leaf extracts, 100 parts of water；
B. the semi-finished product after being processed by operation a are put into and are dried under conditions of temperature is 50 DEG C, get product.
Further, the time that step (3) weaves is within 2 days.
Further, step (4) described Fructus Toosendan leaf extract is the water extract of Melia azedarach L. cotyledon.
Comparative example 1
This comparative example 1 compared with Example 1, when sofening treatment, does not carry out operating a process, directly carries out operating b, c process wicker, and method step in addition is the most identical.
Comparative example 2
This comparative example 2 compared with Example 1, when sofening treatment, does not carry out operating b process, directly carries out operating a, c process wicker, and method step in addition is the most identical.
Matched group
Existing wicker Vermins-proof mildew-proof processing method.
In order to contrast using effect of the present invention, to process by above-mentioned four kinds of methods respectively with a collection of wicker product, then special humidity mycete test experiments is carried out, specific as follows: the wicker products after processing is respectively put in proof box, temperature in Control experiment case is 30 DEG C, normal pressure, relative humidity is 95%, Trichoderma viride, aspergillus niger, aspergillus terreus, green ochre penicillium sp and white rake teeth bacterium it is inoculated with in proof box, statistics by fungal infection area by 5% time total duration of being experienced, representing with mildew-resistant duration, weigh anti-mold effect, following table is corresponding correction data:
| Embodiment 1 | Comparative example 1 | Comparative example 2 | Matched group | |
| Mildew-resistant duration (my god) | 103 | 90 | 80 | 65 |
Claims (3)
1. the method for the wicker products Vermins-proof mildew-proof strengthening wicker braiding, it is characterised in that comprise the steps:
(1) wicker peeling: harvested wicker is carried out peeling operation, then puts it into soaking and washing 20min in the salt solution that mass fraction is 3%, standby after being placed under the sun dry in the sun with clear water after being finally drawn off rinsing well 1 ~ 2 day；
(2) sofening treatment:
A. the wicker after dry in the sun is put into temperature be 140 ~ 150 DEG C, pressure be 5 ~ 6MPa, relative humidity be 70 ~ 75% vapor tight tank in, the state of normal temperature and pressure it is promptly restored to after heat-insulation pressure keeping 1h, put into after taking-up and fill in the compound enzyme aqueous solution that mass fraction is 2%, keeping aqueous temperature is 38 ~ 42 DEG C, put it into again in vapor tight tank after soaking enzymolysis 10min, processing by above-mentioned parameter condition, this is a circulation, amounts to circulation operation 3 times；Containing cellulase, tannase, pectase in described compound enzyme, the weight ratio of three is 5:1:2；
B. the wicker after being processed by operation a is put in the hydrochloric acid solution that mass fraction is 4%, heating keeps solution temperature to be 50 DEG C, immersion treatment 15min, put it in the hydrofluoric acid solution that mass fraction is 5% after taking-up, heating keeps solution temperature to be 65 DEG C, immersion treatment 15min, put it in the salpeter solution that mass fraction is 5% after taking-up, heating keeps solution temperature to be 70 DEG C, immersion treatment 15min, put in the sodium hydroxide solution that mass fraction is 7% after taking-up, heating keeps solution temperature to be 75 DEG C, immersion treatment 15min, rinse well standby after finally taking out with clear water；
C. will operation b process after wicker put into bating liquor dries after immersion treatment 2h standby；Described bating liquor is made up of the material of following weight portion: 0.5 part of trimethyl phosphate, 3 parts of Oleum Brassicae campestriss, 1.5 parts of stearic acid sodium, 2 parts of sodium bicarbonate, 1 part of epoxy modified polysiloxane, 50 parts of water；
(3) wicker braiding:
Wicker after step (2) sofening treatment is woven, after braiding, obtains semi-finished product for standby；
(4) Vermins-proof mildew-proof processes:
A. after step (3) being woven, the semi-finished product of gained soak in complex liquid, and heating keeps the temperature of complex liquid to be 55 DEG C, takes out after immersion treatment 1h, standby after rinsing well with clear water；Described complex liquid is made up of the material of following weight portion: 4 parts of diethanolamine, 5 parts of ethyl acetates, 8 parts of polyvinyl alcohol, 5 parts of Fructus Toosendan leaf extracts, 100 parts of water；
B. the semi-finished product after being processed by operation a are put into and are dried under conditions of temperature is 48 ~ 50 DEG C, get product.
The method of a kind of wicker products Vermins-proof mildew-proof strengthening wicker braiding the most according to claim 1, it is characterised in that the time that step (3) weaves is within 2 days.
The method of a kind of wicker products Vermins-proof mildew-proof strengthening wicker braiding the most according to claim 1, it is characterised in that step (4) described Fructus Toosendan leaf extract is the water extract of Melia azedarach L. cotyledon.