CN106009278A - Dampproof woven bag material - Google Patents
Dampproof woven bag material Download PDFInfo
- Publication number
- CN106009278A CN106009278A CN201610488996.4A CN201610488996A CN106009278A CN 106009278 A CN106009278 A CN 106009278A CN 201610488996 A CN201610488996 A CN 201610488996A CN 106009278 A CN106009278 A CN 106009278A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven bag
- muscovitum
- dampproof
- bag material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of plastic woven bags, particularly a dampproof woven bag material which is prepared by carrying out mixing, drying and stirring, melting and film extrusion on the following raw materials in parts by weight: 100 parts of polypropylene, 50 parts of polytetrafluoroethylene, 6-10 parts of clay, 1-4 parts of limestone, 2-4 parts of epoxy resin, 0.5-1 part of decabromodiphenyl oxide and 15-25 parts of modified additive. The dampproof plastic woven bag produced by the material has excellent dampproof property, thereby protecting the material in the plastic woven bag and prolonging the service life of the plastic woven bag.
Description
Technical field
The present invention relates to Polywoven Bag field, specifically one can damp-proof woven bag material.
Background technology
Polywoven Bag primary raw material composition is polypropylene, polyethylene.It is now widely used for the necks such as cement, fertilizer, chemical industry
Territory.Its main production is to utilize raw material to knit through extrusion film, wire drawing, rolling, circle, print, cut, sew,
Finally give Polywoven Bag finished product.It is all that polypropylene, polyethylene add interpolation masterbatch and be dried and stir that traditional woven bag produces material
Mix and be mixed to prepare, the Polywoven Bag produced is the most aging under summer high temperature and ultraviolet irradiate, peeling, fracture, powder
Broken, easily infiltration is entered in a humid environment, not only affects the article in plastic bag, also affects Polywoven Bag and uses
Effect.
Summary of the invention
In order to make up the deficiencies in the prior art, heretofore described one can damp-proof woven bag material, use the present invention
The Polywoven Bag humidity resistance of the manufacture of materials of formula is superior, i.e. protects material in Polywoven Bag, improves again plastics
The service life of woven bag.
The technical solution adopted for the present invention to solve the technical problems is: one can damp-proof woven bag material, by following heavy
Amount part raw material passes through mixing, dry stirring, melted, film extrusion operation is prepared: polypropylene 100 parts, politef
50 parts, clay 6～10 parts, limestone 1～4 parts, epoxy resin 2～4 parts, deca-BDE 0.5～1 part,
Property-modifying additive 15～25 parts；
Described property-modifying additive is made up of following raw material: Muscovitum 40～50 parts, calcium sulfate 15～18 parts, chlorine
Change sodium 8～13 parts, inactive anhydrous copper sulfate 1～3 parts, aluminium oxide 2～3 parts, silica flour 1～3 parts；Preparation method
Be by Muscovitum with 15～20% hydrochloric acid solution wash 15～25 minutes, then filtration drying process, dried Muscovitum and
Silica flour is sent into together after uniformly mixing and is burnt training in 350～450 DEG C of continuous tunnel furnaces, burns the mixture after training and grinds, and cross 250～
300 mesh mesh screens collect powder, collect powder and mix with other residual componentss, and add deionized water and be stirred, stirring
Response time is 2 hours, granulating and drying the most again, and size is 2-4 millimeter.
Beneficial effect: heretofore described one can damp-proof woven bag material, use inventive formulation manufacture of materials
Polywoven Bag humidity resistance superior, i.e. protect material in Polywoven Bag, improve again the use longevity of Polywoven Bag
Life.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with
Embodiment, is expanded on further the present invention.
One can damp-proof woven bag material, by following raw material by mixing, be dried and stir, melt, be extruded into
Membrane process prepares: polypropylene 100 parts, politef 50 parts, clay 6～10 parts, limestone 1～4 parts, ring
Epoxy resins 2～4 parts, deca-BDE 0.5～1 part, property-modifying additive 15～25 parts；
Described property-modifying additive is made up of following raw material: Muscovitum 40～50 parts, calcium sulfate 15～18 parts, chlorine
Change sodium 8～13 parts, inactive anhydrous copper sulfate 1～3 parts, aluminium oxide 2～3 parts, silica flour 1～3 parts；Preparation method
Be by Muscovitum with 15～20% hydrochloric acid solution wash 15～25 minutes, then filtration drying process, dried Muscovitum and
Silica flour is sent into together after uniformly mixing and is burnt training in 350～450 DEG C of continuous tunnel furnaces, burns the mixture after training and grinds, and cross 250～
300 mesh mesh screens collect powder, collect powder and mix with other residual componentss, and add deionized water and be stirred, stirring
Response time is 2 hours, granulating and drying the most again, and size is 2-4 millimeter.
The ultimate principle of the present invention, principal character and advantage have more than been shown and described.Skilled person will appreciate that of the industry,
The present invention is not restricted to the described embodiments, the principle that the present invention is simply described of the description in above-described embodiment and description,
Without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these changes and improvements are all
Fall in scope of the claimed invention.Claimed scope is by appending claims and equivalent circle thereof
Fixed.
Claims (2)
1. one kind can damp-proof woven bag material, it is characterised in that: by following raw material by mixing, be dried and stir
Mix, melt, film extrusion operation prepares: polypropylene 100 parts, politef 50 parts, clay 6～10 parts, Calx
Stone 1～4 parts, epoxy resin 2～4 parts, deca-BDE 0.5～1 part, property-modifying additive 15～25 parts.
One the most according to claim 1 can damp-proof woven bag material, it is characterised in that: described modified interpolation
Agent is made up of following raw material: Muscovitum 40～50 parts, calcium sulfate 15～18 parts, sodium chloride 8～13 parts, activity
Anhydrous cupric sulfate 1～3 parts, aluminium oxide 2～3 parts, silica flour 1～3 parts；Preparation method is with 15～20% by Muscovitum
Hydrochloric acid solution wash 15～25 minutes, then filtration drying process, dried Muscovitum and silica flour uniformly mix after one
Rise to burn in sending into 350～450 DEG C of continuous tunnel furnaces and train, burn the mixture after training and grind, and cross 250～300 mesh mesh screens collection powder,
Collecting powder to mix with other residual componentss again, and add deionized water and be stirred, the stirring response time is 2 hours, so
After granulating and drying again, size is 2-4 millimeter.