CN106007440A - Magnesium gelling product modifier and preparation method thereof - Google Patents
Magnesium gelling product modifier and preparation method thereof Download PDFInfo
- Publication number
- CN106007440A CN106007440A CN201610349086.8A CN201610349086A CN106007440A CN 106007440 A CN106007440 A CN 106007440A CN 201610349086 A CN201610349086 A CN 201610349086A CN 106007440 A CN106007440 A CN 106007440A
- Authority
- CN
- China
- Prior art keywords
- mixing plant
- salt
- add
- parts
- modifier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a magnesium gelling product modifier and a preparation method thereof. The magnesium gelling product modifier comprises the following components in parts by weight: 15-25 parts of rubber powder, 10-20 parts of brine, 25-35 parts of clear water and 1-3 parts of titanium dioxide. The brine is a magnesium chloride water solution in which the mass ratio of magnesium chloride to water is (0.8-0.9):1. The invention also discloses a preparation method of the magnesium gelling product modifier. The preparation method comprises the following steps: S1: weighing the raw materials; S2: manufacturing the brine; S3: primary proportioning; S4: adding the clear water; S5: adding the titanium dioxide; and S6: adding the auxiliary materials. The magnesium gelling product modifier can improve the accumulation state of 5.1.8 crystal seeds and block capillary channels in the system, thereby achieving the goal of halogenide resistance. The magnesium gelling product modifier can enhance the moisture absorption resistance, halogenide resistance and scumming resistance of the magnesite product and enhance the strength and service life of the magnesite product.
Description
Technical field
The present invention relates to energy-conserving and environment-protective building materials field, a kind of magnesial gelatinized goods formula of modifier and
Its preparation method.
Background technology
When producing magnesite product due to raw material, formula, production technology goes wrong, causes Pedicellus et Pericarpium Trapae
The disadvantage damp suction surface halide accumulation of magnesium products, it is moist that goods occur returning halogen rear surface, the globule occurs, has a strong impact on dress
Decorations quality and Usage parameter control, reduces product strength, shortens product service life.
Summary of the invention
It is an object of the invention to provide a kind of magnesial gelatinized goods formula of modifier and preparation method thereof, with
The problem solving to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme: a kind of magnesial gelatinized goods modifying agent
Formula, including following composition by weight: rubber powder 15-25 part, salt 10-20 part, clear water 25-35 part,
Titanium dioxide 1-3 part；
Wherein, described salt is magnesium chloride brine, and magnesium chloride is 0.8-0.9:1 with the mass ratio of water；
Described rubber powder is phosphate and/or sulfate.
Further, described rubber powder is the mixture of ferrous sulfate and sodium phosphate.
The preparation method of a kind of magnesial gelatinized goods modifying agent, comprises the following steps:
S1: weigh raw material, by the raw material of use in need according to certain ratio, weigh,
And deposit standby respectively；
S2: make salt, the raw material of salt is placed individually in mixing plant and is stirred, during stirring
Between be 10-16 minute, whipping temp is 20-28 degree Celsius, to be mixed complete after, the halogen that will make
Water storage is standby；
S3: preliminary dispensing, the salt and the rubber powder that previous step are made are put into mixing plant and are stirred, and stir
The time of mixing is 18-24 minute, until the bottom of mixing plant no longer has bubble to produce；
S4: add clear water, when not having bubble to produce in mixing plant, add in mixing plant and weigh
Clear water, and continue stirring 5-10 minute；
S5: add titanium dioxide, add load weighted titania powder in mixing plant, and continue
Being stirred, mixing time is 3-15 minute；
S6: complete.
Compared with prior art, the invention has the beneficial effects as follows: the present invention can improve 518 crystal seeds
Stacking states, the capillary channel in blocking system, thus reach the purpose of anti-halogen, magnesite system can be improved
Product anti-moisture absorption returns the ability of halogen, scum, increases magnesite product intensity and service life.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that institute
The embodiment described is only a part of embodiment of the present invention rather than whole embodiments.Based on this
Embodiment in bright, those of ordinary skill in the art are obtained under not making creative work premise
Every other embodiment, broadly falls into the scope of protection of the invention.
Embodiment one
The present invention provides a kind of technical scheme: a kind of magnesial gelatinized goods formula of modifier, including following heavy
Amount component: 10 parts of the salt that mass ratio is 0.8:1 of 15 parts of ferrous sulfate powder, magnesium chloride and water,
25 parts of clear water, titania powder 1 part.
The preparation method of a kind of magnesial gelatinized goods modifying agent, comprises the following steps:
S1: weigh raw material, by the raw material of use in need according to certain ratio, weigh,
And deposit standby respectively；
S2: make salt, the raw material of salt is placed individually in mixing plant and is stirred, during stirring
Between be 10 minutes, whipping temp is 20-28 degree Celsius, to be mixed complete after, the salt made is deposited
Deposit is used；
S3: preliminary dispensing, the salt and the rubber powder that previous step are made are put into mixing plant and are stirred, and stir
The time of mixing is 18 minutes, until the bottom of mixing plant no longer has bubble to produce；
S4: add clear water, when not having bubble to produce in mixing plant, add in mixing plant and weigh
Clear water, and continue to stir 5 minutes；
S5: add titanium dioxide, add load weighted titania powder in mixing plant, and continue
Being stirred, mixing time is 3 minutes；
S6: add adjuvant, add load weighted adjuvant in mixing plant, be stirred, mixing time
It is 2 minutes, completes.
Embodiment two
The present invention provides a kind of technical scheme: a kind of magnesial gelatinized goods formula of modifier, including following heavy
Amount component: ferrous sulfate and sodium phosphate mixed powder 17 parts, 11.013 parts of salt, 28 parts of clear water, dioxy
Change titanium powder 1.5 parts, adjuvant 1.106 parts；
Wherein, described salt is magnesium chloride brine, and magnesium chloride is 0.9:1 with the mass ratio of water.
The preparation method of a kind of magnesial gelatinized goods modifying agent, comprises the following steps:
S1: weigh raw material, by the raw material of use in need according to certain ratio, weigh,
And deposit standby respectively；
S2: make salt, the raw material of salt is placed individually in mixing plant and is stirred, during stirring
Between be 11 minutes, whipping temp is 13 degrees Celsius, to be mixed complete after, will make salt storage
Standby；
S3: preliminary dispensing, the salt and the rubber powder that previous step are made are put into mixing plant and are stirred, and stir
The time of mixing is 19 minutes, until the bottom of mixing plant no longer has bubble to produce；
S4: add clear water, when not having bubble to produce in mixing plant, add in mixing plant and weigh
Clear water, and continue to stir 6 minutes；
S5: add titanium dioxide, add load weighted titania powder in mixing plant, and continue
Being stirred, mixing time is 5 minutes；
S6: add adjuvant, add load weighted adjuvant in mixing plant, be stirred, mixing time
It is 3 minutes, completes.
Embodiment three
The present invention provides a kind of technical scheme: a kind of magnesial gelatinized goods formula of modifier, including following heavy
Amount component: 18 parts of sodium phosphate powder, 13.017 parts of salt, 29 parts of clear water, titania powder 1.8 parts,
Adjuvant 1.408 parts；
Wherein, described salt is magnesium chloride brine, and magnesium chloride is 0.9:1 with the mass ratio of water.
The preparation method of a kind of magnesial gelatinized goods modifying agent, comprises the following steps:
S1: weigh raw material, by the raw material of use in need according to certain ratio, weigh,
And deposit standby respectively；
S2: make salt, the raw material of salt is placed individually in mixing plant and is stirred, during stirring
Between be 13 minutes, whipping temp is 17 degrees Celsius, to be mixed complete after, will make salt storage
Standby；
S3: preliminary dispensing, the salt and the rubber powder that previous step are made are put into mixing plant and are stirred, and stir
The time of mixing is 20 minutes, until the bottom of mixing plant no longer has bubble to produce；
S4: add clear water, when not having bubble to produce in mixing plant, add in mixing plant and weigh
Clear water, and continue to stir 8 minutes；
S5: add titanium dioxide, add load weighted titania powder in mixing plant, and continue
Being stirred, mixing time is 7 minutes；
S6: add adjuvant, add load weighted adjuvant in mixing plant, be stirred, mixing time
It is 6 minutes, completes.
Embodiment four
The present invention provides a kind of technical scheme: a kind of magnesial gelatinized goods formula of modifier, including following heavy
Amount component: ferrous sulfate and magnesium phosphate mixed powder 24 parts, 18.02 parts of salt, 34 parts of clear water, dioxy
Changing titanium valve 2.8 parts, wherein, described salt is magnesium chloride brine, and magnesium chloride is 0.9 with the mass ratio of water:
1。
The preparation method of a kind of magnesial gelatinized goods modifying agent, comprises the following steps:
S1: weigh raw material, by the raw material of use in need according to certain ratio, weigh,
And deposit standby respectively；
S2: make salt, the raw material of salt is placed individually in mixing plant and is stirred, during stirring
Between be 15 minutes, whipping temp is 25 degrees Celsius, to be mixed complete after, will make salt storage
Standby；
S3: preliminary dispensing, the salt and the rubber powder that previous step are made are put into mixing plant and are stirred, and stir
The time of mixing is 22 minutes, until the bottom of mixing plant no longer has bubble to produce；
S4: add clear water, when not having bubble to produce in mixing plant, add in mixing plant and weigh
Clear water, and continue to stir 8 minutes；
S5: add titanium dioxide, add load weighted titania powder in mixing plant, and continue
Being stirred, mixing time is 12 minutes；
S6: add adjuvant, add load weighted adjuvant in mixing plant, be stirred, mixing time
It is 6 minutes, completes.
By above-mentioned four groups of embodiments being carried out contrast experiment, often group embodiment all can improve magnesite product resist
Damp suction surface halide accumulation, the ability of scum, increase magnesite product intensity and service life, the wherein side of embodiment one
Case anti-halogen best results.
Although an embodiment of the present invention has been shown and described, for those of ordinary skill in the art
Speech, it is possible to understand that these embodiments can be carried out without departing from the principles and spirit of the present invention
Multiple change, revising, replace and modification, the scope of the present invention is limited by claims and equivalent thereof
Fixed.
Claims (3)
1. a magnesial gelatinized goods formula of modifier, it is characterised in that include following composition by weight: glue
Powder 15-25 part, salt 10-20 part, clear water 25-35 part, titania powder 1-3 part；
Wherein, described salt is magnesium chloride brine, and magnesium chloride is 0.8-0.9:1 with the mass ratio of water；
Described rubber powder is phosphate and/or sulfate.
Magnesial gelatinized goods formula of modifier the most according to claim 1, it is characterised in that described
Rubber powder is the mixture of ferrous sulfate and sodium phosphate.
3. a preparation method for the magnesial gelatinized goods modifying agent described in claim 1 or 2, its feature
It is, comprises the following steps:
S1: weigh raw material, by the raw material of use in need according to certain ratio, weigh,
And deposit standby respectively；
S2: make salt, the raw material of salt is placed individually in mixing plant and is stirred, during stirring
Between be 10-16 minute, whipping temp is 20-28 degree Celsius, to be mixed complete after, the halogen that will make
Water storage is standby；
S3: preliminary dispensing, the salt and the rubber powder that previous step are made are put into mixing plant and are stirred, and stir
The time of mixing is 18-24 minute, until the bottom of mixing plant no longer has bubble to produce；
S4: add clear water, when not having bubble to produce in mixing plant, add in mixing plant and weigh
Clear water, and continue stirring 5-10 minute；
S5: add titanium dioxide, add load weighted titania powder in mixing plant, and continue
Being stirred, mixing time is 3-15 minute；
S6: complete.