CN105968918A - Antibacterial waterborne polyurethane luminescent reflective road marking coating and preparation method thereof - Google Patents
Antibacterial waterborne polyurethane luminescent reflective road marking coating and preparation method thereof Download PDFInfo
- Publication number
- CN105968918A CN105968918A CN201610567518.2A CN201610567518A CN105968918A CN 105968918 A CN105968918 A CN 105968918A CN 201610567518 A CN201610567518 A CN 201610567518A CN 105968918 A CN105968918 A CN 105968918A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterborne polyurethane
- aqueous polyurethane
- preparation
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial waterborne polyurethane luminescent reflective road marking coating and a preparation method thereof. The antibacterial waterborne polyurethane luminescent reflective road marking coating is prepared from the following raw materials in parts by weight: 1-3 parts of nano silver, 1-3 parts of GdCl3, 1-2 parts of Mg(OH)2, 6-10 parts of ethylene glycol, 40-50 parts of waterborne polyurethane emulsion, 3-5 parts of ethyl acrylate, 1-3 parts of citric acid, 10-15 parts of titanium dioxide, 10-15 parts of barite powder, 10-15 parts of glass beads and appropriate acrylic resin emulsion, deionized water and ethanol. The waterborne polyurethane coating disclosed by the invention has the characteristics of resource saving, pollution reduction, low toxicity and environmental friendliness; and meanwhile, the luminescent property of the waterborne polyurethane coating is improved by a rare-earth nano luminescent material so that the waterborne polyurethane coating is more suitable for the road sections with bad lighting effect, and the potential safety hazard of the road is reduced.
Description
Technical field
The present invention relates to a kind of marking paint, belong to paint field, particularly relate to a kind of antibacterial aqueous polyurethane luminous reflecting road mark paint and preparation method thereof.
Background technology
Roadmarking is used for guiding traffic, is to improve traffic safety, ensure the unimpeded important infrastructure of road traffic.China is stepping up traffic infrastructure level, construction of modern road network, simultaneously being continuously increased along with vehicle, road load and graticule abrasion and is constantly increasing the weight of, and these all illustrate that Current traffic gage mark coating has huge market demand.
Wherein water paint is a kind of relatively new type coating on Coating Market, and for more traditional solvent-based paints coating, water paint is with water as solvent, during producing and using
VOC is well below solvent-based paints, little to human injury, and therefore, water paint is more saved resource, reduced pollution, low toxic and environment-friendly.Progressively replace solvent-based paints coating to represent the developing direction of coating industry with water paint.
Aqueous polyurethane is to replace organic solvent as the new polyurethane system of disperse medium using water, amido-containing acid ester base, urea bond and ionic bond in its molecular structure, cohesive energy is high, cohesive force is strong, and can be by changing the short proportion adjustment polyurethane performance with soft or hard section of soft segment length, so, exploitation aqueous polyurethane marking paint is a good selection.Wu Mingjiang utilizes the Material synthesis such as waterborne polyurethane resin and blanc fixe a kind of white marking paint in the development of aqueous polyurethane marking paint, but reflective function is the most superior, do not possesses luminescent properties simultaneously, limit it in dark location, such as freeway tunnel, and the application of driving in evening.
Rare earth element show because of the electronic structure of its uniqueness excellent monochromaticity, anti-light Bleachability, fluorescence lifetime length and
The characteristics such as Stocke displacement is big and have a wide range of applications in fields such as materials.Rare earth luminescent material has luminosity height, length persistence not available for other luminescent material, wavelength of transmitted light is adjustable, the radiationless advantage such as pollution-free, receives the extensive concern of people about its research applied.
Summary of the invention
Based on above thinking, it is an object of the invention to provide a kind of reflective function good, strong with road adhesive force, easy construction, and there is the aqueous polyurethane road mark paint of luminescent properties.
The technical problem to be solved uses following technical scheme to realize:
1. an antibacterial aqueous polyurethane luminous reflecting road mark paint, it is characterised in that be made up of the raw material of following weight portion:
Nanometer silver 1-3, GdCl3
1-3, Mg (OH)2 1-2, ethylene glycol 6-10, NaF 1-3, aqueous polyurethane emulsion 40-50, ethyl acrylate 3-5, citric acid 1-3, titanium dioxide 10-15, blanc fixe 10-15, glass microballoon 10-15, emulsion acrylic resin is appropriate, and deionized water is appropriate, appropriate amount of ethanol；
The content of described aqueous polyurethane emulsion is 40-50%.
2. one antibacterial aqueous polyurethane luminous reflecting road mark paint described in and preparation method thereof, it is characterised in that be made up of following steps:
a.
By GdCl3It is dissolved in 3-5 part ethylene glycol solution, stirs to clarify solution；
B. NaF is dissolved in residue ethylene glycol solution, after stirring to clarify solution, mixes with step a gained settled solution rapidly, stir；
c.
In step b gained liquid, add sodium lauryl sulphate, move in reactor, put into 20-25h in 150-200 DEG C of baking oven.
d.
Take out reactor after having reacted, be cooled to room temperature, after separating with centrifuge, be filtrated to get precipitation, precipitate 3-5 time by deionized water and washing with alcohol respectively；
e.
It is dried 20-25h under the conditions of step d gained is deposited in 40-80 DEG C, obtains intermediate；
F. by nanometer silver, Mg (OH)2 、Titanium dioxide, blanc fixe, glass microballoon put in ball mill ball milling uniformly after, use ethanol solution ultrasonic disperse, after drying, with emulsion acrylic resin, sprayed in its surface, after continuously stirred 10-30min, be dried, obtain mixture.
G., hydrotropism's polyaminoester emulsion adds step e gained intermediate, step f gained mixture and ethyl acrylate, citric acid, stirs.
3. one antibacterial aqueous polyurethane luminous reflecting road mark paint described in and preparation method thereof, it is characterised in that reactor used by step b is polytetrafluoroethyllining lining stainless steel cauldron, capacity is 15-25mL.
4. one antibacterial aqueous polyurethane luminous reflecting road mark paint described in and preparation method thereof, it is characterised in that centrifuge speed used by step c is 5000-10000r/min, centrifugal 10-15min.
The invention has the beneficial effects as follows:Aqueous polyurethane coating disclosed by the invention has saving resource, reduces pollution, the feature of low toxic and environment-friendly, utilize Study of Nanoscale Rare Earth Luminescent Materials to improve aqueous polyurethane coating luminescent properties simultaneously, its section being more suitable for illuminating effect is bad is made to apply, reduce road safety hidden danger, pedestrian and vehicle safety are ensured, further, add the glass microballoon that reflecting effect is good, higher glistening intensity can be obtained.This coating glue viscosity is good, and ageing resistance is excellent, easy construction, less demanding to the cleaning degree of drying on road surface during construction, is generally applicable to various road surface, has good promotional value；Process inorganic matter raw material with emulsion acrylic resin, enhance the mobility between raw material and masking liquid and amalgamation, thus improve the adhesive force of coating；Coordinate the nanometer silver added, make coating have the performance that sterilization is antibacterial.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment
A kind of antibacterial aqueous polyurethane luminous reflecting road mark paint, it is characterised in that be made up of the raw material of following weight portion:
Nanometer silver 3, GdCl3
3, Mg (OH)2 2, ethylene glycol 10, NaF 3, aqueous polyurethane emulsion 50, ethyl acrylate 5, citric acid 3, titanium dioxide 15, blanc fixe 15, glass microballoon 15, emulsion acrylic resin is appropriate, and deionized water is appropriate, appropriate amount of ethanol；
The content of described aqueous polyurethane emulsion is 40-50%.
Described one antibacterial aqueous polyurethane luminous reflecting road mark paint and preparation method thereof, it is characterised in that be made up of following steps:
a.
By GdCl3It is dissolved in 3-5 part ethylene glycol solution, stirs to clarify solution；
B. NaF is dissolved in residue ethylene glycol solution, after stirring to clarify solution, mixes with step a gained settled solution rapidly, stir；
c.
In step b gained liquid, add sodium lauryl sulphate, move in reactor, put into 20-25h in 150-200 DEG C of baking oven.
d.
Take out reactor after having reacted, be cooled to room temperature, after separating with centrifuge, be filtrated to get precipitation, precipitate 3-5 time by deionized water and washing with alcohol respectively；
e.
It is dried 20-25h under the conditions of step d gained is deposited in 40-80 DEG C, obtains intermediate；
F. by nanometer silver, Mg (OH)2 、Titanium dioxide, blanc fixe, glass microballoon put in ball mill ball milling uniformly after, use ethanol solution ultrasonic disperse, after drying, with emulsion acrylic resin, sprayed in its surface, after continuously stirred 10-30min, be dried, obtain mixture.
G., hydrotropism's polyaminoester emulsion adds step e gained intermediate, step f gained mixture and ethyl acrylate, citric acid, stirs.
Described one antibacterial aqueous polyurethane luminous reflecting road mark paint and preparation method thereof, it is characterised in that reactor used by step b is polytetrafluoroethyllining lining stainless steel cauldron, capacity is 15-25mL.
Described one antibacterial aqueous polyurethane luminous reflecting road mark paint and preparation method thereof, it is characterised in that centrifuge speed used by step c is 5000-10000r/min, centrifugal 10-15min.
This coating property:
Outward appearance: do not lump, it is easy to stirring；
Workability: good；
Do not glue tire drying time :≤15min.
Claims (4)
1. an antibacterial aqueous polyurethane luminous reflecting road mark paint, it is characterised in that be made up of the raw material of following weight portion:
Nanometer silver 1-3, GdCl3
1-3, Mg (OH)2 1-2, ethylene glycol 6-10, NaF 1-3, aqueous polyurethane emulsion 40-50, ethyl acrylate 3-5, citric acid 1-3, titanium dioxide 10-15, blanc fixe 10-15, glass microballoon 10-15, emulsion acrylic resin is appropriate, and deionized water is appropriate, appropriate amount of ethanol；
The content of described aqueous polyurethane emulsion is 40-50%, and emulsion acrylic resin solid content is 20-40%.
One the most according to claim 1 antibacterial aqueous polyurethane luminous reflecting road mark paint and preparation method thereof, it is characterised in that be made up of following steps:
a.
By GdCl3It is dissolved in 3-5 part ethylene glycol solution, stirs to clarify solution；
B. NaF is dissolved in residue ethylene glycol solution, after stirring to clarify solution, mixes with step a gained settled solution rapidly, stir；
c.
In step b gained liquid, add sodium lauryl sulphate, move in reactor, put into 20-25h in 150-200 DEG C of baking oven；
d.
Take out reactor after having reacted, be cooled to room temperature, after separating with centrifuge, be filtrated to get precipitation, precipitate 3-5 time by deionized water and washing with alcohol respectively；
e.
It is dried 20-25h under the conditions of step d gained is deposited in 40-80 DEG C, obtains intermediate；
F. by nanometer silver, Mg (OH)2 、Titanium dioxide, blanc fixe, glass microballoon put in ball mill ball milling uniformly after, use ethanol solution ultrasonic disperse, after drying, with emulsion acrylic resin, sprayed in its surface, after continuously stirred 10-30min, be dried, obtain mixture；
G., hydrotropism's polyaminoester emulsion adds step e gained intermediate, step f gained mixture and ethyl acrylate, citric acid, stirs.
One the most according to claim 2 antibacterial aqueous polyurethane luminous reflecting road mark paint and preparation method thereof, it is characterised in that reactor used by step b is polytetrafluoroethyllining lining stainless steel cauldron, capacity is 15-25mL.
One the most according to claim 2 antibacterial aqueous polyurethane luminous reflecting road mark paint and preparation method thereof, it is characterised in that centrifuge speed used by step c is 5000-10000r/min, centrifugal 10-15min.