CN105949966B - The special UV coating of PP base materials - Google Patents
The special UV coating of PP base materials Download PDFInfo
- Publication number
- CN105949966B CN105949966B CN201610452756.9A CN201610452756A CN105949966B CN 105949966 B CN105949966 B CN 105949966B CN 201610452756 A CN201610452756 A CN 201610452756A CN 105949966 B CN105949966 B CN 105949966B
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- special
- base materials
- adhesion promoter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to the top coat formulation design field of polypropylene plastics packing container industry product, particularly a kind of special UV coating of PP base materials, the coating includes：Two degree of functionality epoxy acrylates, three-functionality-degree urethane acrylate, monomer, initiator, adhesion promoter, levelling agent and diluent.The paint film of the UV coating of the present invention has preferable caking property, hardness and richness；The addition of adhesion promoter, it may be such that the overall adhesion property of paint film is excellent, UV paint films curing rate control (3kw ultraviolets mercury lamp) in 6 seconds is fully cured, it disclosure satisfy that printing streamline production efficiency demand, it is adapted to the covering with paint of PP products, simultaneously suitable for the field in the printing of the container of packing container field, the especially material containing PP.
Description
Technical field
It is special the present invention relates to the top coat formulation design field of polypropylene (PP) plastic packaging containers industry product
It is not a kind of special UV coating of PP base materials.
Background technology
Polypropylene (PP) material is a kind of amorphous polymer with good combination property, be widely used in packaging,
The fields such as household electrical appliances, food, toy, medical treatment.Because PP surfaces are difficult to soak, solvent resistance is strong, and the attachment of all kinds of coating is all present
Certain adhesion problem, UV are coating material solidified no exception.The coating material solidified coatings applied to plastic bottom material of UV are had a variety of
Advantage, but still suffer from many problems have it is to be solved, such as：1) coloring is difficult；2) adhesion problem, UV coating material solidified moments consolidate
Change, it is short to ground infiltrating time, cause poor adhesive force；3) shape issue of object is solidified, complicated shape, dash area solidification are not
Completely.A kind of coloring of exploitation is easy, the special UV coating of the preferable PP base materials of adhesive force is that those skilled in the art will currently study
Technical problem.
The content of the invention
The technical problems to be solved by the invention are：Exist for PP material products surface of the prior art with UV coating
The problem of, propose that one kind colours easy, the special UV coating of the preferable PP base materials of adhesive force.
The technical solution adopted for the present invention to solve the technical problems is：A kind of special UV coating of PP base materials, by weight
Number meter, the coating include：
Two degree of functionality epoxy acrylate 5-10 parts；
Three-functionality-degree urethane acrylate 4-8 parts；
Monomer 15-30 parts；
Initiator 2-5 parts；
Adhesion promoter 0.5-2 parts；
Levelling agent 0.5-2 parts；
Diluent 30-50 parts；The monomer is the propylene diluted acid ester of diethylene glycol phthalate two, hexanediyl
Ester and trimethylolpropane trimethacrylate according to mass ratio 1：(0.5-0.88)：The mixture that (0.7-0.99) is formed.
Further, the initiator is 4- chlorobenzophenones, alpha-hydroxyalkyl benzophenone, α-amine alkyl phenones, 2- hydroxyl -2- first
One kind in base -1- phenyl -1- acetone or 1- hydroxy-cyclohexan alkyl-phenyl ketone.
Further, the diluent is one kind in n-butanol, ethyl acetate or methylisobutylketone.
Further, the adhesion promoter includes each component of following ratio of weight and number：Cyclohexanone 65-75 parts；The third two
Alcohol methyl ether acetate 8-12 parts；Chlorinated polypropylene 8-12 parts；N-cyclohexylmaleimide2-3 parts；Acryloyl morpholine2-3 parts.
Further, the chlorinated polypropylene, chlorinty are 25~35%, viscous in 25 DEG C, 20% toluene solution
It is 5.0~7.0 to spend for 1000~1800mpas, pH value.
Further, the one kind of the levelling agent in dimethyl polysiloxane copolymer, polysiloxane-polyether copolymer
Or two kinds of combination.
Further, the preparation method of the adhesion promoter comprises the following steps：
(1) cyclohexanone, propylene glycol methyl ether acetate are mixed to dispersed, obtains A group raw materials；
(2) by the A group raw materials of chlorinated polypropylene, and 1/3, it is stirred until homogeneous scattered after mixing, obtains B groups original
Material；
(3) by N-cyclohexylmaleimide and acryloyl morpholine and 1/3 A group raw materials, mix, while temperature is adjusted
Up to 55-65 DEG C, continue 40-60min, obtain C group raw materials；
(4) in remaining A groups raw material, B group raw materials is sequentially added into, C group raw materials, are stirred during addition
Mix, while temperature is adjusted to 40-50 DEG C, continues 25-40min, obtains finished product.
A kind of preparation method of the special UV coating of PP base materials, the preparation method include following preparation process：
(1) count in parts by weight, prepare two degree of functionality epoxy acrylate 5-10 parts；Three-functionality-degree urethane acrylate
4-8 parts；Monomer 15-30 parts；Initiator 2-5 parts；Adhesion promoter 0.5-2 parts；Levelling agent 0.5-2 parts；Diluent 30-50
Part；The monomer is the propylene diluted acid ester of diethylene glycol phthalate two, hexanediyl ester and trimethylolpropane tris third
Olefin(e) acid ester according to mass ratio 1：(0.5-0.88)：The mixture that (0.7-0.99) is formed；
(2) two degree of functionality epoxy acrylates, three-functionality-degree urethane acrylate, monomer are sequentially added into reactor
Diluent with 50%, is stirred to uniform；
(3) adhesion promoter and levelling agent are added into above-mentioned mixed liquor, is stirred to uniform；
(4) monomer and remaining diluent are added into above-mentioned mixed liquor, stir to obtain the special UV coating of PP base materials.
The defoamer of 0.4-0.9 parts by weight can also be added in the above-mentioned formula of the present invention when necessary, defoamer is optional
Polysiloxane macromolecule or polyether-modified dimethyl polysiloxane copolymer；The inhibition of 0.2-0.6 parts by weight can also be added
Agent, the polymerization inhibitor are selected from MEHQ, hydroquinones or 2,6- toluene di-tert-butyl phenol.
The present invention can change the close of PP frostings by using above-mentioned component formula, the adhesion promoter of gained
Degree, as adhered to one layer of extremely strong double faced adhesive tape in PP frostings, for bonding the coating of PP frostings and surface, so as to
The PP surfaces that are bonded in for enabling coating strong are not easy to peel off.
Beneficial effect：The paint film of the UV coating of the present invention has preferable caking property, hardness and richness；Adhesive force promotes
The addition of agent, it may be such that the overall adhesion property of paint film is excellent, UV paint films curing rate control (3kw ultraviolet mercury in 6 seconds
Lamp) it is fully cured, it disclosure satisfy that printing streamline production efficiency demand；Once offline qualification rate more than 98%；Primary coating is consolidated
Rate is more than 96%；Hundred lattice experiment (carrying out firmness detection according to GB9286-88) is one-level, i.e., involved area is 5%
Below；After solidification more than hardness of film 3H；The formula of the UV coating of the present invention is adapted to the covering with paint of PP products, while suitable for wrapping
The print field of the container in packaging container field, the especially material containing PP.
Embodiment
With reference to specific embodiment, the present invention will be further described, but the present invention is not limited to following embodiments.
Embodiment one
A kind of preparation method of the special UV coating of PP base materials, the preparation method include following preparation process：
(1) count in parts by weight, prepare 10 parts of two degree of functionality epoxy acrylate；Three-functionality-degree urethane acrylate 8
Part；30 parts of monomer；4.5 parts of initiator；1.5 parts of adhesion promoter；2 parts of levelling agent；50 parts of diluent；
The monomer is the propylene diluted acid ester of diethylene glycol phthalate two, hexanediyl ester and trimethylolpropane
Triacrylate according to mass ratio 1：0.8：0.9 mixture formed；Initiator is 4- chlorobenzophenones, and diluent is positive fourth
Alcohol, levelling agent are selected from dimethyl polysiloxane copolymer,
Adhesion promoter includes each component of following ratio of weight and number：75 parts of cyclohexanone；Propylene glycol methyl ether acetate 12
Part；12 parts of chlorinated polypropylene；2.5 parts of N-cyclohexylmaleimide；2.5 parts of acryloyl morpholine.By cyclohexanone, propane diols first
Ether acetate mixes to dispersed, obtains A group raw materials；By the A group raw materials of chlorinated polypropylene, and 1/3, mixing
After be stirred until homogeneous scattered, obtain B group raw materials；By N-cyclohexylmaleimide, acryloyl morpholine and 1/3 A group raw materials, mix
Stirring is closed, while temperature is heightened to 55-65 DEG C, is continued 40-60min, is obtained C group raw materials；In remaining A groups raw material, respectively
B group raw materials are sequentially added, C group raw materials, are stirred during addition, while temperature is adjusted to 40-50 DEG C, continues 25-
40min, obtain adhesion promoter finished product；
(2) two degree of functionality epoxy acrylates, three-functionality-degree urethane acrylate, monomer are sequentially added into reactor
Diluent with 50%, is stirred to uniform；
(3) adhesion promoter and levelling agent are added into above-mentioned mixed liquor, is stirred to uniform；
(4) monomer and remaining diluent are added into above-mentioned mixed liquor, stir to obtain the special UV coating of PP base materials.
Embodiment two
A kind of preparation method of the special UV coating of PP base materials, the preparation method include following preparation process：
(1) count in parts by weight, prepare 8 parts of two degree of functionality epoxy acrylate；Three-functionality-degree urethane acrylate 6.5
Part；26 parts of monomer；3 parts of initiator；1.5 parts of adhesion promoter；1.5 parts of levelling agent；42 parts of diluent；
The monomer is the propylene diluted acid ester of diethylene glycol phthalate two, hexanediyl ester and trimethylolpropane
Triacrylate according to mass ratio 1：0.8：0.9 mixture formed；Initiator is 1- hydroxy-cyclohexan alkyl-phenyl ketone, dilute
It is methylisobutylketone to release agent, and levelling agent is selected from polysiloxane-polyether copolymer,
Adhesion promoter includes each component of following ratio of weight and number：75 parts of cyclohexanone；Propylene glycol methyl ether acetate 12
Part；12 parts of chlorinated polypropylene；3 parts of N-cyclohexylmaleimide；3 parts of acryloyl morpholine.By cyclohexanone, propylene glycol monomethyl ether vinegar
Acid esters mixes to dispersed, obtains A group raw materials；By the A group raw materials of chlorinated polypropylene, and 1/3, stirred after mixing
Mix to dispersed, obtain B group raw materials；N-cyclohexylmaleimide, acryloyl morpholine and 1/3 A group raw materials, mixing are stirred
Mix, while temperature is heightened to 55-65 DEG C, is continued 40-60min, is obtained C group raw materials；In remaining A groups raw material, respectively successively
B group raw materials are added, C group raw materials, are stirred during addition, while temperature is adjusted to 40-50 DEG C, continues 25-40min, obtains
To adhesion promoter finished product；Remaining step is the same as embodiment one.
Embodiment three
A kind of preparation method of the special UV coating of PP base materials, the preparation method include following preparation process：
(1) count in parts by weight, prepare 6 parts of two degree of functionality epoxy acrylate；Three-functionality-degree urethane acrylate 5.5
Part；20 parts of monomer；2.5 parts of initiator；1 part of adhesion promoter；0.8 part of levelling agent；32 parts of diluent；
The monomer is the propylene diluted acid ester of diethylene glycol phthalate two, hexanediyl ester and trimethylolpropane
Triacrylate according to mass ratio 1：0.88：0.99 mixture formed；Initiator is 1- hydroxy-cyclohexan alkyl-phenyl ketone,
Diluent is methylisobutylketone, and levelling agent is dimethyl polysiloxane copolymer and polysiloxane-polyether copolymer according to weight
Than 1:0.5 mixture formed,
Adhesion promoter includes each component of following ratio of weight and number：70 parts of cyclohexanone；Propylene glycol methyl ether acetate 10
Part；10 parts of chlorinated polypropylene；2.5 parts of N-cyclohexylmaleimide；2.5 parts of acryloyl morpholine.By cyclohexanone, propane diols first
Ether acetate mixes to dispersed, obtains A group raw materials；By the A group raw materials of chlorinated polypropylene, and 1/3, mixing
After be stirred until homogeneous scattered, obtain B group raw materials；By N-cyclohexylmaleimide, acryloyl morpholine and 1/3 A group raw materials, mix
Stirring is closed, while temperature is heightened to 55-65 DEG C, is continued 40-60min, is obtained C group raw materials；In remaining A groups raw material, respectively
B group raw materials are sequentially added, C group raw materials, are stirred during addition, while temperature is adjusted to 40-50 DEG C, continues 25-
40min, obtain adhesion promoter finished product；Remaining step is the same as embodiment one.
Example IV
A kind of preparation method of the special UV coating of PP base materials, the preparation method include following preparation process：
(1) count in parts by weight, prepare 5 parts of two degree of functionality epoxy acrylate；Three-functionality-degree urethane acrylate 4
Part；15 parts of monomer；2 parts of initiator；1 part of adhesion promoter；0.8 part of levelling agent；32 parts of diluent；
The monomer is the propylene diluted acid ester of diethylene glycol phthalate two, hexanediyl ester and trimethylolpropane
Triacrylate according to mass ratio 1：0.88：0.99 mixture formed；Initiator is 1- hydroxy-cyclohexan alkyl-phenyl ketone,
Diluent is methylisobutylketone, and levelling agent is dimethyl polysiloxane copolymer and polysiloxane-polyether copolymer according to weight
Than 1:0.7 mixture formed,
Adhesion promoter includes each component of following ratio of weight and number：65 parts of cyclohexanone；Propylene glycol methyl ether acetate 12
Part；12 parts of chlorinated polypropylene；2 parts of N-cyclohexylmaleimide；3 parts of acryloyl morpholine.By cyclohexanone, propylene glycol monomethyl ether vinegar
Acid esters mixes to dispersed, obtains A group raw materials；By the A group raw materials of chlorinated polypropylene, and 1/3, stirred after mixing
Mix to dispersed, obtain B group raw materials；N-cyclohexylmaleimide, acryloyl morpholine and 1/3 A group raw materials, mixing are stirred
Mix, while temperature is heightened to 55-65 DEG C, is continued 40-60min, is obtained C group raw materials；In remaining A groups raw material, respectively successively
B group raw materials are added, C group raw materials, are stirred during addition, while temperature is adjusted to 40-50 DEG C, continues 25-40min, obtains
To adhesion promoter finished product；Remaining step is the same as embodiment one.
UV coating obtained by above-described embodiment is subjected to dependence test, test result is as follows：Curing of coating speed controls
(3kw ultraviolets mercury lamp) is fully cured in 6 seconds；Once offline qualification rate more than 98%；Primary coating curing degree 96% with
On；Hundred lattice experiment (carrying out firmness detection according to GB9286-88) is one-level, i.e., involved area is below 5%；Applied after solidification
More than film hardness 3H.
Claims (5)
1. a kind of special UV coating of PP base materials, it is characterized in that：Count in parts by weight, the coating includes：
Two degree of functionality epoxy acrylate 5-10 parts；
Three-functionality-degree urethane acrylate 4-8 parts；
Monomer 15-30 parts；
Initiator 2-5 parts；
Adhesion promoter 0.5-2 parts；
Levelling agent 0.5-2 parts；
Diluent 30-50 parts；The monomer be the propylene diluted acid ester of diethylene glycol phthalate two, hexanediyl ester and
Trimethylolpropane trimethacrylate according to mass ratio 1：(0.5-0.88)：The mixture that (0.7-0.99) is formed；
The adhesion promoter includes each component of following ratio of weight and number：Cyclohexanone 65-75 parts；Propylene glycol methyl ether acetate
8-12 parts；Chlorinated polypropylene 8-12 parts；N-cyclohexylmaleimide 2-3 parts；Acryloyl morpholine 2-3 parts.
2. the special UV coating of a kind of PP base materials according to claim 1, it is characterized in that：The initiator is 4- chlorodiphenyl first
Ketone, alpha-hydroxyalkyl benzophenone, α-amine alkyl phenones, 2- hydroxy-2-methyl -1- phenyl -1- acetone or 1- hydroxy-cyclohexans alkyl-benzene
One kind in base ketone.
3. the special UV coating of a kind of PP base materials according to claim 1, it is characterized in that：The diluent is n-butanol, second
One kind in acetoacetic ester or methylisobutylketone.
4. the special UV coating of a kind of PP base materials according to claim 1, it is characterized in that：The chlorinated polypropylene, contains
Chlorine dose is 25~35%, and the viscosity in 25 DEG C, 20% toluene solution is 1000~1800mpas, and pH value is 5.0~7.0.
5. the special UV coating of a kind of PP base materials according to claim 1, it is characterized in that：The levelling agent gathers selected from dimethyl
The combination of one or both of silicone copolymers, polysiloxane-polyether copolymer.